Hydrogen Production by Steam Reforming of Ethanol on Rh-Pt Catalysts: Influence of CeO2, ZrO2, and La2O3 as Supports

CeO2-, ZrO2-, and La2O3-supported Rh-Pt catalysts were tested to assess their ability to catalyze the steam reforming of ethanol (SRE) for H2 production. SRE activity tests were performed using EtOH:H2O:N2 (molar ratio 1:3:51) at a gaseous space velocity of 70,600 h−1 between 400 and 700 °C at atmospheric pressure. The SRE stability of the catalysts was tested at 700 °C for 27 h time on stream under the same conditions. RhPt/CeO2, which showed the best performance in the stability test, also produced the highest H2 yield above 600 °C, followed by RhPt/La2O3 and RhPt/ZrO2. The fresh and aged catalysts were characterized by TEM, XPS, and TGA. The higher H2 selectivity of RhPt/CeO2 was ascribed to the formation of small (~5 nm) and stable particles probably consistent of Rh-Pt alloys with a Pt surface enrichment. Both metals were oxidized and acted as an almost constant active phase during the stability test owing to strong metal-support interactions, as well as the superior oxygen mobility of the support. The TGA results confirmed the absence of carbonaceous residues in all the aged catalysts.

Metal and precursor effect during 1-heptyne selective hydrogenation using an activated carbon as support

Palladium, platinum, and ruthenium supported on activated carbon were used as catalysts for the selective hydrogenation of 1-heptyne, a terminal alkyne. All catalysts were characterized by temperature programmed reduction, X-ray diffraction, transmission electron microscopy, and X-ray photoelectron spectroscopy. TPR and XPS suggest that the metal in all catalysts is reduced after the pretreatment with H2 at 673 K. The TPR trace of the PdNRX catalyst shows that the support surface groups are greatly modified as a consequence of the use of HNO3 during the catalyst preparation. During the hydrogenation of 1-heptyne, both palladium catalysts were more active and selective than the platinum and ruthenium catalysts. The activity order of the catalysts is as follows: PdClRX > PdNRX > PtClRX ≫ RuClRX. This superior performance of PdClRX was attributed in part to the total occupancy of the d electronic levels of the Pd metal that is supposed to promote the rupture of the H2 bond during the hydrogenation reaction. The activity differences between PdClRX and PdNRX catalysts could be attributed to a better accessibility of the substrate to the active sites, as a consequence of steric and electronic effects of the superficial support groups. The order for the selectivity to 1-heptene is as follows: PdClRX = PdNRX > RuClRX > PtClRX, and it can be mainly attributed to thermodynamic effects.

Methane dry reforming over Ni supported on pine sawdust activated carbon: Effects of support surface properties and metal loading

The influence of metal loading and support surface functional groups (SFG) on methane dry reforming (MDR) over Ni catalysts supported on pine-sawdust derived activated carbon were studied. Using pine sawdust as the catalyst support precursor, the smallest variety and lowest concentration of SFG led to best Ni dispersion and highest catalytic activity, which increased with Ni loading up to 3 Ni atoms nm-2. At higher Ni loading, the formation of large metal aggregates was observed, consistent with a lower "apparen" surface area and a decrease in catalytic activity. The H2/CO ratio rose with increasing reaction temperature, indicating that increasingly important side reactions were taking place in addition to MDR.

Physico-chemical characterization of metal-doped bone chars and their adsorption behavior for water defluoridation

New bone chars for fluoride adsorption from drinking water have been synthetized via metallic doping using aluminum and iron salts. A detailed statistical analysis of the metal doping process using the signal-to-noise ratios from Taguchi's experimental designs and its impact on the fluoride adsorption properties of modified bone chars have been performed. The best conditions, including the proper metallic salt, for metal doping were identified to improve the fluoride uptakes of modified bone chars. Results showed that the fluoride adsorption properties of bone chars can be enhanced up to 600% using aluminum sulfate for the surface modification. This aluminum-based adsorbent showed an adsorption capacity of 31 mg/g, which outperformed the fluoride uptakes reported for several adsorbents. Surface interactions involved in the defluoridation process were established using FTIR, DRX and XPS analysis. Defluoridation using the metal-doped bone chars occurred via an ion exchange process between fluoride ions and the hydroxyl groups on the adsorbent surface, whereas the Al(OH)xFy, FexFy, and CaF2 interactions could play also an important role in the removal process. These metal-doped adsorbents anticipate a promising behavior in water treatment, especially in developing countries where the efficiency – cost tradeoff is crucial for implementing new defluoridation technologies.

Molecular signature of highly conductive metal-molecule-metal junctions

The simplicity of single-molecule junctions based on direct bonding of a small molecule between two metallic electrodes makes them an ideal system for the study of fundamental questions related to molecular electronics. Here we study the conductance properties of six different types of molecules by suspending individual molecules between Pt electrodes. All the molecular junctions show a typical conductance of about 1G0 which is ascribed to the dominant role of the Pt contacts. However, despite the metalliclike conductivity, the individual molecular signature is well expressed by the effect of molecular vibrations in the inelastic contribution to the conductance.

VO: a strongly correlated metal close to a Mott-Hubbard transition

Here, we present experimental and computational evidences to support that rocksalt cubic VO is a strongly correlated metal with non-Fermi-liquid thermodynamics and an unusually strong spin-lattice coupling. An unexpected change of sign of metallic thermopower with composition is tentatively ascribed to the presence of a pseudogap in the density of states. These properties are discussed as signatures of the proximity to a magnetic quantum phase transition. The results are summarized in an electronic phase diagram for the 3d monoxides, which resembles that of other strongly correlated systems. The structural and electronic simplicity of 3d monoxides makes them ideal candidates to progress in the understanding of highly correlated electron systems.

Effect of the metal in the production of pollutants during the decomposition of two types of electric wires

Support for this work was provided by the Generalitat Valenciana (Spain) with projects PROMETEO/2009/043/FEDER, and by the Spanish MCT CTQ2008-05520.

Metal-complex ionosilicas: Cationic mesoporus silica with Ni(II) and Cu(II) complexes in their framework

Metal-complex ionosilicas with cationic complexes into the mesoporous silica framework were prepared using anionic surfactants. The electrostatic interaction between the anionic surfactant and the cationic metal complexes incorporated in the silica framework allows for the fine tuning of the mesoporous structure. The gentle procedure of synthesis developed and mild ion-exchange extraction of the surfactant, allowed a cleaner route for the immobilization of homogeneous cationic catalysts in mesoporous silica, while protecting the structural and chemical integrity of the metal complexes.

Low metal content Co and Ni alumina supported catalysts for the CO2 reforming of methane

Low metal content Co and Ni alumina supported catalysts (4.0, 2.5 and 1.0 wt% nominal metal content) have been prepared, characterized (by ICP-OES, TEM, TPR-H2 and TPO) and tested for the CO2 reforming of methane. The objective is to optimize the metal loading in order to have a more efficient system. The selected reaction temperature is 973 K, although some tests at higher reaction temperature have been also performed. The results show that the amount of deposited carbon is noticeably lower than that obtained with the Co and Ni reference catalysts (9 wt%), but the CH4 and CO2 conversions are also lower. Among the catalysts tested, the Co(1) catalyst (the value in brackets corresponds to the nominal wt% loading) is deactivated during the first minutes of reaction because CoAl2O4 is formed, while Ni(1) and Co(2.5) catalysts show a high specific activity for methane conversion, a high stability and a very low carbon deposition.

Decomposition of two types of electric wires considering the effect of the metal in the production of pollutants

Combustion runs at 700 °C in a horizontal laboratory furnace were carried out on two different electric wires (PVC and halogen-free wire). Tests were performed in the presence and in the absence of the metal conductor of the wires. The analyses of the polycyclic aromatic hydrocarbons (PAHs), chlorobenzenes (CBzs), chlorophenols (CPhs), mono- to octa-chlorodibenzo-p-dioxin and dibenzofurans (PCDD/Fs), and dioxin-like PCBs are shown. Regarding semivolatile compounds, PAHs production decreases in the presence of metal, while a higher amount of chlorinated compounds are emitted. Respect to the PCDD/Fs, the PVC wire in the presence of metal presents the highest emission, with a much more emission of furans than dioxins. The maximum emission is with 2 or 3 chlorine atom PCDD/Fs. PCBs emission correlates with PCDD/F production and represents 3–4% of total toxicity, determined by using WHO2005 factors.

Pollutant emissions during pyrolysis and combustion of waste printed circuit boards, before and after metal removal

The constant increase in the production of electronic devices implies the need for an appropriate management of a growing number of waste electrical and electronic equipment. Thermal treatments represent an interesting alternative to recycle this kind of waste, but particular attention has to be paid to the potential emissions of toxic by-products. In this study, the emissions from thermal degradation of printed circuit boards (with and without metals) have been studied using a laboratory scale reactor, under oxidizing and inert atmosphere at 600 and 850 °C. Apart from carbon oxides, HBr was the main decomposition product, followed by high amounts of methane, ethylene, propylene, phenol and benzene. The maximum formation of PAHs was found in pyrolysis at 850 °C, naphthalene being the most abundant. High levels of 2-, 4-, 2,4-, 2,6- and 2,4,6-bromophenols were found, especially at 600 °C. Emissions of PCDD/Fs and dioxin-like PCBs were quite low and much lower than that of PBDD/Fs, due to the higher bromine content of the samples. Combustion at 600 °C was the run with the highest PBDD/F formation: the total content of eleven 2,3,7,8-substituted congeners (tetra- through heptaBDD/Fs) was 7240 and 3250 ng WHO2005-TEQ/kg sample, corresponding to the sample with and without metals, respectively.

Effect of the surface chemical groups of activated carbons on their surface adsorptivity to aromatic adsorbates based on π-π interactions

Three activated carbons with different surface chemical groups were used to analyse the influence of these groups on their adsorption capacities towards aromatic-type molecules whose adsorption is based on π-π interactions with surface arene centres. The three activated carbons studied were a low-functionalized carbon (Merck), an oxygen-rich carbon obtained by HNO3 oxidation of Merck, and a nitrogen-rich carbon also prepared from Merck by mild HNO3 oxidation followed by treatment with a dicyanodiamide/dimethyl formamide mixture at 300 °C. The nature of the surface chemical groups of the three activated carbons was investigated by both physical and chemical techniques (TPD, XPS, Boehm analysis and pH potentiometric titration). A systematic study of the adsorptions of a series of analogous aromatic adsorbates on the three activated carbons was carried out to study the adsorption mechanisms. In all cases the adsorption mechanism is based on π-π interactions between the aromatic moiety of the adsorbates and the arene centres of the graphite sheets. The differences in the normalized adsorption capacities of the adsorbents for a set of adsorbates indicate that the π-donor or π-withdrawing character of the functional groups have a clear influence on the basicity of the arene centres.

Non-covalent immobilization of RhDuphos on carbon nanotubes and carbon xerogels

The immobilization of the chiral complex RhDuphos, by electrostatic or π–π (adsorption) interactions, on carbon nanotubes and carbon xerogels is investigated. To promote such interactions, the supports were either oxidized or heat treated to create carboxylic type surface groups or an apolar surface, respectively. The catalysts were tested in the hydrogenation of methyl 2-acetamidoacrylate. The prepared hybrid catalysts are less active than the homogeneous RhDuphos, but most of them show a high enantioselectivity and the one prepared with the oxidized carbon xerogel is also reusable, being able to give a high substrate conversion, keeping as well a high enantioselectivity. The anchorage by electrostatic interactions is more interesting than the anchorage by π–π interactions, as the π–π adsorption method produces a modification of the metal complex structure leading to an active hybrid catalyst but without enantioselectivity. The creation of carboxylic groups on the support surface has led to some hindering of the complex leaching.

Effects of Ultrasound Irradiation on the Synthesis of Metal Oxide Nanostructures

High intensity ultrasound can be used for the production of novel nanomaterials, including metal oxides. According to previous works in this field, the most notable effects are consequence of acoustic cavitation. In this context, we have studied the preparation of different materials in the presence of ultrasound, including N-doped TiO2 nanopowder, NiTiO3 nanorods and MnOx thin films. Ultrasound did not show a significant effect in all the cases. Exclusively for NiTiO3 nanorods a reduction of the final particle size occurs upon ultrasonic irradiation. From these results, it can be concluded that the ultrasound irradiation does not always play a key role during the synthesis of metal oxides. The effects seem to be particularly relevant in those cases where mass transport is highly hindered and in those procedures that require the rupture of nanoparticle aggregates to obtain a homogenous dispersion.