3 resultados para Fluoride adsorption

em Universidad de Alicante


Relevância:

70.00% 70.00%

Publicador:

Resumo:

This study describes a new synthesis route for bone chars using a CO2 atmosphere and their behavior as adsorbent for fluoride removal from water. Specifically, we have performed a detailed analysis of the adsorption properties of bone char samples obtained at different carbonization conditions and a comparative study with samples of bone char obtained via pyrolysis under nitrogen. Experimental results show that the nature of the gas atmosphere (CO2 versus N2) and the carbonization temperature play a major role to achieve an effective bone char for water defluoridation. In particular, the best adsorption properties of bone char for fluoride removal are obtained with those samples synthesized at 700 °C. Carbonization temperatures above 700 °C under CO2 atmosphere cause the dehydroxylation of the hydroxyapatite in the bone char, thus reducing its fluoride adsorption capacity. The maximum fluoride adsorption capacity for the bone char obtained in this study under CO2 atmosphere (i.e., 5.92 mg/g) is higher than those reported for commercial bone chars.

Relevância:

70.00% 70.00%

Publicador:

Resumo:

New bone chars for fluoride adsorption from drinking water have been synthetized via metallic doping using aluminum and iron salts. A detailed statistical analysis of the metal doping process using the signal-to-noise ratios from Taguchi's experimental designs and its impact on the fluoride adsorption properties of modified bone chars have been performed. The best conditions, including the proper metallic salt, for metal doping were identified to improve the fluoride uptakes of modified bone chars. Results showed that the fluoride adsorption properties of bone chars can be enhanced up to 600% using aluminum sulfate for the surface modification. This aluminum-based adsorbent showed an adsorption capacity of 31 mg/g, which outperformed the fluoride uptakes reported for several adsorbents. Surface interactions involved in the defluoridation process were established using FTIR, DRX and XPS analysis. Defluoridation using the metal-doped bone chars occurred via an ion exchange process between fluoride ions and the hydroxyl groups on the adsorbent surface, whereas the Al(OH)xFy, FexFy, and CaF2 interactions could play also an important role in the removal process. These metal-doped adsorbents anticipate a promising behavior in water treatment, especially in developing countries where the efficiency – cost tradeoff is crucial for implementing new defluoridation technologies.

Relevância:

60.00% 60.00%

Publicador:

Resumo:

This study evaluates the application of denim fiber scraps as a precursor for the synthesis of adsorbents for water treatment via pyrolysis and their application in water defluoridation. The best pyrolysis conditions for the synthesis of this novel adsorbent have been identified and a metal doping route with different salts of Al3 +, La3 + and Fe3 + was proposed to improve its fluoride adsorption behavior. Different spectroscopic and microscopic techniques (i.e., FTIR, XPS, XRF, SEM) were used to characterize the precursor and adsorbents, and to analyze the surface interactions involved in the fluoride removal mechanism. Experimental results showed that these adsorbents were effective for fluoride adsorption showing uptakes up to 4.25 mg/g. The Si-O–metal–F interactions appear to be highly relevant for the fluoride removal. This study highlights the potential of denim textile waste as a raw material for the production of added-value products, thus minimizing their associated disposal cost. It also shows the performance of denim textile waste as a precursor of adsorbents for addressing relevant environmental concerns such as fluoride pollution.