Synthesis and characterization of mesoporous nickel oxide and its application to electrochemical capacitor

Mesoporous Ni(OH)(2) was synthesized using cationic surfactant as template and urea as hydrolysis-controlling agent. Mesoporous NiO with centralized pore size distribution was obtained by calcining Ni(OH)(2) at different temperatures. The BET specific surface area reaches 477.7 m(2).g(-1) for NiO calcined at 523 K. Structure characterizations indicate the polycrystalline pore wall of mesoporous nickel oxide. The pore-formation mechanism is also deduced to be quasi-reverse micelle mechanism. Cyclic voltammetry shows the good capacitive behavior of these NiO samples due to its unique mesoporous structure when using large amount of NiO to fabricate electrode. Compared with NiO prepared by dip-coating and cathodic precipitation methods, this mesoporous NiO with controlled pore structure can be used in much larger amount to fabricate the electrode and still maintains high specific capacitance and good capacitive behavior.

Synthesis and electrochemical properties of mesoporous nickel oxide

Mesoporous Ni(OH)(2) is synthesized using sodium dodecyl sulfate as a template and urea as a hydrolysis-controlling agent. Mesoporous NiO with a centralized pore-size distribution is obtained by calcining Ni(OH)(2) at different temperatures. The BET specific surface area reaches 477.7 m(2) g(-1) for NiO calcined at 250 degreesC. Structure characterizations indicate a good mesoporous structure for the nickel oxide samples. Cyclic voltammetry shows the NiO to have good capacitive behaviour due to its unique mesoporous structure when using a large amount of NiO to fabricate the electrode. Compared with NiO prepared by dip-coating and cathodic precipitation methods, mesoporous NiO with a controlled pore structure can be used in much larger amounts to fabricate electrodes and still maintain a high specific capacitance and good capacitive behaviour. (C) 2004 Elsevier B.V. All rights reserved.

Biomolecular screening with novel organosilica microspheres

Organosilica microspheres synthesised via a novel surfactant-free emulsion-based method show applicability towards optical encoding, solid-phase synthesis and high-throughput screening of bound oligonucleotide and peptide sequences.

Carrier transport in PbS nanocrystal conducting polymer composites

In this letter we report the carrier mobilities in an inorganic nanocrystal: conducting polymer composite. The composite material in question (lead sulphide nanocrystals in the conducting polymer poly [2-methoxy-5-(2(')-ethyl-hexyloxy)-p-phenylene vinylene] (MEH-PPV) was made using a single-pot, surfactant-free synthesis. Mobilties were measured using time of flight techniques. We have found that the inclusion of PbS nanocrystals in MEH-PPV both balances and markedly increases the hole and electron mobilities-the hole mobility is increased by a factor of similar to 10(5) and the electron mobility increased by similar to 10(7) under an applied bias of 5 kV cm(-1). These results explain why dramatic improvements in electrical conductivity and photovoltaic performance are seen in devices fabricated from these composites.

Silica membrane reactors for hydrogen production from water gas shift

This paper presents an analysis of membrane reactor (MR) operation and design for enhanced hydrogen production from the water gas shift (WGS) reaction. It has been established that membrane reactors can enhance an equilibrium limited reaction through product separation. However, the detailed effects of reactor setup, membrane configuration and catalyst volume have yet to be properly analysed for this reaction. This paper investigates new ideas for membrane reactors such as the development of new catalytic films, for improved interaction between the reaction and separation zones. Current membrane reactors utilise a packed bed of catalyst within the membrane tube, utilising a large volume of catalyst to drive reaction. This is still inefficient and provides only limited benefits over conventional WGS reactors. New reactor configurations look to optimise the interactive effects between reaction and separation to provide improved operation. In this paper, thin film catalysts were produced using dip coating and spray coating techniques. This technique produced catalyst coatings with good thickness, though the abrasion strength of the dip coated catalyst was quite low. The catalyst was tested in a packed bed reactor for temperature activity at low temperatures and catalyst activity at varying levels of excess water

'Free' surfactant in gastric aspirates and bronchoalveolar lavage in children with and without reflux oesophagitis

Aim: Dipalmitoylphosphatidycholine (DPPC) is the characteristic and main constituent of surfactant. Adsorption of surfactant to epithelial surfaces may be important in the masking of receptors. The aims of the study were to (i) compare the quantity of free DPPC in the airways and gastric aspirates of children with gastroesophageal reflux disease (GORD) to those without and (ii) describe the association between free DPPC levels with airway cellular profile and capsaicin cough sensitivity. Methods: Children aged < 14 years were defined as 'coughers' if a history of cough in association with their GORD symptoms was elicited before gastric aspirates and nonbronchoscopic bronchoalveolar lavage (BAL) were obtained during elective flexible upper gastrointestinal endoscopy. GORD was defined as histological presence of reflux oesophagitis. Spirometry and capsaicin cough-sensitivity test was carried out in children aged > 6 years before the endoscopy. Results: Median age of the 68 children was 9 years (interquartile range (IQR) 7.2). Median DPPC level in BAL of children with cough (72.7 mu g/mL) was similar to noncoughers (88.5). There was also no significant difference in DPPC levels in both BAL and gastric aspirates of children classified according to presence of GORD. There was no correlation between DPPC levels and cellular counts or capsaicin cough-sensitivity outcome measures. Conclusion: We conclude that free DPPC levels in the airways and gastric aspirate is not influenced by presence of cough or GORD defined by histological presence of reflux oesophagitis. Whether quantification of adsorbed surfactant differs in these groups remain unknown. Free DPPC is unlikely to have a role in masking of airway receptors.

The influence of coating materials on some properties of alginate beads and survivability of microencapsulated probiotic bacteria

The probiotics, Lactobacillus acidophilus 547, Bifidobacterium bifidum ATCC 1994, and Lactobacillus casei 01, were encapsulated into uncoated calcium alginate beads and the same beads were coated with three types of material, chitosan, sodium alginate, and poly-L-lysine in combination with alginate. The thickness of the alginate beads increased with the addition of coating materials. No differences were detectable in the bead strength by texture analysis or in the thickness of the beads with different types of coating materials by transmission electron microscopy. The survivability of three probiotics in uncoated beads, coated beads, and as free cells (unencapsulated) was conducted in 0.6% bile salt solution and simulated gastric juice (pH 1.55) followed by incubation in simulated intestinal juice with and without 0.6% bile salt. Chitosan-coated alginate beads provided the best protection for L. acidophilus and L. casei in all treatments. However, B. bifidum did not survive the acidic conditions of gastric juice even when encapsulated in coated heads. (C) 2004 Elsevier Ltd. All rights reserved.

Postsynthesis stabilization of free-standing mesoporous silica films

Mixed ammonia-water vapor postsynthesis treatment provides a simple and convenient method for stabilizing mesostructured silica films. X-ray diffraction, transmission electron microscopy, nitrogen adsorption/desorption, and solid-state NMR (C-13, Si-29) were applied to study the effects of mixed ammonia-water vapor at 90 degreesC on the mesostructure of the films. An increased cross-linking of the silica network was observed. Subsequent calcination of the silica films was seen to cause a bimodal pore-size distribution, with an accompanying increase in the volume and surface area ratios of the primary (d = 3 nm) to secondary (d = 5-30 nm) pores. Additionally, mixed ammonia-water treatment was observed to cause a narrowing of the primary pore-size distribution. These findings have implications for thin film based applications and devices, such as sensors, membranes, or surfaces for heterogeneous catalysis.

Preparation of poly (alkylcyanoacrylate) nanoparticles by polymerization of water-free microemulsions

Phase diagrams of the pseudoternary systems ethyloleate, polyoxyethylene 20 sorbitan mono-oleate/sorbitan monolaurate and propylene glycol with and without butanol as a co-surfactant were prepared. Areas containing optically isotropic, one-phase systems were identified and samples therein designated as droplet, bicontinuous or solution type microemulsions using conductivity, viscosity and self-diffusion NMR. Nanoparticles were prepared by polymerization of selected microemulsions with ethyl-2-cyanoacrylate and the morphology of the particles was investigated. Addition of monomer to all types of microemulsions led to the formation of nanoparticles, which had an average size of 244 +/- 25 nm, an average polydispersity index of 0.15 +/- 0.04 and a zeta-potential of -17 +/- 3 mV. The formation of particles from water-free microemulsions of different types is surprising, particularly considering that polymerization is expected to occur at a water-oil interface by base-catalysed polymerization. It would appear that propylene glycol is sufficiently nucleophilic to initiate the polymerization. The use of water-free microemulsions as templates for the preparation of poly (alkylcyanoacrylate) nanoparticles opens up interesting opportunities for the encapsulation of bioactives which do not have suitable properties for encapsulation on the basis of water-containing microemulsions.

Postharvest characteristics and handling of litchi fruit - an overview

Litchi ( Litchi chinensis Sonn.) is a tropical to subtropical crop that originated in South-East Asia. Litchi fruit are prized on the world market for their flavour, semi-translucent white aril and attractive red skin. Litchi is now grown commercially in many countries and production in Australia, China, Israel, South Africa and Thailand has expanded markedly in recent years. Increased production has made significant contributions to economic development in these countries, especially those in South-East Asia. Non-climacteric litchi fruit are harvested at their visual and organoleptic optimum. They are highly perishable and, consequently, have a short life that limits marketability and potential expansion of demand. Pericarp browning and pathological decay are common and important defects of harvested litchi fruit. Postharvest technologies have been developed to reduce these defects. These technologies involve cooling and heating the fruit, use of various packages and packaging materials and the application of fungicides and other chemicals. Through the use of fungicides and refrigeration, litchi fruit have a storage life of about 30 days. However, when they are removed from storage, their shelf life at ambient temperature is very short due to pericarp browning and fruit rotting. Low temperature acclimation or use of chitsoan as a coating can extend the shelf life. Sulfur dioxide fumigation effectively reduces pericarp browning, but approval from Europe, Australia and Japan for this chemical is likely to be withdrawn due to concerns over sulfur residues in fumigated fruit. Thus, sulfur-free postharvest treatments that maintain fruit skin colour are increasingly important. Alternatives to SO2 fumigation for control of pericarp browning and fruit rotting are pre-storage pathogen management, anoxia treatment, and dipping in 2% hydrogen chloride solution for 6-8 min following storage at 0 degrees C. Insect disinfestation has become increasingly important for the expansion of export markets because of quarantine issues associated with some fruit fly species. Thus, effective disinfestation protocols need to be developed. Heat treatment has shown promise as a quarantine technology, but it injures pericarp tissue and results in skin browning. However, heat treatment can be combined with an acid dip treatment that inhibits browning. Therefore, the primary aim of postharvest litchi research remains the achievement of highly coloured fruit which is free of pests and disease. Future research should focus on disease control before harvest, combined acid and heat treatments after harvest and careful temperature management during storage and transport.