A novel method to prepare mesoporous nano-zirconia

A novel method to prepare mesoporous zirconia was developed. The synthesis was carried out in the presence of PEO surfactants via solid-state reaction. The materials exhibit strong diffraction peak at low 2-theta angle and their nitrogen adsorption/desorption isotherms are typical of IV type with H3 hysteresis loops. The pore structure examined by TEM can be described as wormhole domains. The tetragonal zirconia nanocrystals are uniform in size (around 1.5nm) and their pores center at around 4.6nm. The zirconia nanocrystal growth is mainly via an aggregation mechanism. This study also reveals that the PEO surfactants can interact with the Zr-O-Zr framework to reinforce the thermal stability of zirconia. The ratio of NaOH to ZrOCl2, crystallization and calcination temperature play an important role in the synthesis of mesoporous zirconia.

Synthesis and characterization of nano-hetero-structured dy doped CeO2 solid electrolytes using a combination of spark plasma sintering and conventional sintering

Doped ceria (CeO2) compounds are fluorite-type oxides that show oxide ionic conductivity higher than yttria-stabilized zirconia in oxidizing atmosphere. As a consequence of this, considerable interest has been shown in application of these materials for low (500 degrees-650 degrees C) temperature operation of solid oxide fuel cells (SOFCs). To improve the conductivity in dysprosium (Dy) doped CeO2, nano-size round shape particles were prepared using a coprecipitation method. The dense sintered bodies with small grain sizes (< 300 nm) were fabricated using a combined process of spark plasma sintering (SPS) and conventional sintering (CS). Dy-doped CeO2 sintered body with large grains (1.1 mu m) had large micro-domains. The conductivity in the sintered body was low (-3.2 S/cm at 500 degrees C). On the other hand, the conductivity in the specimens obtained by the combined process was considerably improved. The micro-domain size in the grain was minimized using the present process. It is concluded that the enhancement of conductivity in dense specimens produced by the combined process (SPS+CS) is attributable to the microstructural changes within the grains.

Momentum transfer effects in the transport of adsorbate at a nano-patterned surface

Adsorbate molecules scattered in the repulsive field of a surface feature in the form of a semi-cylindrical stripe may be considered as a simple model for a nano-patterned surface. The extent of scattering was conveniently expressed as the tangential momentum accommodation coefficient. An analytical result was obtained using a simple local specular reflection hypothesis in contrast to the more complicated situation of an array of atoms discussed elsewhere, in which screening and secondary reflection may occur (Nicholson and Bhatia 2005). It was also demonstrated that a simple 2D representation leads to the same result for the tangential momentum accommodation coefficient.

Nano-emulsion production by sonication and microfluidization - A comparison

The efficiency of sonication and microfluidization to produce nano-emulsions were evaluated in this study. The purpose was to produce an oil-in-water nano-emulsion of d-limonene to apply it in the next step for nano-particle encapsulation. In the entrapment and retention of volatiles or for the microencapsulation efficiency, emulsion size is one of the critical factors. In this study, a bench-top sonicator and an air-driven microfluidizer were used to prepare the emulsions. Results show that, while both methods were capable of producing nano-emulsions of the size range of 150-700 nm, the microfluidizer produced emulsions with narrower size distributions and sonication was more convenient in terms of operation and cleaning. In general, the size of the emulsions decreased with increasing sonication time, or the microfluidization pressure and duration. However, for both sonication and microfluidization, optimal conditions were necessary for emulsification beyond which the emulsion sizes would either increase or have little change with further processing.

Molecular motors-based micro- and nano-biocomputation devices

Protein molecular motors, which are natural nano-machines that convert the chemical energy into mechanical work for cellular motion, muscle contraction and cell division, have been integrated in the last decade in primitive nanodevices based on the motility of nano-biological objects in micro- and nano-fabricated structures. However, the motility of microorganisms powered by molecular motors has not been similarly exploited. Moreover, among the proposed devices based on molecular motors, i.e., nanosensors, nano-mechanical devices and nano-imaging devices, biocomputation devices are conspicuously missing. The present contribution discusses, based on the present state of the art nano- and micro-fabrication, the comparative advantages and disadvantages of using nano- and micro-biological objects in future computation devices. (c) 2006 Elsevier B.V. All rights reserved.

Visoelastic studies on thermoplastic polyurethane nanocomposites using a nano-hardness tester

The viscoelastic behaviour of a range of polyurethane thermoplastic elastomer montmorillonite nanocomposites has been studied using a nanohardness tester. For softer Shore hardness 80A materials, the introduction of the organo-clay increased the creep strain obtained while the nano-indentor was held at constant load. The increase in creep strain was greatest for materials containing an organo-clay modified with a more hydrophilic quaternary alkylammonium surfactant and with higher loadings of the hydrophilic organo-clay. This suggested the effect might be due to a plasticising effect of the excess surfactant. For the harder Shore hardness 55D materials, the addition of the organo-clays produced only a small decrease in the creep strain, probably due to the interconnected hard domains in this material.

Effect of microstructure on material removal mechanisms in nano/micro grinding of tungsten carbide mould inserts

Nano/micro grinding of tungsten carbide (WC) mould inserts was performed. A form accuracy of 〜200nm (in PV) and a surface roughness of 〜7nm were achieved. Nanoindentation revealed that small chipping or cracking occurred even at a penetration depth of 38nm, which could hinder the further improvement of surface quality during grinding. It was found that when grinding was conducted at nanometric scale, the microstructure of the work material and the morphology of the WC grains should be taken into account to enable a fully ductile removal. Copyright 2005 by the Japan Society of Mechanical Engineers