The effect of iron on liquid film migration and sintering of an Al-Cu-Mg alloy

Analytical transmission electron microscopy indicates that liquid film migration occurs during sintering of an Al-Cu-Mg alloy, that intragranular liquid pools develop from migrating films and that iron segregates to these pools. It is suggested that a high localised iron concentration retards the liquid film migration rate by reducing the coherency strain in the retreating grain, causing a region of the film to detach from the boundary, thus forming an intragranular pool in the advancing grain. Alloys with low iron levels develop few intragranular pools and have high sintered densities. (C) 2003 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Light alloy castings for automotive applications: The case of Al vs Mg

The economical and environmental effects of mass reduction through Al and Mg primary alloys substitutions for cast iron and steel in automotive components are discussed using MF. Ashby's penalty functions method The viability of Mg alloy substitutions for existing Al alloy cast components is also considered. The cost analysis shows that direct, equal-volume, Al alloy substitutions for cast iron and steel are the most feasible in terms of the CAFE liability, followed by substitutions involving flat panels of prescribed stiffness. When the creation of CO2 associated to the production of Al and Mg is considered, the potential gasoline savings over the lifespan of the car compensate for the intrinsic environmental burden of Al in all applications, while electrolytic Mg substitutions for cast iron and steel are feasible for equal volume and panels only. Magnesium produced by the Pidgeon thermal process appears to be too primary energy intensive to be competitive in structural applications. Magnesium substitutions for existing Al alloy beams and panels are generally unviable. The current higher recycling efficiency of Al casting alloys confers Al a significant advantage over Mg alloys.

Semisolid structure formation and semisolid casting

Semisolid metal forming has now been accepted as a viable technology for production of components with complex shape and high integrity. The advantages of semisolid metal forming can only be achieved when the feedstock material has a non-dendritic semisolid structure. A controlled nucleation method has been developed to produce such structures for semisolid forming. By controlling grain nucleation and growth, fine-grained and non-dendritic microstructures that are suitable for semisolid casting can be generated. The method was applied to hypoeutectic and hypereutectic Al-Si casting alloys, Al wrought alloys and a Mg alloy. Parameters such as pouring temperature, cooling rate and grain refiner addition were controlled to achieve copious nucleation, nuclei survival and dendritic growth suppression during solidification. The influences of the controlling parameters on the formation of semisolid structure were different for each of these alloy groups. The as-cast structures were then partially remelted and isothermally held. Semisolid structures were developed and followed by semisolid casting into a stepped die.

Alloying of pure magnesium with Mg-33.3 wt-%Zr master alloy

To capitalise on the strengthening potential of zirconium as a potent grain refiner for magnesium alloys, the mechanisms of adding zirconium to magnesium and its subsequent grain refining action need to be understood. Using a Mg-33.3Zr master alloy (Zirmax supplied by Magnesium Elektron Ltd) as a zirconium alloying additive, the influence of different alloying conditions on the dissolution of zirconium in magnesium was investigated. It was found that owing to the highly alloyable microstructure of Zirmax, the dissolution of zirconium was generally complete within a few minutes in the temperature range 730 to 780degreesC. Prolonging and/or intensifying stirring were found to have no conspicuous influence on further enhancing the dissolution of zirconium. In all cases studied, the average grain size increased with increasing holding time at temperature while the total zirconium content decreased. The finest grain structure and highest total zirconium content corresponded to sampling immediately after stirring. Pick up of iron by molten magnesium from the mild steel crucibles used for melting and holding, was significantly delayed or avoided in the temperature range 730 to 780degreesC by coating the crucibles with boron nitride. It is therefore feasible to conduct zirconium alloying at 730degreesC without the need of a considerable excess of Zirmax addition using a properly coated or lined steel crucible.

Morphology and crystallography of Mg24Y5 precipitate in Mg-Y alloy

Orientation relationships between Mg24Y5 precipitates and matrix in a Mg-Y alloy were accurately determined using Kikuchi line diffraction. The Burgers relationship with habit planes of {10 (1) over bar0}(H) and {31 (4) over bar0}(H) were observed for all precipitates. Compared with the Mg17Al12 precipitate in AZ91, the precipitation hardening effect in this alloy was significantly increased. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Stress corrosion cracking and hydrogen embrittlement of an Al-Zn-Mg-Cu alloy

The age hardening, stress corrosion cracking (SCC) and hydrogen embrittlement (HE) of an Al-Zn-Mg-Cu 7175 alloy were investigated experimentally. There were two peak-aged states during ageing. For ageing at 413 K, the strength of the second peak-aged state was slightly higher than that of the first one, whereas the SCC susceptibility was lower, indicating that it is possible to heat treat 7175 to high strength and simultaneously to have high SCC resistance. The SCC susceptibility increased with increasing Mg segregation at the grain boundaries. Hydrogen embrittlement (HE) increased with increased hydrogen charging and decreased with increasing ageing time for the same hydrogen charging conditions. Computer simulations were carried out of (a) the Mg grain boundary segregation using the embedded atom method and (b) the effect of Mg and H segregation on the grain boundary strength using a quasi-chemical approach. The simulations showed that (a) Mg grain boundary segregation in Al-Zn-Mg-Cu alloys is spontaneous, (b) Mg segregation decreases the grain boundary strength, and (c) H embrittles the grain boundary more seriously than does Mg. Therefore, the SCC mechanism of Al-Zn-Mg Cu alloys is attributed to the combination of HE and Mg segregation induced grain boundary embrittlement. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Age hardening of a sintered Al-Cu-Mg-Si-(Sn) alloy

The age hardening response of a sintered Al-3.8 wt% Cu-1.0 wt% Mg-0.70 wt% Si alloy with and without 0.1 wt% Sn was investigated. The sequence of precipitation was characterised using transmission electron microscopy. The ageing response of the sintered Al-Cu-Mg-Si-(Sn) alloy is similar to that of cognate wrought 2xxx series alloys. Peak hardness was associated with a fine, uniform dispersion of lath shaped precipitates, believed to be either the betaor Q phase, oriented along < 010 >. directions and theta' plates lying on {001}(alpha). planes. Natural ageing also resulted in comparable behaviour to that observed in wrought alloys. Porosity in the powder metallurgy alloys did not significantly affect the kinetics of precipitation during artificial ageing. Trace levels of tin, used to aid sintering, slightly reduced the hardening response of the alloy. However, this was compensated for by significant improvements in density and hardness. (c) 2005 Elsevier B.V. All rights reserved.

Precipitation induced densification in a sintered Al-Zn-Mg-Cu alloy

It is demonstrated that slow cooling to 200 degrees C from a high sintering temperature (620 degrees C) reduces porosity in an Al-8Zn-2.5Mg-1Cu powder compact when compared to isothermal sintering at the higher temperature for a longer time. The reduction in porosity is attributed to shrinkage associated with removal of solute from the aluminium solid solution and heterogeneous precipitation of the eta phase (MgZn2), particularly onto pore surfaces. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Crystallographyof Mg17Al12 precipitates in AZ91D alloy

Kikuchi diffraction was used to accurately determine the orientation relationship (OR) between Mg17Al12 precipitates and matrix in an AZ91D alloy. For both continuous and discontinuous precipitations, the Burgers OR and the Potter OR were equally observed. The lattice parameter of Mg17Al12 associated with the former is bigger than that of the latter. (C) 2002 Acta Materialia Inc. Published by Elsevier Science Ltd. All rights reserved.

Strength-ductility behaviour of Al-Si-Cu-Mg casting alloys in T6 temper

A comparative study of the mechanical properties of 20 experimental alloys has been carried out. The effect of different contents of Si, Cu, Mg, Fe and Mn, as well as solidification rate, has been assessed using a strength-ductility chart and a quality index-strength chart developed for the alloys. The charts show that the strength generally increases and the ductility decreases with an increasing content of Cu and Mg. Increased Fe (at Fe/Mn ratio 0.5) dramatically lowers the ductility and strength of low Si alloys. Increased Si content generally increases the strength and the ductility. The increase in ductility with increased Si is particularly significant when the Fe content is high. The charts are used to show that the cracking of second phase particles imposes a limit to the maximum achievable strength by limiting the ductility of strong alloys. The (Cu + Mg) content (at.%), which determines the precipitation strengthening and the volume fraction of Cu-rich and Mg-rich intermetallics, can be used to select the alloys for given strength and ductility, provided the Fe content stays below the Si-dependent critical level for the formation of pre-eutectic alpha-phase particles or beta-phase plates.

Hall-Petch parameters for tension and compression in cast Mg

The flow stress in tensile and compressive deformation has been determined in cast Mg, for a wide range of grain sizes between 36 mum and 1.5 mm. The grain size was varied by alloying Mg with small amounts of Zr. It was found that the 0.2% offset flow stress, sigma(y) (MPa), varies with the grain size, d (m), as sigma(y) = 17.7 + 0.25 d(-1/2) in tension, while sigma(y) = -2.3 + 0.39 d(-1/2) in compression. Possible reasons for the difference between tension and compression are discussed.

Effect of Si additions and heat treatment on the mechanical behaviour of an Al-5Mg casting alloy

Adding 1%Si to binary Al-5Mg alloy slightly increases the yield stress in comparison with the Si free alloy but dramatically reduces the ductility and tensile strength due to the formation of brittle eutectic Mg2Si and pi-Al8FeMg3Si6 particles. Adding 3%Si slightly reduces the yield stress, presumably due to some of the Mg being tied up in the Mg2Si, and further reduces the ductility due to the increased volume fraction of intermetallics. Solution heat treatment at 436degreesC decreases the yield stress of both Si containing alloys, and slightly increases the ductility in the alloy with 3%Si. Subsequent ageing at 180degreesC has no further effects on the strength or ductility. The loss in strength of the heat treated alloys seems to be due to overageing Of Mg2Si precipitates dispersed in the bulk of the alloy. (C) 2004 W. S. Maney Son Ltd.

Corrosion resistance of aged die cast magnesium alloy AZ91D

The corrosion behaviour of die cast magnesium alloy AZ91D aged at 160degreesC was investigated. The corrosion rate of the alloy decreases with ageing time in the initial stages and then increases again at ageing times greater than 45 h. The dependence of the corrosion rate on ageing time can be related to the changes in microstructure and local composition during ageing. Precipitation of the beta phase (Mg17Al12) occurs exclusively along the grain boundaries during ageing. The beta phase acts as a barrier, resulting in a decreasing corrosion rate in the initial stages of ageing. In the later stages, the decreasing aluminium content of alpha grains makes the alpha matrix more active, causing an increase in the corrosion rate. Electrochemical testing results also confirm the combined effects of the changes in alpha and beta phases on the corrosion resistance of the aged die cast AZ91D alloy. (C) 2003 Elsevier B.V. All rights reserved.

Effect of iron on grain refinement of high-purity MG-Al alloys

The effect of iron on the grain refinement of high-purity Mg-3%Al and Mg-91%Al alloys has been investigated using anhydrous FeCl3 as an iron additive at 750degreesC in carbon-free aluminium titanite crucibles. It was shown that grain refinement was readily achievable for both alloys. Fe- and Al-rich intermetallic particles were observed in many magnesium grains. (C) 2004 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.