Phase and microstructural evolution during the heat treatment of Sm-Ca-alpha-sialon ceramics

The phase and microstructural evolution of multi-cation Sm-Ca-alpha-sialon ceramics was investigated. Six samples were prepared, ranging from a pure Sm-sialon to a pure Ca-sialon, with calcium replacing samarium in 20 eq% increments, thus maintaining an equivalent design composition in all samples. After pressureless sintering at 1820 degreesC for 2 It, all samples were subsequently heat treated up to 192 h at 1450 and 1300 degreesC. The amount of grain boundary glass in the samples after sintering was observed to decrease with increasing calcium levels. A M-ss' or M-ss',-gehlenite solid solution was observed to form during the 1450 degreesC heat treatment of all Sm-containing samples, and this phase forms in clusters in the high-Sm samples. The thermal stability of the alpha-sialon phase was improved in the multi-cation systems. Heat treatment at 1300 degreesC produces SmAlO3 in the high-Sm samples, a M-ss',-gehlenite solid solution in the high-Ca samples, and a Sm-Ca-apatite phase in some intermediate samples. (C) 2002 Elsevier Science Ltd. All rights reserved.

A numerical study of effect of grain boundaries on elastic and plastic properties in nanocomposite materials

Nanocomposite materials have received considerable attention in recent years due to their novel properties. Grain boundaries are considered to play an important role in nanostructured materials. This work focuses on the finite element analysis of the effect of grain boundaries on the overall mechanical properties of aluminium/alumina composites. A grain boundary is incorporated into the commonly used unit cell model to investigate its effect on material properties. By combining the unit cell model with an indentation model, coupled with experimental indentation measurements, the ''effective'' plastic property of the grain boundary is estimated. In addition, the strengthening mechanism is also discussed based on the Estrin-Mecking model.

Microstructural evidence for the mechanism of the alpha-beta phase transformation in ytterbium SiAlON ceramics

Detailed microstructural evidence for the mechanism of the alpha-beta phase transformation in ytterbium SiAlON ceramics is presented. Grains, which show partial transformation, have been examined using transmission electron microscopy. We suggest that the transformation proceeds as a discernable reaction front and the accompanying lattice mismatch is accommodated be a series of complex dislocations. The stabilizing cation is ejected from the transformed alpha- phase and diffuse along the dislocation to accumulate as isolated pockets in a way similar to that observed in metal systems and termed pipe diffusion. High-resolution electron microscopy reveals the details of each of these features.

Synthesis, characterization, and electrical conduction of 10 mol% Dy2O3 doped CeO2 ceramics

Well-densified 10 mol% Dy2O3-doped CeO2 (20DDC) ceramics with average grain sizes of similar to 0.12-1.5 mu m were fabricated by pressureless sintering at 950-1550 degrees C using a reactive powder thermally decomposed from a carbonate precursor, which was synthesized via a carbonate coprecipitation method employing nitrates as the starting salts and ammonium carbonate as the precipitant. Electrical conductivity of the ceramics, measured by the dc three-point impedance method, shows a V-shape curve against the average grain size. The sample with the smallest grain size of 0.12 mu m exhibits a high conductivity of similar to 10(-1.74) S/cm at the measurement temperature of 700 degrees C, which is about the same conduction level of the micro-grained 10 mol% Sm2O3- or Gd2O3-doped CeO2, two leading electrolyte materials. (c) 2004 Elsevier Ltd. All rights reserved.

Bifurcation in growth patterns for arrays of parallel Griffith, edge and sliding cracks

This paper presents the recent finding by Muhlhaus et al [1] that bifurcation of crack growth patterns exists for arrays of two-dimensional cracks. This bifurcation is a result of the nonlinear effect due to crack interaction, which is, in the present analysis, approximated by the dipole asymptotic or pseudo-traction method. The nonlinear parameter for the problem is the crack length/ spacing ratio lambda = a/h. For parallel and edge crack arrays under far field tension, uniform crack growth patterns (all cracks having same size) yield to nonuniform crack growth patterns (i.e. bifurcation) if lambda is larger than a critical value lambda(cr) (note that such bifurcation is not found for collinear crack arrays). For parallel and edge crack arrays respectively, the value of lambda(cr) decreases monotonically from (2/9)(1/2) and (2/15.096)(1/2) for arrays of 2 cracks, to (2/3)(1/2)/pi and (2/5.032)(1/2)/pi for infinite arrays of cracks. The critical parameter lambda(cr) is calculated numerically for arrays of up to 100 cracks, whilst discrete Fourier transform is used to obtain the exact solution of lambda(cr) for infinite crack arrays. For geomaterials, bifurcation can also occurs when array of sliding cracks are under compression.

α′ phase stability in Nd-Li-sialon systems

The formability and stability of the alpha-sialon (alpha') phase was investigated in multi-cation Nd-Li-sialon systems. Four samples were prepared, ranging from a pure Nd-sialon to a pure Li-sialon, with two intermediate samples being prepared with either lithium or neodymium replacing the other alpha'-stabilising additive by 20 eq.%, as to maintain an equivalent design composition in all samples. After sintering, all samples were subsequently heat treated up to 192 h at 1450 and 1300 degreesC. While significant quantities of the beta'-sialon (beta' phase were found in most samples, the high-lithium Li-Nd-sialon sample was found to be almost pure a' phase after sintering. Furthermore, the long-term stability of the a' phase on heat treatment was also found to be superior in both multi-cation samples than in either of the single-alpha'-stabilising-cation samples. This is thought to be related to improved retention of the lithium in the multi-cation systems, as much of the lithium was found to volatilise during sintering in the neodymium-free sample. (C) 2002 Elsevier Science Ltd. All rights reserved.

Scavenging of siliceous grain-boundary phase of 8-mol%-ytterbia-stabilized zirconia without additive

The grain-boundary conductivity (sigma (gb),) of 8-mol%-ytterbiastabilized zirconia increased markedly with heat treatment between 1000 degrees and 1300 degreesC with a slow heating rate (0.1 degreesC/min) before sintering. The extent of the sigma (gb) improvement was the same or larger than that via Al2O3 addition. The heat treatment did not affect the grain-interior conduction when sintered at 1600 degreesC, while Al2O3-derived scavenging significantly did, given the larger increment of total conductivity in the heat-treated sample. The formation of a silicon-containing phase in a discrete form was suggested as a possible route of scavenging the resistive phase from the correlation between average grain size and sigma (gb).

Superplasticity and superplastic forming ability of a Zr-Ti-Ni-Cu-Be bulk metallic glass in the supercooled liquid recgion

The superplastic deformation behavior and superplastic forming ability of the Zr41.25Ti13.75Ni10Cu12.5Be22.5 (at.%) bulk metallic glass (BMG) in the supercooled liquid region were investigated. The isothermal tensile results indicate (hat the BMG exhibits a Newtonian behavior at low strain rates but a non-Newtonian behavior at hiqh-strain rates in the initial deformation stage. The maximum elongation reaches as high as 1624% at 656 K. and nanocrystallization was found to occur during the deformation process. Based cm the analysis on tensile deformation. a gear-like micropart is successfully die-forged via a superplastic forgings process. demonstrating that the BMG has excellent workability in the supercooled liquid region. (C) 2004 Elsevier B.V. All rights reserved.

A novel route to the synthesis of mesoporous Titania with full anatase nanocrystalline domains

A porous, high surface area TiO2 with anatase or rutile crystalline domains is advantageous for high efficiency photonic devices. Here, we report a new route to the synthesis of mesoporous titania with full anatase crystalline domains. This route involves the preparation of anatase nanocrystalline seed suspensions as the titania precursor and a block copolymer surfactant, Pluronic P123 as the template for the hydrothermal self-assembly process. A large pore (7 - 8 nm) mesoporous titania with a high surface area of 106 - 150 m(2)/g after calcination at 400degreesC for 4 h in air is achieved. Increasing the hydrothermal temperature decreases the surface area and creates larger pores. Characteristics of the seed precursors as well as the resultant mesoporous titania powder were studied using XRD analysis, N-2-adsorption/desorption analysis, and TEM. We believe these materials will be especially useful for photoelectrochemical solar cell and photocatalysis applications.

Characterisation of xerogels derived from sucrose templated sol-gel synthesis

This work presents the results of the nanostructural characterisation of the effect of sucrose as a template added to a sol derived from a tetraethoxysilane acid catalysed process. By increasing the sucrose template ratio, N-2 adsorption isotherms showed that the xerogel samples changed from a micropore to a mesopore nanostructure as evidenced by the formation of hysteresis at 0.5 partial pressure. In turn, this led to a direct increase in surface areas, pore volumes and average pore sizes. Sucrose has two molecular components of the same molecular weight: D-fructose and D-glucose. D-fructose resulted in the formation of higher pore volumes and pore sizes, while D-glucose formed higher surface area xerogels. Depending of the template ratio employed in the xerogel synthesis, average pore radius ranged from 8.8 to 26 Angstrom, while surface areas increased by over two fold up to 750 m(2) . g(-1). However, pore volumes increased by as much as six fold, from 0.15 to almost 1 cm(3) . g(-1).

Synthesis and characterization of nano-hetero-structured dy doped CeO2 solid electrolytes using a combination of spark plasma sintering and conventional sintering

Doped ceria (CeO2) compounds are fluorite-type oxides that show oxide ionic conductivity higher than yttria-stabilized zirconia in oxidizing atmosphere. As a consequence of this, considerable interest has been shown in application of these materials for low (500 degrees-650 degrees C) temperature operation of solid oxide fuel cells (SOFCs). To improve the conductivity in dysprosium (Dy) doped CeO2, nano-size round shape particles were prepared using a coprecipitation method. The dense sintered bodies with small grain sizes (< 300 nm) were fabricated using a combined process of spark plasma sintering (SPS) and conventional sintering (CS). Dy-doped CeO2 sintered body with large grains (1.1 mu m) had large micro-domains. The conductivity in the sintered body was low (-3.2 S/cm at 500 degrees C). On the other hand, the conductivity in the specimens obtained by the combined process was considerably improved. The micro-domain size in the grain was minimized using the present process. It is concluded that the enhancement of conductivity in dense specimens produced by the combined process (SPS+CS) is attributable to the microstructural changes within the grains.

Mesoporous bioactive glasses. I. Synthesis and structural characterization

Highly ordered mesoporous bioactive glasses (MBGs) with different compositions have been synthesized by a combination of surfactant templating, sol-gel method and evaporation-induced self-assembly (EISA) processes. The texture properties and compositional homogeneity of MBGs have been characterized and compared with conventional bioactive glasses (BGs) synthesized in the absence of surfactants by evaporation method. The formation mechanism (pore - composition dependence) and compositional homogeneity in the case of MBG materials are different from those in conventional BGs. Unlike conventional sol-gel-derived BGs that shows a direct correlation between their composition and pore architecture, MBGs with different compositions may possess similar pore volume and uniformly distributed pore size when the same structure-directing agent is utilized. The framework of MBG is homogeneously distributed in composition at the nanoscale and the inorganic species generally exists in the form of amorphous phase. MBGs calcined at temperatures

Enhanced glass-forming ability of a Zr-based bulk metallic glass with yttrium doping

A significant enhancement in glass formation in a newly developed Zr51Cu20.7Ni12Al16.3 alloy has been achieved by yttrium doping. With just 0.5 at.% yttrium doping, the critical diameter of the as-cast alloys for glass formation has been increased from 3 mm to at least 10 mm. In the undoped, large-sized alloys, massive oxygen stabilized crystalline phases are observed but disappear in yttrium doped alloys. Very small amounts of stable alpha-Y2O3 phases found in the yttrium doped alloys, and their negligible effect on the metallic glasses' properties, provide a superior solution to achieve metallic glasses with a high glass formability. (c) 2006 Elsevier B.V. All rights reserved.

Oxidation mechanism of Si3N4-bonded SiC ceramics by CO, CO2 and steam

This paper presents a theoretical and experimental investigation into the oxidation reactions of Si3N4-bonded SiC ceramics. Such ceramics which contain a small amount of silicon offer increased oxidation and wear resistance and are widely used as lining refractories in blast furnaces. The thermodynamics of oxidation reactions were studied using the JANAF tables. The weight gain was measured using a thermogravimetric analysis technique to study the kinetics. The temperature range of oxidation measurements is from 1073 to 1573 K and the oxidation atmosphere is water vapour, pure CO and CO-CO2 gas mixtures with various CO-to-CO2 ratios. Thermodynamic simulations showed that the oxidation mechanism of Si3N4-bonded SiC ceramics is passive oxidation and all components contribute to the formation of a silica film. The activated energies of the reactions follow the sequence Si3N4>SiC>Si. The kinetic study revealed that the oxidation of Si3N4-bonded SiC ceramics occurred in a mixed regime controlled by both interface reaction and diffusion through the silica film. Under the atmosphere conditions prevailing in the blast furnace, this ceramic is predicted to be passively oxidized with the chemical reaction rate becoming more dominant as the CO concentration increases. (C) 1998 Chapman & Hall.