Piezoresponse force microscopy of ferroelectric relaxors

Nesta tese, ferroeléctricos relaxor (I dont know uf the order is correct) de base Pb das familias (Pb,La)(Zr,Ti)O3 (PLZT), Pb(Mg1/3,Nb2/3)O3-PbTiO3 (PMN-PT), Pb(Zn1/3,Nb2/3)O3-PbTiO3 (PZN-PT) foram investigados e analisados. As propriedades ferroeléctricas e dieléctricas das amostras foram estudadas por métodos convencionais de macro e localmente por microscopia de força piezoeléctrica (PFM). Nos cerâmicos PLZT 9.75/65/35 o contraste da PFM à escala nanometrica _ foi investigado em função do tamanho e orientação dos grãos. Apurou-se que a intensidade do sinal piezoeléctrico das nanoestruturas diminui com o aumento da temperatura e desaparece a 490 K (La mol. 8%) e 420 K (9,5%). Os ciclos de histerese locais foram obtidos em função da temperatura. A evolução dos parâmetros macroscópicos e locais com a temperatura de superfície sugere um forte efeito de superfície nas transições de fase ferroeléctricas do material investigado. A rugosidade da parede de domínio é determinada por PFM para a estrutura de domínio natural existente neste ferroeléctrico policristalino. Além disso, os domínios ferroeléctricos artificiais foram criados pela aplicação de pulsos eléctricos à ponta do condutor PFM e o tamanho de domínio in-plane foi medido em função da duração do pulso. Todas estas experiências levaram à conclusão de que a parede de domínio em relaxors do tipo PZT é quase uma interface unidimensional. O mecanismo de contraste na superfície de relaxors do tipo PLZT é medido por PFMAs estruturas de domínio versus evolução da profundidade foram estudadas em cristais PZN-4,5%PT, com diferentes orientações através da PFM. Padrões de domínio irregulares com tamanhos típicos de 20-100 nm foram observados nas superfícies com orientação <001> das amostras unpoled?. Pelo contrário, os cortes de cristal <111> exibem domínios regulares de tamanho mícron normal, com os limites do domínio orientados ao longo dos planos cristalográficos permitidos. A existência de nanodomínios em cristais com orientação <001> está provisoriamente (wrong Word) atribuída à natureza relaxor de PZN-PT, onde pequenos grupos polares podem formar-se em coindições de zero-field-cooling (ZFC). Estes nanodomínios são considerados como os núcleos do estado de polarização oposta e podem ser responsáveis pelo menor campo coercitivo para este corte de cristal em particular. No entanto, a histerese local piezoelétrica realizada pelo PFM à escala nanométrica indica uma mudança de comportamento de PZN-PT semelhante para ambas as orientações cristalográficas investigadas. A evolução das estruturas de domínio com polimento abaixo da superfície do cristal foi investigada. O domínio de ramificações e os efeitos de polarização de triagem após o polimento e as medições de temperatura têm sido estudados pela PFM e pela análise SEM. Além disso, verificou-se que a intensidade do sinal piezoeléctrico a partir das estruturas de nanodomínio diminui com o aumento da temperatura, acabando por desaparecer aos 430 K (orientaçáo <111>) e 470 K (orientação <100>). Esta diferença de temperatura nas transições de fase local em cristais de diferentes orientações é explicada pelo forte efeito de superfície na transição da fase ferroelétrica em relaxors.A comutação da polarização em relaxor ergódico e nas fases ferroeléctricas do sistema PMN-PT foram realizadas pela combinação de três métodos, Microscopia de Força Piezoeléctrica, medição de um único ponto de relaxamento eletromecânico e por ultimo mapeamento de espectroscopia de tensão. A dependência do comportamento do relaxamento na amplitude e tempo da tensão de pulso foi encontrada para seguir um comportamento logarítmico universal com uma inclinação quase constante. Este comportamento é indicativo da progressiva população dos estados de relaxamento lento, ao contrário de uma relaxação linear na presença de uma ampla distribuição do tempo de relaxamento. O papel do comportamento de relaxamento, da não-linearidade ferroeléctrica e da heterogeneidade espacial do campo na ponta da sonda de AFM sobre o comportamento do ciclo de histerese é analisada em detalhe. Os ciclos de histerese para ergódica PMN- 10%PT são mostrados como cineticamente limitados, enquanto que no PMN, com maior teor de PT, são observados verdadeiros ciclos de histerese ferroeléctrica com viés de baixa nucleação.

Ferroelectric : CNTs structures fabrication for advanced functional nano devices

This work is about the combination of functional ferroelectric oxides with Multiwall Carbon Nanotubes for microelectronic applications, as for example potential 3 Dimensional (3D) Non Volatile Ferroelectric Random Access Memories (NVFeRAM). Miniaturized electronics are ubiquitous now. The drive to downsize electronics has been spurred by needs of more performance into smaller packages at lower costs. But the trend of electronics miniaturization challenges board assembly materials, processes, and reliability. Semiconductor device and integrated circuit technology, coupled with its associated electronic packaging, forms the backbone of high-performance miniaturized electronic systems. However, as size decreases and functionalization increases in the modern electronics further size reduction is getting difficult; below a size limit the signal reliability and device performance deteriorate. Hence miniaturization of siliconbased electronics has limitations. On this background the Road Map for Semiconductor Industry (ITRS) suggests since 2011 alternative technologies, designated as More than Moore; being one of them based on carbon (carbon nanotubes (CNTs) and graphene) [1]. CNTs with their unique performance and three dimensionality at the nano-scale have been regarded as promising elements for miniaturized electronics [2]. CNTs are tubular in geometry and possess a unique set of properties, including ballistic electron transportation and a huge current caring capacity, which make them of great interest for future microelectronics [2]. Indeed CNTs might have a key role in the miniaturization of Non Volatile Ferroelectric Random Access Memories (NVFeRAM). Moving from a traditional two dimensional (2D) design (as is the case of thin films) to a 3D structure (based on a tridimensional arrangement of unidimensional structures) will result in the high reliability and sensing of the signals due to the large contribution from the bottom electrode. One way to achieve this 3D design is by using CNTs. Ferroelectrics (FE) are spontaneously polarized and can have high dielectric constants and interesting pyroelectric, piezoelectric, and electrooptic properties, being a key application of FE electronic memories. However, combining CNTs with FE functional oxides is challenging. It starts with materials compatibility, since crystallization temperature of FE and oxidation temperature of CNTs may overlap. In this case low temperature processing of FE is fundamental. Within this context in this work a systematic study on the fabrication of CNTs - FE structures using low cost low temperature methods was carried out. The FE under study are comprised of lead zirconate titanate (Pb1-xZrxTiO3, PZT), barium titanate (BaTiO3, BT) and bismuth ferrite (BiFeO3, BFO). The various aspects related to the fabrication, such as effect on thermal stability of MWCNTs, FE phase formation in presence of MWCNTs and interfaces between the CNTs/FE are addressed in this work. The ferroelectric response locally measured by Piezoresponse Force Microscopy (PFM) clearly evidenced that even at low processing temperatures FE on CNTs retain its ferroelectric nature. The work started by verifying the thermal decomposition behavior under different conditions of the multiwall CNTs (MWCNTs) used in this work. It was verified that purified MWCNTs are stable up to 420 ºC in air, as no weight loss occurs under non isothermal conditions, but morphology changes were observed for isothermal conditions at 400 ºC by Raman spectroscopy and Transmission Electron Microscopy (TEM). In oxygen-rich atmosphere MWCNTs started to oxidized at 200 ºC. However in argon-rich one and under a high heating rate MWCNTs remain stable up to 1300 ºC with a minimum sublimation. The activation energy for the decomposition of MWCNTs in air was calculated to lie between 80 and 108 kJ/mol. These results are relevant for the fabrication of MWCNTs – FE structures. Indeed we demonstrate that PZT can be deposited by sol gel at low temperatures on MWCNTs. And particularly interesting we prove that MWCNTs decrease the temperature and time for formation of PZT by ~100 ºC commensurate with a decrease in activation energy from 68±15 kJ/mol to 27±2 kJ/mol. As a consequence, monophasic PZT was obtained at 575 ºC for MWCNTs - PZT whereas for pure PZT traces of pyrochlore were still present at 650 ºC, where PZT phase formed due to homogeneous nucleation. The piezoelectric nature of MWCNTs - PZT synthesised at 500 ºC for 1 h was proved by PFM. In the continuation of this work we developed a low cost methodology of coating MWCNTs using a hybrid sol-gel / hydrothermal method. In this case the FE used as a proof of concept was BT. BT is a well-known lead free perovskite used in many microelectronic applications. However, synthesis by solid state reaction is typically performed around 1100 to 1300 ºC what jeopardizes the combination with MWCNTs. We also illustrate the ineffectiveness of conventional hydrothermal synthesis in this process due the formation of carbonates, namely BaCO3. The grown MWCNTs - BT structures are ferroelectric and exhibit an electromechanical response (15 pm/V). These results have broad implications since this strategy can also be extended to other compounds of materials with high crystallization temperatures. In addition the coverage of MWCNTs with FE can be optimized, in this case with non covalent functionalization of the tubes, namely with sodium dodecyl sulfate (SDS). MWCNTs were used as templates to grow, in this case single phase multiferroic BFO nanorods. This work shows that the use of nitric solvent results in severe damages of the MWCNTs layers that results in the early oxidation of the tubes during the annealing treatment. It was also observed that the use of nitric solvent results in the partial filling of MWCNTs with BFO due to the low surface tension (<119 mN/m) of the nitric solution. The opening of the caps and filling of the tubes occurs simultaneously during the refluxing step. Furthermore we verified that MWCNTs have a critical role in the fabrication of monophasic BFO; i.e. the oxidation of CNTs during the annealing process causes an oxygen deficient atmosphere that restrains the formation of Bi2O3 and monophasic BFO can be obtained. The morphology of the obtained BFO nano structures indicates that MWCNTs act as template to grow 1D structure of BFO. Magnetic measurements on these BFO nanostructures revealed a week ferromagnetic hysteresis loop with a coercive field of 956 Oe at 5 K. We also exploited the possible use of vertically-aligned multiwall carbon nanotubes (VA-MWCNTs) as bottom electrodes for microelectronics, for example for memory applications. As a proof of concept BiFeO3 (BFO) films were in-situ deposited on the surface of VA-MWCNTs by RF (Radio Frequency) magnetron sputtering. For in situ deposition temperature of 400 ºC and deposition time up to 2 h, BFO films cover the VA-MWCNTs and no damage occurs either in the film or MWCNTs. In spite of the macroscopic lossy polarization behaviour, the ferroelectric nature, domain structure and switching of these conformal BFO films was verified by PFM. A week ferromagnetic ordering loop was proved for BFO films on VA-MWCNTs having a coercive field of 700 Oe. Our systematic work is a significant step forward in the development of 3D memory cells; it clearly demonstrates that CNTs can be combined with FE oxides and can be used, for example, as the next 3D generation of FERAMs, not excluding however other different applications in microelectronics.

Electromechanical properties of engineered lead free potassium sodium niobate based materials

K0.5Na0.5NbO3 (KNN), is the most promising lead free material for substituting lead zirconate titanate (PZT) which is still the market leader used for sensors and actuators. To make KNN a real competitor, it is necessary to understand and to improve its properties. This goal is pursued in the present work via different approaches aiming to study KNN intrinsic properties and then to identify appropriate strategies like doping and texturing for designing better KNN materials for an intended application. Hence, polycrystalline KNN ceramics (undoped, non-stoichiometric; NST and doped), high-quality KNN single crystals and textured KNN based ceramics were successfully synthesized and characterized in this work. Polycrystalline undoped, non-stoichiometric (NST) and Mn doped KNN ceramics were prepared by conventional ceramic processing. Structure, microstructure and electrical properties were measured. It was observed that the window for mono-phasic compositions was very narrow for both NST ceramics and Mn doped ceramics. For NST ceramics the variation of A/B ratio influenced the polarization (P-E) hysteresis loop and better piezoelectric and dielectric responses could be found for small stoichiometry deviations (A/B = 0.97). Regarding Mn doping, as compared to undoped KNN which showed leaky polarization (P-E) hysteresis loops, B-site Mn doped ceramics showed a well saturated, less-leaky hysteresis loop and a significant properties improvement. Impedance spectroscopy was used to assess the role of Mn and a relation between charge transport – defects and ferroelectric response in K0.5Na0.5NbO3 (KNN) and Mn doped KNN ceramics could be established. At room temperature the conduction in KNN which is associated with holes transport is suppressed by Mn doping. Hence Mn addition increases the resistivity of the ceramic, which proved to be very helpful for improving the saturation of the P-E loop. At high temperatures the conduction is dominated by the motion of ionized oxygen vacancies whose concentration increases with Mn doping. Single crystals of potassium sodium niobate (KNN) were grown by a modified high temperature flux method. A boron-modified flux was used to obtain the crystals at a relatively low temperature. XRD, EDS and ICP analysis proved the chemical and crystallographic quality of the crystals. The grown KNN crystals exhibit higher dielectric permittivity (29,100) at the tetragonal-to-cubic phase transition temperature, higher remnant polarization (19.4 μC/cm2) and piezoelectric coefficient (160 pC/N) when compared with the standard KNN ceramics. KNN single crystals domain structure was characterized for the first time by piezoforce response microscopy. It could be observed that <001> - oriented potassium sodium niobate (KNN) single crystals reveal a long range ordered domain pattern of parallel 180° domains with zig-zag 90° domains. From the comparison of KNN Single crystals to ceramics, It is argued that the presence in KNN single crystal (and absence in KNN ceramics) of such a long range order specific domain pattern that is its fingerprint accounts for the improved properties of single crystals. These results have broad implications for the expanded use of KNN materials, by establishing a relation between the domain patterns and the dielectric and ferroelectric response of single crystals and ceramics and by indicating ways of achieving maximised properties in KNN materials. Polarized Raman analysis of ferroelectric potassium sodium niobate (K0.5Na0.5)NbO3 (KNN) single crystals was performed. For the first time, an evidence is provided that supports the assignment of KNN single crystals structure to the monoclinic symmetry at room temperature. Intensities of A′, A″ and mixed A′+A″ phonons have been theoretically calculated and compared with the experimental data in dependence of crystal rotation, which allowed the precise determination of the Raman tensor coefficients for (non-leaking) modes in monoclinic KNN. In relation to the previous literature, this study clarifies that assigning monoclinic phase is more suitable than the orthorhombic one. In addition, this study is the basis for non-destructive assessments of domain distribution by Raman spectroscopy in KNN-based lead-free ferroelectrics with complex structures. Searching a deeper understanding of the electrical behaviour of both KNN single crystal and polycrystalline materials for the sake of designing optimized KNN materials, a comparative study at the level of charge transport and point defects was carried out by impedance spectroscopy. KNN single crystals showed lower conductivity than polycrystals from room temperature up to 200 ºC, but above this temperature polycrystalline KNN displays lower conductivity. The low temperature (T < 200 ºC) behaviour reflects the different processing conditions of both ceramics and single crystals, which account for less defects prone to charge transport in the case of single crystals. As temperature increases (T > 200 ºC) single crystals become more conductive than polycrystalline samples, in which grain boundaries act as barriers to charge transport. For even higher temperatures the conductivity difference between both is increased due to the contribution of ionic conduction in single crystals. Indeed the values of activation energy calculated to the high temperature range (T > 300 ºC) were 1.60 and 0.97 eV, confirming the charge transport due to ionic conduction and ionized oxygen vacancies in single crystals and polycrystalline KNN, respectively. It is suggested that single crystals with low defects content and improved electromechanical properties could be a better choice for room temperature applications, though at high temperatures less conductive ceramics may be the choice, depending on the targeted use. Aiming at engineering the properties of KNN polycrystals towards the performance of single crystals, the preparation and properties study of (001) – oriented (K0.5Na0.5)0.98Li0.02NbO3 (KNNL) ceramics obtained by templated grain growth (TGG) using KNN single crystals as templates was undertaken. The choice of KNN single crystals templates is related with their better properties and to their unique domain structure which were envisaged as a tool for templating better properties in KNN ceramics too. X-ray diffraction analysis revealed for the templated ceramics a monoclinic structure at room temperature and a Lotgering factor (f) of 40% which confirmed texture development. These textured ceramics exhibit a long range ordered domain pattern consisting of 90º and 180º domains, similar to the one observed in the single crystals. Enhanced dielectric (13017 at TC), ferroelectric (2Pr = 42.8 μC/cm2) and piezoelectric (d33 = 280 pC/N) properties are observed for textured KNNL ceramics as compared to the randomly oriented ones. This behaviour is suggested to be due to the long range ordered domain patterns observed in the textured ceramics. The obtained results as compared with the data previously reported on texture KNN based ceramics confirm that superior properties were found due to ordered repeated domain pattern. This study provides an useful approach towards properties improvement of KNN-based piezoelectric ceramics. Overall, the present results bring a significant contribution to the pool of knowledge on the properties of sodium potassium niobate materials: a relation between the domain patterns and di-, ferro-, and piezo-electric response of single crystals and ceramics was demonstrated and ways of engineering maximised properties in KNN materials, for example by texturing were established. This contribution is envisaged to have broad implications for the expanded use of KNN over the alternative lead-based materials.

Biology, ecology, population dynamics and distribution of metals in Sepia officinalis on a typical estuarine coastal lagoon - Ria de Aveiro

The common cuttlefish, Sepia officinalis, is a necto-benthic cephalopod that can live in coastal ecosystems, with high influence of anthropogenic pressures and thus be vulnerable to exposure to various types of contaminants. The cuttlefish is a species of great importance to the local economy of Aveiro, considering the global data of catches of this species in the Ria de Aveiro. However, studies on this species in Ria de Aveiro are scarce, so the present study aims to fill this information gap about the cuttlefish in the Ria de Aveiro. The cuttlefish enters Ria de Aveiro in the spring and summer to reproduce, returning to deeper waters in the winter. In terms of abundance, the eastern and center regions of the lagoon, closer to the sea, showed the highest values of abundance, while the northern and southern regions of the main channel had the lowest abundance. This fact may be related to abiotic factors, as well as depth, salinity and temperature. In the most southern point of the Ria de Aveiro (Areão) no cuttlefish was caught. This site had the lowest values of salinity and depth. The cuttlefish has an allometric the females being heavier than males to mantle lengths greater than 82.4 mm. Males reach sexual maturity first than females. In Ria de Aveiro in a generation of parents was found. The cuttlefish, presents itself as opportunistic predators, consuming a wide variety of prey from different taxa. The diet was similar in different sampling locations observing significant differences for the seasons. S. officinalis was captured at 10 sites in the Ria de Aveiro with different anthropogenic sources of contamination. Thus, levels of metals analyzed were similar at all sampling sites, with the exception of a restricted area, Laranjo, which showed higher values. The cuttlefish has the ability to accumulate metals in your body. The levels of Fe, Zn, Cu, Cd, Pb and Hg found in the digestive gland and mantle reflect a differential accumulation of metals in the tissues. This accumulation is related to the type and function of tissue analyzed and the type of metal analysis (essential and non-essential). The metal concentrations in the digestive gland are higher than in the mantle, with the exception of mercury. This may be due to the high affinity of the mantle for the incorporation of methylmercury (MeHg), the most abundant form of mercury. The accumulation of metals can vary over a lifetime, depending on the metal. The concentrations of Zn, Cd and Hg increases throughout life, while Pb decreases and essential metals such as Fe and Cu remain constant. The data collected suggest that the cuttlefish (Sepia officinalis) can be used as a bioindicator of environmental contamination for some metals.