Metal-organic frameworks based on phosphonate linkers

During the last few decades, Metal-Organic Frameworks (MOFs), also known as Coordination Polymers, have attracted worldwide research attentions due to their incremented fascinating architectures and unique properties. These multidimensional materials have been potential applications in distinct areas: gas storage and separation, ion exchange, catalysis, magnetism, in optical sensors, among several others. The MOF research group at the University of Aveiro has prepared MOFs from the combination of phosphonate organic primary building units (PBUs) with, mainly, lanthanides. This thesis documents the last findings in this area involving the synthesis of multidimensional MOFs based on four di- or tripodal phosphonates ligands. The organic PBUs were designed and prepared by selecting and optimizing the best reaction conditions and synthetic routes. The self-assembly between phosphonate PBUs and rare-earths cations led to the formation of several 1D, 2D and 3D families of isotypical MOFs. The preparation of these materials was achieved by using distinct synthetic approaches: hydro(solvo)thermal, microwave- and ultrasound-assisted, one-pot and ionothermal synthesis. The selection of the organic PBUs showed to have an important role in the final architectures: while flexible phosphonate ligands afforded 1D, 2D and dense 3D structures, a large and rigid organic PBU isolated a porous 3D MOF. The crystal structure of these materials was successfully unveiled by powder or single-crystal X-ray diffraction. All multidimensional MOFs were characterized by standard solid-state techniques (FT-IR, electron microscopy (SEM and EDS), solid-state NMR, elemental and thermogravimetric analysis). Some MOF materials exhibited remarkable thermal stability and robustness up to ca. 400 ºC. The intrinsic properties of some MOFs were investigated. Photoluminescence studies revealed that the selected organic PBUs are suitable sensitizers of Tb3+ leading to the isolation of intense green-emitting materials. The suppression of the O−H quenchers by deuteration or dehydration processes improves substantially the photoluminescence of the optically-active Eu3+-based materials. Some MOF materials exhibited high heterogeneous catalytic activity and excellent regioselectivity in the ring-opening reaction of styrene oxide (PhEtO) with methanol (100% conversion of PhEtO at 55 ºC for 30 min). The porous MOF material was employed in gas separation processes. This compound showed the ability to separate propane over propylene. The ionexchanged form of this material (containing K+ cations into its network) exhibited higher affinity for CO2 being capable to separate acetylene over this environment non-friendly gas.

Study of multiferroic materials

The present PhD work aims the research and development of materials that exhibit multiferroic properties, in particular having a significant interaction between ferromagnetism and ferroelectricity; either directly within an intrinsic single phase or by combining extrinsic materials, achieving the coupling of properties through mechanic phenomena of the respective magnetostriction and piezoelectricity. These hybrid properties will allow the cross modification of magnetic and electric polarization states by the application of cross external magnetic and/or electric fields, giving way to a vast area for scientific investigation and potential technological applications in a new generation of electronic devices, such as computer memories, signal processing, transducers, sensors, etc. Initial experimental work consisted in chemical synthesis of nano powders oxides by urea pyrolysis method: A series of ceramic bulk composites with potential multiferroic properties comprised: of LuMnO3 with La0.7Sr0.3MnO3 and BaTiO3 with La0.7Ba0.3MnO3; and a series based on the intrinsic multiferroic LuMn1-zO3 phase modified with of Manganese vacancies. The acquisition of a new magnetron RF sputtering deposition system, in the Physics Department of Aveiro University, contributed to the proposal of an analogous experimental study in multiferroic thin films and multilayer samples. Besides the operational debut of this equipment several technical upgrades were completed like: the design and construction of the heater electrical contacts; specific shutters and supports for the magnetrons and for the substrate holder and; the addition of mass flow controllers, which allowed the introduction of N2 or O2 active atmosphere in the chamber; and the addition of a second RF generator, enabling co-deposition of different targets. Base study of the deposition conditions and resulting thin films characteristics in different substrates was made from an extensive list of targets. Particular attention was given to thin film deposition of magnetic phases La1-xSrxMnO3, La1-xBaxMnO3 and Ni2+x-yMn1-xGa1+y alloy, from the respective targets: La0.7Sr0.3MnO3, La0.7Ba0.3MnO3; and NiGa with NiMn. Main structural characterization of samples was performed by conventional and high resolution X-Ray Diffraction (XRD); chemical composition was determined by Electron Dispersion Spectroscopy (EDS); magnetization measurements recur to a Vibrating Sample Magnetometer (VSM) prototype; and surface probing (SPM) using Magnetic-Force (MFM) and Piezo-Response (PFM) Microscopy. Results clearly show that the composite bulk samples (LuM+LSM and BTO+LBM) feat the intended quality objectives in terms of phase composition and purity, having spurious contents below 0.5 %. SEM images confirm compact grain packaging and size distribution around the 50 nm scale. Electric conductivity, magnetization intensity and magneto impedance spreading response are coherent with the relative amount of magnetic phase in the sample. The existence of coupling between the functional phases is confirmed by the Magnetoelectric effect measurements of the sample “78%LuM+22%LSM” reaching 300% of electric response for 1 T at 100 kHz; while in the “78%BTO+22%LBM” sample the structural transitions of the magnetic phase at ~350 K result in a inversion of ME coefficient the behavior. A functional Magneto-Resistance measurement system was assembled from the concept stage until the, development and operational status; it enabled to test samples from 77 to 350 K, under an applied magnetic field up to 1 Tesla with 360º horizontal rotation; this system was also designed to measure Hall effect and has the potential to be further upgraded. Under collaboration protocols established with national and international institutions, complementary courses and sample characterization studies were performed using Magneto-Resistance (MR), Magneto-Impedance (MZ) and Magneto-Electric (ME) measurements; Raman and X-ray Photoelectron Spectroscopy (XPS); SQUID and VSM magnetization; Scanning Electron Microscopy (SEM) and Rutherford Back Scattering (RBS); Scan Probe Microscopy (SPM) with Band Excitation Probe Spectroscopy (BEPS); Neutron Powder Diffraction (NPD) and Perturbed Angular Correlations (PAC). Additional collaboration in research projects outside the scope of multiferroic materials provided further experience in sample preparation and characterization techniques, namely VSM and XPS measurements were performed in cubane molecular complex compounds and enable to identify the oxidation state of the integrating cluster of Ru ions; also, XRD and EDS/SEM analysis of the acquired targets and substrates implied the devolution of some items not in conformity with the specifications. Direct cooperation with parallel research projects regarding multiferroic materials, enable the assess to supplementary samples, namely a preliminary series of nanopowder Y1-x-yCaxØyMn1O3 and of Eu0.8Y0.2MnO3, a series of micropowder composites of LuMnO3 with La0.625Sr0.375MnO3 and of BaTiO3 with hexagonal ferrites; mono and polycrystalline samples of Pr1-xCaxMnO3, La1-xSrxMnO3 and La1-xCaxMnO3.

Estudo óptico de cristais e heterostruturas de CdTe

Neste trabalho privilegiam-se as técnicas ópticas, nomeadamente a fotoluminescência a transmissão, a reflexão e a difusão de Raman na caracterização de defeitos e impurezas em cristais e heterostruturas de CdTe/GaAs. No primeiro capítulo efectua-se uma revisão sucinta das propriedades dos compostos II-VI e são colocados os problemas a investigar. O segundo capítulo é dedicado a alguns aspectos teóricos relevantes para a análise dos resultados obtidos nos capítulos quatro a nove. O equipamento utilizado e as experiências realizadas são descritas no terceiro capítulo. A caracterização por espectroscopia de luminescência do tipo de transições e dos defeitos envolvidos nas amostras de fábrica é efectuada com detalhe no quarto capítulo. Neste capítulo são analisadas ainda as emissões devidas a desvios estequiométricos causados pelo recozimento com excesso e defeito de Cd. No capítulo cinco são estudadas por fotoluminescência amostras dopadas intencionalmente com oxigénio por difusão e mostra-se que este elemento se comporta como trapa isoelectrónica no CdTe tal como acontece no ZnTe. Neste capítulo são estudadas também amostras dopadas com ferro pelo mesmo método e são apresentadas as dificuldades em colocar este dopante em sítios substitucionais, nomeadamente no sítio do Cd. No sexto capítulo é estudada a região 1.4 eV, evidenciando o seu comportamento em função da temperatura e da potência de excitação, o seu perfil e a interacção electrãorede. No sétimo capítulo mostra-se que a técnica micro-Raman com luz visível coerente não permite extrair conclusões fiáveis acerca das inclusões de Te na superfície do CdTe, uma vez que a radiação ao ser focada nas amostras, induz a formação de aglomerados nos quais o Te é o elemento dominante. Neste capítulo calcula-se também a concentração de portadores livres através da interacção do plasmão com o fonão óptico longitudinal. O oitavo capítulo é dedicado ao estudo de camadas de CdTe/GaAs com diferentes espessuras nomeadamente na análise da distribuição das deslocações e da deformação na superfície em função da espessura. Os resultados obtidos são comparados através da largura a meia altura das curvas de DCXRD (“Double Crystal X Ray Diffraction”) e dos espectros de reflectância. Por fotoluminescência, são caracterizados os defeitos introduzidos durante o crescimento, são utilizados e desenvolvidos modelos complementares na distinção do tipo de transições ópticas obtidas. No nono capítulo, por espectroscopia de absorção e de reflexão em cristais de CdTe e em camadas de CdTe/GaAs na região reststrahlen são determinadas as frequências dos modos ópticos longitudinal e transversal com bastante precisão. Os resultados obtidos — pelas relações de dispersão de Kramers- Kronig — são simulados pelo modelo do oscilador harmónico classico, mostrando que ambos os métodos descrevem de forma semelhante o comportamento do CdTe nessa região sendo possível determinar as frequências ópticas transversal e longitudinal, as constantes dieléctrica óptica e estática e os coeficientes de amortecimento e de Szigeti. Nas heterostruturas e nas camadas mais espessas determina-se também a concentração de portadores de carga n. No décimo capítulo resumem-se as conclusões do trabalho e são abordados aspectos relacionados com desenvolvimentos possíveis de futuros trabalhos.

Assessment of biocompatibility of selected ferroelectric ceramics

Desde há muitas décadas que é sabido que os organismos vivos, em especial os tecidos, reagem fisicamente a estímulos eléctricos, podendo esses efeitos reproduzirem-se numa libertação de químicos endógenos, ou deformar a sua estrutura física. O tecido ósseo por si só é considerado um material/tecido piezoeléctrico, deformando-se mecanicamente quando lhe é induzido um estímulo eléctrico e vice-versa, ou seja, produz um potencial eléctrico quando sofre uma tracção ou compressão mecânica. A hipótese de que um material ferroeléctrico possa vir a produzir efeitos no desempenho deste tipo de tecidos é então proposta, como por exemplo, para uma melhor, mais rápida e eficaz regeneração óssea. Estes mesmos materiais ferroeléctricos podem porventura alterar as cargas de superfície dos tecidos vivos de modo a atrair, atrasar ou até impedir o fluxo iónico de elementos químicos específicos responsáveis pelo processo de regeneração. São escolhidos então o niobato de lítio e o tantalato de lítio como cerâmicos ferroeléctricos e foi estudada pela primeira vez a sua bioactividade in vitro, esperando-se encontrar pistas relativas à sua bioactividade in vivo. Estes cerâmicos ferroeléctricos foram seleccionados devido às suas importantes propriedades piezoeléctricas e ferroeléctricas. Estas propriedades podem abrir um novo e importante leque de aplicações biomédicas caso estes cerâmicos sejam bioactivos. Este trabalho foi dividido em 3 fases: (i) sintetização dos pós de niobato de lítio e tantalato de lítio, (ii) caracterização dos pós e (iii) preparação das amostras e (iv) estudo da bioactividade destes cerâmicos ferroeléctricos. Os pós foram produzidos através de um processo simples de mistura/moagem seguido de calcinação. Foram estudadas as fases cristalinas presentes através de Difracção de raios-X (DRX) e avaliadas as características morfológicas destes pós, nomeadamente o diâmetro de partículas e área superficial específica. De modo a simular o ambiente do plasma humano, foi produzido sinteticamente um “Simulated Body Fluid” (SBF). Seguidamente as amostras foram imersas nesse ambiente líquido por 1, 3, 7, 15 e 21 dias. Após remoção dos pós foram realizadas uma série de análises de modo a estudar a sua bioactividade. De entre estes testes destacam-se a microscopia electrónica de varrimento (SEM/EDS), DRX e espectroscopia de Infravermelho por transformada de Fourier com reflectância total atenuada (FTIR-ATR). Embora não tenham sido detectadas alterações no DRX realizado aos pós, verificou-se a formação de aglomerados de fosfato de cálcio na superfície dos pós através do SEM, resultados estes, reforçados pelo EDS e FTIR-ATR. Estes precipitados de fosfato de cálcio indiciam a capacidade destes pós cerâmicos ferroeléctricos se comportarem como bioactivos em contacto com tecidos ósseos in vivo.