Alkaline-earth aluminosilicate-based glass and glass-ceramic sealants for functional applications

The planar design of solid oxide fuel cell (SOFC) is the most promising one due to its easier fabrication, improved performance and relatively high power density. In planar SOFCs and other solid-electrolyte devices, gas-tight seals must be formed along the edges of each cell and between the stack and gas manifolds. Glass and glass-ceramic (GC), in particular alkaline-earth alumino silicate based glasses and GCs, are becoming the most promising materials for gas-tight sealing applications in SOFCs. Besides the development of new glass-based materials, new additional concepts are required to overcome the challenges being faced by the currently existing sealant technology. The present work deals with the development of glasses- and GCs-based materials to be used as a sealants for SOFCs and other electrochemical functional applications. In this pursuit, various glasses and GCs in the field of diopside crystalline materials have been synthesized and characterized by a wide array of techniques. All the glasses were prepared by melt-quenching technique while GCs were produced by sintering of glass powder compacts at the temperature ranges from 800−900 ºC for 1−1000 h. Furthermore, the influence of various ionic substitutions, especially SrO for CaO, and Ln2O3 (Ln=La, Nd, Gd, and Yb), for MgO + SiO2 in Al-containing diopside on the structure, sintering and crystallization behaviour of glasses and properties of resultant GCs has been investigated, in relevance with final application as sealants in SOFC. From the results obtained in the study of diopside-based glasses, a bilayered concept of GC sealant is proposed to overcome the challenges being faced by (SOFCs). The systems designated as Gd−0.3 (in mol%: 20.62MgO−18.05CaO−7.74SrO−46.40SiO2−1.29Al2O3 − 2.04 B2O3−3.87Gd2O3) and Sr−0.3 (in mol%: 24.54 MgO−14.73 CaO−7.36 SrO−0.55 BaO−47.73 SiO2−1.23 Al2O3−1.23 La2O3−1.79 B2O3−0.84 NiO) have been utilized to realize the bi-layer concept. Both GCs exhibit similar thermal properties, while differing in their amorphous fractions, revealed excellent thermal stability along a period of 1,000 h. They also bonded well to the metallic interconnect (Crofer22APU) and 8 mol% yttrium stabilized zirconium (8YSZ) ceramic electrolyte without forming undesirable interfacial layers at the joints of SOFC components and GC. Two separated layers composed of glasses (Gd−0.3 and Sr−0.3) were prepared and deposited onto interconnect materials using a tape casting approach. The bi-layered GC showed good wetting and bonding ability to Crofer22APU plate, suitable thermal expansion coefficient (9.7–11.1 × 10–6 K−1), mechanical reliability, high electrical resistivity, and strong adhesion to the SOFC componets. All these features confirm the good suitability of the investigated bi-layered sealant system for SOFC applications.

Efeito do revestimento nas propriedades das rolhas de cortiça

A utilização de revestimentos poliméricos em rolhas de cortiça natural é uma prática recorrente na indústria de produção de rolhas. A sua aplicação tem como principal objetivo a melhoria da qualidade visual das rolhas. Contudo, este tratamento altera também as suas caraterísticas de molhabilidade, pelo que é importante otimizar os processos de revestimento de superfície. O presente trabalho teve como objetivo principal a averiguação da influência de um revestimento colorido e de diferentes tratamentos de superfície no comportamento da rolha em garrafa. Foram utilizadas amostras, cedidas pela Cork Supply Portugal, provenientes de quatro branqueamentos distintos (LVL, CSP, CPI e SIL). Foram estudadas amostras com e sem revestimento colorido e, todas elas, tratadas superficialmente com quatro tipos de tratamento (TS1, TS2, TS3 e TS4), sendo as quantidades de parafina e silicone administradas todas diferentes. Para observar o efeito do revestimento colorido e dos tratamentos de superfície nas rolhas de cortiça, procedeu-se a testes para determinação de capilaridade, inserções e forças de extração, simulando as condições de engarrafamento/extração do cliente, de forma a verificar a conformidade dos resultados. Todos estes testes procederam-se nas instalações da CSP. Foram também efetuados testes de molhabilidade pela determinação de ângulos de contacto para três diferentes solventes, nomeadamente água, formamida e diiodometano, e obtidos os Wetting Envelopes, pelo método de OWRK, de forma a prever a molhabilidade das várias amostras. Os procedimentos experimentais descritos efetuaram-se nos laboratórios da Universidade de Aveiro. Aliando as análises aos vários testes efetuados, concluiu-se que o revestimento colorido tem um possível efeito favorecedor nas propriedades mecânicas das rolhas de cortiça, possui maior recetividade aos agentes lubrificantes e maior molhabilidade. Relativamente aos tratamentos de superfície, o melhor, tendo em conta os fatores de molhabilidade, foi o TS4, proporcionando melhor vedação ao vinho. Já a respeito da lubrificação, verificou-se melhores resultados para os tratamentos TS1 e TS2. A lavação SIL apresenta menor afinidade aos agentes vedantes e a CSP possui maior recetibilidade aos agentes lubrificantes.