Optimization of Li-ion solid electrolytes

The synthesis and optimization of two Li-ion solid electrolytes were studied in this work. Different combinations of precursors were used to prepare La0.5Li0.5TiO3 via mechanosynthesis. Despite the ability to form a perovskite phase by the mechanochemical reaction it was not possible to obtain a pure La0.5Li0.5TiO3 phase by this process. Of all the seven combinations of precursors and conditions tested, the one where La2O3, Li2CO3 and TiO2 were milled for 480min (LaOLiCO-480) showed the best results, with trace impurity phases still being observed. The main impurity phase was that of La2O3 after mechanosynthesis (22.84%) and Li2TiO3 after calcination (4.20%). Two different sol-gel methods were used to substitute boron on the Zr-site of Li1+xZr2-xBx(PO4)3 or the P-site of Li1+6xZr2(P1-xBxO4)3, with the doping being achieved on the Zr-site using a method adapted from Alamo et al (1989). The results show that the Zr-site is the preferential mechanism for B doping of LiZr2(PO4)3 and not the P-site. Rietveld refinement of the unit-cell parameters was performed and it was verified by consideration of Vegard’s law that it is possible to obtain phase purity up to x = 0.05. This corresponds with the phases present in the XRD data, that showed the additional presence of the low temperature (monoclinic) phase for the powder sintered at 1200ºC for 12h of compositions with x ≥ 0.075. The compositions inside the solid solution undergo the phase transition from triclinic (PDF#01-074-2562) to rhombohedral (PDF#01-070-6734) when heating from 25 to 100ºC, as reported in the literature for the base composition. Despite several efforts, it was not possible to obtain dense pellets and with physical integrity after sintering, requiring further work in order to obtain dense pellets for the electrochemical characterisation of Li Zr2(PO4)3 and Li1.05Zr1.95B0.05(PO4)3.

Nonaqueous sol-gel routes to doped metal oxide nanoparticles: synthesis, characterization, assembly and properties

The results presented in this thesis have been achieved under the Ph.D. project entitled “Nonaqueous Sol-Gel routes to doped metal oxide nanoparticles: Synthesis, characterization, assembly and properties”. The purpose of this study is the investigation of metal oxide nanostructures doped with metals of a diverse nature, leading to different type of applications. The easier control over the reaction kinetics in solvothermal routes, compared to aqueous methods, allows to better match the reactivity between metal oxide precursors, paving the way to a facile and low temperature production of doped oxides. In this manuscript diverse examples of the exploitation of the “Benzyl Alcohol Route” are discussed. Such a powerful pathway was utilized for the synthesis of transition metal doped zirconia, hafnia and various perovskites, and the study of their magnetic properties, as well as the synthesis of rare earth doped zirconium oxide. A further extension, proving the solidity of the synthetic method, is shown for the preparation of Li4Ti5O12 nanocrystals carrying excellent electrochemical properties for lithium-ion battery applications. Finally, the effect of doping and other reaction parameters on the assembly of the nanocrystals is discussed. These studies were carried out principally at the University of Aveiro, as well as at the University of Montpellier II and at the Seoul National University due to complementary available expertises and equipments.