Reconfigurable transmitters for software-defined radios

Flexible radio transmitters based on the Software-Defined Radio (SDR) concept are gaining an increased research importance due to the unparalleled proliferation of new wireless standards operating at different frequencies, using dissimilar coding and modulation schemes, and targeted for different ends. In this new wireless communications paradigm, the physical layer of the radio transmitter must be able to support the simultaneous transmission of multi-band, multi-rate, multi-standard signals, which in practice is very hard or very inefficient to implement using conventional approaches. Nevertheless, the last developments in this field include novel all-digital transmitter architectures where the radio datapath is digital from the baseband up to the RF stage. Such concept has inherent high flexibility and poses an important step towards the development of SDR-based transmitters. However, the truth is that implementing such radio for a real world communications scenario is a challenging task, where a few key limitations are still preventing a wider adoption of this concept. This thesis aims exactly to address some of these limitations by proposing and implementing innovative all-digital transmitter architectures with inherent higher flexibility and integration, and where improving important figures of merit, such as coding efficiency, signal-to-noise ratio, usable bandwidth and in-band and out-of-band noise will also be addressed. In the first part of this thesis, the concept of transmitting RF data using an entirely digital approach based on pulsed modulation is introduced. A comparison between several implementation technologies is also presented, allowing to state that FPGAs provide an interesting compromise between performance, power efficiency and flexibility, thus making them an interesting choice as an enabling technology for pulse-based all-digital transmitters. Following this discussion, the fundamental concepts inherent to pulsed modulators, its key advantages, main limitations and typical enhancements suitable for all-digital transmitters are also presented. The recent advances regarding the two most common classes of pulse modulated transmitters, namely the RF and the baseband-level are introduced, along with several examples of state-of-the-art architectures found on the literature. The core of this dissertation containing the main developments achieved during this PhD work is then presented and discussed. The first key contribution to the state-of-the-art presented here consists in the development of a novel ΣΔ-based all-digital transmitter architecture capable of multiband and multi-standard data transmission in a very flexible and integrated way, where the pulsed RF output operating in the microwave frequency range is generated inside a single FPGA device. A fundamental contribution regarding the simultaneous transmission of multiple RF signals is then introduced by presenting and describing novel all-digital transmitter architectures that take advantage of multi-gigabit data serializers available on current high-end FPGAs in order to transmit in a time-interleaved approach multiple independent RF carriers. Further improvements in this design approach allowed to provide a two-stage up-conversion transmitter architecture enabling the fine frequency tuning of concurrent multichannel multi-standard signals. Finally, further improvements regarding two key limitations inherent to current all-digital transmitter approaches are then addressed, namely the poor coding efficiency and the combined high quality factor and tunability requirements of the RF output filter. The followed design approach based on poliphase multipath circuits allowed to create a new FPGA-embedded agile transmitter architecture that significantly improves important figures of merit, such as coding efficiency and SNR, while maintains the high flexibility that is required for supporting multichannel multimode data transmission.

Electromechanical properties of engineered lead free potassium sodium niobate based materials

K0.5Na0.5NbO3 (KNN), is the most promising lead free material for substituting lead zirconate titanate (PZT) which is still the market leader used for sensors and actuators. To make KNN a real competitor, it is necessary to understand and to improve its properties. This goal is pursued in the present work via different approaches aiming to study KNN intrinsic properties and then to identify appropriate strategies like doping and texturing for designing better KNN materials for an intended application. Hence, polycrystalline KNN ceramics (undoped, non-stoichiometric; NST and doped), high-quality KNN single crystals and textured KNN based ceramics were successfully synthesized and characterized in this work. Polycrystalline undoped, non-stoichiometric (NST) and Mn doped KNN ceramics were prepared by conventional ceramic processing. Structure, microstructure and electrical properties were measured. It was observed that the window for mono-phasic compositions was very narrow for both NST ceramics and Mn doped ceramics. For NST ceramics the variation of A/B ratio influenced the polarization (P-E) hysteresis loop and better piezoelectric and dielectric responses could be found for small stoichiometry deviations (A/B = 0.97). Regarding Mn doping, as compared to undoped KNN which showed leaky polarization (P-E) hysteresis loops, B-site Mn doped ceramics showed a well saturated, less-leaky hysteresis loop and a significant properties improvement. Impedance spectroscopy was used to assess the role of Mn and a relation between charge transport – defects and ferroelectric response in K0.5Na0.5NbO3 (KNN) and Mn doped KNN ceramics could be established. At room temperature the conduction in KNN which is associated with holes transport is suppressed by Mn doping. Hence Mn addition increases the resistivity of the ceramic, which proved to be very helpful for improving the saturation of the P-E loop. At high temperatures the conduction is dominated by the motion of ionized oxygen vacancies whose concentration increases with Mn doping. Single crystals of potassium sodium niobate (KNN) were grown by a modified high temperature flux method. A boron-modified flux was used to obtain the crystals at a relatively low temperature. XRD, EDS and ICP analysis proved the chemical and crystallographic quality of the crystals. The grown KNN crystals exhibit higher dielectric permittivity (29,100) at the tetragonal-to-cubic phase transition temperature, higher remnant polarization (19.4 μC/cm2) and piezoelectric coefficient (160 pC/N) when compared with the standard KNN ceramics. KNN single crystals domain structure was characterized for the first time by piezoforce response microscopy. It could be observed that <001> - oriented potassium sodium niobate (KNN) single crystals reveal a long range ordered domain pattern of parallel 180° domains with zig-zag 90° domains. From the comparison of KNN Single crystals to ceramics, It is argued that the presence in KNN single crystal (and absence in KNN ceramics) of such a long range order specific domain pattern that is its fingerprint accounts for the improved properties of single crystals. These results have broad implications for the expanded use of KNN materials, by establishing a relation between the domain patterns and the dielectric and ferroelectric response of single crystals and ceramics and by indicating ways of achieving maximised properties in KNN materials. Polarized Raman analysis of ferroelectric potassium sodium niobate (K0.5Na0.5)NbO3 (KNN) single crystals was performed. For the first time, an evidence is provided that supports the assignment of KNN single crystals structure to the monoclinic symmetry at room temperature. Intensities of A′, A″ and mixed A′+A″ phonons have been theoretically calculated and compared with the experimental data in dependence of crystal rotation, which allowed the precise determination of the Raman tensor coefficients for (non-leaking) modes in monoclinic KNN. In relation to the previous literature, this study clarifies that assigning monoclinic phase is more suitable than the orthorhombic one. In addition, this study is the basis for non-destructive assessments of domain distribution by Raman spectroscopy in KNN-based lead-free ferroelectrics with complex structures. Searching a deeper understanding of the electrical behaviour of both KNN single crystal and polycrystalline materials for the sake of designing optimized KNN materials, a comparative study at the level of charge transport and point defects was carried out by impedance spectroscopy. KNN single crystals showed lower conductivity than polycrystals from room temperature up to 200 ºC, but above this temperature polycrystalline KNN displays lower conductivity. The low temperature (T < 200 ºC) behaviour reflects the different processing conditions of both ceramics and single crystals, which account for less defects prone to charge transport in the case of single crystals. As temperature increases (T > 200 ºC) single crystals become more conductive than polycrystalline samples, in which grain boundaries act as barriers to charge transport. For even higher temperatures the conductivity difference between both is increased due to the contribution of ionic conduction in single crystals. Indeed the values of activation energy calculated to the high temperature range (T > 300 ºC) were 1.60 and 0.97 eV, confirming the charge transport due to ionic conduction and ionized oxygen vacancies in single crystals and polycrystalline KNN, respectively. It is suggested that single crystals with low defects content and improved electromechanical properties could be a better choice for room temperature applications, though at high temperatures less conductive ceramics may be the choice, depending on the targeted use. Aiming at engineering the properties of KNN polycrystals towards the performance of single crystals, the preparation and properties study of (001) – oriented (K0.5Na0.5)0.98Li0.02NbO3 (KNNL) ceramics obtained by templated grain growth (TGG) using KNN single crystals as templates was undertaken. The choice of KNN single crystals templates is related with their better properties and to their unique domain structure which were envisaged as a tool for templating better properties in KNN ceramics too. X-ray diffraction analysis revealed for the templated ceramics a monoclinic structure at room temperature and a Lotgering factor (f) of 40% which confirmed texture development. These textured ceramics exhibit a long range ordered domain pattern consisting of 90º and 180º domains, similar to the one observed in the single crystals. Enhanced dielectric (13017 at TC), ferroelectric (2Pr = 42.8 μC/cm2) and piezoelectric (d33 = 280 pC/N) properties are observed for textured KNNL ceramics as compared to the randomly oriented ones. This behaviour is suggested to be due to the long range ordered domain patterns observed in the textured ceramics. The obtained results as compared with the data previously reported on texture KNN based ceramics confirm that superior properties were found due to ordered repeated domain pattern. This study provides an useful approach towards properties improvement of KNN-based piezoelectric ceramics. Overall, the present results bring a significant contribution to the pool of knowledge on the properties of sodium potassium niobate materials: a relation between the domain patterns and di-, ferro-, and piezo-electric response of single crystals and ceramics was demonstrated and ways of engineering maximised properties in KNN materials, for example by texturing were established. This contribution is envisaged to have broad implications for the expanded use of KNN over the alternative lead-based materials.