Novel temperature-activated, humidity-sensitive optical sensor

A novel, colorimetric, temperature-activated humidity indicator is presented, with a colour change based on the semi-reversible aggregation of thiazine dyes (esp. methylene blue, MB) encapsulated within the polymer, hydroxypropyl cellulose (HPC). The initially purple MB/HPC film is activated by heat treatment at 370 °C for 4 s, at which point the film (with a colour associated with a highly aggregated form of MB; λmax = 530 nm) becomes blue (indicating the presence of monomeric and dimeric MB; i.e. with λmax = 665; 605 nm respectively). The blue, heat-treated MB/HPC films respond to an ambient environment with a relative humidity (RH) exceeding 70% at 21 °C within seconds, returning to their initial purple colour. This colour change is irreversible until the film is heat-treated once more. When exposed to a lower RH of up to ca. 47%, the film is stable in its blue form. In contrast, a MB/HPC film treated only at 220 °C for 15 s also turns a blue colour and responds in the same way to a RH value of ca. 70%, but it is unstable at moderate RH 37-50% values, so that it gradually returns to its purple form over a period of approximately 6 hours. The possible use of the high heat-treated MB/HPC humidity indicator in the packaging of goods that cannot tolerate high RH, such as dry foods and electronics, is discussed.

The Use of a Pressure-Indicating Sensor Film to Provide Feedback upon Hydrogel-Forming Microneedle Array Self-Application In Vivo

PURPOSE:
To evaluate the combination of a pressure-indicating sensor film with hydrogel-forming microneedle arrays, as a method of feedback to confirm MN insertion in vivo.
METHODS:
Pilot in vitro insertion studies were conducted using a Texture Analyser to insert MN arrays, coupled with a pressure-indicating sensor film, at varying forces into excised neonatal porcine skin. In vivo studies involved twenty human volunteers, who self-applied two hydrogel-forming MN arrays, one with a pressure-indicating sensor film incorporated and one without. Optical coherence tomography was employed to measure the resulting penetration depth and colorimetric analysis to investigate the associated colour change of the pressure-indicating sensor film.
RESULTS:
Microneedle insertion was achieved in vitro at three different forces, demonstrating the colour change of the pressure-indicating sensor film upon application of increasing pressure. When self-applied in vivo, there was no significant difference in the microneedle penetration depth resulting from each type of array, with a mean depth of 237 μm recorded. When the pressure-indicating sensor film was present, a colour change occurred upon each application, providing evidence of insertion.
CONCLUSIONS:
For the first time, this study shows how the incorporation of a simple, low-cost pressure-indicating sensor film can indicate microneedle insertion in vitro and in vivo, providing visual feedback to assure the user of correct application. Such a strategy may enhance usability of a microneedle device and, hence, assist in the future translation of the technology to widespread clinical use.