Preparation and surface modification of submicron YAl2 particles by mixed milling with magnesium for fabricating YAl2p/MgLiAl composites

A new process for the preparation and surface modification of submicron YAl2 intermetallic particles was proposed to control the agglomeration of ultrafine YAl2 particles and interface in the fabrication of YAl2p/MgLiAl composites. The morphological and structural evolution during mechanical milling of YAl2 powders (< 30 μm) with magnesium particles (~ 100 μm) has been characterized by scanning electron microscopy, transmission electron microscopy, and X-ray diffraction. The results show that YAl2 particles are refined to submicron scale and separately cladded in magnesium coatings after mixed milling with magnesium particles for 20 h. Mechanical and metallurgical bonds have been found in YAl2/Mg interfaces without any interface reactions. Both the refining and mechanical activation efficiencies for YAl2 particles are enhanced, which may be related to the addition of magnesium particles leading to atomic solid solution and playing a role as “dispersion stabilizer”.

Fabrication of Ti-Al coatings by mechanical alloying method

By means of the mechanical alloying (MA) method, Al and Ti + Al coatings were deposited on Ti alloy substrates. During the mechano-activation processing, the substrate surface was impacted by a large number of flying balls along with particles of powder. The repeated ball collisions with the substrate resulted in the deposition of powder on its surface. MA technique produced Ti + Al coating with a thickness of 200 µm and Al one with a thickness of 50 µm after 2 h milling at room temperature. The as-synthesized coatings showed structures with high apparent density and free of porosity. The surface morphology of the MA-coatings was very rough. Annealing treatment led to the leveling of this uneven morphology. Annealing at temperatures ranging between 600 °C and 1100 °C gave different aluminide phases on the samples. In the case of Al coating, Al3Ti and Ti3Al compound were observed upon heating up to 1100 °C. In the case of Ti + Al coating, Al3Ti, Al2Ti, TiAl and Ti3Al were formed on the surface.

Creation of damage-free ferroelectric nanocapacitors via focused ion beam milling

We present a novel method for creating damage-free ferroelectric nanostructures with a focused ion beam milling machine. Using a standard e-beam photoresist followed by a dilute acid wash, nanostructures ranging in size from 1 mu m down to 250 nm were created in a 90 nm thick lead zirconate titanate ( PZT) wafer. Transmission electron microscopy and piezoresponse force microscopy ( PFM) confirmed that the surfaces of the nanostructures remained damage free during fabrication, and showed no gallium implantation, and that there was no degradation of ferroelectric properties. In fact DC strain loops, obtained using PFM, demonstrated that the nanostructures have a higher piezoresponse than unmilled films. As the samples did not have any top hard mask, the method presented is unique as it allows for imaging of the top surface to understand edge effects in well-defined nanostructures. In addition, as no post-mill annealing was necessary, it facilitates investigation of nanoscale domain mechanisms without process-induced artefacts.