Thickness independence of true phase transition temperatures in barium strontium titanate films

The functional properties of two types of barium strontium titanate (BST) thin film capacitor structures were studied: one set of structures was made using pulsed-laser deposition (PLD) and the other using chemical solution deposition. While initial observations on PLD films looking at the behavior of T-m (the temperature at which the maximum dielectric constant was observed) and T-c(*) (from Curie-Weiss analysis) suggested that the paraelectric-ferroelectric phase transition was progressively depressed in temperature as BST film thickness was reduced, further work suggested that this was not the case. Rather, it appears that the temperatures at which phase transitions occur in the thin films are independent of film thickness. Further, the fact that in many cases three transitions are observable, suggests that the sequence of symmetry transitions that occur in the thin films are the same as in bulk single crystals. This new observation could have implications for the validity of the theoretically produced thin film phase diagrams derived by Pertsev [Phys. Rev. Lett. 80, 1988 (1998)] and extended by Ban and Alpay [J. Appl. Phys. 91, 9288 (2002)]. In addition, the fact that T-m measured for virgin films does not correlate well with the inherent phase transition behavior, suggests that the use of T-m alone to infer information about the thermodynamics of thin film capacitor behavior, may not be sufficient. (C) 2004 American Institute of Physics.

Electrode field penetration: A new interpretation of tunneling currents in barium strontium titanate (BST) thin films

This paper shows that penetration of the applied electric field into the electrodes of a ferroelectric thin film capacitor produces both an interfacial capacitance and an effective mechanism for electron tunneling. The model predictions are compared with experimental results on Au-BST-SrRuO3 capacitors of varying thicknesses, and the agreement is excellent.

Investigation of dead-layer thickness in SrRuO3/Ba0.5Sr0.5TiO3/Au thin-film capacitors

Thin-film capacitors, with barium strontium titanate (BST) dielectric layers between 7.5 and 950 nm in thickness, were fabricated by pulsed-laser deposition. Both crystallography and cation chemistry were consistent with successful growth of the BST perovskite. At room temperature, all capacitors displayed frequency dispersion such that epsilon (100 kHz)/epsilon (100 Hz) was greater than 0.75. The dielectric constant as a function of thickness was fitted, using the series capacitor model, for BST thicknesses greater than 70 nm. This yielded a large interfacial d(i)/epsilon (i) ratio of 0.40 +/-0.05 nm, implying a highly visible parasitic dead layer within the capacitor structure. Modeled consideration of the dielectric behavior for BST films, whose total thickness was below that of the dead layer, predicted anomalies in the plots of d/epsilon against d at the dead-layer thickness. In the capacitors studied here, no anomaly was observed. Hence, either (i) 7.5 nm is an upper limit for the total dead-layer thickness in the SRO/BST/Au system, or (ii) dielectric collapse is not associated with a distinct interfacial dead layer, and is instead due to a through-film effect. (C) 2001 American Institute of Physics.

Scaling of domain periodicity with thickness measured in BaTiO3 single crystal lamellae and comparison with other ferroics

The focused ion beam microscope has been used to cut parallel-sided {100}-oriented thin lamellae of single crystal barium titanate with controlled thicknesses, ranging from 530 nm to 70 nm. Scanning transmission electron microscopy has been used to examine domain configurations. In all cases, stripe domains were observed with {011}-type domain walls in perovskite unit-cell axes, suggesting 90 degrees domains with polarization in the plane of the lamellae. The domain widths were found to vary as the square root of the lamellar thickness, consistent with Kittel's law, and its later development by Mitsui and Furuichi and by Roytburd. An investigation into the manner in which domain period adapts to thickness gradient was undertaken on both wedge-shaped lamellae and lamellae with discrete terraces. It was found that when the thickness gradient was perpendicular to the domain walls, a continuous change in domain periodicity occurred, but if the thickness gradient was parallel to the domain walls, periodicity changes were accommodated through discrete domain bifurcation. Data were then compared with other work in literature, on both ferroelectric and ferromagnetic systems, from which conclusions on the widespread applicability of Kittel's law in ferroics were made.

Intrinsic dielectric response in ferroelectric nano-capacitors

Measurements on 'free-standing' single-crystal barium titanate capacitors with thickness down to 75 nm show a dielectric response typical of large single crystals, rather than conventional thin films. There is a notable absence of any broadening or temperature shift of the dielectric peak or loss tangent. Peak dielectric constants of similar to25 000 are observed, and Curie-Weiss analysis demonstrates first order transformation behaviour. This is in dramatic contrast to results on conventionally deposited thin film capacitor heterostructures, which show large dielectric peak broadening and temperature shifts (e.g. Parker et al 2002 Appl. Phys. Lett. 81 340), as well as an apparent change in the nature-of the paraelectric-ferroelectric transition from first to second order. Our data are compatible with a recent model by Bratkovsky and Levanyuk (2004 Preprint cond-mat/0402100), which attributes dielectric peak broadening to gradient terms that will exist in any thin film capacitor heterostructure. The observed recovery of first order transformation behaviour is consistent with the absence of significant substrate clamping in our experiment, as modelled by Pertsev et al (1998,Phys. Rev. Lett. 80 1988), and illustrates that the second order behaviour seen in conventionally deposited thin films cannot be attributed to the effects of reduced dimensionality in the system, nor to the influence of an intrinsic universal interfacial capacitance associated with the electrode- ferroelectric interface.

Toward Self-Assembled Ferroelectric Random Access Memories: Hard-Wired Switching Capacitor Arrays with Almost Tb/in.2 Densities

We report on the successful fabrication of arrays of switchable nanocapacitors made by harnessing the self-assembly of materials. The structures are composed of arrays of 20-40 nm diameter Pt nanowires, spaced 50-100 nm apart, electrodeposited through nanoporous alumina onto a thin film lower electrode on a silicon wafer. A thin film ferroelectric (both barium titanate (BTO) and lead zirconium titanate (PZT)) has been deposited on top of the nanowire array, followed by the deposition of thin film upper electrodes. The PZT nanocapacitors exhibit hysteresis loops with substantial remnant polarizations, while although the switching performance was inferior, the low-field characteristics of the BTO nanocapacitors show dielectric behavior comparable to conventional thin film heterostructures. While registration is not sufficient for commercial RAM production, this is nevertheless an embryonic form of the highest density hard-wired FRAM capacitor array reported to date and compares favorably with atomic force microscopy read-write densities.

Studies of switching kinetics in ferroelectric thin films

Experimental studies are reported concerning the importance of interfacial capacitance (including electrode screening, space-charge layers, and/or chemically discrete dead layers). on domain switching behaviour in thin films of ferroelectric lead zirconate-titanate (PZT), strontium bismuth tantalate (SBT), and barium strontium titanate (BST). Emphasis is placed upon studies at applied field values very near the coercive field E, asymmetry in fatigue for positive and negative polarity coercive fields, and in the case of BST, of the coexistence of ferroelectric and paraelectric phases Studies of dielectric loss show important correlations between tan 6 and fatigue (polarization decrease) as a function of bipolar switching cycles N. This is a priori not obvious, since the former is a linear response and the latter, a nonlinear response. Modelling of enlarged interfacial,space-charge layers in PZT films and chemically distinct dead (paraelectric) layers in BST films shows contradictory tendencies of coercive-voltage changes with the growth of passive layers.

Switching dynamics in ferroelectric thin films: An experimental survey

We have conducted a broad survey of switching behavior in thin films of a range of ferroelectric materials, including some materials that are not typically considered for FeRAM applications, and are hence less studied. The materials studied include: strontium bismuth tantalate (SBT), barium strontium titanate (BST), lead zicronate titanate (PZT), and potassium nitrate (KNO3). Switching in ferroelectric thin films is typically considered to occur by domain nucleation and growth. We discuss two models of frequency dependence of coercive field, the Ishisbashi-Orihara theory where the limiting step is domain growth and the model of Du and Chen where the limiting step is nucleation. While both models fit the data fairly well the temperature dependence of our results on PZT and BST suggest that the nucleation model of Du and Chen is more appropriate for the experimental results that we have obtained.

Sulfur-tolerant NOx storage traps: an infrared and thermodynamic study of the reactions of alkali and alkaline-earth metal sulfates

The sulfur tolerance of a barium-containing NOx storage/reduction trap was investigated using infrared analysis. It was confirmed that barium carbonate could be replaced by barium sulfate by reaction with low concentrations of sulfur dioxide (50 ppm) in the presence of large concentrations of carbon dioxide (10%) at temperatures up to 700 degreesC. These sulfates could at least be partially removed by switching to hydrogen-rich conditions at elevated temperatures. Thermodynamic calculations were used to evaluate the effects of gas composition and temperature on the various reactions of barium sulfate and carbonate under oxidizing and reducing conditions. These calculations clearly showed that if, under a hydrogen-rich atmosphere, carbon dioxide is included as a reactant and barium carbonate as a product then barium sulfate can be removed by reaction with carbon dioxide at a much lower temperature than is possible by decomposition to barium oxide. It was also found that if hydrogen sulfide was included as a product of decomposition of barium sulfate instead of sulfur dioxide then the temperature of reaction could be significantly lowered. Similar calculations were conducted using a selection of other alkaline-earth and alkali metals. In this case calculations were simulated in a gas mixture containing carbon monoxide, hydrogen and carbon dioxide with partial pressures similar to those encountered in real exhausts during switches to rich conditions. The results indicated that there are metals such as lithium and strontium with less stable sulfates than barium, which may also possess sufficient NOx storage capacity to give sulfur-tolerant NOx traps.

The influence of Notches on Domain Dynamics in Ferroelectric Nanowires

The extent to which notches inhibit axial switching of polarization in ferroelectric nanowires was investigated by monitoring the switching behavior of single crystal BaTiO(3) wires before and after patterning triangular notches along their lengths. Static zero-field domain patterns suggested a strong domain-notch interaction, implying that notches should act as pinning sites for domain wall propagation. Surprisingly though, notches appeared to assist, rather than inhibit, polar switching. The origin of this effect was rationalized using finite element modeling of the electric field distribution along the notched wire; it was found that the air gap associated with the notch acted to enhance the local field, both in the air, and in the adjacent region of the ferroelectric. It seems that this local field enhancement outweighs any pinning interactions.

Variable temperature, variable-gap Otto prism coupler for use in a vacuum environment

The field of surface polariton physics really took off with the prism coupling techniques developed by Kretschmann and Raether, and by Otto. This article reports on the construction and operation of a rotatable, in vacuo, variable temperature, Otto coupler with a coupling gap that can be varied by remote control. The specific design attributes of the system offer additional advantages to those of standard Otto systems of (i) temperature variation (ambient to 85 K), and (ii) the use of a valuable, additional reference point, namely the gap-independent reflectance at the Brewster angle at any given, fixed temperature. The instrument is placed firmly in a historical context of developments in the field. The efficacy of the coupler is demonstrated by sample attenuated total reflectance results on films of platinum, niobium, and yttrium barium copper oxide and on aluminum/gallium arsenide (Al/GaAs) Schottky diode structures. (C) 2000 American Institute of Physics. [S0034-6748(00)02411-4].