Ethylene oxidation over platinum: In situ electrochemically controlled promotion using Na-beta'' alumina and studies with a Pt(111)/Na model catalyst

Electrochemically modified ethylene oxidation over a PI film supported on the Na+ ion conductor beta '' alumina has been studied over a range of conditions encompassing both promotion and poisoning, The system exhibits reversible behavior, and the data are interpreted in terms of (i) Na-enhanced oxygen chemisorption and (ii) poisoning of the surface by accumulation of Na compounds. At low Na coverages the first effect results in increased competitive adsorption of oxygen at the expense of ethylene, resulting in an increased rate, At very negative catalyst potentials (high Na coverage) both effects operate to poison the system: the increased strength of the Pt-O bond and coverage of the catalytic surface by compounds of Na strongly suppress the rate, Kinetic and spectroscopic results for ethylene oxidation over a Pt(111)-Na model catalyst shed light on important aspects of the electrochemically controlled system, Low levels of Na promote the reaction and high levels poison it, mirroring the behavior observed under electrochemical control and strongly suggesting that sodium pumped from the solid electrolyte is the key species, XP and Auger spectra show that under reaction conditions, the sodium exists as a surface carbonate. Post-reaction TPD spectra and the use of (CO)-C-13 demonstrate that CO is formed as a stable reaction intermediate, The observed activation energy (56 +/- 3 kJ/mol) is similar to that measured for CO oxidation under comparable conditions, suggesting that the rate limiting step is CO oxidation. (C) 1996 Academic Press, Inc.

The role of low coverage sodium surface species on electrochemical promotion in a Pt/YSZ system

The effect of sodium-modification on the catalyst and electrocatalytic properties of a platinum catalyst supported on a YSZ solid electrolyte was studied. Increasing the sodium coverage on the catalyst surface appears to block some of the three-phase boundary (tpb) sites and reduces the rate of the charge transfer reaction. The promotion of the platinum surface reaction (ethylene oxidation) seems to a first approximation to be a function of the rate of oxygen supply or removal to or from the surface irrespective of whether this is contaminated by sodium or not (samples with sodium contamination require a higher overpotential to achieve the same current density as a clean sample because of poisoning in the tpb). At high negative polarisations (oxygen removed from the surface) the sodium contaminated samples show a significant increase in rate, possibly due to the decomposition of e.g. sodium hydroxides and carbonates. © 2012 Elsevier B.V.

Electrochemical promotion of a metal catalyst supported on a mixed-ionic conductor

It has been found that the catalytic activity and selectivity of a metal film deposited on a solid electrolyte could be enhanced dramatically and in a reversible way by applying an electrical current or potential between the metal catalyst and the counter electrode (also deposited on the electrolyte). This phenomenon is know as NEMCA [S. Bebelis, C.G. Vayenas, Journal of Catalysis, 118 (1989) 125-146.] or electrochemical promotion (EP) [J. Prichard, Nature, 343 (1990) 592.] of catalysis. Yttria-doped barium zirconate, BaZr_0.9Y_0.1O_{3 - α} (BZY), a known proton conductor, has been used in this study. It has been reported that proton conducting perovskites can, under the appropriate conditions, act also as oxide ion conductors. In mixed conducting systems the mechanism of conduction depends upon the gas atmosphere that to which the material is exposed. Therefore, the use of a mixed ionic (oxide ion and proton) conducting membrane as a support for a platinum catalyst may facilitate the tuning of the promotional behaviour of the catalyst by allowing the control of the conduction mechanism of the electrolyte. The conductivity of BZY under different atmospheres was measured and the presence of oxide ion conduction under the appropriate conditions was confirmed. Moreover, kinetic experiments on ethylene oxidation corroborated the findings from the conductivity measurements showing that the use of a mixed ionic conductor allows for the tuning of the reaction rate. © 2006 Elsevier B.V. All rights reserved.

The partially reversible formation of Li-metal particles on a solid Li electrolyte:applications toward nanobatteries

The feasibility of large-scale implementation of Li-air batteries (LABs) hinges on understanding the thermodynamic and kinetic factors that control charge-discharge rates, efficiency and life times. Here, the kinetics of bias-induced reactions is explored locally on the surface of Li-ion conductive glass ceramics, a preferred electrolyte for LABs, using direct current-voltage and strain spectroscopies. Above a critical bias, particle growth kinetics were found to be linear in both the bias and time domains. Partial reversibility was observed for Li particles as evidenced by the presence of anodic peaks following the Li(+) reduction, as well an associated reduction in particle height. The degree of reversibility was highest for the smallest particles formed. These observations thus suggest the possibility of producing nanobatteries with an active anode volume of the order of 0.1 al.

Fabrication and characterization of SSZ tape cast electrolyte-supported solid oxide fuel cells

A 10 mol%Sc₂O₃, 1 mol%CeO₂ stabilized-ZrO₂ (SSZ) powder was successfully prepared using the sol-gel method. Subsequent SSZ electrolyte pellets were prepared by tape casting technique and sintered at 1400 °C, 1450 °C, 1500 °C, 1550 °C and 1600 °C. These were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and electrochemical impedance spectroscopy (EIS). SSZ showed a pure cubic phase after sintering, the grain size of SSZ increased with the increase of sintering temperature. The SSZ sintered at 1550 °C showed the highest ion conductivity. The maximum power densities of Ni-SSZ/SSZ/La_0.8Sr_0.2MnO_3-δ (LSM)-SSZ single cells sintered at 1550 °C were 0.18, 0.36, 0.51 and 0.72 W cm^-2 at 650, 700, 750 and 800 °C, respectively. The polarization resistance (R_p) of the single cell attained 0.201 Ω cm² at 800 °C.

In-situ Monitoring of Solid Oxide Electrolysis Cells

High temperature co-electrolysis of steam and carbon dioxide using a solid oxide cell (SOC) has been shown to be an efficient route to produce syngas (CO + H-2), which can then be converted to synthetic fuel. Optimization of co-electrolysis requires detailed understanding of the complex reactions, transport processes and degradation mechanisms occurring in the SOC during operation. Thermal imaging, Raman spectroscopy and Diffuse Reflectance Infrared Fourier Transform Spectroscopy are being developed to probe in-situ both the reactions occurring during operation and any associated changes within the structure of the electrodes and electrolyte. Here we discuss the challenges in designing experimental apparatus suitable for high temperature operation with optical spectroscopic access to the areas of the SOC that are of interest. In particular, issues with sealing, temperature gradients, signal strength and cell configuration are discussed and final designs are presented. Preliminary results obtained during co-electrolysis operation are also presented.

Electrochemical promotion of catalysis using solid-state proton-conducting membranes

A solid-state electrochemical reactor with ceramic proton-conducting membrane has been used to study the effect of electrochemically induced hydrogen spillover on the catalytic activity of platinum during ethylene oxidation. Suitable proton-conducting electrolyte membranes (Gd-doped BaPrO ₃ (BPG) and Y-doped BaZrO₃ (BZY)) were fabricated. These materials were chosen because of their protonic conductivity in the operational temperature region of the reaction (400-700 °C). The BZY-based electrochemical cell was used to investigate the open-circuit voltage (OCV) dependence on H₂ partial pressure with comparison being made to the theoretical OCV as predicted by the Nernst equation. Furthermore, the BZY pellets were used to study the effect of proton transfer of the catalytic activity of platinum during ethylene oxidation. The reaction was found to exhibit electrochemical promotion at 400 °C and to be electrophilic in nature, i.e. proton addition to the platinum surface resulted in an increase in reaction rate. At higher temperatures, the rate was not affected, within experimental error, by proton addition or removal. Under similar conditions, AC impedance showed that there was a large overall cell resistance at 400 °C with significantly decreased resistance at higher temperatures. It is possible that there could be a relationship between large cell resistances and the onset of electrochemical promotion in this system but there is, as yet, no conclusive evidence for this. © 2003 Elsevier B.V. All rights reserved.

Development of the Oxide Ion Conductor Na0.5Bi0.5TiO3 (NBT) for Solid Oxide Cells

Na0.5Bi0.5TiO3 (NBT) is a well-known lead-free piezoelectric material with potential to replace lead zirconate titanate (PZT),1 however high leakage conductivity for the material has been widely reported.2 Through a combination of Impedance Spectroscopy (IS), O2- ion transference (EMF) number experiments and O18 tracer diffusion measurements, combined with Time-of-flight Secondary Ion Mass Spectrometry (TOFSIMS), it was identified that this leakage conductivity was due to oxygen ion conductivity. The volatilization of bismuth during synthesis, causing oxygen vacancies, is believed to be responsible for the leakage conductivity.3 The oxide-ion conductivity, when doped with magnesium, exceeds that of yttria-stabilized zirconia (YSZ) at ~500 °C,3 making it a potential electrolyte material for Intermediate Temperature Solid Oxide Cells (ITSOCs). Figure 1 shows the comparison of bulk oxide ion conductivity between 2 at.% Mg-doped NBT and other known oxide ion conductors.

As part of the UK wide £5.7m 4CU project, research has concentrated on trying to develop NBT for use in Intermediate Temperature Solid Oxide Cells (ITSOCS). With the aim of achieving mixed ionic and electronic conduction, transition metals were chemically doped on to the Ti-site. A range of experimental techniques was used to characterize the materials aimed at investigating both conductivity and material structure (Scanning Electron Microscopy (SEM), IS, X-ray Photoelectron Spectroscopy (XPS) and X-ray Absorption Spectroscopy (XAS)). The potential for NBT as an ITSOC material, as well as the challenges of developing the material, will be discussed.

(1) Takenaka T. et al. Jpn. J. Appl. Phys 1999, 30, 2236.

(2) Hiruma Y. et al. J. Appl. Phys 2009, 105, 084112.

(3) Li. M. et al. Nature Materials 2013, 13, 31.

Flash-Sintering and Characterization of La0.8Sr0.2Ga0.8Mg0.2O3-δ Electrolytes for Solid Oxide Fuel Cells

La_0.8Sr_0.2Ga_0.8Mg_0.2O_3-δ (LSGM), a promising electrolyte material for intermediate temperature solid oxide fuel cells, can be sintered to a fully dense state by a flash-sintering technique. In this work, LSGM is sintered by the current-limiting flash-sintering process at 690°C under an electric field of 100 V cm^-1, in comparison with up to 1400°C or even higher temperature in conventional furnace sintering. The resultant LSGM samples are investigated by scanning electron microscopy, X-ray diffraction, and electrochemical impedance spectroscopy. The SEM images exhibit well-densified microstructures while XRD results show that the perovskite structure after flash-sintering does not changed. EIS results show that the conductivity of LSGM sintered by the current-limiting flash-sintering process increases with sintering current density value. The conductivity of samples sintered at 120 mA mm^-2 reaches 0.049 σ cm^-1 at 800°C, which is approximate to the value of conventional sintered LSGM samples at 1400°C. Additionally, the flash-sintering process is interpreted by Joule heating theory. Therefore, the current-limiting flash-sintering technique is proved to be an energy-efficient and eligible approach for the densification of LSGM and other materials requiring high sintering temperature.

Fabrication and evaluation of NiO/Y2O3-stabilized-ZrO2 hollow fibers for anode-supported micro-tubular solid oxide fuel cells

In this work NiO/3mol% Y₂O₃-ZrO₂ (3YSZ) and NiO/8mol% Y₂O₃-ZrO₂ (8YSZ) hollow fibers were prepared by phase-inversion. The effect of different kinds of YSZ (3YSZ and 8YSZ) on the porosity, electrical conductivity, shrinkage and flexural strength of the hollow fibers were systematically evaluated. When compared with Ni-8YSZ the porosity and shrinkage of Ni-3YSZ hollow fibers increases while the electrical conductivity decreases, while at the same time also exhibiting enhanced flexural strength. Single cells with Ni-3YSZ and Ni-8YSZ hollow fibers as the supported anode were successfully fabricated showing maximum power densities of 0.53 and 0.67Wcm^-2 at 800°C, respectively. Furthermore, in order to improve the cell performance, a Ni-8YSZ anode functional layer was added between the electrolyte and Ni-YSZ hollow fiber. Here enhanced peak power densities of 0.79 and 0.73Wcm^-2 were achieved at 800°C for single cells with Ni-3YSZ and Ni-8YSZ hollow fibers, respectively.

High performance cobalt-free Cu1.4Mn1.6O4 spinel oxide as an intermediate temperature solid oxide fuel cell cathode

In this work Cu_1.4Mn_1.6O₄ (CMO) spinel oxide is prepared and evaluated as a novel cobalt-free cathode for intermediate temperature solid oxide fuel cells (IT-SOFCs). Single phase CMO powder with cubic structure is identified using XRD. XPS results confirm that mixed Cu⁺/Cu²⁺ and Mn³⁺/Mn⁴⁺ couples exist in the CMO sample, and a maximum conductivity of 78 S cm⁻¹ is achieved at 800 °C. Meanwhile, CMO oxide shows good thermal and chemical compatibility with a 10 mol% Sc₂O₃ stabilized ZrO₂ (ScSZ) electrolyte material. Impedance spectroscopy measurements reveals that CMO exhibits a low polarization resistance of 0.143 Ω cm² at 800 °C. Furthermore, a Ni-ScSZ/ScSZ/CMO single cell demonstrates a maximum power density of 1076 mW cm⁻² at 800 °C under H₂ (3% H₂O) as the fuel and ambient air as the oxidant. These results indicate that Cu_1.4Mn_1.6O₄ is a superior and promising cathode material for IT-SOFCs.

Improved electrochemical performance of Sr2Fe1.5Mo0.4Nb0.1O6-δ -Sm0.2Ce0.8O2-δ composite cathodes by a one-pot method for intermediate temperature solid oxide fuel cells

In this paper, Sr₂Fe_1.5Mo_0.4Nb_0.1O_6-δ (SFMNb)-xSm_0.2Ce_0.8O_2-δ (SDC) (x = 0, 20, 30, 40, 50 wt%) composite cathode materials were synthesized by a one-pot combustion method to improve the electrochemical performance of SFMNb cathode for intermediate temperature solid oxide fuel cells (IT-SOFCs). The fabrication of composite cathodes by adding SDC to SFMNb is conducive to providing extended electrochemical reaction zones for oxygen reduction reactions (ORR). X-ray diffraction (XRD) demonstrates that SFMNb is chemically compatible with SDC electrolytes at temperature up to 1100 °C. Scanning electron microscope (SEM) indicates that the SFMNb-SDC composite cathodes have a porous network nanostructure as well as the single phase SFMNb. The conductivity and thermal expansion coefficient of the composite cathodes decrease with the increased content of SDC, while the electrochemical impedance spectra (EIS) exhibits that SFMNb-40SDC composite cathode has optimal electrochemical performance with low polarization resistance (R_p) on the La_0.9Sr_0.1Ga_0.8Mg_0.2O₃ electrolyte. The R_p of the SFMNb-40SDC composite cathode is about 0.047 Ω cm² at 800 °C in air. A single cell with SFMNb-40SDC cathode also displays favorable discharge performance, whose maximum power density is 1.22 W cm^-2 at 800 °C. All results indicate that SFMNb-40SDC composite material is a promising cathode candidate for IT-SOFCs.