Studies of switching kinetics in ferroelectric thin films

Experimental studies are reported concerning the importance of interfacial capacitance (including electrode screening, space-charge layers, and/or chemically discrete dead layers). on domain switching behaviour in thin films of ferroelectric lead zirconate-titanate (PZT), strontium bismuth tantalate (SBT), and barium strontium titanate (BST). Emphasis is placed upon studies at applied field values very near the coercive field E, asymmetry in fatigue for positive and negative polarity coercive fields, and in the case of BST, of the coexistence of ferroelectric and paraelectric phases Studies of dielectric loss show important correlations between tan 6 and fatigue (polarization decrease) as a function of bipolar switching cycles N. This is a priori not obvious, since the former is a linear response and the latter, a nonlinear response. Modelling of enlarged interfacial,space-charge layers in PZT films and chemically distinct dead (paraelectric) layers in BST films shows contradictory tendencies of coercive-voltage changes with the growth of passive layers.

Switching dynamics in ferroelectric thin films: An experimental survey

We have conducted a broad survey of switching behavior in thin films of a range of ferroelectric materials, including some materials that are not typically considered for FeRAM applications, and are hence less studied. The materials studied include: strontium bismuth tantalate (SBT), barium strontium titanate (BST), lead zicronate titanate (PZT), and potassium nitrate (KNO3). Switching in ferroelectric thin films is typically considered to occur by domain nucleation and growth. We discuss two models of frequency dependence of coercive field, the Ishisbashi-Orihara theory where the limiting step is domain growth and the model of Du and Chen where the limiting step is nucleation. While both models fit the data fairly well the temperature dependence of our results on PZT and BST suggest that the nucleation model of Du and Chen is more appropriate for the experimental results that we have obtained.

Structural and electrical anisotropy of (001)-, (116)-, and (103)-oriented epitaxial SrBi2Ta2O9 thin films on SrTiO3 substrates grown by pulsed laser deposition

Epitaxial SrBi2Ta2O9 (SBT) thin films with well-defined (001), (116), and (103) orientations have been grown by pulsed laser deposition on (001)-, (011)-, and (111)-oriented Nb-doped SrTiO3 substrates. X-ray diffraction pole figure and phi -scan measurements revealed that the three-dimensional epitaxial orientation relation SBT(001)parallel to SrTiO3(001), and SBT[1(1) over bar 0]parallel to SrTiO3[100] is valid for all cases of SET thin films on SrTiO3 substrates, irrespective of their orientations. Atomic force microscopy images of the c-axis-oriented SET revealed polyhedron-shaped grains showing spiral growth around screw dislocations. The terrace steps of the c-axis-oriented SET films were integral multiples of a quarter of the lattice parameter c of SBT (similar to 0.6 nm). The grains of (103)-oriented SET films were arranged in a triple-domain configuration consistent with the symmetry of the SrTiO3(111) substrate. The measured remanent polarization (2P(r)) and coercive field (2E(c)) of (116)-oriented SBT films were 9.6 muC/cm(2) and 168 kV/cm, respectively, for a maximum applied electric field of 320 kV/cm. Higher remanent polarization (2P(r)=10.4 muC/cm(2)) and lower coercive field (2E(c)=104 kV/cm) than those of SBT(116) films were observed in (103)-oriented SET thin films, and (001)-oriented SET revealed no ferroelectricity along the [001] axis. The dielectric constants of (001)-, (116)-, and (103)-oriented SBT were 133, 155, and 189, respectively. (C) 2000 American Institute of Physics.

Epitaxial growth of non-c-oriented ferroelectric SrBi2Ta2O9 thin films on Si(100) substrates

Epitaxial SrBi2Ta2O9 (SBT) thin films with well-defined (116) orientation have been grown by pulsed laser deposition on Si(100) substrates covered with an yttria-stabilized ZrO2 (YSZ) buffer layer and an epitaxial layer of electrically conductive SrRuO3. Studies on the in-plane crystallographic relations between SrRuO3 and YSZ revealed a rectangle-on-cube epitaxy with respect to the substrate. X-ray diffraction pole figure measurements revealed well defined orientation relations, viz. SBT(116)\\ SrRuO3(110)\\ YSZ(100)\\ Si(100), SBT[110]\\ SrRuO3[001], and SrRuO3[111]\\ YSZ[110]\\ Si[110].