Stimulation of phosphate uptake and polyphosphate accumulation by activated sludge microorganisms in response to sulfite addition

Enhanced phosphate removal from wastewaters is dependent on the synthesis and intracellular accumulation of polyphosphate by sludge microorganisms. However the role played by polyphosphate in microbial metabolism and the factors that trigger its formation remain poorly-understood. Many examples of the accumulation of the biopolymer by environmental microorganisms are documented; these include a recent report of the presence of large polyphosphate inclusions in sulfur-oxidizing marine bacteria. To investigate whether any link might exist outside the marine environment between the presence of reduced sulfur compounds and enhanced levels of microbial phosphate uptake and polyphosphate accumulation, activated sludge cultures were grown under laboratory conditions in media that contained sulfite, thiosulfate, hydrosulfite or tetrathionate. Only in the presence of sulfite was there any evidence of a stimulatory effect; in medium that contained 0.5 mM sodium sulfite some 17% more phosphate was removed by the sludge, whilst there was an almost two-fold increase in intracellular polyphosphate levels. No indications of sulfite toxicity were observed.

The preparation of highly ordered single layer ZSM-5 coating on prefabricated stainless steel microchannels

An elegant way to prepare catalytically active microreactors is by applying a coating of zeolite crystals onto a metal microchannel structure. In this study the hydrothermal formation of ZSM-5 zeolitic coatings on AISI 316 stainless steel plates with a microchannel structure has been investigated at different synthesis mixture compositions. The procedures of coating and thermal treatment have also been optimized. Obtaining a uniform thickness of the coating within 0.5 mm wide microchannels requires a careful control of various synthesis variables. The role of these factors and the problems in the synthesis of these zeolitic coatings are discussed. In general, the synthesis is most sensitive to the H2O/Si ratio as well as to the orientation of the plates with respect to the gravity vector. Ratios of H2O/Si=130 and Si/template=13 were found to be optimal for the formation of a zeolitic film with a thickness of one crystal at a temperature of 130 degreesC and a synthesis time of about 35 h. At such conditions, ZSM-5 crystals were formed with a typical size of 1.5 mu mx1.5 mu mx1.0 mum and a very narrow (within 0.2 mum) crystal size distribution. The prepared samples proved to be active in the selective catalytic reduction (SCR) of NO with ammonia. The activity tests have been carried out in a plate-type microreactor. The microreactor shows no mass transfer limitations and a larger SCR reaction rate is observed in comparison with pelletized Ce-ZSM-5 catalysts; (C) 2001 Elsevier Science B.V. All rights reserved.

Structural and magnetic properties of Ni>1-x>Zn>x>Fe>2>O>4> (x=0, 0.5 and 1) nanopowders prepared by sol-gel method

>A series of nanostructured Ni-Zn ferrites Ni1-xZnxFe2O4 (x=0, 0.5 and 1) with a grain size from 24 to 65 nm have been prepared with a sol-gel method. The effect of composition and sintering temperature on morphology, magnetic properties, Curie temperature, specific heating rate at 295 kHz and hysteresis loss have been studied. The highest coercivity of 50 and 40 Oe, were obtained for NiFe2O4 and Ni0.5Zn0.5Fe2O4 samples with the grain size of 35 and 29 nm, respectively. The coercivity of Ni and Ni-Zn mixed ferrites decreased with temperature. The Bloch exponent was 1.5 for all samples. As the grain size increased, the Curie temperature of NiFe2O4 increased from 849 to 859 K. The highest saturation magnetization of 70 emu/g at 298 K and the highest specific heating rate of 1.6 K/s under radiofrequency heating at 295 kHz were observed over NiFe2O4 calcined at 1073 K. Both the magnitude of the hysteresis loss and the temperature dependence of the loss are influenced by the sintering temperature and composition.>

Development of sampling methods for Raman analysis of solid dosage forms of therapeutic and illicit drugs

The results of a study aimed at determining the most important experimental parameters for automated, quantitative analysis of solid dosage form pharmaceuticals (seized and model 'ecstasy' tablets) are reported. Data obtained with a macro-Raman spectrometer were complemented by micro-Raman measurements, which gave information on particle size and provided excellent data for developing statistical models of the sampling errors associated with collecting data as a series of grid points on the tablets' surface. Spectra recorded at single points on the surface of seized MDMA-caffeine-lactose tablets with a Raman microscope (lambda(ex) = 785 nm, 3 mum diameter spot) were typically dominated by one or other of the three components, consistent with Raman mapping data which showed the drug and caffeine microcrystals were ca 40 mum in diameter. Spectra collected with a microscope from eight points on a 200 mum grid were combined and in the resultant spectra the average value of the Raman band intensity ratio used to quantify the MDMA: caffeine ratio, mu(r), was 1.19 with an unacceptably high standard deviation, sigma(r), of 1.20. In contrast, with a conventional macro-Raman system (150 mum spot diameter), combined eight grid point data gave mu(r) = 1.47 with sigma(r) = 0.16. A simple statistical model which could be used to predict sigma(r) under the various conditions used was developed. The model showed that the decrease in sigma(r) on moving to a 150 mum spot was too large to be due entirely to the increased spot diameter but was consistent with the increased sampling volume that arose from a combination of the larger spot size and depth of focus in the macroscopic system. With the macro-Raman system, combining 64 grid points (0.5 mm spacing and 1-2 s accumulation per point) to give a single averaged spectrum for a tablet was found to be a practical balance between minimizing sampling errors and keeping overhead times at an acceptable level. The effectiveness of this sampling strategy was also tested by quantitative analysis of a set of model ecstasy tablets prepared from MDEA-sorbitol (0-30% by mass MDEA). A simple univariate calibration model of averaged 64 point data had R-2 = 0.998 and an r.m.s. standard error of prediction of 1.1% whereas data obtained by sampling just four points on the same tablet showed deviations from the calibration of up to 5%.

Dioxouranium(VI) extraction in microchannels using ionic liquids

The extraction of uranium(VI) from aqueous nitric acid solutions by tributylphosphate {TBP; 30%(v/v)} dissolved in the ionic liquid 1-butyl-3-methylimidazolium bis{(trifluoromethyl)sulfonyl}amide was investigated. The experiments were performed in a Teflon microchannel of 0.5 mm internal diameter, while the dioxouranium(VI) concentrations in the aqueous and the ionic liquid phases were determined by UV-Vis spectroscopy. The effects of initial nitric acid concentration (0.01-3 M), residence time, and phase flow rate ratio were studied. It was found that, with increasing nitric acid concentration, the percentage of dioxouranium(VI) extracted decreased and then increased again, while the extraction efficiency followed a slightly different trend. Overall mass transfer coefficients varied between 0.049 s and 0.312 s . © 2012 Elsevier B.V. All rights reserved.

Electrochemical sensor for catechol and dopamine based on a catalytic molecularly imprinted polymer-conducting polymer hybrid recognition element

One of the difficulties with using molecularly imprinted polymers (MIPs) and other electrically insulating materials as the recognition element in electrochemical sensors is the lack of a direct path for the conduction of electrons from the active sites to the electrode. We have sought to address this problem through the preparation and characterization of novel hybrid materials combining a catalytic MIP, capable of oxidizing the template, catechol, with an electrically conducting polymer. In this way a network of "molecular wires" assists in the conduction of electrons from the active sites within the MIP to the electrode surface. This was made possible by the design of a new monomer that combines orthogonal polymerizable functionality; comprising an aniline group and a methacrylamide. Conducting films were prepared on the surface of electrodes (Au on glass) by electropolymerization of the aniline moiety. A layer of MIP was photochemically grafted over the polyaniline, via N,N'-diethyldithiocarbamic acid benzyl ester (iniferter) activation of the methacrylamide groups. Detection of catechol by the hybrid-MIP sensor was found to be specific, and catechol oxidation was detected by cyclic voltammetry at the optimized operating conditions: potential range -0.6 V to +0.8 V (vs Ag/AgCl), scan rate 50 mV/s, PBS pH 7.4. The calibration curve for catechol was found to be linear to 144 µM, with a limit of detection of 228 nM. Catechol and dopamine were detected by the sensor, whereas analogues and potentially interfering compounds, including phenol, resorcinol, hydroquinone, serotonin, and ascorbic acid, had minimal effect (=3%) on the detection of either analyte. Nonimprinted hybrid electrodes and bare gold electrodes failed to give any response to catechol at concentrations below 0.5 mM. Finally, the catalytic properties of the sensor were characterized by chronoamperometry and were found to be consistent with Michaelis-Menten kinetics. © 2009 American Chemical Society.

Studies of the Room-Temperature Multiferroic Pb(Fe>0.5>Ta>0.5>)>0.4>(Zr>0.53>Ti>0.47>)>0.6>O>3>: Resonant Ultrasound Spectroscopy, Dielectric, and Magnetic Phenomena

Recently, lead iron tantalate/lead zirconium titanate (PZTFT) was demonstrated to possess large, but unreliable, magnetoelectric coupling at room temperature. Such large coupling would be desirable for device applications but reproducibility would also be critical. To better understand the coupling, the properties of all 3 ferroic order parameters, elastic, electric, and magnetic, believed to be present in the material across a range of temperatures, are investigated. In high temperature elastic data, an anomaly is observed at the orthorhombic mm2 to tetragonal 4mm transition, Tot = 475 K, and a softening trend is observed as the temperature is increased toward 1300 K, where the material is known to become cubic. Thermal degradation makes it impos- sible to measure elastic behavior up to this temperature, however. In the low temperature region, there are elastic anomalies near ≈40 K and in the range 160–245 K. The former is interpreted as being due to a magnetic ordering transition and the latter is interpreted as a hysteretic regime of mixed rhom- bohedral and orthorhombic structures. Electrical and magnetic data collected below room temperature show anomalies at remarkably similar temperature ranges to the elastic data. These observations are used to suggest that the three order parameters in PZTFT are strongly coupled.

One-dimensional porous La>0.5>Sr>0.5>CoO>2.91> nanotubes as a highly efficient electrocatalyst for rechargeable lithium-oxygen batteries

>The electrochemical performance of one-dimensional porous La>0.5>Sr>0.5>CoO>2.91> nanotubes as a cathode catalyst for rechargeable nonaqueous lithium-oxygen (Li-O>2>) batteries is reported here for the first time. In this study, one-dimensional porous La>0.5>Sr>0.5>CoO>2.91> nanotubes were prepared by a simple and efficient electrospinning technique. These materials displayed an initial discharge capacity of 7205 mAh g>-1> with a plateau at around 2.66 V at a current density of 100 mA g>-1>. It was found that the La>0.5>Sr>0.5>CoO>2.91> nanotubes promoted both oxygen reduction and oxygen evolution reactions in alkaline media and a nonaqueous electrolyte, thereby improving the energy and coulombic efficiency of the Li-O>2> batteries. The cyclability was maintained for 85 cycles without any sharp decay under a limited discharge depth of 1000 mAh g>-1>, suggesting that such a bifunctional electrocatalyst is a promising candidate for the oxygen electrode in Li-O>2> batteries.>

Investigation into the effect of molybdenum-site substitution on the performance of Sr>2>Fe>1.5>Mo>0.5>O>6-δ >for intermediate temperature solid oxide fuel cells

>In this paper, niobium doping is evaluated as a means of enhancing the electrochemical performance of a Sr>2>Fe>1.5>Mo>0.5>O>6-δ> (SFM) perovskite structure cathode material for intermediate temperature solid oxide fuel cells (IT-SOFCs) applications. As the radius of Nb approximates that of Mo and exhibits +4/+5 mixed valences, its substitution is expected to improve material performance. A series of Sr>2>Fe>1.5>Mo>0.5-x>Nb>x>O>6-δ> (x = 0.05, 0.10, 0.15, 0.20) cathode materials are prepared and the phase structure, chemical compatibility, microstructure, electrical conductivity, polarization resistance and power generation are systematically characterized. Among the series of samples, Sr>2>Fe>1.5>Mo>0.4>Nb>0.10>O>6-δ> (SFMNb>0.10>) exhibits the highest conductivity value of 30 S cm>-1> at 550°C, and the lowest area specific resistance of 0.068 Ω cm>2> at 800°C. Furthermore, an anode-supported single cell incorporating a SFMNb>0.10> cathode presents a maximum power density of 1102 mW cm>-2> at 800°C. Furthermore no obvious performance degradation is observed over 15 h at 750°C with wet H>2>(3% H>2>O) as fuel and ambient air as the oxidant. These results demonstrate that SFMNb shows great promise as a novel cathode material for IT-SOFCs.>

Investigation into the effect of Fe-site substitution on the performance of Sr>2>Fe>1.5>Mo>0.5>O>6-δ >anodes for SOFCs

>Ni-substituted Sr>2>Fe>1.5-x>Ni>x>Mo>0.5>O>6-δ> (SFNM) materials have been investigated as anode catalysts for intermediate temperature solid oxide fuel cells. Reduced samples (x = 0.05 and 0.1) maintained the initial perovskite structure after reduction in H>2>, while metallic nickel particles were detected on the grain surface for x = 0.2 and 0.3 using transmission electron microscopy. Temperature programmed reduction results indicate that the stable temperature for SFNM samples under reduction conditions decreases with Ni content. In addition, X-ray photoelectron spectroscopy analysis suggests that the incorporation of Ni affects the conductivity of SFNM through changing the ratios of Fe>3+>/Fe>2+> and Mo>6+>/Mo>5+>. Sr>2>Fe>1.4>Ni>0.1>Mo>0.5>O>6-δ> shows the highest electrical conductivity of 20.6 S cm>-1> at 800 °C in H>2>. The performance of this anode was further tested with electrolyte-supported cells, giving 380 mW cm>-2> at 750 °C in H>2>, hence demonstrating that Ni doping in the B-site is beneficial for Sr>2>Fe>1.5>Mo>0.5>O>6-δ> anode performance. >

Characterisation of a two-dimensional liquid-filled ion chamber detector array using flattened and unflattened beams for small fields, small MUs and high dose-rates

In this study, the PTW 1000SRS array with Octavius 4D phantom was characterised for FF and FFF beams. MU linearity, field size, dose rate, dose per pulse (DPP) response and dynamic conformal arc treatment accuracy of the 1000SRS array were assessed for 6MV, 6FFF and 10FFF beams using a Varian TrueBeam STx linac. The measurements were compared with a pinpoint IC, microdiamond IC and EBT3 Gafchromic film. Measured dose profiles and FWHMs were compared with film measurements. Verification of FFF volumetric modulated arc therapy (VMAT) clinical plans were assessed using gamma analysis with 3%/3 mm and 2%/2 mm tolerances (10% threshold). To assess the effect of cross calibration dose rate, clinical plans with different dose rates were delivered and analysed. Output factors agreed with film measurements to within 4.5% for fields between 0.5 and 1 cm and within 2.7% for field sizes between 1.5 and 10 cm and were highly correlated with the microdiamond IC detector. Field sizes measured with the 1000SRS array were within 0.5 mm of film measurements. A drop in response of up to 1.8%, 2.4% and 5.2% for 6MV, 6FFF and 10FFF beams respectively was observed with increasing nominal dose rate. With an increase in DPP, a drop of up to 1.7%, 2.4% and 4.2% was observed in 6MV, 6FFF and 10FFF respectively. The differences in dose following dynamic conformal arc deliveries were less than 1% (all energies) from calculated. Delivered VMAT plans showed an average pass percentage of 99.5(±0.8)% and 98.4(±3.4)% with 2%/2 mm criteria for 6FFF and 10FFF respectively. A drop to 97.7(±2.2)% and 88.4(±9.6)% were observed for 6FFF and 10FFF respectively when plans were delivered at the minimum dose rate and calibrated at the maximum dose rate. Calibration using a beam with the average dose rate of the plan may be an efficient method to overcome the dose rate effects observed by the 1000SRS array.