Performance and wear of coated carbide drill in machining of carbon fibre reinforced composite/titanium stack

In this research we investigate the performance of drilling process in carbon fibre reinforced composite (CFC) material, titanium alloy and the hybrid stack of these two materials, using coated carbide drill bit. We study the effect of the process parameters such as the feed rate and speed on the induced forces and torques, also on the wear of drill and surface roughness of the holes. In the composite material the percentage of surface damage in both drilling CFC on its own and drilling in stack form is estimated. Also, the effect of worn drill on the surface damage is identified. In the titanium, the burr formation in stack and non-stack form is investigated. The wear of the drill results in increased forces and torques required for drilling. This increases the surface delaminations substantially at the entrance in drilling of CFC. However, the surface roughness of the holes reduces with the wear of the drill in CFC drilling. Also, the surface delamination and surface roughness of the holes in the CFC whilst drilled in hybrid form reduces significantly. This is despite the increase of the forces and torques required in drilling CFC in stack form. Copyright © 2012 Inderscience Enterprises Ltd.

Analysis of the compressive behaviour of the three-dimensional printed porous titanium for dental implants using a modified cellular solid model

A set of cylindrical porous titanium test samples were produced using the three-dimensional printing and sintering method with samples sintered at 900 °C, 1000 °C, 1100 °C, 1200 °C or 1300 °C. Following compression testing, it was apparent that the stress-strain curves were similar in shape to the curves that represent cellular solids. This is despite a relative density twice as high as what is considered the threshold for defining a cellular solid. As final sintering temperature increased, the compressive behaviour developed from being elastic-brittle to elastic-plastic and while Young's modulus remained fairly constant in the region of 1.5 GPa, there was a corresponding increase in 0.2% proof stress of approximately 40-80 MPa. The cellular solid model consists of two equations that predict Young's modulus and yield or proof stress. By fitting to experimental data and consideration of porous morphology, appropriate changes to the geometry constants allow modification of the current models to predict with better accuracy the behaviour of porous materials with higher relative densities (lower porosity).

Comparative study of tool life and hole quality in drilling of CFRP/titanium stack using coated carbide drill

The use of hybrid materials including carbon fiber reinforced plastics (CFRPs) and lightweight metals such as titanium are increasing particularly in aerospace applications. Multi-material stacks require a number of holes for the assembly purposes. In this research, drilling trials have been carried out in CFRP, Ti-6Al-4V and CFRP/Ti-6Al-4V stack workpieces using AlTiN coated tungsten carbide drill bit. The effects of process parameters have been investigated. The thrust force, torque, burr formation, delamination, surface roughness and tool wear have been analyzed at various processing condition. The experimental results have shown that the thrust force, torque, burr formation and the average surface roughness increase with the increased feed rate and decrease with the increased cutting speed in drilling of Ti-6Al-4V. In drilling CFRP, delamination and the average surface roughness has similar tendency with the cutting parameters however thrust force and torque rises with the increased cutting speed. The results showed that after making 15 holes in CFRP/Ti-6Al-4V stack, measured thrust forces were increased by 20% in CFRP and by 45% in Ti-6Al-4V. Delamination was found to be much smaller in drilling of CFRP in stack from compared to drilling single CFRP. Tool life was significantly shortened in drilling of stack due to the combination of the wear mechanisms.

Di-mu-chloro-bis({2-[(2-hydroxyethyl)iminomethyl]phenolato-kappa N-3,O,O '} nickel(II)) methanol solvate

The title compound, [Ni2Cl2(C9H10NO2)(2)]center dot CH3OH, is a dinuclear unit built up by two nickel(II) complexes, bridged by two Cl atoms. The coordination geometry around each Ni-II atom can be considered as distorted square-pyramidal, with the tridendate chelate Schiff base ligands coordinating in a trans conformation through their imine N atom and phenoxy and alkoxy O atoms.

Atmospheric pressure chemical vapour deposition of boron doped titanium dioxide for photocatalytic water reduction and oxidation

Boron-doped titanium dioxide (B-TiO) films were deposited by atmospheric pressure chemical vapour deposition of titanium(iv) chloride, ethyl acetate and tri-isopropyl borate on steel and fluorine-doped-tin oxide substrates at 500, 550 and 600 °C, respectively. The films were characterised using powder X-ray diffraction (PXRD), which showed anatase phase TiO at lower deposition temperatures (500 and 550 °C) and rutile at higher deposition temperatures (600 °C). X-ray photoelectron spectroscopy (XPS) showed a dopant level of 0.9 at% B in an O-substitutional position. The ability of the films to reduce water was tested in a sacrificial system using 365 nm UV light with an irradiance of 2 mW cm. Hydrogen production rates of B-TiO at 24 μL cm h far exceeded undoped TiO at 2.6 μL cm h. The B-TiO samples were also shown to be active for water oxidation in a sacrificial solution. Photocurrent density tests also revealed that B-doped samples performed better, with an earlier onset of photocurrent. © 2013 The Owner Societies.

Soil-Geochemical Factors controlling the Distribution and Oral Bioaccessibility of Nickel, Vanadium and Chromium in Northern Ireland Soils

Geogenic nickel (Ni), vanadium (V) and chromium (Cr) are present at elevated levels in soils in Northern Ireland. Whilst Ni, V and Cr total soil concentrations share common geological origins, their respective levels of oral bioaccessibility are influenced by different soil-geochemical factors. Oral bioaccessibility extractions were carried out on 145 soil samples overlying 9 different bedrock types to measure the bioaccessible portions of Ni, V and Cr. Principal component analysis identified two components (PC1 and PC2) accounting for 69% of variance across 13 variables from the Northern Ireland Tellus Survey geochemical data. PC1 was associated with underlying basalt bedrock, higher bioaccessible Cr concentrations and lower Ni bioaccessibility. PC2 was associated with regional variance in soil chemistry and hosted factors accounting for higher Ni and V bioaccessibility. Eight per cent of total V was solubilised by gastric extraction on average across the study area. High median proportions of bioaccessible Ni were observed in soils overlying sedimentary rock types. Whilst Cr bioaccessible fractions were low (max = 5.4%), the highest measured bioaccessible Cr concentration reached 10.0 mg kg-1, explained by factors linked to PC1 including high total Cr concentrations in soils overlying basalt bedrock.

Effect of fretting on fatigue performance of Ti-1023 titanium alloy

The plain fatigue and fretting fatigue tests of Ti-1023 titanium alloy were performed using a high-frequency push-pull fatigue testing machine. Both σmax versus number of cycles to failure curves were obtained for comparative analysis of the fretting effect on fatigue performance of the titanium alloy. Meanwhile, by analyzing the fracture of plain fatigue and fretting fatigue, the fretting scar and the fretting debris observed by scanning electron microscopy (SEM), the mechanism of fretting fatigue failure of Ti-1023 titanium alloy is discussed. The fretting fatigue strength of Ti-1023 titanium alloy is 175 MPa under 10 MPa contact pressure, which is 21% of plain fatigue strength (836 MPa). Under fretting condition, the Ti-1023 titanium alloy fatigue fracture failure occurs in a shorter fatigue life. When it comes to σmax versus number of cycles to failure curves, data points in the range of 106–107 cycles under plain fatigue condition moved to the range of 105–106 under fretting fatigue condition. The integrity of the fatigue specimen surface was seriously damaged under the effect of fretting. With the alternating stress loaded on specimen, the stress concentrated on the surface of fretting area, which brought earlier the initiation and propagation of crack.

Effect of shotpeening on sliding wear and tensile behavior of titanium implant alloys

Titanium has good biocompatibility and so its alloys are used as implant materials, but they suffer from having poor wear resistance. This research aims to improve the wear resistance and the tensile strength of titanium alloys potentially for implant applications. Titanium alloys Ti–6Al–4V and Ti–6Al–7Nb were subjected to shotpeening process to study the wear and tensile behavior. An improvement in the wear resistance has been achieved due to surface hardening of these alloys by the process of shotpeening. Surface microhardness of shotpeened Ti–6Al–4V and Ti–6Al–7Nb alloys has increased by 113 and 58 HV(0.5), respectively. After shotpeening, ultimate tensile strength of Ti–6Al–4V increased from 1000 MPa to 1150 MPa, higher than improvement obtained for heat treated titanium specimens. The results confirm that shotpeening pre-treatment improved tensile and sliding wear behavior of Ti–6Al–4V and Ti–6Al–7Nb alloys. In addition, shotpeening increased surface roughness.

Correlation of phantom-based and log file patient-specific QA with complexity scores for VMAT

The motivation for this study was to reduce physics workload relating to patient- specific quality assurance (QA). VMAT plan delivery accuracy was determined from analysis of pre- and on-treatment trajectory log files and phantom-based ionization chamber array measurements. The correlation in this combination of measurements for patient-specific QA was investigated. The relationship between delivery errors and plan complexity was investigated as a potential method to further reduce patient-specific QA workload. Thirty VMAT plans from three treatment sites - prostate only, prostate and pelvic node (PPN), and head and neck (H&N) - were retrospectively analyzed in this work. The 2D fluence delivery reconstructed from pretreatment and on-treatment trajectory log files was compared with the planned fluence using gamma analysis. Pretreatment dose delivery verification was also car- ried out using gamma analysis of ionization chamber array measurements compared with calculated doses. Pearson correlations were used to explore any relationship between trajectory log file (pretreatment and on-treatment) and ionization chamber array gamma results (pretreatment). Plan complexity was assessed using the MU/ arc and the modulation complexity score (MCS), with Pearson correlations used to examine any relationships between complexity metrics and plan delivery accu- racy. Trajectory log files were also used to further explore the accuracy of MLC and gantry positions. Pretreatment 1%/1 mm gamma passing rates for trajectory log file analysis were 99.1% (98.7%-99.2%), 99.3% (99.1%-99.5%), and 98.4% (97.3%-98.8%) (median (IQR)) for prostate, PPN, and H&N, respectively, and were significantly correlated to on-treatment trajectory log file gamma results (R = 0.989, p < 0.001). Pretreatment ionization chamber array (2%/2 mm) gamma results were also significantly correlated with on-treatment trajectory log file gamma results (R = 0.623, p < 0.001). Furthermore, all gamma results displayed a significant correlation with MCS (R > 0.57, p < 0.001), but not with MU/arc. Average MLC position and gantry angle errors were 0.001 ± 0.002 mm and 0.025° ± 0.008° over all treatment sites and were not found to affect delivery accuracy. However, vari- ability in MLC speed was found to be directly related to MLC position accuracy. The accuracy of VMAT plan delivery assessed using pretreatment trajectory log file fluence delivery and ionization chamber array measurements were strongly correlated with on-treatment trajectory log file fluence delivery. The strong corre- lation between trajectory log file and phantom-based gamma results demonstrates potential to reduce our current patient-specific QA. Additionally, insight into MLC and gantry position accuracy through trajectory log file analysis and the strong cor- relation between gamma analysis results and the MCS could also provide further methodologies to both optimize the VMAT planning and QA process. 

The photocatalytic decomposition of microcystin-LR using selected titanium dioxide materials

Microcystins (cyclic heptapeptides) produced by a number of freshwater cyanobacteria are a potential cause for concern in potable water supplies due to their acute and chronic toxicity. TiO₂ photocatalysis is a promising technology for removal of these toxins from drinking water. It is, however, necessary to have a sufficient knowledge of how the catalyst materials cause the degradation of the toxins through the photocatalytic process. The present study reports microcystin degradation products of the photocatalytic oxidation by using a number of commercial TiO₂ powder (P25, PC50, PC500 and UV100) and granular (KO1, KO3, TiCat-C, TiCat-S) materials, so aiding the mechanistic understanding of this process. Liquid chromatography-mass spectrometry analysis demonstrated that the major destruction pathway of microcystin for all the catalysts tested followed almost the same pathway, indicating the physical properties of the catalysts had little effects on the degradation pathway of microcystin-LR. 

Photocatalytic destruction of geosmin using novel pelleted titanium dioxide

Geosmin is produced by cyanobacteria and actinomycetes in surface waters. It causes undesirable earthy off-flavours in freshwater fish and is a major concern for the drinking water industry. This paper presents the first published study on the use of the novel pelleted Ti0₂ photocatalyst, Hombikat K01/C, for the removal of geosmin from water. Ti0₂ in pelleted form eliminates the requirement for the separation of the catalyst from the water following treatment which is normally the case with the widely used powdered catalysts. A laboratory reactor was designed to limit system loss since the compound adsorbs to a wide range of surfaces. Initial concentration, aeration rate and irradiation were evaluated. It was found that degradation of geosmin followed the Langmuir-Hinshelwood model. Elevated aeration had no effect on the photocatalytic removal of geosmin, but increasing irradiation was found to increase degradation rates. The catalyst proved effective within 10 min under optimum conditions. 

The application of Raman and anti-stokes Raman spectroscopy for in situ monitoring of structural changes in laser irradiated titanium dioxide materials

The use of Raman and anti-stokes Raman spectroscopy to investigate the effect of exposure to high power laser radiation on the crystalline phases of TiO₂ has been investigated. Measurement of the changes, over several time integrals, in the Raman and anti-stokes Raman of TiO₂ spectra with exposure to laser radiation is reported. Raman and anti-stokes Raman provide detail on both the structure and the kinetic process of changes in crystalline phases in the titania material. The effect of laser exposure resulted in the generation of increasing amounts of the rutile crystalline phase from the anatase crystalline phase during exposure. The Raman spectra displayed bands at 144 cm^-1 (A1g), 197 cm^-1 (Eg), 398 cm^-1 (B1g), 515 cm^-1 (A1g), and 640 cm^-1 (Eg) assigned to anatase which were replaced by bands at 143 cm^-1 (B1g), 235 cm^-1 (2 phonon process), 448 cm^-1 (Eg) and 612 cm^-1 (A1g) which were assigned to rutile. This indicated that laser irradiation of TiO₂ changes the crystalline phase from anatase to rutile. Raman and anti-stokes Raman are highly sensitive to the crystalline forms of TiO₂ and allow characterisation of the effect of laser irradiation upon TiO₂. This technique would also be applicable as an in situ method for monitoring changes during the laser irradiation process

On-line monitoring of laser modification of titanium dioxide using optical surface second harmonic

TiO₂ photocatalysis is a promising technology for the destruction of organic pollutants in both waste and potable waters with the mineralisation of a wide range of compounds having been reported. TiO ₂ has many advantages over other semiconductors, it is highly photoreactive, cheap, non-toxic, chemically and biologically inert, and photostable. The photocatalytic activity of TiO₂ has been shown to depend upon many criteria including the ratio of anatase/rutile crystal phase, particle size and oxidation state. This paper reports the use of optical surface second harmonic generation (SSHG) to monitor modifications in TiO ₂ powder induced following laser treatment. SSHG is a non-contact, non-destructive technique, which is highly sensitive to both surface chemical and physical changes. Results show that three different SSH intensities were observable as the TiO₂ samples were irradiated with the laser light. These regions were related to changes in chemical characteristics and particle size of the TiO₂ powder

The destruction of 2-methylisoborneol and geosmin using titanium dioxide photocatalysis

Geosmin (GSM) and 2-methylisoborneol (MIB) are semi-volatile compounds produced by cyanobacteria in surface waters. These compounds present problems to the drinking water industry and in aquaculture because they can taint water and fish producing an earthy-musty flavour. This paper presents an initial study on the use of TiO₂ photocatalysis for the destruction of these compounds in water. The process proved effective with the complete destruction of MIB and GSM being achieved within 60 min. These results suggest that TiO₂ photocatalysis will be a successful method for removal of taint compounds from potable water supplies and fish farms.