Reductive elimination of hypersilyl halides from zinc (II) complexes. Implications for electropositive metal thin film growth

Treatment of Zn(Si(SiMe3)3)2 with ZnX2 (X = Cl, Br, I) in tetrahydrofuran (THF) at 23 °C afforded [Zn(Si(SiMe3)3)X(THF)]2 in 83–99% yield. X-ray crystal structures revealed dimeric structures with Zn2X2 cores. Thermogravimetric analyses of [Zn(Si(SiMe3)3)X(THF)]2 demonstrated a loss of coordinated THF between 50 and 155 °C and then single-step weight losses between 200 and 275 °C. The nonvolatile residue was zinc metal in all cases. Bulk thermolyses of [Zn(Si(SiMe3)3)X(THF)]2 between 210 and 250 °C afforded zinc metal in 97–99% yield, Si(SiMe3)3X in 91–94% yield, and THF in 81–98% yield. Density functional theory calculations confirmed that zinc formation becomes energetically favorable upon THF loss. Similar reactions are likely to be general for M(SiR3)n/MXn pairs and may lead to new metal-film-growth processes for chemical vapor deposition and atomic layer deposition.

Silent screen: book review.

Book Review. Kevin Rockett, Irish film censorship: a cultural journey from silent cinema to internet pornography (Dublin, 2004) and Mary Corcoran and Mark O'Brien (eds), Political censorship and the democratic state: the Irish broadcasting ban (Dublin, 2005)

Simultaneous observation of current oscillations and porous film growth during anodization of InP

The observation of spontaneous oscillations in current during the anodization of InP in relatively high concentrations of KOH electrolytes is reported. Oscillations were observed under potential sweep and constant potential conditions. Well-defined oscillations are observed during linear potential sweeps of InP in 5 mol dm-3 KOH to potentials above ∼1.7 V (SCE) at scan rates in the range of 50 to 500 mV s-1. The oscillations observed exhibit an asymmetrical current versus potential profile, and the charge per cycle was found to increase linearly with potential. More complex oscillatory behavior was observed under constant potential conditions. Periodic damped oscillations are observed in high concentrations of electrolyte whereas undamped sinusoidal oscillations are observed in relatively lower concentrations. In both cases, the anodization of InP results in porous InP formation, and the current in the oscillatory region corresponds to the cyclical effective area changes due to pitting dissolution of the InP surface with the coincidental growth of a thick porous In2O3 film.

Anodic behavior of InP: film growth, porous structures and current oscillations.

We review our recent work on the anodization of InP in KOH electrolytes. The anodic oxidation processes are shown to be remarkably different in different concentrations of KOH. Anodization in 2 - 5 mol dm-3 KOH electrolytes results in the formation of porous InP layers but, under similar conditions in a 1 mol dm-3 KOH, no porous structure is evident. Rather, the InP electrode is covered with a thin, compact surface film at lower potentials and, at higher potentials, a highly porous surface film is formed which cracks on drying. Anodization of electrodes in 2 - 5 mol dm-3 KOH results in the formation of porous InP under both potential sweep and constant potential conditions. The porosity is estimated at ~65%. A thin layer (~ 30 nm) close to the surface appears to be unmodified. It is observed that this dense, near-surface layer is penetrated by a low density of pores which appear to connected it to the electrolyte. Well-defined oscillations are observed when InP is anodized in both the KOH and (NH4)2S. The charge per cycle remains constant at 0.32 C cm-2 in (NH4)2S but increases linearly with potential in KOH. Although the characteristics of the oscillations in the two systems differ, both show reproducible and well-behaved values of charge per cycle.