Reductive elimination of hypersilyl halides from zinc (II) complexes. Implications for electropositive metal thin film growth

Treatment of Zn(Si(SiMe3)3)2 with ZnX2 (X = Cl, Br, I) in tetrahydrofuran (THF) at 23 °C afforded [Zn(Si(SiMe3)3)X(THF)]2 in 83–99% yield. X-ray crystal structures revealed dimeric structures with Zn2X2 cores. Thermogravimetric analyses of [Zn(Si(SiMe3)3)X(THF)]2 demonstrated a loss of coordinated THF between 50 and 155 °C and then single-step weight losses between 200 and 275 °C. The nonvolatile residue was zinc metal in all cases. Bulk thermolyses of [Zn(Si(SiMe3)3)X(THF)]2 between 210 and 250 °C afforded zinc metal in 97–99% yield, Si(SiMe3)3X in 91–94% yield, and THF in 81–98% yield. Density functional theory calculations confirmed that zinc formation becomes energetically favorable upon THF loss. Similar reactions are likely to be general for M(SiR3)n/MXn pairs and may lead to new metal-film-growth processes for chemical vapor deposition and atomic layer deposition.

Loading effect in copper(II) oxide cluster-surface-modified titanium(IV) oxide on visible- and UV-light activities

Cu(acac)2 is chemisorbed on TiO2 particles [P-25 (anatase/rutile = 4/1 w/w), Degussa] via coordination by surface Ti–OH groups without elimination of the acac ligand. Post-heating of the Cu(acac)2-adsorbed TiO2 at 773 K yields molecular scale copper(II) oxide clusters on the surface (CuO/TiO2). The copper loading amount (Γ/Cu ions nm–2) is controlled in a wide range by the Cu(acac)2 concentration and the chemisorption–calcination cycle number. Valence band (VB) X-ray photoelectron and photoluminescence spectroscopy indicated that the VB maximum of TiO2 rises up with increasing Γ, while vacant midgap levels are generated. The surface modification gives rise to visible-light activity and concomitant significant increase in UV-light activity for the degradation of 2-naphthol and p-cresol. Prolonging irradiation time leads to the decomposition to CO2, which increases in proportion to irradiation time. The photocatalytic activity strongly depends on the loading, Γ, with an optimum value of Γ for the photocatalytic activity. Electrochemical measurements suggest that the surface CuO clusters promote the reduction of adsorbed O2. First principles density functional theory simulations clearly show that, at Γ < 1, unoccupied Cu 3d levels are generated in the midgap region, and at Γ > 1, the VB maximum rises and the unoccupied Cu 3d levels move to the conduction band minimum of TiO2. These results suggest that visible-light excitation of CuO/TiO2 causes the bulk-to-surface interfacial electron transfer at low coverage and the surface-to-bulk interfacial electron transfer at high coverage. We conclude that the surface CuO clusters enhance the separation of photogenerated charge carriers by the interfacial electron transfer and the subsequent reduction of adsorbed O2 to achieve the compatibility of high levels of visible and UV-light activities.

Synthesis of iminophosphine and phosphinoiminol cyclometallated Pt (II) and Pt (IV) chloro complexes and studies into their biological and photophysical properties

This thesis focuses on the synthesis and analysis of novel chloride based platinum complexes derived from iminophosphine and phosphinoamide ligands, along with studies on their reactivity towards substitution and oxidation reactions. Also explored here are the potential applications of these complexes for biological and luminescent purposes. Chapter one provides an extensive overview of platinum coordination chemistry with examples of various mixed donor ligands along with the history of platinum anticancer therapy. It also looks at metals in medicine, both for biological functions as well as for therapeutic purposes and gives a background to some other applications for platinum complexes. Chapter two outlines the design and synthetic strategies employed for the development of novel platinum (II) chloride complexes from iminophosphine and phosphinoamide ligands. Also reported is the cyclometallation of these complexes to form stable tridentate mixed donor platinum (II) compounds. In Chapter three the development of a direct method for displacing a chloride from a platinum metal centre with a desired phosphine is reported. Numerous methods for successful oxidation of the platinum (II) complexes will also be explored, leading to novel platinum (IV) complexes being reported here also. The importance of stabilisation of the displaced anion, chloride, by the solvent system will also be discussed in this chapter. Chapter four investigates the reactivity of the platinum (II) complexes towards two different biomolecules to form novel platinum bio-adducts. The potential application of the platinum (II) cyclometallates as chemotherapeutics will also be explored here using in-vitro cancer cell testing. Finally, luminescence studies are also reported here for the ligands and platinum complexes reported in chapter two and three to investigate potential applications in this field also. Chapter five provides a final conclusion and an overall summary of the entire project as well as identifying key areas for future work.

Atomic layer deposition of copper for CMOS interconnects

This work concerns the atomic layer deposition (ALD) of copper. ALD is a technique that allows conformal coating of difficult topographies such as narrow trenches and holes or even shadowed regions. However, the deposition of pure metals has so far been less successful than the deposition of oxides except for a few exceptions. Challenges include difficulties associated with the reduction of the metal centre of the precursor at reasonable temperatures and the tendency of metals to agglomerate during the growth process. Cu is a metal of special technical interest as it is widely used for interconnects on CMOS devices. These interconnects are usually fabricated by electroplating, which requires the deposition of thin Cu seed layers onto the trenches and vias. Here, ALD is regarded as potential candidate for replacing the current PVD technique, which is expected to reach its limitations as the critical dimensions continue to shrink. This work is separated into two parts. In the first part, a laboratory-scale ALD reactor was constructed and used for the thermal ALD of Cu. In the second part, the potentials of the application of Cu ALD on industry scale fabrication were examined in a joint project with Applied Materials and Intel. Within this project precursors developed by industrial partners were evaluated on a 300 mm Applied Materials metal-ALD chamber modified with a direct RF-plasma source. A feature that makes ALD a popular technique among researchers is the possibility to produce high- level thin film coatings for micro-electronics and nano-technology with relatively simple laboratory- scale reactors. The advanced materials and surfaces group (AMSG) at Tyndall National Institute operates a range of home-built ALD reactors. In order to carry out Cu ALD experiments, modifications to the normal reactor design had to be made. For example a carrier gas mechanism was necessary to facilitate the transport of the low-volatile Cu precursors. Precursors evaluated included the readily available Cu(II)-diketonates Cu-bis(acetylacetonate), Cu-bis(2,2,6,6-tetramethyl-hepta-3,5-dionate) and Cu-bis(1,1,1,5,5,5-hexafluoacetylacetonate) as well as the Cu-ketoiminate Cu-bis(4N-ethylamino- pent-3-en-2-onate), which is also known under the trade name AbaCus (Air Liquide), and the Cu(I)- silylamide 1,3-diisopropyl-imidazolin-2-ylidene Cu(I) hexamethyldisilazide ([NHC]Cu(hmds)), which was developed at Carleton University Ottawa. Forming gas (10 % H2 in Ar) was used as reducing agent except in early experiments where formalin was used. With all precursors an extreme surface selectivity of the deposition process was observed and significant growth was only achieved on platinum-group metals. Improvements in the Cu deposition process were obtained with [NHC]Cu(hmds) compared with the Cu(II) complexes. A possible reason is the reduced oxidation state of the metal centre. Continuous Cu films were obtained on Pd and indications for saturated growth with a rate of about 0.4 Å/cycle were found for deposition at 220 °C. Deposits obtained on Ru consisted of separated islands. Although no continuous films could be obtained in this work the relatively high density of Cu islands obtained was a clear improvement as compared to the deposits grown with Cu(II) complexes. When ultra-thin Pd films were used as substrates, island growth was also observed. A likely reason for this extreme difference to the Cu films obtained on thicker Pd films is the lack of stress compensation within the thin films. The most likely source of stress compensation in the thicker Pd films is the formation of a graded interlayer between Pd and Cu by inter-diffusion. To obtain continuous Cu films on more materials, reduction of the growth temperature was required. This was achieved in the plasma assisted ALD experiments discussed in the second part of this work. The precursors evaluated included the AbaCus compound and CTA-1, an aliphatic Cu-bis(aminoalkoxide), which was supplied by Adeka Corp.. Depositions could be carried out at very low temperatures (60 °C Abacus, 30 °C CTA-1). Metallic Cu could be obtained on all substrate materials investigated, but the shape of the deposits varied significantly between the substrate materials. On most materials (Si, TaN, Al2O3, CDO) Cu grew in isolated nearly spherical islands even at temperatures as low as 30 °C. It was observed that the reason for the island formation is the coalescence of the initial islands to larger, spherical islands instead of forming a continuous film. On the other hand, the formation of nearly two-dimensional islands was observed on Ru. These islands grew together forming a conductive film after a reasonably small number of cycles. The resulting Cu films were of excellent crystal quality and had good electrical properties; e.g. a resistivity of 2.39 µΩ cm was measured for a 47 nm thick film. Moreover, conformal coating of narrow trenches (1 µm deep 100/1 aspect ratio) was demonstrated showing the feasibility of the ALD process.