Effects of water flow on ablation rate and morphological changes in human enamel and dentin after Er:YAG laser irradiation

Purpose: To investigate the laboratory effect of Er:YAG laser on ablation rate and morphological changes in human enamel and dentin with varying water flow. Methods: 23 human third molars were sectioned in mesio-distal and buccal-lingual directions. The slabs were flattened and weighted on an analytical laboratory balance (control). A 4-mm(2) area was demarcated and the samples were randomly assigned into three groups according to water flow employed during the laser irradiation (1.0, 1.5, and 2.0 mL/minute). An Er:YAG laser was used to ablate enamel (80.22-J/cm(2), 300 mJ/4Hz) and dentin (96.26-J/cm(2), 250 mJ/4Hz). After irradiation, the samples were immersed in distilled water for 1 hour and then weighted again. The final mass was obtained and laser-irradiated substrate mass loss was calculated by the difference between the initial and final mass. Afterwards, specimens were prepared for SEM. Results: Data were submitted to ANOVA and Tukey's test (P< 0.05). It was observed that the 2.0 mL/minute resulted in a higher mass loss, 1.0 mL/minute showed a lower mass loss, and 1.5 mL/minute demonstrated intermediate results (P< 0.05). The increase of water flow promoted less melting areas and cracks. Furthermore, dentin was more ablated than enamel. It may be concluded that the water flow of Er:YAG laser and the substrates affected the ablation rate. Among the tested parameters, 2.0 mL/minute improved the ability of ablation in enamel and dentin, with less morphologic surface alteration. (Am J Dent 20 12;25:332-336).

Effects of Er:YAG and Er,Cr:YSGG lasers on dentine hypersensitivity. Short-term clinical evaluation

Dentine hypersensitivity (DH) is a painful condition and is a clinical challenge due to the different treatment strategies available. High-intensity lasers have been studied as a possible option. The aim of this randomized, controlled, double-blind clinical study was to evaluate the effects of Er:YAG and Er,Cr:YSGG lasers on DH. The study group comprised 28 subjects who met the inclusion criteria. A visual analogue scale was used to quantify sensitivity before treatment as baseline, immediately before and immediately after treatment, and 1 week and 1 month after treatment. Teeth were assigned to four groups: group 1 control (no treatment), group 2 Er:YAG laser treatment (2 Hz/32.4 mJ/5.9 J/cm(2)), group 3 Er,Cr:YSGG laser treatment (0.25 W/4.4 J/cm(2)), and group 4 Er,Cr:YSGG laser treatment (0.50 W/ 8.9 J/cm(2)). Data were collected and submitted to statistical analysis for both evaporative (air) and mechanical (probe) stimulation. For both the air and probe stimulation no differences were observed between the pretreatment sensitivities. With the evaporative stimulus, the pain level immediately after treatment was reduced; however, after this the values remained stable. Irradiation with the Er:YAG laser was associated with the lowest level of pain. With the mechanical stimulus, group 4 showed the most pronounced decrease in pain immediately after treatment; however, by the end of the study, pain levels had increased. Groups 1, 2 and 3 showed a reduction in pain that was significantly different from that in group 4 after the 4 weeks of clinical follow up. Based on the results and within the limits of this study, it can be concluded that none of the laser treatments studied was capable of completely eliminating pain, but the Er:YAG and Er,Cr:YSGG lasers are suitable for the treatment of DH.

Nd:YAG Laser Irradiation of Etched/Unetched Dentin Through an Uncured Two-step Etch-and-Rinse Adhesive and its Effect on Microtensile Bond Strength

Purpose: To evaluate whether Nd:YAG laser irradiation of etched and unetched dentin through an uncured adhesive affected the microtensile bond strength (pTBS). Materials and Methods: Flat dentin surfaces were created in 19 extracted human third molars. Adper Single Bond (SB) adhesive was applied over etched (groups 1 to 3) or unetched dentin (groups 4 to 6). The dentin was then irradiated with a Nd:YAG laser through the uncured adhesive, using 0.75 or 1 W power settings, except for the control groups (groups 1 and 4). The adhesive was light cured and composite crowns were built up. After 24 h, the teeth were sectioned into beams, with cross-sectional areas of 0.49 mm(2), and were stressed under tension. Data were statistically analyzed using two-way ANOVA and Tukey's test (alpha = 5%). Dentin surfaces of fractured specimens and the interfaces of untested beams were observed under scanning electron microscopy (SEM). Results: Acid etching, laser irradiation, and their interaction significantly affected bonding (p < 0.05). Laser irradiation did not improve bonding of etched dentin to resin (p > 0.05). However, higher pTBS means were found on unetched lased dentin (groups 5 and 6), but only in comparison to group 4, where neither lasing nor etching was performed. Groups 4 to 6 showed the lowest pTBS means among all groups tested (p < 0.05). Laser irradiation did not change the characteristics of the hybrid layers created, while solidification globules were observed on lased dentin surfaces under SEM. Conclusion: Laser irradiation of dentin through the uncured adhesive did not significantly improve the pTBS in comparison to the suggested manufacturer's technique.

Argon and Nd:YAG Lasers for Caries Prevention in Enamel

Objective: The aim of this study was to investigate the effect of Nd:YAG and argon laser irradiations on enamel demineralization after two different models to induce artificial caries. Background data: It is believed that the use of the high-intensity laser on the dental structure can lead to a more acid-resistant surface. Materials and methods: Twenty-one extracted human third molars were sectioned into tooth quarters. The quarters were distributed in three groups: Group I (control), untreated; Group II, Nd:YAG laser (60 mJ, 15 pps, 47.77 J/cm(2), 30 sec); and Group III, argon laser (250mW, 12 J/cm(2), 48 sec). Tooth quarters from each group were subjected to two different demineralization models: cycle 1, a 14 day demineralization (pH 4.5; 6 h) and remineralization (pH 7.0; 18 h) solutions, 37 degrees C and cycle 2, 48 h in demineralization solution (pH 4.5). Samples were prepared in slices (60-100 mu m thick) to be evaluated under polarized light microscopy. Demineralization areas were measured (mm(2)) (n = 11). Data were analyzed by ANOVA and Tukey's test (p < 0.05). Results: Means followed by different letters are significantly different: 0.25 A (control, cycle 48 h); 0.18 AB (control, cycle 14 days); 0.17 AB (Nd:YAG, cycle 14 days); 0.14 BC (argon, cycle 48 h); 0.09 BC (Nd:YAG, cycle 48 h), and 0.06 C (argon, cycle 14 days). Conclusions: The argon laser was more effective for caries preventive treatment than Nd: YAG laser, showing a smaller demineralization area in enamel.

Microtensile bond strength of resin composite to dentin treated with Er:YAG laser of bleached teeth

The objective of this study was to evaluate the influence of Er:YAG laser (lambda = 2.94 mu m) on microtensile bond strength (mu TBS) and superficial morphology of bovine dentin bleached with 16% carbamide peroxide. Forty bovine teeth blocks (7 x 3 x 3 mm(3)) were randomly assigned to four groups: G1- bleaching and Er:YAG irradiation with energy density of 25.56 J/cm(2) (focused mode); G2 - bleaching; G3 - no-bleaching and Er:YAG irradiation (25.56 J/cm(2)); G4 - control, non-treated. G1 and G2 were bleached with 16% carbamide peroxide for 6 h during 21 days. Afterwards, all blocks were abraded with 320 to 600-grit abrasive papers to obtain flat standardized dentin surfaces. G1 and G3 were Er:YAG irradiated. Blocks were immediately restored with 4-mm-high composite resin (Adper Single Bond 2, Z-250-3 M/ESPE). After 24 h, the restored blocks (n = 9) were serially sectioned and trimmed to an hour-glass shape of approximately 1 mm(2) at the bonded interface area, and tested in tension in a universal testing machine (1 mm/ min). Failure mode was determined at a magnification of 100x using a stereomicroscope. One block of each group was selected for scanning electron microscope (SEM) analysis. mu TBS data was analyzed by two-way ANOVA and Tukey test (alpha = 0.05). Mean bond strengths (SD) in MPa were: G1- 32.7 (5.9)(A); G2- 31.1 (6.3)(A); G3- 25.2 (8.3)(B); G4- 36.7 (9.9).(A) Groups with different uppercase letters were significantly different from each other (p < .05). Enamel bleaching procedure did not affect mu TBS values for dentin adhesion. Er:YAG laser irradiation with 25.56 J/cm(2) prior to adhesive procedure of bleached teeth did not affect mu TBS at dentin and promoted a dentin surface with no smear layer and opened dentin tubules observed under SEM. On the other hand, Er:YAG laser irradiation prior to adhesive procedure of non-bleached surface impaired mu TBS compared to the control group.

Temperature rise during Er:YAG cavity preparation of primary enamel

This study aimed to assess in vitro thermal alterations taking place during the Er:YAG laser cavity preparation of primary tooth enamel at different energies and pulse repetition rates. Forty healthy human primary molars were bisected in a mesio-distal direction, thus providing 80 fragments. Two small orifices were made on the dentin surface to which type K thermocouples were attached. The fragments were individually fixed with wax in a cylindrical PlexiglassA (R) abutment and randomly assigned to eight groups, according to the laser parameters (n = 10): G1 -aEuro parts per thousand 250 mJ/ 3 Hz, G2 -aEuro parts per thousand 250 mJ/ 4 Hz, G3 -aEuro parts per thousand 250 mJ/ 6 Hz, G4 -aEuro parts per thousand 250 mJ/10 Hz, G5 -aEuro parts per thousand 250 mJ/ 15 Hz, G6 -aEuro parts per thousand 300 mJ/ 3 Hz, G7 -aEuro parts per thousand 300 mJ/ 4 Hz and G8 -aEuro parts per thousand 300 mJ/ 6 Hz. An area of 4 mm(2) was delimited. Cavities were done (2 mm long x 2 mm wide x 1 mm thick) using non-contact (12 mm) and focused mode. Temperature values were registered from the start of laser irradiation until the end of cavity preparation. Data were analyzed by one-way ANOVA and Tukey test (p a parts per thousand currency signaEuro parts per thousand 0.05). Groups G1, G2, G6, and G7 were statistically similar and furnished the lowest mean values of temperature rise. The set 250 mJ/10 and 15 Hz yielded the highest temperature values. The sets 250 and 300 mJ and 6 Hz provided temperatures with mean values below the acceptable critical value, suggesting that these parameters ablate the primary tooth enamel. Moreover, the temperature elevation was directly related to the increase in the employed pulse repetition rates. In addition, there was no direct correlation between temperature rise and energy density. Therefore, it is important to use a lower pulse frequency, such as 300 mJ and 6 Hz, during cavity preparation in pediatric patients.

Bactericidal effects of two parameters of Er:YAG laser intracanal irradiation: ex-vivo study

The success of endodontic treatment depends on the complete elimination of microorganisms from the root canal system, thus the search for new procedures to eliminate them is justified. The aim of this study was to assess bacterial reduction after intracanal irradiation with the Er:YAG laser. The canals of 70 extracted human maxillary canines were prepared up to file #40 using 1% NaOCl, irrigated with 17% EDTA, and then washed with physiological solution activated by ultrasound. The roots were sterilized by autoclaving, inoculated with 10 mu l of a suspension containing 1.5 x 10(8) CFU/ml of Enterococcus faecalis ATCC 29212 and incubated at 37A degrees C for 72 h. The canals were irradiated with the Er:YAG laser using two energy settings: 60 mJ and 15 Hz, and 100 mJ and 10 Hz. The remaining bacteria were counted immediately and 48 h after laser irradiation. The results showed a high bacterial reduction at both time points. With 60 mJ and 15 Hz there was an immediate reduction of 99.73% and the reduction was 77.02% after 48 h, and with 100 mJ and 10 Hz there was an immediate reduction of 99.95% and the reduction was 84.52% after 48 h. Although the best results were observed with 100 mJ of energy, the difference between the two settings was not statistically significant. The count performed 48 h after irradiation showed that E. faecalis were able to survive, and can grow even from small numbers.

Thermal alteration and morphological changes of sound and demineralized primary dentin after Er:YAG laser ablation

The purpose of this study was to assess the influence of Er:YAG laser pulse repetition rate on the thermal alterations occurring during laser ablation of sound and demineralized primary dentin. The morphological changes at the lased areas were examined by scanning electronic microscopy (SEM). To this end, 60 fragments of 30 sound primary molars were selected and randomly assigned to two groups (n = 30); namely A sound dentin (control) and B demineralized dentin. Each group was divided into three subgroups (n = 10) according to the employed laser frequencies: I4 Hz; II6 Hz, and III10 Hz. Specimens in group B were submitted to a pH-cycling regimen for 21 consecutive days. The irradiation was performed with a 250 mJ pulse energy in the noncontact and focused mode, in the presence of a fine water mist at 1.5 mL/min, for 15 s. The measured temperature was recorded by type K thermocouples adapted to the dentin wall relative to the pulp chamber. Three samples of each group were analyzed by SEM. The data were submitted to the nonparametric Kruskal-Wallis test and to qualitative SEM analysis. The results revealed that the temperature increase did not promote any damage to the dental structure. Data analysis demonstrated that in group A, there was a statistically significant difference among all the subgroups and the temperature rise was directly proportional to the increase in frequency. In group B, there was no difference between subgroup I and II in terms of temperature. The superficial dentin observed by SEM displayed irregularities that augmented with rising frequency, both in sound and demineralized tissues. In conclusion, temperature rise and morphological alterations are directly related to frequency increment in both demineralized and sound dentin. Microsc. Res. Tech., 2011. (c) 2011 Wiley Periodicals, Inc.

Thermal effects and morphological aspects of human dentin surface irradiated with different frequencies of Er:YAG laser

This study reports the effects on micromorphology and temperature rise in human dentin using different frequencies of Er:YAG laser. Sixty human dentin fragments were randomly assigned into two groups (n = 30): carious or sound dentin. Both groups were divided into three subgroups (n = 10), according to the Er:YAG laser frequency used: 4, 6, or 10 Hz (energy: 200 mJ; irradiation distance: 12 mm; and irradiation time: 20 s). A thermocouple adapted to the tooth fragment recorded the initial temperature value (degrees C); then, the temperature was measured after the end of the irradiation (20 s). Morphological analysis was performed using images obtained with scanning electron microscope. There was no difference between the temperatures obtained with 4 and 6 Hz; the highest temperatures were achieved with 10 Hz. No difference was observed between carious and sound dentin. Morphological analyses revealed that all frequencies promoted irregular surface in sound dentin, being observed more selectively ablation especially in intertubular dentin with tubule protrusion. The caries dentin presented flat surface for all frequencies used. Both substrates revealed absence of any signs of thermal damage. It may be concluded that the parameters used in this study are capable to remove caries lesion, having acceptable limits of temperature rise and no significant morphological alterations on dentin surface. Microsc. Res. Tech. 2012. (c) 2012 Wiley Periodicals, Inc.

Análise microscópica de incisões realizadas com três diferentes pontas do laser Erbio YAG

The study analised microscopic wound healing of incision made with Er:YAg laser with three different tips. In six Rattus norvegicus, incision was made with Laser Er-YAG (KeyLaser) using tips 2051, 2055 and 2056. The animals were killed at 7 e 14 and the sites of incision are photographed in this time. The parts containing the incision area were prepared for microscopic analysis, performing sections of 7µm and staining with haematoxylin and eosin. Zone of tissue ablation, zone of thermal necrosis, the presence and character of inflammatory cell infiltrate and wound healing were measured. The 2051 tip produced faster and defined edges of the wound. To create wound 1.30 mm in depth lasers tips required at last five passes within the same line of incision. Microscopic analysis shows no difference with use of three different laser tips

Effect of Nd:YAG laser combined with fluoride on the prevention of primary tooth enamel demineralization

Most studies dealing with the caries preventive action of Nd:YAG laser have been done in permanent teeth and studies on primary teeth are still lacking. The aim of this study was to evaluate in vitro the effect of Nd:YAG laser combined or not with fluoride sources on the acid resistance of primary tooth enamel after artificial caries induction by assessing longitudinal microhardness and demineralization depth. Sixty enamel blocks obtained from the buccal/lingual surface of exfoliated human primary molars were coated with nail polish/wax, leaving only a 9 mm² area exposed on the outer enamel surface, and randomly assigned to 6 groups (n=10) according to the type of treatment: C-control (no treatment); APF: 1.23% acidulated phosphate fluoride gel; FV: 5% fluoride varnish; L: Nd:YAG laser 0.5 W/10 Hz in contact mode; APFL: fluoride gel + laser; FVL: fluoride varnish + laser. After treatment, the specimens were subjected to a des-remineralization cycle for induction of artificial caries lesions. Longitudinal microhardness data (%LMC) were analyzed by the Kruskal-Wallis test and demineralization depth data were analyzed by oneway ANOVA and Fisher’s LSD test (á=0.05). APFL and APF groups presented the lowest percentage of microhardness change (p<0.05). Demineralization depth was smaller in all treated groups compared with the untreated control. In conclusion, Nd:YAG laser combined or not with fluoride gel/varnish was not more effective than fluoride alone to prevent enamel demineralization within the experimental period.