Poly(2,5-bibenzimidazole) Membranes: Physico-Chemical Characterization Focused on Fuel Cell Applications

Membranes of Poly(2,5-benzimidazole) (ABPBI), prepared by polycondensation in polyphosphoric acid, were characterized from the fuel cell application point of view: mechanical properties of the membranes for different acid doping levels, thermal stability, permeability for the different gases/vapors susceptible of use in the cell (hydrogen, oxygen, methanol and ethanol), electro-osmotic water drag coefficient, oxidation stability to hydroxyl radicals, phosphoric acid leaching rate and, finally, in-plane membrane conductivity. ABPBI membranes presented an excellent thermal stability, above 500 degrees C in oxygen, suitable mechanical properties for high phosphoric acid doping levels, a low methanol and ethanol limiting permeation currents, and oxygen permeability compared to Nafion membranes, and a low phosphoric acid leaching rate when exposed to water vapor. On the contrary, hydrogen permeation current was higher than that of Nafion, and the chemical stability was very limited. Membrane conductivity achieved 0.07 S cm(-1) after equilibration with a humid environment. Fuel cell tests showed reasonable good performances, with a maximum power peak of 170 mW cm(-2) for H-2/air at 170 degrees C operating under a humidified hydrogen stream, 39.9 mW cm(-2) for CH3OH/O-2 at 200 degrees C for a methanol/water weight ratio of 1: 2, and 31.5 mW cm(-2) for CH3CH2OH/O-2 at the same conditions than for methanol. (C) 2012 The Electrochemical Society. [DOI: 10.1149/2.014207jes] All rights reserved.

Performance of a poly(2,5-benzimidazole)-based polymer electrolyte membrane fuel cell

The performance of an ABPBI-based High Temperature H-2/O-2 PEMFC system was studied under different experimental conditions. Increasing the temperature from 130 to 170 degrees C improved the cell performance, even though further increase was not beneficial for the system. Humidification of the H-2 stream ameliorated this behaviour, even though operating above 170 degrees C is not advisable in terms of cell performance. A significant electrolyte dehydration seems to negatively affect the fuel cell performance, especially in the case of the anode. In the presence of 2% vol. CO in the H-2 stream, the temperature exerted a positive effect on the cell performance, reducing the strong adsorption of this poison on the platinum sites. Moreover, humidification of the H-2 + CO stream increased the maximum power densities of the cell, further alleviating the CO poisoning effects. Actual CO-O-2 fuel cell results confirmed the significant beneficial effect of the relative humidity on the kinetics of the CO oxidation process. Copyright (C) 2011, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

Terbium(III) and dysprosium(III) 8-connected 3D networks containing 2,5-thiophenedicarboxylate anion: Crystal structures and photoluminescence studies

Two novel coordination polymers with the formula {[Ln(2)(2,5-tdc)(3)(dmso)(2)].H2O}(n) (Ln = Tb(III) for (1) and Dy(III) for (2)), (2,5-tdc(2-) = 2,5-thiophenedicarboxylate and dmso = dimethylsulfoxide) have been synthesized by the diffusion method and characterized by thermal analysis, vibrational spectroscopy and single crystal X-ray diffraction analysis. Structure analysis reveals that 2,5-tdc(2-) play a versatile role toward different lanthanide ions to form three-dimensional metal-organic frameworks (MOFs) in which the lanthanides ions are heptacoordinated. Photophysical properties were studied using excitation and emission spectra, where the photoluminescence data show the high emission intensity of the characteristic transitions D-5(4 ->) F-7(J) (J= 6, 5, 4 and 3) for (1) and (F9/2 -> HJ)-F-4-H-6 (J = 15/2, 13/2 and 11/2) for (2), indicating that 2,5-tdc(2-) is a good sensitizer. (C) 2012 Elsevier Ltd. All rights reserved.

Molecular organization and doping in poly(2-methoxyaniline)/Ni(dmit)(2) films obtained with the Langmuir-Blodgett technique

The control of the properties of materials at the molecular level is pursued for many applications, especially those associated with nanostructures. In this paper, we show that the coordination compound [Ni(dmit)(2)], where (dmit) is the 1,3-dithiole-2-thione-4,5-dithiolate ligand, can induce doping of poly(2-methoxyaniline) (POMA) in molecularly ordered Langmuir and Langmuir-Blodgett (LB) films. Doping was associated with interactions between the components and the compression of the Langmuir film at the air-water interface, according to polarization-modulated infrared reflection-absorption spectroscopy (PM-IRRAS) data. Taking these results together with in situ UV-Vis absorption measurements, we could identify the molecular groups involved in the interaction, including the way they were reoriented upon film compression. The Langmuir films were sufficiently stable to be transferred as Y-type LB films, while the hybrid POMA/[Ni(dmit)(2)] films remain doped in the solid state. As expected, the molecular charges affected the film morphology, as observed from combined atomic and electric force microscopy measurements. In summary, with adequate spectroscopy and microscopy tools we characterized molecular-level interactions, which may allow one to design molecular electronic devices with controlled electrical properties.

Nebulized 0.5, 2.5 and 5 ml L-epinephrine for post-extubation stridor in children: a prospective, randomized, double-blind clinical trial

Nebulized l-epinephrine has been recommended for the treatment of viral croup. However, the few studies assessing its effect on post-extubation stridor (PES) have shown conflicting results. We compared the efficacy and safety of nebulized l-epinephrine at three different doses for the treatment of PES. We conducted a prospective, randomized, double-blind trial including all consecutive children with a PES score of a parts per thousand yen4 (Westley score). The primary efficacy outcome was change in PES score at 40 min. A reduction of a parts per thousand yen2 points in stridor score was defined as clinically significant. A total of 96 patients were randomly assigned to receive one of three doses of nebulized l-epinephrine upon achieving a PES score of 4 or more following extubation. Stridor score and vital signs were recorded before treatment, and at 20, 40, 60 and 180 min after nebulization. Baseline characteristics were similar among all study groups. No significant difference was detected among the treatments based on change in Westley score by intent-to-treat analysis. In addition, the difference in the number of patients who clinically improved among the treatment groups was not significant (p = 0.54). Patients receiving 5 ml nebulized epinephrine had a significant increase of systolic and diastolic blood pressure at 40 and 180 min. Nebulized l-epinephrine at doses of 0.5, 2.5 and 5 ml demonstrated a lack of dose response in effect on PES and a modestly clinically significant increase in undesired side effects (heart rate and blood pressure) at higher doses.

Synthesis, anti-inflammatory activity and molecular docking studies of 2,5-diarylfuran amino acid derivatives

A series of 2,5-diaryl substituted furans functionalized with several amino acids were synthesized and evaluated as the cyclooxygenases COX-1 and COX-2 enzymes inhibitors. The proline-substituted compound inhibited PGE(2) secretion by LPS-stimulated neutrophils, suggesting selectivity for COX-2. Molecular docking studies in the binding site of COX-2 were performed. (C) 2011 Elsevier Masson SAS. All rights reserved.

A complex chromosomal rearrangement involving chromosomes 2, 5, and X in autism spectrum disorder

Here, we describe a female patient with autism spectrum disorder and dysmorphic features that harbors a complex genetic alteration, involving a de novo balanced translocation t(2;X)(q11;q24), a 5q11 segmental trisomy and a maternally inherited isodisomy on chromosome 5. All the possibly damaging genetic effects of such alterations are discussed. In light of recent findings on ASD genetic causes, the hypothesis that all these alterations might be acting in orchestration and contributing to the phenotype is also considered. (C) 2012 Wiley Periodicals, Inc.

Efficiency of extrinsic and intrinsic charge-carrier photogeneration processes obtained from the steady-state photocurrent action spectra of poly(p-phenylene vinylene) derivatives

The efficiency of the charge-carrier photogeneration processes in poly(2,5-bis(3',7'-dimethyl-octyloxy)-1,4-phenylene vinylene) (OC(1)OC10-PPV) has been analyzed by the spectral response of the photocurrent of devices in ITO/polymer/Al structures. The symbatic response of the photocurrent action spectra of the OC1OC10-PPV devices, obtained for light-excitation through the ITO electrode and for forward bias, has been fitted using a phenomenological model which considers that the predominant transport mechanism under external applied electric field is the drift of photogenerated charge-carriers, neglecting charge-carrier diffusion. The proposed model takes into account that charge-carrier photogeneration occurs via intermediate stages of bounded pairs (excitonic states), followed by dissociation processes. Such processes result in two different contributions to the photoconductivity: The first one, associated to direct creation of unbound polaron pairs due to intrinsic photoionization; and the second one is associated to secondary processes like extrinsic photoinjection at the metallic electrodes. The results obtained from the model have shown that the intrinsic component of the photoconductivity at higher excitation energies has a considerably higher efficiency than the extrinsic one, suggesting a dependence on the photon energy for the efficiency of the photogeneration process.

Carbon source pulsed feeding to attain high yield and high productivity in poly(3-hydroxybutyrate) (PHB) production from soybean oil using Cupriavidus necator

Poly(3-hydroxybutyrate) (PHB) biosynthesis from soybean oil by Cupriavidus necator was studied using a bench scale bioreactor. The highest cell concentration (83 g l(-1)) was achieved using soybean oil at 40 g l(-1) and a pulse of the same concentration. The PHB content was 81% (w/w), PHB productivity was 2.5 g l(-1) h(-1), and the calculated Y-p/s value was 0.85 g g(-1). Growth limitation and the onset of PHB biosynthesis took place due to exhaustion of P, and probably also Cu, Ca, and Fe.

Self-Assembly of Poly(4-vynil-N-alkylpyridinium) Bromide onto Silica: Effect of Side-Chain Length on Structural Aspects at a Molecular Level

Self-assembly of poly(4-vynil-N-alkyl)pyridinium bromide with alkyl side chains of 2, 5, 7, 10, or 16 carbons from ethanolic solutions onto flat silica surfaces was studied by means of ellipsometry, atomic force microscopy (AFM), contact angle measurements, and sum-frequency generation (SFG) vibrational spectroscopy in the CH3 and CH2 stretch region. Ab initio quantum-chemical calculations on the N-alkylpyridinium side-group with restricted Hartree-Fock (RHF) method and 6-311G (d,p) basis set were C one to estimate the charge distribution along the pyridinium ring and the alkyl side-chain. SFG results showed that longer side chains promote the disorientation of the alkyl groups at the surface, corroborating with the contact angle values. AFM images revealed film homogeneity, regardless the alkyl side group. However, after 24 h contact with water, ringlike structures appeared on the film surfaces, when the polycation alkyl side chain had 7 or less carbons, and as the alkyl chain increased to 10 or 16 carbons, the films dewetted because the hydrophobic interactions prevailed over the electrostatic interactions between the pyridinium charged groups and the negatively charged SiO2 surface. Under acid conditions (HCl 0.1 mol.L-1), the film mean thickness values decreased up to 50% of original values when the alkyl side chains were ethyl or pentyl groups due to ion-pair disruption, but for longer groups they remained unchanged. Quantum-chemical optimization and Mulliken electron population showed that (i) from C2 to C15 the positive charge at the headgroup (HG) decreased 0.025, while the charge at combined HG + alpha-CH2 increased 0.037; and (ii) for C6 or longer, the alkyl side group presents a tilt in the geometry, moving away from the plane. Such effects summed up over the whole polymer chain give support to suggest that when the side chains are longer than 7 carbons, the hydrophobic interaction decreases film stability and increases acid resistance.

Synthesis and characterization of [Ru(eta(6)-C10H14)(dppf)X][PF6] (X = Cl, Br, I, SnF3) compounds: The X-ray structure of [Ru(eta(6)-C10H14)(dppf)Cl][SnCl3]center dot 0.45CH(2)Cl(2)

The arene-ruthenium complex [Ru(eta(6)-C10H14)(dppf)Cl]PF6 (1) was used as a precursor for the syntheses of the [Ru(eta(6)-C10H14)(dppf)Br]PF6 (2), [Ru(eta(6)-C10H14)(dppf)I]PF6 (3). [Ru(eta(6)-C10H14)(dppf)SnF3]PF6 (4) and [Ru(eta(6)-C10H14)(dppf)Cl][SnCl3]center dot 0.45CH(2)Cl(2) (5) complexes by its reactions with KBr, Kl, SnF2 and SnCl2. respectively. All of the compounds were characterized by NMR, IR, Fe-57 and Sn-119-Mossbauer spectroscopy, and cyclic voltammetry. The single-crystal X-ray structure analysis of the [Ru(eta(6)-C10H14)(dppf)Cl] [SnCl3]center dot 0.45CH(2)Cl(2) complex revealed the expected piano-stool geometry. Cyclic voltammograms of the complexes showed only one quasi-reversible electrochemical process, involving the oxidation of Fe(II) and Ru(II) at the same potential, which was confirmed by exhaustive electrolysis experiments. Fe-57-Mossbauer parameters obtained for the complexes (1-5) were fitted with one doublet corresponding to a site of one iron(II). The Sn-119-Mossbauer parameters of the complex (4) indicate that tin is tetra covalent. (c) 2012 Elsevier Ltd. All rights reserved.

Effect of a polymeric protective coating on optical and electrical properties of poly (p-phenylene vinylene) derivatives

The resistance to photodegradation of poly [(2-methoxy-5-n-hexyloxy)-p-phenylene vinylene] (OC1OC6-PPV) films was significantly enhanced by the use of poly(vinyl alcohol) 99% hydrolyzed as protective coating. The deposition of poly(vinyl alcohol) onto OC1OC6-PPV films did not affect the absorption and the emission spectra of the luminescent polymer. The protected film showed 5% drop on the absorbance at 500nm after 270 hours of light exposure while the unprotected film completely degraded in the same conditions. The conductivity of the protected film remained stable (around 7 × 10-10 S/m) while the value for the unprotected one dropped around two orders of magnitude after 100 hours of light exposure.