Effect of the relationship between particle size, inter-particle distance, and metal loading of carbon supported fuel cell catalysts on their catalytic activity

The effect of the relationship between particle size (d), inter-particle distance (x(i)), and metal loading (y) of carbon supported fuel cell Pt or PtRu catalysts on their catalytic activity, based on the optimum d (2.5-3 nm) and x(i)/d (>5) values, was evaluated. It was found that for y < 30 wt%, the optimum values of both d and x(i)/d can be always obtained. For y >= 30 wt%, instead, the positive effect of a thinner catalyst layer of the fuel cell electrode than that using catalysts with y < 30 wt% is concomitant to a decrease of the effective catalyst surface area due to an increase of d and/or a decrease of x(i)/d compared to their optimum values, with in turns gives rise to a decrease in the catalytic activity. The effect of the x(i)/d ratio has been successfully verified by experimental results on ethanol oxidation on PtRu/C catalysts with same particle size and same degree of alloying but different metal loading. Tests in direct ethanol fuel cells showed that, compared to 20 wt% PtRu/C, the negative effect of the lower x(i)/d on the catalytic activity of 30 and 40 wt% PtRu/C catalysts was superior to the positive effect of the thinner catalyst layer.

Kinetics of thermal decomposition of niobium hydride

High-purity niobium powders can be obtained from the well-known hydride-dehydride (HDH) process. The aim of this work was the investigation of the structural phase transition of the niobium hydride to niobium metal as function of temperature, heating rate and time. The niobium powder used in this work was obtained by high-temperature hydriding of niobium machining chips followed by conventional ball milling and sieving. X-ray diffraction measurements were carried out in vacuum using a high-temperature chamber coupled to an X-ray diffractometer. During the dehydriding process, it is possible to follow the phase transition from niobium hydride to niobium metal starting at about 380 degrees C for a heating rate of 20 degrees C/min. The heating rate was found to be an important parameter, since complete dehydriding was obtained at 490 degrees C for a heating rate of 20 degrees C/min. The higher dehydriding rate was found at 500 degrees C. Results contribute to a better understanding of the kinetics of thermal decomposition of niobium hydride to niobium metal. (C) 2011 Elsevier Ltd. All rights reserved.

Magnetic nanohydrometallurgy: A promising nanotechnological approach for metal production and recovery using functionalized superparamagnetic nanoparticles

We report on a new, promising nanotechnological approach for hydrometallurgy based on recyclable, chemically functionalized superparamagnetic nanoparticles. In this process, the metal ions (e.g. Cu2+) are captured by the nanoparticles and confined at the electrode surface by means of an external magnet. Due to the pre-concentration effect the electrodeposition process is greatly improved, yielding the pure metal in a much shorter time in comparison with the conventional electrodeposition process. After the electrolysis, the magnetic nanoparticles are ready to return to the process. The proposed strategy can advantageously be incorporated in hydrometallurgy, reducing the number of steps associated with complexation, organic solvent extraction, metal release and diffusional electroprocessing, leading to a more sustainable technology. (C) 2012 Elsevier B.V. All rights reserved.