We prove that the hard thermal loop contribution to static thermal amplitudes can be obtained by setting all the external four-momenta to zero before performing the Matsubara sums and loop integrals. At the one-loop order we do an iterative procedure for all the one-particle irreducible one-loop diagrams, and at the two-loop order we consider the self-energy. Our approach is sufficiently general to the extent that it includes theories with any kind of interaction vertices, such as gravity in the weak field approximation, for d space-time dimensions. This result is valid whenever the external fields are all bosonic.

Niobium Effects on the Recrystallization Behavior on a Full Austenitic 15Cr-15Ni Stainless Steel Investigated Using Adaptive Neural Networks (ANN)

A new series of austenitic stainless steels-Nb stabilized, without Mo additions, non-susceptible to delta ferrite formation and devoid of intemetallic phases (sigma and chi), without deformation induced martensite is being developed, aiming at high temperature applications as well as for corrosive environments. The base steel composition is a 15Cr-15Ni with normal additions of Nb of 0.5, 1.0 and 2 wt%. Mechanical properties, oxidation and corrosion resistance already have been invetigated in previous papers. In this paper, the effects of Nb on the SFE, strain hardening and recrystallization resistance are evaluated with the help of Adaptive Neural Networks (ANN).

Characterization of NiCrAlC PTA coatings

Surface tailoring with plasma transferred arc (PTA) hardfacing involves the deposition of powder mixtures to produce coatings with an almost unlimited chemical composition. PTA hardfacing is particularly important for processing low weldability alloys, such as those for high-temperature applications, of which NiCrAlC is an example. This study analyzed NiCrAlC coatings processed by PTA using a mixture of elemental powders. Deposition on AISI316L plates was carried out with currents of 100 A and 130 A to induce variations in the chemical composition of the coatings, which were also subjected to isothermal exposure at temperatures of up to 1000 ºC for up to 72 hours in an air furnace. The results show that the aluminide compounds were stable, the coatings that solidified more slowly having the highest hardness after temperature exposure and potentially being suitable for use in high-temperature abrasion environments.

Poly(2,5-bibenzimidazole) Membranes: Physico-Chemical Characterization Focused on Fuel Cell Applications

Membranes of Poly(2,5-benzimidazole) (ABPBI), prepared by polycondensation in polyphosphoric acid, were characterized from the fuel cell application point of view: mechanical properties of the membranes for different acid doping levels, thermal stability, permeability for the different gases/vapors susceptible of use in the cell (hydrogen, oxygen, methanol and ethanol), electro-osmotic water drag coefficient, oxidation stability to hydroxyl radicals, phosphoric acid leaching rate and, finally, in-plane membrane conductivity. ABPBI membranes presented an excellent thermal stability, above 500 degrees C in oxygen, suitable mechanical properties for high phosphoric acid doping levels, a low methanol and ethanol limiting permeation currents, and oxygen permeability compared to Nafion membranes, and a low phosphoric acid leaching rate when exposed to water vapor. On the contrary, hydrogen permeation current was higher than that of Nafion, and the chemical stability was very limited. Membrane conductivity achieved 0.07 S cm(-1) after equilibration with a humid environment. Fuel cell tests showed reasonable good performances, with a maximum power peak of 170 mW cm(-2) for H-2/air at 170 degrees C operating under a humidified hydrogen stream, 39.9 mW cm(-2) for CH3OH/O-2 at 200 degrees C for a methanol/water weight ratio of 1: 2, and 31.5 mW cm(-2) for CH3CH2OH/O-2 at the same conditions than for methanol. (C) 2012 The Electrochemical Society. [DOI: 10.1149/2.014207jes] All rights reserved.

Temperature impact on the tunnel fet off-state current components

In this work, the temperature impact on the off-state current components is analyzed through numerical simulation and experimentally. First of all, the band-to-band tunneling is studied by varying the underlap in the channel/drain junction, leading to an analysis of the different off-state current components. For pTFET devices, the best behavior for off-state current was obtained for higher values of underlap (reduced BTBT) and at low temperatures (reduced SRH and TAT). At high temperature, an unexpected off-state current occurred due to the thermal leakage current through the drain/channel junction. Besides, these devices presented a good performance when considering the drain current as a function of the drain voltage, making them suitable for analog applications. (C) 2012 Elsevier Ltd. All rights reserved.

Direct Access to Oxidation-Resistant Nickel Catalysts through an Organometallic Precursor

The synthesis of nickel catalysts for industrial applications is relatively simple; however, nickel oxidation is usually difficult to avoid, which makes it challenging to optimize catalytic activities, metal loadings, and high-temperature activation steps. A robust, oxidation-resistant and very active nickel catalyst was prepared by controlled decomposition of the organometallic precursor [bis(1,5-cyclooctadiene)nickel(0)], Ni(COD)(2), over silica-coated magnetite (Fe3O4@SiO2). The sample is mostly Ni(0), and surface oxidized species formed after exposure to air are easily reduced in situ during hydrogenation of cyclohexene under mild conditions recovering the initial activity. This unique behavior may benefit several other reactions that are likely to proceed via Ni heterogeneous catalysis.