Luminous efficiency enhancement of PVK based OLEDs with fac-[ClRe(CO)(3)(bpy)]

The luminous efficiency of organic light-emitting diodes based on poly(N-vinylcarbazole), PVK, was improved by adding fac-[ClRe(CO)(3)(bpy)], bpy = 2,2`-bipyridine, to PVK host. Emissive layers with various Re(I) complex/host ratio were employed and optoelectronic properties were compared with the single PVK device. The single PVK device exhibits a characteristic electroluminescence with blue emission, lambda(max) 420 nm, assigned to the PVK excimer. On the other hand, the intense and broad band at lambda(max) 580 nm of the Re(I) complex/PVK OLEDs is ascribed to the metal-to-ligand charge transfer excited state emission of fac-[ClRe(CO)(3)(bpy)]. At 30 V, the device luminous efficiency increased from 16 mcd/A for the single PVK device to 211 mcd/A for the 11% (w/w) Re(I) complex/PVK OLED, in which fac-[ClRe(CO)(3)(bpy)] acts as an electron-trap in PVK films. The device current is space-charge limited and exhibits typical emissive layer thickness dependence. (C) 2011 Elsevier B.V. All rights reserved.

Polymer Light Emitting Diode Using PFT-Poly(9,9 `-n-dihexil-2,7-fluorenodiilvinylene-alt-2,5thiophene)

The development of new electroluminescence polymers for specific colour tuning in Polymer Light Emitting Devices (PLEDs) is currently one of the most important fields for organic electronics. This work reports a synthesis of a new electroluminescent polymer and the concomitant test as PLED emissive layer. The polymer, synthesised from fluorene, is poly(9,9`-n-dihexil-2,7-fluorenodiilvinylene-alt-2,5thiophene) or PFT The luminescence shows large bands with maxima around 480 nm in absorption and 560 nm in emission. The device was made in a three layer structure, with PEDOT:PSS as hole transport layer, PFT as emissive layer and butyl-PBD as electron transport layer. The electroluminescence spectrum shows a strong band peaked at 540 nm. For an applied voltage of 12 Volt, the brightness at normal angle of viewing is near 10 cd/m(2) and the luminous efficiency is of 0.01 lm/W. A discussion about carrier transport and the electroluminescence properties is made.

Transient and d.c. analysis of the operation mechanism of light-emitting electrochemical cells

Light-emitting electrochemical cells (LECs) made of electroluminescent polymers were studied by d.c. and transient current-voltage and luminance-voltage measurements to elucidate the operation mechanisms of this kind of device. The time and external voltage necessary to form electrical double layers (EDLs) at the electrode interfaces could be determined from the results. In the low-and intermediate-voltage ranges (below 1.1 V), the ionic transport and the electronic diffusion dominate the current, being the device operation better described by an electrodynamic model. For higher voltages, electrochemical doping occurs, giving rise to the formation of a p-i-n junction, according to an electrochemical doping model. Copyright (C) EPLA, 2012

UV-Ozone Generation from Modified High Intensity Discharge Mercury Vapor Lamps for Treatment of Indium Tin Oxide Films

In a homemade UV-Ozone generator, different ignition tubes extracted from HID mercury vapor lamps were investigated, namely: 80, 125, 250 and 400 watts. The performance of the generator in function of the type of the ignition lamp was monitored by the measurements of the ozone concentration and the temperature increment. The results have shown that the 400 W set up presented the highest ozone production, which was used in the treatment of indium tin oxide (ITO) films. Polymer light emitting diodes were assembled using ITO films, treated for 10, 20 and 30 min, as an anode. The overall results indicate improvement of the threshold voltage (reduction) and electroluminescence of these devices.