Bacterial cellulose-collagen nanocomposite for bone tissue engineering

A nanocomposite based on bacterial cellulose (BC) and type I collagen (COL) was evaluated for in vitro bone regeneration. BC membranes were modified by glycine esterification followed by cross-linking of type I collagen employing 1-ethyl-3-(3-dimethylaminopropyl)-carbodiimide. Collagen incorporation was studied by spectroscopy analysis. X-Ray diffraction showed changes in the BC crystallinity after collagen incorporation. The elastic modulus and tensile strength for BC-COL decreased, while the strain at failure showed a slight increase, even after sterilization, as compared to pristine BC. Swelling tests and contact angle measurements were also performed. Cell culture experiments performed with osteogenic cells were obtained by enzymatic digestion of newborn rat calvarium revealed similar features of cell morphology for cultures grown on both membranes. Cell viability/proliferation was not different between BC and BC-COL membranes at day 10 and 14. The high total protein content and ALP activity at day 17 in cells cultured on BC-COL indicate that this composite allowed the development of the osteoblastic phenotype in vitro. Thus, BC-COL should be considered as alternative biomaterial for bone tissue engineering.

Impact of experimental Nano-HAP pastes on bovine enamel and dentin submitted to a pH cycling model

This in vitro study evaluated the preventive potential of experimental pastes containing 10% and 20% hydroxyapatite nanoparticles (Nano-HAP), with or without fluoride, on dental demineralization. Bovine enamel (n=15) and root dentin (n=15) specimens were divided into 9 groups according to their surface hardness: control (without treatment), 20 Nanop paste (20% HAP), 20 Nanop paste plus (20% HAP + 0.2% NaF), 10 Nanop paste (10% HAP), 10 Nanop paste plus (10% HAP + 0.2% NaF), placebo paste (without fluoride and HAP), fluoride paste (0.2% NaF), MI paste (CPP-ACP, casein phosphopeptide-amorphous calcium phosphate), and MI paste plus (CPP-ACP + 0.2% NaF). Both MI pastes were included as commercial control products containing calcium phosphate. The specimens were treated with the pastes twice a day (1 min), before and after demineralization. The specimens were subjected to a pH-cycling model (demineralization–6-8 h/ remineralization-16-18 h a day) for 7 days. The dental subsurface demineralization was analyzed using cross-sectional hardness (kgf/mm 2 , depth 10-220 µm). Data were tested using repeated-measures two-way ANOVA and Bonferroni's test (p<0.05). The only treatment able to reduce the loss of enamel and dentin subsurface hardness was fluoride paste (0.2% NaF), which differed significantly from the control at 30- and 50-µm depth (p<0.0001). The other treatments were not different from each other or compared with the control. The experimental Nanop pastes, regardless of the addition of fluoride, were unable to reduce dental demineralization in vitro.

Comparative analysis of Enterococcus Faecalis biofilm formation on different substrates

Introduction: The aim of this study was to compare Enterococcus faecalis biofilm formation on different substrates. Methods: Cell culture plates containing growth medium and E. faecalis (ATCC 29212) were used to grow biofilm on bovine dentin, gutta-percha, hydroxyapatite, or bovine bone. Substrates were incubated at 37 C for 14 or 21 days, and the medium was changed every 48 hours. After the growth induction periods, specimens (n = 5 per group and per induction period) were stained by using Live/Dead, and the images were analyzed under a confocal microscope. The total biovolume (mm3), live bacteria biovolume (mm3), and substrate coverage (%) were quantified by using the BioImage_L software. Results obtained were analyzed by nonparametric tests (P = .05). Results: Biofilm formation was observed in all groups. Gutta-percha had the lowest total biovolume at 14 days (P < .05) and hydroxyapatite the highest at 21 days (P < .05). No significant difference was observed in green biovolume at 14 days. At 21 days, however, hydroxyapatite had the highest volume (P < .05). The percentages of coverage were similar among all substrates at 21 days (P > .05), but at 14 days, bovine bone presented the highest coverage (P < .05). Conclusions: E. faecalis was capable of forming biofilm on all substrates during both growth periods; hydroxyapatite presented the highest rates of biofilm formation. The type of substrate influenced the biofilm characteristics, according to the parameters evaluated

Exploring anorganic bovine bone granules as osteoblast carriers for bone bioengineering: a study in rat critical-size calvarial defects

It is known that current trends on bone bioengineering seek ideal scaffolds and explore innovative methods to restore tissue function. In this way, the objective of this study was to evaluate the behavior of anorganic bovine bone as osteoblast carrier in critical-size calvarial defects. MC3T3-E1 osteoblast cells (1x10(5) cells/well) were cultured on granules of anorganic bovine bone in 24-well plates and after 24 h these granules were implanted into rat critical-size calvarial defects (group Biomaterial + Cells). In addition, other groups were established with different fillings of the defect: Blood Clot (negative control); Autogenous Bone (positive control); Biomaterial (only granules) and Cells (only MC3T3-E1 cells). After 30 days, the animals were euthanized and the calvaria were technically processed in order to allow histological and morphometric analysis. It was possible to detect blood vessels, connective tissue and newly formed bone in all groups. Particularly in the Biomaterial + Cells group, it was possible to observe a profile of biological events between the positive control group (autogenous bone) and the group in which only anorganic bovine granules were implanted. Altogether, the results of the present study showed that granules of anorganic bovine bone can be used as carrier to osteoblasts and that adding growth factors at the moment of implantation should maximize these results.