Fatigue crack growth assessments in welded components including crack closure effects: Experiments and 3-D numerical modeling

This work provides a numerical and experimental investigation of fatigue crack growth behavior in steel weldments including crack closure effects and their coupled interaction with weld strength mismatch. A central objective of this study is to extend previously developed frameworks for evaluation of crack clo- sure effects on FCGR to steel weldments while, at the same time, gaining additional understanding of commonly adopted criteria for crack closure loads and their influence on fatigue life of structural welds. Very detailed non-linear finite element analyses using 3-D models of compact tension C ( T ) fracture spec- imens with center cracked, square groove welds provide the evolution of crack growth with cyclic stress intensity factor which is required for the estimation of the closure loads. Fatigue crack growth tests con- ducted on plane-sided, shallow-cracked C ( T ) specimens provide the necessary data against which crack closure effects on fatigue crack growth behavior can be assessed. Overall, the present investigation pro- vides additional support for estimation procedures of plasticity-induced crack closure loads in fatigue analyses of structural steels and their weldments

Issues on the mean stress effect in fretting fatigue of a 7050-T7451 Al alloy posed by new experimental data

The aims of this work are: (i) to produce new experimental data for fretting fatigue considering the presence of a mean bulk stress and (ii) to assess two design methodologies against failure by fretting fatigue. Tests on a cylinder–flat contact configuration were conducted using a fretting apparatus mounted on a servo-hydraulic machine. The material used for both the pads and fatigue specimen was an aeronautical 7050-T7451 Al alloy. The experimental program was designed with all relevant parameters, apart from the mean bulk load (always applied before the contact loads), kept constant. The mean bulk stress varied from compressive to tensile values while maintaining a high peak pressure in order to encourage crack initiation. Two methodologies against fretting fatigue are proposed and confronted against the experimental data. The non-local stress-based methodology considers the evaluation of a critical plane fatigue criterion at the center of a process zone located beneath the contacting surfaces. The results showed that it correctly predicts crack initiation, but was not capable to provide successful prediction of the integrity of the specimens. Alternatively, we considered a crack arrest criterion which has the potential to provide a more complete description about the integrity of the specimens.