Bone tissue, cellular, and molecular responses to titanium implants treated by anodic spark deposition

A myriad of titanium (Ti) surface modifications has been proposed to hasten the osseointegration. In this context, the aim of this study was to perform histomorphometric, cellular, and molecular analyses of the bone tissue grown in close contact with Ti implants treated by anodic spark deposition (ASD-AK). Acid-etched (AE) Ti implants either untreated or submitted to ASD-AK were placed into dog mandibles and retrieved at 3 and 8 weeks. It was noticed that both implants, AE and ASD-AK, were osseointegrated at 3 and 8 weeks. Histomorphometric analysis showed differences between treatments only for bone-to-implant contact, being higher on AE implants. Although not backed by histomorphometric results, gene expression of key bone markers was higher for bone grown in close contact with ASD-AK and for cells harvested from these fragments and cultured until subconfluence. Cell proliferation at days 7 and 10 and alkaline phosphatase activity at day 10 was higher on AE surfaces. No statistical significant difference was noticed for extracellular matrix mineralization at 17 days. Our results have shown that the Ti fixtures treated by ASD-AK allowed in vivo osseointegration and induced higher expression of key markers of osteoblast phenotype, suggesting that this surface treatment could be considered to produce implants for clinical applications. (c) 2012 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 100A:30923098, 2012.

Three-Dimensional Finite Element Analysis of Stress Distribution on Different Bony Ridges With Different Lengths of Morse Taper Implants and Prosthesis Dimensions

This finite element analysis (FEA) compared stress distribution on different bony ridges rehabilitated with different lengths of morse taper implants, varying dimensions of metal-ceramic crowns to maintain the occlusal alignment. Three-dimensional FE models were designed representing a posterior left side segment of the mandible: group control, 3 implants of 11 mm length; group 1, implants of 13 mm, 11 mm and 5 mm length; group 2, 1 implant of 11 mm and 2 implants of 5 mm length; and group 3, 3 implants of 5 mm length. The abutments heights were 3.5 mm for 13- and 11-mm implants (regular), and 0.8 mm for 5-mm implants (short). Evaluation was performed on Ansys software, oblique loads of 365N for molars and 200N for premolars. There was 50% higher stress on cortical bone for the short implants than regular implants. There was 80% higher stress on trabecular bone for the short implants than regular implants. There was higher stress concentration on the bone region of the short implants neck. However, these implants were capable of dissipating the stress to the bones, given the applied loads, but achieving near the threshold between elastic and plastic deformation to the trabecular bone. Distal implants and/or with biggest occlusal table generated greatest stress regions on the surrounding bone. It was concluded that patients requiring short implants associated with increased proportions implant prostheses need careful evaluation and occlusal adjustment, as a possible overload in these short implants, and even in regular ones, can generate stress beyond the physiological threshold of the surrounding bone, compromising the whole system.

The effect of implant design on insertion torque and immediate micromotion

Objectives: To evaluate the effect of insertion torque on micromotion to a lateral force in three different implant designs. Material and methods: Thirty-six implants with identical thread design, but different cutting groove design were divided in three groups: (1) non-fluted (no cutting groove, solid screw-form); (2) fluted (901 cut at the apex, tap design); and (3) Blossomt (Patent pending) (non-fluted with engineered trimmed thread design). The implants were screwed into polyurethane foam blocks and the insertion torque was recorded after each turn of 901 by a digital torque gauge. Controlled lateral loads of 10N followed by increments of 5 up to 100N were sequentially applied by a digital force gauge on a titanium abutment. Statistical comparison was performed with two-way mixed model ANOVA that evaluated implant design group, linear effects of turns and displacement loads, and their interaction. Results: While insertion torque increased as a function of number of turns for each design, the slope and final values increased (Po0.001) progressively from the Blossomt to the fluted to the non-fluted design (M +/- standard deviation [SD] = 64.1 +/- 26.8, 139.4 +/- 17.2, and 205.23 +/- 24.3 Ncm, respectively). While a linear relationship between horizontal displacement and lateral force was observed for each design, the slope and maximal displacement increased (Po0.001) progressively from the Blossomt to the fluted to the non-fluted design (M +/- SD 530 +/- 57.7, 585.9 +/- 82.4, and 782.33 +/- 269.4 mm, respectively). There was negligible to moderate levels of association between insertion torque and lateral displacement in the Blossomt, fluted and non-fluted design groups, respectively. Conclusion: Insertion torque was reduced in implant macrodesigns that incorporated cutting edges, and lesser insertion torque was generally associated with decreased micromovement. However, insertion torque and micromotion were unrelated within implant designs, particularly for those designs showing the least insertion torque.

Implant Stability Measurements of Two Immediate Loading Protocols for the Edentulous Mandible: Rigid and Semi-rigid Splinting of the Implants

Aim: Primary and secondary stabilities of immediately loaded mandibular implants restored with fixed prostheses (FP) using rigid or semirigid splinting systems were clinically and radiographically evaluated. Methods: Fifteen edentulous patients were rehabilitated using hybrid FP; each had 5 implants placed between the mental foramens. Two groups were randomly divided: group 1-FP with the conventional rigid bar splinting the implants and group 2-semi-rigid cantilever extension system with titanium bars placed in the 2 distal abutment cylinders. Primary stability was evaluated using resonance frequency analysis after installation of the implant abutments. The measurements were made at 3 times: T0, at baseline; T1, 4 months after implant placement; and T2, 8 months after implant placement. Presence of mobility and inflammation in the implant surrounding regions were checked. Stability data were submitted to statistical analysis for comparison between groups (P, 0.05). Results: Implant survival rate for the implants was of 100% in both groups. No significant differences in the mean implant stability quotient values were found for both groups from baseline and after the 8-month follow-up. Conclusion: The immediate loading of the implants was satisfactory, and both splinting conditions (rigid and semi-rigid) can be successfully used for the restoration of edentulous mandibles. (Implant Dent 2012;21:486-490)

Morse taper implants at different bone levels: a finite element analysis of stress distribution

AIM: To explore the biomechanical effects of the different implantation bone levels of Morse taper implants, employing a finite element analysis (FEA). METHODS: Dental implants (TitamaxCM) with 4x13 mm and 4x11 mm, and their respective abutments with 3.5 mm height, simulating a screwed premolar metal-ceramic crown, had their design performed using the software AnsysWorkbench 10.0. They were positioned in bone blocks, covered by 2.5 mm thickness of mucosa. The cortical bone was designed with 1.5 mm thickness and the trabecular bone completed the bone block. Four groups were formed: group 11CBL (11 mm implant length on cortical bone level), group 11TBL (11 mm implant length on trabecular bone level), group 13CBL (13mm implant length on cortical bone level) and group 13TBL (13 mm implant length on trabecular bone level). Oblique 200 N loads were applied. Von Mises equivalent stresses in cortical and trabecular bones were evaluated with the same design program. RESULTS: The results were shown qualitatively and quantitatively by standard scales for each type of bone. By the results obtained, it can be suggested that positioning the implant completely in trabecular bone brings harm with respect to the generated stresses. Its implantation in the cortical bone has advantages with respect to better anchoring and locking, reflecting a better dissipation of the stresses along the implant/bone interfaces. In addition, the search for anchoring the implant in its apical region in cortical bone is of great value to improve stabilization and consequently better stress distribution. CONCLUSIONS: The implant position slightly below the bone in relation to the bone crest brings advantages as the best long-term predictability with respect to the expected neck bone loss.

Short implants (6 mm) installed immediately into extraction sockets: An experimental study in dogs

Aim: To evaluate the effect of implant length (6 mm vs. 11 mm) on osseointegration (bone-toimplant contact) of implants installed into sockets immediately after tooth extraction. Material and methods: In six Labrador dogs, the pulp tissue of the mesial roots of P-3(3) was removed and the root canals were filled. Flaps were elevated bilaterally, the premolars hemisectioned and the distal roots removed. Recipient sites were prepared in the distal alveolus and a 6 mm or an 11 mm long implant was installed at the test and control sites, respectively. Non-submerged healing was allowed. After 4 months of healing, block sections of the implant sites were obtained for histological processing and peri-implant tissue assessment. Results: No statistically significant differences were found between test and control sites both for hard and soft tissue parameters. The bone-to-implant contact evaluated at the apical region of the implants was similar as well. Although not statistically significant, the location of the top of the bony crest at the buccal aspect was more apical in relation to the implant shoulder at the test compared with the control sites (2.0 +/- 1.4 and 1.2 +/- 1.1 mm, respectively). Conclusions: Shorter implants (6 mm) present with equal osseointegration than do longer implants (11 mm).

Effect of Si addition on Ca- and P-impregnated implant surfaces with nanometer-scale roughness: an experimental study in dogs

Objectives: To investigate the effect of Si addition on a nanometer-scale roughness Ca and P implant surfaces in a canine tibia model by biomechanical and histomorphometric evaluations. Material and methods: The implant surfaces comprised a resorbable media CaP microblasted (control) and a CaP resorbable media + silica-boost microblasted (experimental) surfaces. Surfaces were characterized by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), and optical interferometry (IFM) down to the nanometric level. The animal model involved the bilateral placement of control (n = 24) and experimental surface (n = 24) implants along the proximal tibiae of six dogs, remaining in vivo for 2 or 4 weeks. After euthanization, half of the specimens were torquedto- interface failure, and the other half was subjected to histomorphologic and bone-to-implant contact (BIC) evaluation. Torque and BIC statistical evaluation was performed by the Friedman test at 95% level of significance, and comparisons between groups was performed by the Dunn test. Results: IFM and SEM observations depicted comparable roughness parameters for both implant surfaces on the micrometer and nanometer scales. XPS analysis revealed similar chemical composition, except for the addition of Si on the experimental group. Torque-to-interface failure and BIC mean values showed no significant differences (P = 0.25 and 0.51, respectively) at both 2- and 4-week evaluation points for experimental and control groups. Early bone healing histomorphologic events were similar between groups. Conclusions: The experimental surface resulted in not significantly different biomechanical fixation and BIC relative to control. Both surfaces were biocompatible and osseoconductive.

Early peri-implant endosseous healing of two implant surfaces placed in surgically created circumferential defects. A histomorphometric and fluorescence study in dogs

Objective Several implant surfaces are being developed, some in the nanoscale level. In this study, two different surfaces had their early healing properties compared in context of circumferential defects of various widths. Material and methods Six dogs had the mandibular premolars extracted. After 8weeks, four implants were placed equicrestally in each side. One acted as control, while the others were inserted into sites with circumferential defects of 1.0, 1.5 and 2.0mm wide and 5mm deep. A nano-modified surface was used on one side and a micro-rough on the other. Bone markers were administered on the third day after implant placement and then after 1, 2, 4weeks to investigate the bone formation dynamic through fluorescence analysis. Ground sections were prepared from 8-week healing biopsies and histomorphometry was performed. Results The fluorescence evaluation of the early healing showed numerically better results for the nano-modified group; however this trend was not followed by the histomorphometric evaluation. A non-significant numerical superiority of the micro-rough group was observed in terms of vertical bone apposition, defect bone fill, bone-to-implant contact and bone density. In the intra-group analysis, the wider defects showed the worse results while the control sites showed the best results for the different parameters, but without statistical relevance. Conclusion Both surfaces may lead to complete fill of circumferential defects, but the gap width has to be considered as a challenge. The nano-scale modification was beneficial in the early stages of bone healing, but the micro-rough surface showed numerical better outcomes at the 8-week final period.

Biomechanical and histologic evaluation of non-washed resorbable blasting media and alumina-blasted/acid-etched surfaces

Objectives: To compare the biomechanical fixation and histomorphometric parameters between two implant surfaces: non-washed resorbable blasting media (NWRBM) and alumina-blasted/acid-etched (AB/AE), in a dog model. Material and methods: The surface topography was assessed by scanning electron microscopy, optical interferometry and chemistry by X-ray photoelectron spectroscopy (XPS). Six beagle dogs of similar to 1.5 years of age were utilized and each animal received one implant of each surface per limb (distal radii sites). After a healing period of 3 weeks, the animals were euthanized and half of the implants were biomechanically tested (removal torque) and the other half was referred to nondecalcified histology processing. Histomorphometric analysis considered bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). Following data normality check with the Kolmogorov-Smirnov test, statistical analysis was performed by paired t-tests at 95% level of significance. Results: Surface roughness parameters Sa (average surface roughness) and Sq (mean root square of the surface) were significantly lower for the NWRBM compared with AB/ AE. The XPS spectra revealed the presence of Ca and P in the NWRBM. While no significant differences were observed for both BIC and BAFO parameters (P>0.35 and P>0.11, respectively), a significantly higher level of torque was observed for the NWRBM group (P = 0.01). Bone morphology was similar between groups, which presented newly formed woven bone in proximity with the implant surfaces. Conclusion: A significant increase in early biomechanical fixation was observed for implants presenting the NWRBM surface.

Effects of type I collagen coating on titanium osseointegration: histomorphometric, cellular and molecular analyses

The investigation of titanium (Ti) surface modifications aiming to increase implant osseointegration is one of the most active research areas in dental implantology. This study was carried out to evaluate the benefits of coating Ti with type I collagen on the osseointegration of dental implants. Acid etched Ti implants (AETi), either untreated or coated with type I collagen (ColTi), were placed in dog mandibles for three and eight weeks for histomorphometric, cellular and molecular evaluations of bone tissue response. While the histological aspects were essentially the same with both implants being surrounded by lamellar bone trabeculae, histomorphometric analysis showed more abundant bone formation in ColTi, mainly at three weeks. Cellular evaluation showed that cells harvested from bone fragments in close contact with ColTi display lower proliferative capacity and higher alkaline phosphatase activity, phenotypic features associated with more differentiated osteoblasts. Confirming these findings, molecular analyses showed that ColTi implants up-regulates the expression of a panel of genes well known as osteoblast markers. Our results present a set of evidences that coating AETi with collagen fastens the osseointegration by stimulating bone formation at the cellular and molecular levels, making this combination of morphological and biochemical modification a promising approach to treat Ti surfaces.

Implant Osseointegration in Circumferential Bone Defects Treated with Latex-Derived Proteins or Autogenous Bone in Dog's Mandible

Background: In sites with diminished bone volume, the osseointegration of dental implants can be compromised. Innovative biomaterials have been developed to aid successful osseointegration outcomes. Purpose: The aim of this study was to evaluate the osteogenic potential of angiogenic latex proteins for improved bone formation and osseointegration of dental implants. Materials and Methods: Ten dogs were submitted to bilateral circumferential defects (5.0 x 6.3 mm) in the mandible. Dental implant (3.3 x 10.0 mm, TiUnite MK3 (TM), Nobel Biocare AB, Goteborg, Sweden) was installed in the center of the defects. The gap was filled either with coagulum (Cg), autogenous bone graft (BG), or latex angiogenic proteins pool (LPP). Five animals were sacrificed after 4 weeks and 12 weeks, respectively. Implant stability was evaluated using resonance frequency analysis (Osstell Mentor T, Osstell AB, Goteborg, Sweden), and bone formation was analyzed by histological and histometric analysis. Results: LPP showed bone regeneration similar to BG and Cg at 4 weeks and 12 weeks, respectively (p >= 3.05). Bone formation, osseointegration, and implant stability improved significantly from 4 to 12 weeks (p <= 2.05). Conclusion: Based on methodological limitations of this study, Cg alone delivers higher bone formation in the defect as compared with BG at 12 weeks; compared with Cg and BG, the treatment with LPP exhibits no advantage in terms of osteogenic potential in this experimental model, although overall osseointegration was not affected by the treatments employed in this study.