Development of nanohydrogels as a vehicle for the release of bioactive compounds in food matrices

PhD in Chemical and Biological Engineering

Thermo-compression molding of chitosan with a deep eutectic mixture for biofilms development

Supplementary information available at: http://www.rsc.org/suppdata/c5/gc/c5gc02231b/c5gc02231b1.pdf

Effects of residues on the degradation of PHA produced from mixed microbial cultures and processed in extrusion

Thermal degradation upon melting is one of the major drawbacks reported for polyhydroxyalkanoates (PHA). However, the role of residues originating from the fermentation and the extraction steps on the thermal stability of this class of biopolymers still needs to be clarified. In the particular case of PHA produced from mixed microbial cultures (MMC), this topic is even less documented in the literature. Here, two polyhydroxy(butyrate-co-valerate) (PHBV) produced from MMC enriched in PHA accumulating organisms and fed with cheese whey were studied. A micro extrusion line is used to produce filaments and assess the processability and the degradation of processed PHBV. The prototype micro extrusion line allows for studying grams of materials. The two PHBV contain 18 mol% HV. PHBV was recovered with 11 wt% residues, and further submitted to a purification procedure resulting in a second biopolyester containing less than 2 wt% impurities. The thermorheological characterization of the two PHBV is first presented, together with their semicrystalline properties. Then the processing windows of the two biopolyesters are presented. Finally, the properties of extruded filaments are reported and the thermomechanical degradation of PHBV is extensively studied. The structure was assessed by wide angle X-ray diffraction, mechanical and rheological properties are reported, thermal properties are studied with differential scanning calorimetry and thermogravimetric analysis, whereas Fourier Transform Infrared spectroscopy was used to assess the impact of the extrusion on PHBV chemical structure. All results obtained with the two PHBV are compared to assess the effects of residues on both PHBV processability and degradation.

Structural, mechanical and piezoelectric properties of polycrystalline AlN films sputtered on titanium bottom electrodes

Polycrystalline AlN coatings deposited on Ti-electrodes films were sputtered by using nitrogen both as reactive gas and sputtering gas, in order to obtain high purity coatings with appropriate properties to be further integrated into wear resistance coatings as a piezoelectric monitoring wear sensor. The chemical composition, the structure and the morphology of the films were investigated by X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy and atomic force microscopy techniques. These measurements show the formation of highly (101), (102) and (103) oriented AlN films with good piezoelectric and mechanical properties suitable for applications in electronic devices. Through the use of lower nitrogen flow a densification of the AlN coating occurs in the microstructure, with an improvement of the crystallinity along with the increase of the hardness. Thermal stability of aluminum nitride coatings at high temperature was also examined. It was found an improvement of the piezoelectric properties of the highly (10x) oriented AlN films which became c-axis (002) oriented after annealing. The mechanical behavior after heat treatment shows an important enhancement of the surface hardness and Young’s modulus, which decrease rapidly with the increase of the indentation depth until approach constant values close to the substrate properties after annealing. Thus, thermal annealing energy promotes not only the rearrangement of Al–N network, but also the occurrence of a nitriding process of unsaturated Al atoms which cause a surface hardening of the film.

Polymer electrolyte based on DNA and N,N,N-trimethyl-N-(2-hydroxyethyl)ammonium bis(trifluoromethylsulfonyl)imide

Combining ionic liquids (ILs) with polymers offers the prospect of new applications, where they surpass the performance of conventional media, such as organic solvents, giving advantages in terms of improved safety and a higher operating temperature range. In this work we have investigated the morphology, thermal and electrochemical properties of polymer electrolytes prepared through the addition of con- trolled quantities of the cholinium based IL N,N,N-trimethyl-N-(2-hydroxyethyl)ammonium bis(trifluo- romethylsulfonyl)imide ([N1 1 1 2(OH)] [NTf2]) to a deoxyribonucleic acid (DNA) host network. These novel IL-based electrolytes have been analyzed aiming at applications in electrochemical devices. An optimized sample showed good thermal stability up to 155 °C and a wide electrochemical window of ~3.5 V. The highest conductivity was registered for the DNA[N1 1 1 2(OH)][NTf2] (1:1) (2.82 × 10-5 and 1.09 × 10-3 S cm-1 at 30 and 100 °C, respectively).

Desenvolvimento e caracterização de membranas de remoção de compostos de arsénio em água

Dissertação de mestrado em Técnicas de Caracterização e Análise Química

Evolution of the functional properties of titanium–silver thin films for biomedical applications: Influence of in-vacuum annealing

In this work, the thermal stability of TiAgx thin films, deposited by magnetron sputtering, was evaluated, envisaging their application in biomedical devices, namely as electrodes for biosignal acquisition. Based on the composition and microstructural characterization, a set of four representative TiAgx thin films was selected in order to infer whether they are thermally stable in terms of functional properties. In order to achieve this purpose, the structural and morphological evolution of the films with annealing temperature was correlated with their electrical, mechanical and thermal properties. Two distinct zones were identified and two samples from each zone were extensively analysed. In the first zone (zone I), Ti was the main component (Ti-rich zone) while in the second, zone II, the Ag content was more significant. The selected samples were annealed in vacuum at four different temperatures up to 500 oC. For the samples produced within zone I, small microstructural changes were observed due to the recrystallization of the Ti structure and grain size increment. Also, no significant changes were observed with annealing temperature regarding the f l ’ functional properties, being thermally stable up to 500 oC. For higher Ag contents (zone II) the energy supplied by thermal treatments was sufficient to activate the crystallization of Ti-Ag intermetallic phases. A strong increase of the grain size of these phases was also reported. The structural and morphological organization proved to be determinant for the physical responses of the TiAgx system. The hardness and Y g’s modulus were significantly improved with the formation of the intermetallic phases. The silver addition and annealing treatments also played an important role in the electrical conductivity of the films, which was once again improved by the formation of Ti-Ag phases. The thermal diffusivity of the films was practically unchanged with the heat-treatment. This set of results shows that this intermetallic-like thin film system has good thermal stability up to high temperatures (as high as 500 oC), which in case of the highest Ag content zone is particularly evident for electrical and mechanical properties, showing an important improvement. Hardness increases about three times, while resistivity values become half of those from the lowest Ag contents zone. These set of characteristics are consistent with the targeted applications, namely in terms of biomedical sensing devices.

Efeito da adição de Zr no endurecimento de ligas Al-Sc

Dissertação de mestrado integrado em Engenharia de Materiais

Patterned CNT-PDMS nanocomposites for flexible pressure sensors

This paper reports the fabrication process and characterization of a flexible pressure sensor based on polydimethylsiloxane (PDMS) and multi-walled carbon nanotubes (CNT-PDMS). The proposed approach relies on patterned CNT-PDMS nanocomposite strain gauges fabricated with SU-8 microstructures (with the micropatterns) in a low‑cost and simple fabrication process. This nanocomposite polymer is mounted over a PDMS membrane, which, in turn, lies on top of a PDMS diaphragm like structure. This configuration enables the PDMS membrane to bend when pressure is applied, thereby affecting the nanocomposite strain gauges, effectively changing their electrical resistance. Carbon nanotubes have several advantages such as excellent mechanical properties, high electrical conductivity and thermal stability. Furthermore, the measurement range of the proposed sensor can be adapted according to the application by varying the CNTs content and geometry of microstructure. In addition, the sensor’s biocompatibility, low cost and simple fabrication makes it very appealing for biomechanical strain sensing. The sensor’s sensitivity was about 0.073%ΔR/mmHg.

Development and characterization of lipid-based nanosystems for controlled release of bioactive compounds

Tese de Doutoramento em Engenharia Química e Biológica.