Pulsed plasma treatment of polluted gas using wet/low temperature corona reactors

pplication of pulsed plasma for gas cleaning is gaining prominence in recent years mainly from the energy consideration point of view. Normally, gas treatment is carried out, at or above room temperature, by a conventional dry type corona reactor. However, this treatment is still inadequate in the removal of certain stable gases present in the exhaust/flue gas mixture. The authors report some interesting results of the treatment of such stable gases with pulsed plasma at very low ambient temperature. Also reported in the paper is an improvement in DeNO/DeNOx efficiency using unconventional wet-type reactors, designed and fabricated by the authors, operating at different ambient temperatures. Apart from laboratory tests on simulated gas mixtures, field tests were also carried out on the exhaust gas of a 8 kW diesel engine. Further, an attempt was made to test the feasibility of a helical wire as a corona electrode in place of the conventional straight wire electrode. A comparative analysis of the various tests is presented together with a note on the energy consideration

Pulsed plasma treatment of polluted gas using wet/low temperature corona reactors

Application of pulsed plasma for gas cleaning is gaining prominence in recent years mainly from the energy consideration point of view. Normally, gas treatment is carried out, at or above room temperature, by a conventional dry type corona reactor. However, this treatment is still inadequate in the removal of certain stable gases present in the exhaust/flue gas mixture. The authors report some interesting results of the treatment of such stable gases with pulsed plasma at very low ambient temperature. Also reported in the paper is an improvement in DeNO/DeNOx efficiency using unconventional wet-type reactors, designed and fabricated by the authors, operating at different ambient temperatures. Apart from laboratory tests on simulated gas mixtures, field tests were also carried out on the exhaust gas of a 8 kW diesel engine. Further, an attempt was made to test the feasibility of a helical wire as a corona electrode in place of the conventional straight wire electrode. A comparative analysis of the various tests is presented together with a note on the energy consideration

A gravimetric procedure for the determination of wet precipitated sulphur, dissolved sulphur, soluble sulphides and hydrogen sulphide

Elemental sulphur (in wet precipitated form or dissolved in organic solvents) and hydrogen sulphide have been determined gravimetrically at room temperature by conversion into copper sulphide by elemental copper in presence of an organic solvent such as benzene or acetonitrile. Any solvent in which sulphur is soluble can be used. The black copper sulphide formed can be weighed or determined iodometrically. Analysis indicates the black compound to be Cu1.8S. This room temperature method is a versatile one-step procedure sensitive to microgram or macro amounts of sulphur. It has been used for determining the solubility of sulphur in tetrahydrofuran and dioxan. The apparent heat of solution indicates that sulphur dissolves in these solvents without any marked solute—solvent interactions.

'Wet N2O oxidation' process and interface state density characterization of nanoscale nitrided SiO2 for flash memory application

In this paper we first present the 'wet N2O' furnace oxidation process to grow nitrided tunnel oxides in the thickness range 6 to 8 nm on silicon at a temperature of 800 degrees C. Electrical characteristics of MOS capacitors and MOSFETs fabricated using this oxide as gate oxide have been evaluated and the superior features of this oxide are ascertained The frequency response of the interface states, before and after subjecting the MOSFET gate oxide to constant current stress, is studied using a simple analytical model developed in this work.

Studies on the ionic transport and structural investigations of La0.5Li0.5TiO3 perovskite synthesized by wet chemical methods and the effect of Ce, Zr substitution at Ti site

La0.5Li0.5TiO3 perovskite was synthesized by various wet chemical methods. By adopting low temperature methods of preparation lithium loss from the material is prevented. La0.5Li0.5TiO3 (LLTO) was formed with cubic symmetry at 1473 K. LLTO was formed at relatively lower temperature by using hydrothermal preparation method. PVA gel-decomposition route yield tetragonal LLTO on annealing the dried gel at 1473 K. By using gel-carbonate route LiTi2O4 minor phase was found to remain even after heat-treatment at 1473 K. The hydroxylation of LLTO was done in deionized water as well as in dilute acetic acid medium. By hydroxylation process incorporation of hydroxyls and leaching out of Li+ was observed from the material. The Li+ concentration of these compositions was examined by AAS. The electrical conductivities of these compositions were measured by dc and ac impedance techniques at elevated temperatures. The activation energies of electrical conduction for these compositions were estimated from the experimental results. The measured activation energy of Li+ conduction is 0.34 eV. Unhydroxylated samples exhibit only Li+ conduction, whereas, the hydroxylated LLTO show proton conductivity at 298-550 K in addition to Li+ conductivity. The effect of Zr or Ce substitution in place of Ti were attempted. La0.5Li0.5ZrO3 Perovskite was not formed; instead pyrochlore phase (La2Zr2O7) along with monoclinic ZrO2 phases was observed above 1173 K; below 1173 K cubic ZrO2 is stable. (La0.5Li0.5)(2)CeO4 solid solution was formed in the case of Ce substitution at Ti sublattice on heat-treatment up to 1673 K. (c) 2005 Springer Science + Business Media, Inc.

Wet chemical syntheses of ultrafine multicomponent ceramic powders through gel to crystallite conversion

Coarse (BOn/2)-O-n+/xH(2)O (10temperature or superparamagnetic hexaferrites. Through the same route, luminescent phosphors of aluminates doped with rare-earth metals could be prepared. The present results indicate the general features of the gel-crystallite (G-C) conversion involving the instability of the metal hydroxide gel brought about by the disruption of the ionic pressure in the gel as a result of the faster diffusion of A(2+) ions through the solvent cavities within the gel frame work. This is accompanied by the splitting of the bridging groups like B-(OH)-B or B-O-B, leading to the breakdown of the gel into crystallites. G-C conversion has advantages as a method of synthesis of ceramics in terms of operational cost and procedural simplicity.

Structural, optical and EPR studies on ZnO:Cu nanopowders prepared via low temperature solution combustion synthesis

Cu (0.1 mol%) doped ZnO nanopowders have been successfully synthesized by a wet chemical method at a relatively low temperature (300 degrees C). Powder X-ray diffraction (PXRD) analysis, scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Fourier transformed infrared (FTIR) spectroscopy, UV-Visible spectroscopy, Photoluminescence (PL) and Electron Paramagnetic Resonance (EPR) measurements were used for characterization. PXRD results confirm that the nanopowders exhibit hexagonal wurtzite structure of ZnO without any secondary phase. The particle size of as-formed product has been calculated by Williamson-Hall (W-H) plots and Scherrer's formula is found to be in the range of similar to 40 nm. TEM image confirms the nano size crystalline nature of Cu doped ZnO. SEM micrographs of undoped and Cu doped ZnO show highly porous with large voids. UV-Vis spectrum showed a red shift in the absorption edge in Cu doped ZnO. PL spectra show prominent peaks corresponding to near band edge UV emission and defect related green emission in the visible region at room temperature and their possible mechanisms have been discussed. The EPR spectrum exhibits a broad resonance signal at g similar to 2.049, and two narrow resonances one at g similar to 1.990 and other at g similar to 1.950. The broad resonance signal at g similar to 2.049 is a characteristic of Cu2+ ion whereas the signal at g similar to 1.990 and g similar to 1.950 can be attributed to ionized oxygen vacancies and shallow donors respectively. The spin concentration (N) and paramagnetic susceptibility (X) have been evaluated and discussed. (C) 2011 Elsevier B. V. All rights reserved.

Study of temperature distribution along an artificially polluted insulator string

Insulator becomes wet partially or completely, and the pollution layer on it becomes conductive, when collecting pollutants for an extended period during dew, light rain, mist, fog or snow melting. Heavy rain is a complicated factor that it may wash away the pollution layer without initiating other stages of breakdown or it may bridge the gaps between sheds to promote flashover. The insulator with a conducting pollution layer being energized, can cause a surface leakage current to flow (also temperature-rise). As the surface conductivity is non-uniform, the conducting pollution layer becomes broken by dry bands (at spots of high current density), interrupting the flow of leakage current. Voltage across insulator gets concentrated across dry bands, and causes high electric stress and breakdown (dry band arcing). If the resistance of the insulator surface is sufficiently low, the dry band arcs can be propagated to bridge the terminals causing flashover. The present paper concerns the evaluation of the temperature distribution along the surface of an energized artificially polluted insulator string.

Low-temperature electrical conductivity of LaNi1-xFexO3

We report the electrical conductivity between 2 and 300 K for LaNi1-xFexO3 across the composition-controlled metal-insulator (m-i) transition. Using a method first suggested by Mobius, we identify the critical concentration x(c) to be 0.3 for the m-i transition. The negative temperature coefficient of resistivity observed at low temperatures in the metallic phase follows a temperature dependence characteristic of disorder effects. The semiconducting compositions (x greater than or equal to 0.3) do not show a simple activation energy but exhibit variable-range hopping at high temperatures confirming that the m-i transition in this system is driven by increasing disorder effects.

High temperature deformation and densification in alumina-yttria composites

Pinning by second phase particles offers a potent means for limiting grain growth and enhancing superplasticity in alumina-based ceramics. In the present study, a colloidal technique was used to produce green bodies of alumina-yttria composites; at elevated temperatures, the yttria particles react with alumina to produce YAG particles. The densification and high temperature deformation characteristics of alumina-YAG composites were studied using conventional free sintering and sinter-forging, which involves the application of a compressive stress without any lateral constraints. It is shown that the YAG particles retard both densification and grain growth. The experiments indicate also that the presence of YAG particles does not significantly alter the stress exponent for creep deformation.

Temperature dependent vibrational lifetimes in supercritical fluids near the critical point

Vibrational relaxation measurements on the CO asymmetric stretching mode (similar to 1980 cm(-1)) of tungsten hexacarbonyl (W(CO)(6)) as a function of temperature at constant density in several supercritical solvents in the vicinity of the critical point are presented. In supercritical ethane, at the critical density, there is a region above the critical temperature (Tc) in which the lifetime increases with increasing temperature. When the temperature is raised sufficiently (similar to T-c + 70 degrees C), the lifetime decreases with further increase in temperature. A recent hydrodynamic/thermodynamic theory of vibrational relaxation in supercritical fluids reproduces this behavior semiquantitatively. The temperature dependent data for fixed densities somewhat above and below the critical density is in better agreement with the theory. In fluoroform solvent at the critical density, the vibrational lifetime also initially increases with increasing temperature. However, in supercritical CO2 at the critical density, the temperature dependent vibrational lifetime decreases approximately linearly with temperature beginning almost immediately above T-c. The theory does not reproduce this behavior. A comparison between the absolute lifetimes in the three solvents and the temperature trends is made.

The high temperature mechanical characteristics of superplastic 3 mol% yttria stabilized zirconia

A detailed study was undertaken to characterize the deformation behavior of a superplastic 3 mol% yttria-stabilized tetragonal zirconia (3YTZ) over a wide range of strain rates, temperatures and grain sizes. The experimental data were analyzed in terms of the following equation for high temperature deformation: Image Full-size image ∞ σn d−pexp(−Q/RT), where Image Full-size image is the strain rate, σ is the flow stress, d is the grain size, Q is the activation energy, R is the gas constant, T is the absolute temperature, and n and p are constants termed the stress exponent and the inverse grain size exponent, respectively. The experimental data over a wide range of stresses revealed a transition in stress exponent. Deformation in the low and high stress regions was associated with n not, vert, similar 3 and p not, vert, similar 1, and n not, vert, similar 2 and p not, vert, similar 3, respectively. The transition stress between the two regions decreased with increasing grain size. The activation energy was similar for both regions with a value of not, vert, similar 550 kJ mol−1. Microstructural measurements revealed that grains remained essentially equiaxed after the accumulation of large strains, and very limited concurrent grain growths occurred in most experiments. Assessment of possible rate controlling creep mechanisms and comparison with previous studied indicate that in the n not, vert, similar 2 region, deformation occurs by a grain boundary sliding process whose rate is independent of impurity content. Deformation in the n not, vert, similar 3 region is controlled by an interface reaction that is highly sensitive to impurity content. It is concluded that an increase in impurity content increases yttrium segregation to grain boundaries, which enhances the rate of the interface reaction, thereby decreasing the apparent transition stress between the n not, vert, similar 2 and n not, vert, similar 3 regions. This unified approach incorporating two sequential mechanisms can rationalize many of the apparently dissimilar results that have been reported previously for deformation of 3YTZ.

Electrical Conductivity and Magneto-Resistance Studies on Polyaniline-Pmma Blends at Very Low Temperature

D.C. electrical conductivity of polyaniline (33%,40%) blended with PMMA was measured from 5K to 300mK. The conductivity behaviour is consistent with fluctuation induced tunneling. Magneto-resistance (MR) was measured between 300K and 2K. From 20K to 2K, a large positive MR was observed. At 2K, for low magnetic fields (<1 Tesla), a deviation from the normal H-2 behaviour was observed.

Time-temperature histories of spherical food products during bulk forced-air precooling

A general mathematical model for forced air precooling of spherical food products in bulk is developed. The food products are arranged inline to form a rectangular parallelepiped. Chilled air is blown along the height of the package. The governing equations for the transient two-dimensional conduction with internal heat generation in the product, simultaneous heat and mass transfer at the product-air interface and one-dimensional transient energy and species conservation equations for the moist air are solved numerically using finite difference methods. Results are presented in the form of time-temperature histories. Experiments are conducted with model foods in a laboratory scale air precooling tunnel. The agreement between the theoretical and experimental results is found to be good. In general, a single product analysis fails to predict the precooling characteristics of bulk loads of food products. In the range of values investigated, the respiration heat is found to have a negligible effect.

High-Temperature Phase Transition Studies in a Novel Fast Ion Conductor, Na2Cd(SO4)2, Probed by Raman Spectroscopy

Temperature-dependent Raman spectroscopic studies were carried out on Na2Cd(SO4)(2) from room temperature to 600 degrees C. We observe two transitions at around 280 and 565 degrees C. These transitions are driven by the change in the SO4 ion. On the basis of these studies, one can explain the changes in the conductivity data observed around 280 and 565 degrees C. At 280 degrees C, spontaneous tilting of the SO4 ion leads to restriction of Na+ mobility. Above 565 degrees C, the SO4 ion starts to rotate freely, leading to increased mobility of Na+ ion in the channel.