Improved magneto-electric response in Na0.5Bi0.5TiO3-MnFe2O4 composites

Magneto-electric composites comprising Na0.5Bi0.5TiO3 (NBT) and MnFe2O4 (MFO) were fabricated using their fine powders obtained via sol-gel method. X-ray diffraction and scanning electron microscopy results confirmed the single-phase formation of NBT and MFO and the composite nature when these were mixed and sintered at appropriate temperatures. The dielectric constant (epsilon(r)) and dielectric loss (D) decreased with increase in frequency (40-110 MHz). Room temperature magnetization measurements established these composites to be soft magnetic. Further, the nature of these composites were established to be magneto-electric at 300 K. The highest ME response of 0.19 % was observed in 30NBT-70MFO composite. The ME coefficient (alpha) was 240 mV/cm Oe for the same composition. The present study demonstrated the effectiveness of NBT/MFO as a lead-free multiferroic composite and provides an alternative for environment-friendly ME device applications.

Graphene Oxide-MnFe2O4 Magnetic Nanohybrids for Efficient Removal of Lead and Arsenic from Water

We show that the hybrids of single-layer graphene oxide with manganese ferrite magnetic nanoparticles have the best adsorption properties for efficient removal of Pb(II), As(III), and As(V) from contaminated water. The nanohybrids prepared by coprecipitation technique were characterized using atomic force and scanning electron microscopies, Fourier transformed infrared spectroscopy, Raman spectroscopy, X-ray diffraction, and surface area measurements. Magnetic character of the nanohybrids was ascertained by a vibrating sample magnetometer. Batch experiments were carried out to quantify the adsorption kinetics and adsorption capacities of the nanohybrids and compared with the bare nanoparticles of MnFe2O4. The adsorption data from our experiments fit the Langmuir isotherm, yielding the maximum adsorption capacity higher than the reported values so far. Temperature-dependent adsorption studies have been done to estimate the free energy and enthalpy of adsorption. Reusability, ease of magnetic separation, high removal efficiency, high surface area, and fast kinetics make these nanohybrids very attractive candidates for low-cost adsorbents for the effective coremoval of heavy metals from contaminated water.

Enhanced electric field tunable magnetic properties of lead-free Na0.5Bi0.5TiO3-MnFe2O4 multiferroic composites

Strong magnetoelectric (ME) interaction was exhibited at both dc and microwave frequencies in a lead-free multiferroic particulate composites of Na0.5Bi0.5TiO3 (NBT) and MnFe2O4 (MFO) multiferroic, which were prepared by sol-gel route. The room temperature permeability measurements were carried out in the frequency range of 1 MHz-1 GHz. A systematic study of structural, magnetic and ME properties were undertaken. The room temperature ferromagnetic resonance (FMR) was studied. Strong ME coupling is demonstrated in 70NBT-30MFO composite by an electrostatically tunable FMR field shift up to 428 Oe (at E = 4 kV/cm), which increases to a large value of 640 Oe at E = 8 kV/cm. Furthermore, these lead-free multiferroic composites exhibiting electrostatically induced magnetic resonance field at microwave frequencies provide great opportunities for electric field tunable microwave devices.

MnFe2O4-Fe3O4 core-shell nanoparticles as a potential contrast agent for magnetic resonance imaging

In recent years, magnetic core-shell nanoparticles have received widespread attention due to their unique properties that can be used for various applications. We introduce here a magnetic core-shell nanoparticle system for potential application as a contrast agent in magnetic resonance imaging (MRI). MnFe2O4-Fe3O4 core-shell nanoparticles were synthesized by the wet-chemical synthesis method. Detailed structural and compositional charaterization confirmed the formation of a core-shell microstructure for the nanoparticles. Magnetic charaterization revealed the superparamagnetic nature of the as-synthesized core-shell nanoparticles. Average size and saturation magnetization values obtained for the as-synthesized core-shell nanoparticle were 12.5 nm and 69.34 emu g(-1) respectively. The transverse relaxivity value of the water protons obtained in the presence of the core-shell nanoparticles was 184.1 mM(-1) s(-1). To investigate the effect of the core-shell geometry towards enhancing the relaxivity value, transverse relaxivity values were also obtained in the presence of separately synthesized single phase Fe3O4 and MnFe2O4 nanoparticles. Average size and saturation magnetization values for the as-synthesized Fe3O4 nanoparticles were 12 nm and 65.8 emu g(-1) respectively. Average size and saturation magnetization values for the MnFe2O4 nanoparticles were 9 nm and 61.5 emu g(-1) respectively. The transverse relaxivity value obtained in the presence of single phase Fe3O4 and MnFe2O4 nanoparticles was 96.6 and 83.2 mM(-1) s(-1) respectively. All the nanoparticles (core-shell and single phase) were coated with chitosan by a surfactant exchange reaction before determining the relaxivity values. For similar nanoparticle sizes and saturation magnetization values, the highest value of the transverse relaxivity in the case of core-shell nanoparticles clearly illustrated that the difference in the magnetic nature of the core and shell phases in the core-shell nanoparticles creates greater magnetic inhomogeneity in the surrounding medium yielding a high value for proton relaxivity. The MnFe2O4-Fe3O4 core-shell nanoparticles exhibited extremely low toxicity towards the MCF-7 cell line. Taken together, this opens up new avenues for the use of core-shell nanoparticles in MRI.

A Remarkably Efficient MnFe2O4-based Oxidase Nanozyme

Nanomaterials-based enzyme mimetics (nanozymes) have attracted considerable interest due to their applications in imaging, diagnostics, and therapeutic treatments. Particularly, metal-oxide nanozymes have been shown to mimic the interesting redox properties and biological activities of metalloenzymes. Here we describe an efficient synthesis of MnFe2O4 nanomaterials and show how the morphology can be controlled by using a simple co-precipitation method. The nanomaterials prepared by this method exhibit a remarkable oxidase-like activity. Interestingly, the activity is morphology-dependent, with nanooctahedra (NOh) exhibiting a catalytic efficiency of 2.21 x 10(9) M-1 s(-1), the highest activity ever reported for a nanozyme.