Tl1-xPbxCaSr2Cu2O7: Another 1122 high-Tc superconductor

The 1122 member of the Tl(Ca, Sr)n+1CunO2n+3 system is stabilized by partial substitution of Tl by Pb. Tl1?xPbxCaSr2Cu2O7 with x=0.25 and 0.5 have both primitive tetragonal structures (c 12.1 Å) showing onset of superconductivity around 70 K and 90 K, respectively.

Photoemission study of the high-Tc superconductor Bi1.8Pb0.4Sr2Ca2.2Cu3O10

Ultraviolet and X-ray photoemission spectroscopic (UPS and XPS) studies to characterize the electronic structure of bismuth cuprate superconductor with nominal composition of Bi1.8Pb0.4Sr2Ca2.2Cu3O10 have been carried out. The data clearly shows the metallic emission at the Fermi level (EF). The shoulder (-1.2 eV) near the EF is attributed to the Cu-O derived states. Cu satellite structures observed both in the UPS and XPS show the strongly correlated nature of the Cu 3d electrons. Core level shifts indicate that 3+ and 4+ are the main oxidation of Bi and Pb, respectively. The Pb core lines show two components indicating their inequivalent sites. Core level O 1s spectrum is deconvoluted to show the presence of structurally non-equivalent oxygen sites.

Laser processing of high-Tc superconducting thin films

High-Tc superconducting thin films can be deposited and processed by pulsed and CW lasers, and a respectable materials technology for the Y-Ba-Cu-O superconductor is rapidly emerging. The pulsed laser deposition technique is simple because it produces films with compositions nearly identical to those of the target pellets. A larger variety of substrates can be used, compared to other deposition technologies, because of the relatively low temperature requirements. The laser deposition mechanism has been investigated. As-deposited superconducting films, epitaxial films with smooth surfaces, and multilayer structures with abrupt interfaces have been produced. The electrical transport properties can be changed locally using a focused argon-ion laser by modifying the oxygen stoichiometry. This laser writing can be erased by room-temperature exposure to an oxygen plasma. Other laser patterning methods such as material removal, melt-quench, and direct pattern transfer are being developed.

Comparison of the effect of processing parameters and degradation on the DC and microwave properties of thin films and polycrystalline bulk high-Tc superconducting materials

The sharp increase in microwave power loss (the reverse of what has previously been reported) at the transition temperature in high-Tc superconducting systems such as YBaCu oxide (polycrystalline bulk and thin films obtained by the laser ablation technique) and BiPbSrCaCu oxide is reported. The differences between DC resistivity ( rho ) and the microwave power loss (related to microwave surface resistance) are analysed from the data obtained by a simultaneous measurement set-up. The influence of various parameters, such as preparation conditions, thickness and aging of the sample and the probing frequency (6-18 GHz), on the variation of microwave power loss with temperature is outlined.

Phenomenological aspects of phase fluctuation in high Tc superconductors: Cooper pair droplets

We point out how fluctuation of the phase of the superconducting order parameter can play a key role in our understanding of high Te superconductors. A simple universal criterion is given which illustrates why all oxide superconductors in contrast to classical superconductors ought to behave as a lattice of cooper pairs. T-c is to be thought of as the temperature of phase coherence or the temperature above which the lattice of Cooperpair 'melts' into a phase of Cooper-pair droplets that starts forming at T approximate to T-* . This is the pseudo-gap region. Quantum fluctuation of the phase predicts a superconductor to insulator phase transition for all underdoped materials.

Relation between high-tc superconductivity and structure - a study of la3-xba3+xcu6o14+delta and yba2cu3o7-delta systems

Superconductivity is found in tetragonal La3−x Ba3+x Cu6O14+δ and La, Ba)6−x Sr x Cu6O14+δ even though they do not possess Cu-O chains or the K2NiF4 structure. Resistivity measurements confirm the occurrence of a transformation from chain-superconductivity to sheet-superconductivity in YBa2Cu3O7−δ as δ is varied in the range 0.0–0.5.

High-Tc superconductivity in the Er---Ba---Cu---O and related systems

ErBa2Cu3O7 and Er0.5Y0.5Ba2Cu3O7 are both high-Tc superconductors attaining zero resistance above 80 K. Preliminary studies indicate that Yb1−xYxBa2Cu3O7 also exhibits zero resistance above 77 K.

HIGH-Tc superconductivity in perovskite oxides of the Y-Ba-Cu-O system

Several biphasic compositions of the type Y3-xBa3+xCu6O14 show an onset of superconductivity in the 90-115K range, attaining zero resistance in the 70-85K range. The phase responsible for superconductivity in these compositions is a perovskite oxide of composition YBa2Cu3 O7. This oxide annealed in oxygen shows the onset of superconductivity at 120K and zero resistance at 87K. YBa2,Cu3O7 shows the highest Meissner effect of all oxide superconductors. The superconducting behaviour of the two perovskite oxides, Y0.95Ba1.95,Cu3O7 and Y1.05Ba1.95Cu3O7 show interesting features; a marked decrease in resistivity is observed from room temperature itself in the former oxide with zero resistance at 89K. Electron microscopy and infrared spectra of these oxides are briefly discussed.

Oxygen desorption from high Tc YBa2Cu3O7−δ (δ = 0.05, 0.5)

From a temperature programmed desorption study employing a quadrupole mass spectrometer, the superconducting oxide YBa2Cu3O7−δ (δ = 0.05) showed two distinct oxygen desorption peaks, one below and one above 470°C. The activation energy of oxygen desorption of the superconducting oxide was 28 Kcals/mole and that of non-superconducting oxide (YBa2Cu3O6.5) was 54 Kcals/mole. No impurity peaks due to H2O, CO and CO2 from the bulk or adsorbed on surfaces could be observed when a well prepared superconducting oxide was heated up to 650°C.

Surface electronic structure of the high-Tc oxides

Electron energy loss spectroscopy (EELS) has been employed to monitor surface conductivity changes in YBa2Cu3O7 as a function of temperature. Concomitant use of x-ray photoelectron spectroscopy (XPS) establishes that the formation of oxygen dimers with lowering of temperature is accompanied by a simultaneous increase of surface conductivity.

Novel 1122 thallium cuprates showing high Tc superconductivity: TlCa1-xY,Ba2Cu2Oy,T,1-xPbxCaSr2Cu2Oy and TlCa0.5Ln0.5Sr2Cu2Oy

Substitution of Ca by Y in TlCaBa2Cu2Oy does not favour superconductivity, but substitution of Tl by Pb or of Ca by Ln (Ln = Y or rare earth) in TlCaSr2Cu2Oy results in high Tc superconductivity (Tc π 60-90 K). TlCa1-xLnxSr2Cu2Oy is a new series of high Tc superconductors, but the x = 0.0 composition does not exhibit bulk superconductivity.

Study of the electronic structures of high Tc cuprate superconductors by electron energy loss and secondary electron emission spectroscopies

Energy loss spectra of superconducting YBa2Cu3O6.9' Bi1.5Pb0.5Ca2.5Sr1.5Cu3O10+δ and Tl2CaBa2Cu3O8 obtained at primary electron energies in the 170–310 eV range show features reflecting the commonalities in their electronic structures. The relative intensity of the plasmon peak shows a marked drop across the transition temperature. Secondary electron emission spectra of the cuprates also reveal some features of the electronic structure.

As-deposited near-single crystalline high Tc and Jc superconducting thin films by a pulsed lased deposition process

As-deposited high Tc superconducting Y1Ba2Cu3O7−x films with zero resistance temperatures of similar, equals89 K and critical current densities about 0.7×106 A/cm2 at 77 K have been reproducibly fabricated at a substrate holder temperature at 650°C, using pulsed laser deposition, without post-annealing. One key to these results is the injection of gaseous oxygen into laser produced plume just in front of the target. In this way, the correct amount of oxygen is incorporated into the as-grown film so that post-deposition treatment becomes unnecessary. Axial ion channeling in these as-deposit high Tc superconducting films on (100) SrTiO3 and X-ray photoelectron spectroscopy (XPS) on the film surfaces were performed. Angular yield profile near the film surface for Ba, and the surface peak intensity were measured using 3 MeV He ions. For channeling normal to the substrate a minimum yield of 7%, compared to similar, equals3% for single crystals, was obtained. The results of ion channeling and XPS studies indicate that the as-deposited films have good crystallinity as well as toichiometry to within similar, equals1 nm of the film surface. The in-situ growth of such high Tc and Jc films is an important step in the use of the laser deposition technique to fabricate multilayer structures and the surface perfection is of importance in tunneling devices such as Josephson junctions.

Hole pairing within an extended Anderson impurity model applicable to the high-Tc cuprates

We calculate the binding energy of a hole pair within the extended Anderson Hamiltonian for the high-Tc cuprates including a Cu impurity and an oxygen-derived band. The results indicate that stable hole pairs can be formed for intra-atomic and interatomic Coulomb repulsion strengths larger than 6 and 3.5 eV, respectively. It is also shown that the total hybridization strength between the Cu 3d and oxygen p band should be less than 2.5 eV. The hole pairing takes place primarily within the oxygen-derived p band. The range of parameter values for which hole pairing occurs is also consistent with the earlier photoemission results from these cuprates.