Low temperature sulfurization of electrodeposited Cu(In,Al)Se-2 thin films

Sulfurization of Cu(In,Al)Se-2 films is carried out in an indigenously made set up at moderately low temperature. The films are sulfurized for different time durations of 15, 30, 45 and 60 min at 150 degrees C. InSe and Cu2S phases occurred in the films during the initial stage of sulfurization along with Cu(In,Al)(Se,S)(2) phase. The compositional analysis shows that the sulfur incorporation is saturated after 30 min. Crystallinity increased with the increase in sulfurization time. The band gap of the Cu(In,Al)Se-2 film increased up to 1.35 eV with the addition of sulfur. Single phase Cu(In,Al)(Se,S)(2) with high crystallinity is obtained after 60 min of sulfurization. (C) 2014 Elsevier B.V. All rights reserved.

Growth and electrical transport properties of InGaN/GaN heterostructures grown by PAMBE

InGaN epitaxial films were grown on GaN template by plasma-assisted molecular beam epitaxy. The composition of indium incorporation in single phase InGaN film was found to be 23%. The band gap energy of single phase InGaN was found to be similar to 2.48 eV: The current-voltage (I-V) characteristic of InGaN/GaN heterojunction was found to be rectifying behavior which shows the presence of Schottky barrier at the interface. Log-log plot of the I-V characteristics under forward bias indicates the current conduction mechanism is dominated by space charge limited current mechanism at higher applied voltage, which is usually caused due to the presence of trapping centers. The room temperature barrier height and the ideality factor of the Schottky junction were found to 0.76 eV and 4.9 respectively. The non-ideality of the Schottky junction may be due to the presence of high pit density and dislocation density in InGaN film. (C) 2014 Elsevier Ltd. All rights reserved.

Electrospun SnSb Crystalline Nanoparticles inside Porous Carbon Fibers as a High Stability and Rate Capability Anode for Rechargeable Batteries

In an electrochemical alloying reaction, the electroactive particles become mechanically unstable owing to large volume changes occurring as a result of high amounts of lithium intake. This is detrimental for long-term battery performance. Herein, a novel synthesis approach to minimize such mechanical instabilities in tin particles is presented. An optimal one-dimensional assembly of crystalline single-phase tin-antimony (SnSb) alloy nanoparticles inside porous carbon fibers (abbreviated SnSb-C) is synthesized for the first time by using the electrospinning technique (employing non-oxide precursors) in combination with a sintering protocol. The ability of antimony to alloy independently with lithium is beneficial as it buffers the unfavorable volume changes occurring during successive alloying/dealloying cycles in Sn. The SnSb-C assembly provides nontortuous (tortuosity coefficient, =1) fast conducting pathways for both electrons and ions. The presence of carbon in SnSb-C completely nullifies the conventional requirement of other carbon forms during cell electrode assembly. The SnSb-C exhibited remarkably high electrochemical lithium stability and high specific capacities over a wide range of currents (0.2-5Ag(-1)). In addition to lithium-ion batteries, it is envisaged that SnSb-C also has potential as a noncarbonaceous anode for other battery chemistries, such as sodium-ion batteries.

Optical and dielectric study of strontium modified barium zirconium titanate ceramic prepared by high energy ball milling

Strontium modified barium zirconium titanate with general formula Ba1-xSrxZr0.05Ti0.95O3 ceramics have been prepared by solid state and high energy ball milling technique. The X-ray diffraction and Rietveld refinement studies show that all the compositions have single phase symmetry. The composition BaZr0.05Ti0.95O3 shows orthorhombic symmetric with space group Amm2. The structure changes from orthorhombic to tetragonal with strontium doping up to x = 0.3 and with further addition, changes to cubic. The scanning electron micrographs show that the grain size decreases with increase in strontium content. The temperature dependent dielectric behavior shows three phase transition in the parent material which merges with an increase in Sr content The transition temperature and dielectric constant decreases with an increase in Sr concentration. The phase transition becomes more diffused with increment in doping concentration. The ferroelectric behavior of the ceramics is studied by the hysteresis loop. The optical behavior is studied by the UV-visible spectroscopy and found that the optical band gap increases with Sr concentration. (C) 2015 Elsevier B.V. All rights reserved.

Metal-insulator transition characteristics of vanadium dioxide thin films synthesized by ultrasonic nebulized spray pyrolysis of an aqueous combustion mixture

We report the synthesis of high quality vanadium dioxide (VO2) thin films by a novel spray pyrolysis technique, namely ultrasonic nebulized spray pyrolysis of aqueous combustion mixture (UNSPACM). This simple and cost effective two step process involves synthesis of a V2O5 film on an LaAlO3 substrate followed by a controlled reduction to form single phase VO2. The formation of M1 phase (p21/c) is confirmed by Raman spectroscopic studies. A thermally activated metal-insulator transition (MIT) was observed at 61 degrees C, where the resistivity changes by four orders of magnitude. Activation energies for the low conduction phase and the high conduction phase were obtained from temperature variable resistance measurements. The infrared spectra also show a dramatic change in reflectance from 13% to over 90% in the wavelength range of 7-15 mu m. This indicates the suitability of the films for optical switching applications at infrared frequencies.

On the Room Temperature Ferromagnetic and Ferroelectric Properties of Pb(Fe1/2Nb1/2)O-3

We report the origin of room temperature (RT) ferromagnetic and ferroelectric properties of Pb(Fe1/2Nb1/2)O-3 (PFN) ceramic sample prepared by modified solid-state reaction synthesis by a single-step method, based on X-ray diffraction (XRD), neutron diffraction (ND), Mossbauer spectroscopy and electron paramagnetic resonance (EPR) spectroscopy results. Formation of single-phase monoclinic PFN ceramic with Cm space group was confirmed by XRD and ND at RT. The morphology studied by scanning electron microscopy (SEM) confirmed uniform microstructure of the sample with average grain size of similar to 2 mu m. The ND, Mossbauer spectroscopy, M-H loop and EPR studies were carried out to confirm the existence of weak ferromagnetism at RT. A clear opening of hysteresis (M-H) loop is evidenced as the existence of weak ferromagnetism at RT. EPR spectrum clearly shows the ferromagnetism through a good resonance signal. The symmetric EPR line shape with g = 1.9895 observed in PFN sample was identified to be due to Fe3+ ions. Mossbauer spectroscopy at RT shows superparamagnetic behaviour with presence of Fe in 3+ valence state. Ferroelectric P-E loops on PFN at RT confirm the existing ferroelectric ordering. Our observation is in agreement with literature, and it supports that the origin of ferromagnetism and ferroelectricity is isolated, i.e. from different regions in the sample. Our results do not support the multiferroic nature of PFN at RT.

Origin of room temperature weak-ferromagnetism in antiferromagnetic Pb(Fe2/3W1/3)O-3 ceramic

We report the origin of room temperature weak ferromagnetic behavior of polycrystalline Pb(Fe2/3W1/3)O-3 (PFW) powder. The structure and magnetic properties of the ceramic powder prepared by a Columbite method were characterized by X-ray and neutron diffraction, Mossbauer spectroscopy and magnetization measurements. Rietveld analysis of diffraction data confirm the formation of single phase PFW, without traces of any parasitic pyrochlore phase. PFW was found to crystallize in the cubic structure at room temperature. The Rietveld refinement of neutron diffraction data measured at room temperature confirmed the G-type antiferromagnetic structure of PFW in our sample. However, along with the antiferromagnetic (AFM) ordering of the Fe spins, we have observed the existence of weak ferromagnetism at room temperature through: (i) a clear opening of hysteresis (M-H) loop, (ii) bifurcation of the field cooled and zero-field cooled susceptibility; supported by Mossbauer spectroscopy results. The P-E loop measurements showed a non-linear slim hysteresis loop at room temperature due to the electronic conduction through the local inhomogeneities in the PFW crystallites and the inter-particle regions. By corroborating all the magnetic measurements, especially the spin glass nature of the sample, with the conduction behavior of the sample, we report here that the observed ferromagnetism originates at these local inhomogeneous regions in the sample, where the Fe-spins are not perfectly aligned antiferromagnetically due to the compositional disordering. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

MnFe2O4-Fe3O4 core-shell nanoparticles as a potential contrast agent for magnetic resonance imaging

In recent years, magnetic core-shell nanoparticles have received widespread attention due to their unique properties that can be used for various applications. We introduce here a magnetic core-shell nanoparticle system for potential application as a contrast agent in magnetic resonance imaging (MRI). MnFe2O4-Fe3O4 core-shell nanoparticles were synthesized by the wet-chemical synthesis method. Detailed structural and compositional charaterization confirmed the formation of a core-shell microstructure for the nanoparticles. Magnetic charaterization revealed the superparamagnetic nature of the as-synthesized core-shell nanoparticles. Average size and saturation magnetization values obtained for the as-synthesized core-shell nanoparticle were 12.5 nm and 69.34 emu g(-1) respectively. The transverse relaxivity value of the water protons obtained in the presence of the core-shell nanoparticles was 184.1 mM(-1) s(-1). To investigate the effect of the core-shell geometry towards enhancing the relaxivity value, transverse relaxivity values were also obtained in the presence of separately synthesized single phase Fe3O4 and MnFe2O4 nanoparticles. Average size and saturation magnetization values for the as-synthesized Fe3O4 nanoparticles were 12 nm and 65.8 emu g(-1) respectively. Average size and saturation magnetization values for the MnFe2O4 nanoparticles were 9 nm and 61.5 emu g(-1) respectively. The transverse relaxivity value obtained in the presence of single phase Fe3O4 and MnFe2O4 nanoparticles was 96.6 and 83.2 mM(-1) s(-1) respectively. All the nanoparticles (core-shell and single phase) were coated with chitosan by a surfactant exchange reaction before determining the relaxivity values. For similar nanoparticle sizes and saturation magnetization values, the highest value of the transverse relaxivity in the case of core-shell nanoparticles clearly illustrated that the difference in the magnetic nature of the core and shell phases in the core-shell nanoparticles creates greater magnetic inhomogeneity in the surrounding medium yielding a high value for proton relaxivity. The MnFe2O4-Fe3O4 core-shell nanoparticles exhibited extremely low toxicity towards the MCF-7 cell line. Taken together, this opens up new avenues for the use of core-shell nanoparticles in MRI.

Neutron diffraction, Mossbauer effect and Electron Paramagnetic Resonance studies on multiferroic Pb(Fe2/3W1/3)O-3

Multiferroic Pb(Fe2/3W1/3)O-3 ceramics were synthesized via a modified two-stage Columbite method. Single phase formation was confirmed from the analysis of x-ray and neutron diffraction patterns recorded at room temperature. Structural analysis of the diffraction data reveals cubic phase (space group Pm-3m) for the title compound. Magnetic structure of the title compound at room temperature exhibits G-type antiferromagnetic structure. The Mossbauer spectroscopy and Electron Paramagnetic Resonance (EPR) studies were carried out at 300 K. The isomer shift and quadrupole splitting of the Mossbauer spectra confirms the trivalent state of iron (Fe3+). The Mossbauer spectra also suggest that the iron and tungsten are randomly distributed at the octahedral, B site. EPR spectra show a single broad line associated with Fe3+ ions. Both spectra clearly exhibit weak ferromagnetic behaviour of Pb(Fe2/3W1/3)O-3 ceramic at 300 K. Considering neutron diffraction, Mossbauer and EPR results together, it may be stated here that Pb(Fe2/3W1/3)O-3 exhibits antiferromagnetic behavior along with weak ferromagnetism at room temperature.

Exploring the Colour of 3d Transition-Metal Ions in Trigonal Bipyramidal Coordination: Identification of Purple-Blue (CoO5) and Beige-Red (NiO5) Chromophores in LiMgBO3 Host

In an attempt to develop new coloured inorganic oxides, we have investigated the substitution of 3d transition-metal ions in LiMgBO3 host where Mg-II has a trigonal bipyramidal (TBP) oxygen coordination]. We find that single-phase materials are formed for (LiMg1-xCoxBO3)-B-II (0 < x 1.0), (LiMg1-xNixBO3)-B-II (0 < x 0.1), (LiMg1-xCuxBO3)-B-II (0 < x 0.1) and also (Li1-xMg1-xFexBO3)-B-III (0 < x 0.1) of which the Co-II and Ni-II derivatives are strongly coloured, purple-blue and beige-red, respectively, thus identifying TBP CoO5 and NiO5 as new chromophores for these colours.

A Simple Hysteretic Energy Harvesting Method for Nonneutral AC Switches in Load Automation

This paper presents a simple hysteretic method to obtain the energy required to operate the gate-drive, sensors, and other circuits within nonneutral ac switches intended for use in load automated buildings. The proposed method features a switch-mode low part-count self-powered MOSFET ac switch that achieves efficiency and load current THD figures comparable to those of an externally gate-driven switch built using similar MOSFETS. The fundamental operation of the method is explained in detail, followed by the modifications required for practical implementation. Certain design rules that allow the method to accommodate a wide range of single-phase loads from 10 VA to 1 kVA are discussed, along with an efficiency enhancement feature based on inherent MOSFET characteristics. The limitations and side effects of the method are also mentioned according to their levels of severity. Finally, experimental results obtained using a prototype sensor switch are presented, along with a performance comparison of the prototype with an externally gate-driven MOSFET switch.

Development of an automated ultrasonic spray pyrolysis system and the growth of Cu2ZnSnS4 thin films

An automated ultrasonic spray pyrolysis system is fabricated for the growth of thin films. The system is equipped with x-y movement and enables film deposition in different patterns and spray rates. Cu-2(Zn,Sn)S-4 (CZTS) films are deposited using this setup. The substrate temperature (T-s) is varied from 240 to 490 degrees C. Kesterite CZTS phase is observed in all the films together with binary phases. The films prepared at T-s <340 degrees C showed SnxSy phase and those at T-s >340 degrees C showed Cu2S phase. Sulfur incorporation is maximum (40%) at 440 degrees C and the films showed better morphology. The Cu and S concentrations are varied to remove binary phases. Depth wise elemental analysis confirmed the existence of single phase CZTS. p-Type CZTS films of resistivity in the range of 10(2)-10(3) Omega cm are obtained. (C) 2015 Elsevier B.V. All rights reserved.

Phase transitions and rare-earth magnetism in hexagonal and orthorhombic $DyMnO_{3}$ single crystals

The floating-zone method with different growth ambiences has been used to selectively obtain hexagonal or orthorhombic DyMnO3 single crystals. The crystals were characterized by x-ray powder diffraction of ground specimens and a structure refinement as well as electron diffraction. We report magnetic susceptibility, magnetization and specific heat studies of this multiferroic compound in both the hexagonal and the orthorhombic structure. The hexagonal DyMnO3 shows magnetic ordering of Mn3+ (S = 2) spins on a triangular Mn lattice at T-N(Mn) = 57 K characterized by a cusp in the specific heat. This transition is not apparent in the magnetic susceptibility due to the frustration on the Mn triangular lattice and the dominating paramagnetic susceptibility of the Dy3+ (S = 9/2) spins. At T-N(Dy) = 3 K, a partial antiferromagnetic order of Dy moments has been observed. In comparison, the magnetic data for orthorhombic DyMnO3 display three transitions. The data broadly agree with results from earlier neutron diffraction experiments, which allows for the following assignment: a transition from an incommensurate antiferromagnetic ordering of Mn3+ spins at T-N(Mn) = 39 K, a lock-in transition at Tlock-in = 16 K and a second antiferromagnetic transition at T-N(Dy) = 5 K due to the ordering of Dy moments. Both the hexagonal and the orthorhombic crystals show magnetic anisotropy and complex magnetic properties due to 4f-4f and 4f-3d couplings.

A New PWM Control Method for Three-Phase Autosequentially Commutated Current Source Inverters

A new current pulsewidth modulation (PWM) method is presented which uses the principle of creating zero three-phase currents at selected instants of time, through which the load current harmonic content can be controlled along with the magnitude of its fundamental content. This gives rise to reduction of motor torque ripples through the selection of suitable PWM patterns and a fast current control in the inverter by varying the pulsewidths of the PWM pattern. Under this new PWM mode of operation, the autosequentially commutated inverter (ASCI) circuit can be modified easily so that a higher number of pulses can be accomodated within a half-cycle, compared to the normal ASCI circuit. The experimental oscillograms verify the effectiveness of the new PWM method.

Localized reversible nanoscale phase separation in Pr0.63Ca0.37MnO3 single crystal using a scanning tunneling microscope tip

We report the destabilization of the charge ordered insulating (COI) state in a localized region of Pr0.63Ca0.37MnO3 single crystal by current injection using a scanning tunneling microscope tip. This leads to controlled phase separation and formation of localized metallic nanoislands in the COI matrix which have been detected by local tunneling conductance mapping. The metallic regions thus created persist even after reducing the injected current to lower values. The original conductance state can be restored by injecting a current of similar magnitude but of opposite polarity. We thus achieve reversible nanoscale phase separation that gives rise to the possibility to "write, read, and erase" nanosized conducting regions in an insulating matrix with high spatial resolution. (c) 2007 American Institute of Physics.