Thermal rearrangement of diethylamino5-(m methoxyphenoxy)-pent-2-yne (3) gives 1-(m-methexyphenoxy)-pent-3,4-diene (14) in about 8% yield. Hydration of the latter yields 1-(m-methoxyphenoxy)-pentan-4-one (6), which has been synthesised by an unambiguous route. A mechanism of formation of the allene (14) from the amine (3) has been suggested.

Chemical potentials of oxygen for fayalite-quartz-lron and fayalite-quartz-magnetite equilibria

The oxygen potentials corresponding to fayalite-quartz-iron (FQI) and fayalite-quartz-magnetite (FQM) equilibria have been determined using solid-state galvanic cells: Pt,Fe + Fe2SiO4 + SiO2/(Y2O3)ZrO2/Fe + \r"FeO,\l"Pt and Pt, Fe3O4 + Fe2SiO4 + SiO2/(Y2O3)ZrO2/Ni + NiO, Pt in the temperature ranges 900 to 1400 K and 1080 to 1340 K, respectively. The cells are written such that the right-hand electrodes are positive. Silica used in this study had the quartz structure. The emf of both cells was found to be reversible and to vary linearly with temperature. From the emf, Gibbs energy changes were deduced for the reactions: 0.106Fe (s) + 2Fe0.947O (r.s.) + SiO2 (qz) → Fe2SiO4 (ol) δG‡= -39,140+ 15.59T(± 150) J mol-1 and 3Fe2SiO4 (ol) + O2 (g) → 2Fe3O4 (sp) + 3SiO2 (qz) δG‡ = -471,750 + 160.06 T±} 1100) J mol-1 The “third-law≓ analysis of fayalite-quartz-wustite and fayalite-quartz-magnetite equilibria gives value for δH‡298 as -35.22 (±0.1) and -528.10 (±0.1) kJ mol-1, respectively, independent of temperature. The Gibbs energy of formation of the spinel form of Fe2SiO4 is derived by com-bining the present results on FQI equilibrium with the high-pressure data on olivine to spinel transformation of Fe2SiO4.

Thermodynamics of GdMnO3 and GdMn2O5 phases determined by the EMF method

Using solid oxide galvanic cells of the type: MnO + Gd2O3 + GdMnO3/O-2/Ni + NiO and Mn3O4 + GdMnO3 + GdMn2O5/O-2/air the equilibrium oxygen pressure for the following reactions :MnO + 1/2Gd(2)O(3) + 1/4O(2) = GdMnO3 1/3Mn(3)O(4) + GdMnO3 + 1/3O(2) = GdMn2O5 was determined in the temperature range from 1073 to 1450 K. From the determined equilibrium oxygen partial pressure the corresponding G i b b s free energy change for these reactions was derived: Delta G(f,GdMnO3)(0) (+/- 425J) 132721(+/ - 2240) +51.91(+/ - 0.81)T Delta G(f,GdMn2O5)(0)(+/- 670J) 121858(+/ - 6176) + 79.52(+/ - 4.83)T From these data, standard G i b b s energies, enthalpies and entropies of formation of GdMnO3 and GdMn2O5 from component oxides and from the elements are derived. Thermodynamic data tables for the two ternary phases are compiled from 298.15 to 1400 K.

Refinement of the thermodynamic properties of ruthenium dioxide and osmium dioxide

The standard Gibbs energies of formation of RuO2 and OsO2 at high temperature have been determined with high precision, using a novel apparatus that incorporates a buffer electrode between the reference and working electrodes, The buffer electrode absorbs the electrochemical flux of oxygen through the solid electrolyte from the electrode with higher oxygen chemical potential to the electrode with lower oxygen potential, The buffer electrode prevents polarization of the measuring electrode and ensures accurate data, The standard Gibbs energies of formation (Delta(f)G degrees) of RuO2, in the temperature range of 900-1500 K, and OsO2, in the range of 900-1200 K, can be represented by the equations Delta(f)G degrees(RuO2)(J/mol) = -324 720 + 354.21T - 23.490T In T Delta(f)G degrees(OsO2)(J/mol) = -304 740 + 318.80T - 18.444T In T where the temperature T is given in Kelvin and the deviation of the measurement is +/- 80 J/mol, The high-temperature heat ;capacities of RuO2 and OsO2 are measured using differential scanning calorimetry. The information for both the low- and high-temperature heat rapacity of RuO2 is coupled with the Delta(f)G degrees data obtained in this study to evaluate the standard enthalpy of formation of RuO2 at 298.15 K (Delta(f)H degrees(298.15K)). The low-temperature heat capacity of OsO2 has not been measured: therefore, the standard enthalpy and entropy of formation of OsO2 at 298.15 K (Delta(f)H degrees(298.15K) and S degrees(298.15K), respectively) are derived simultaneously through an optimization procedure from the high-temperature heat capacity and the Gibbs energy of formation. Both Delta fH degrees(298.15K) and S degrees(298.15K) are treated as variables in the optimization routine, For RuO2, the standard enthalpy of formation at 298.15 K is Delta fH degrees(298.15K) (RuO2) -313.52 +/- 0.08 kJ/mol, and that for OsO2 is Delta(f)H degrees(298.15K) (OSO2) = -295.96 +/- 0.08 kJ/mol. The standard entropy of OsO2 at 298.15 K that has been obtained from the optimization is given as S degrees(298.15K) (OsO2) = 49.8 +/- 0.2 J (mol K)(-1).

Phase relations and thermodynamic properties of compounds in the pseudobinary system BaO-Y2O3

The coexisting phases in the pseudobinary system BaO-Y2O3 have been identified by equilibrating samples containing different amounts of component oxides at 1173, 1273 and 1373 K. Only two ternary oxides, BaY2O4 and Ba3Y4O9, have been found to be stable in the temperature range of investigation. Solid state galvanic cells: Pt, O2+BaO+BaF2double vertical barBaF2+2mol%Al2O3double vertical barBaF2+BaY2O4+Y2O3+O2, Pt and Pt, O2+BaO+BaF2double vertical barBaF2+2mol% Al2O3double vertical barBaF2+BaY2O4+Ba3Y4O9+O2, Pt have been employed for determining the Gibbs' energies of formation of BaY2O4 and Ba3Y4O9 from the component oxides in the range 850 to 1250 K. A composite solid electrolyte incorporating Al2O3-dispersed BaF2 was used in the cells. To prevent interaction between the Al2O3 powder and electrode materials, the solid electrolyte was coated with pure BaF2. The Gibbs' energies of formation of BaY2O4 and Ba3Y4O9 from component oxides are given by: Δf0 (BaY2O4, s)=−128,310+5.211T (±580) J mol−1, (850less-than-or-equals, slantTless-than-or-equals, slant1250 K) and ΔGfo(Ba3Y4O9, s)= −317,490 −24.704T (±1100) J mol−1, (850less-than-or-equals, slantTless-than-or-equals, slant1250 K).

Experimental and Computational Characterization of Alloy--Spinel--Corundum Equilibrium in the System Fe--Co--Al--O at 1873K

The three-phase equilibrium between alloy, spinel solid solution and alpha -Al sub 2 O sub 3 in the Fe--Co--Al--O system at 1873k was fully characterized as a function of alloy composition using both experimental and computational methods. The equilibrium oxygen content of the liquid alloy was measured by suction sampling and inert gas fusion analysis. The O potential corresponding to the three-phase equilibrium was determined by emf measurements on a solid state galvanic cell incorporating (Y sub 2 O sub 3 )ThO sub 2 as the solid electrolyte and Cr + Cr sub 2 O sub 3 as the reference electrode. The equilibrium composition of the spinel phase formed at the interface between the alloy and alumina crucible was measured by electron probe microanalysis (EPMA). The experimental results were compared with the values computed using a thermodynamic model. The model used values for standard Gibbs energies of formation of pure end-member spinels and Gibbs energies of solution of gaseous O in liquid Fe and cobalt available in the literature. The activity--composition relationship in the spinel solid solution was computed using a cation distribution model. The variation of the activity coefficient of O with alloy composition in the Fe--Co--O system was estimated using both the quasichemical model of Jacob and Alcock and Wagner's model along with the correlations of Chiang and Chang and Kuo and Chang. The computed results of spinel composition and O potential are in excellent agreement with the experimental data. Graphs. 29 ref.--AA

Characterization of Alloy-Spinel-Corundum Equilibrium in the System Fe-Ni-Al-O

The three phase equilibrium between alloy, spinel solid solution and α-alumina in the Fe-Ni-Al-O system has been fully characterized at 1823K as a function of alloy composition using both experimental and computational methods. The oxygen potential was measured using a solid state cell incorporating yttria-doped thoria as the electrolyte and Cr+ Cr2O3 as the reference electrode. Oxygen concentration of the alloy was determined by an inert gas fusion technique. The composition of the spinel solid solution, formed at the interface between the alloy and an alumina crucible, was determined by EPMA. The variation of the oxygen concentration and potential and composition of the spinel solid solution with mole fraction of nickel in the alloy have been computed using activities in binary Fe-Ni system, free energies of formation of end member spinels FeO•(1+x)Al2O3 and NiO•(1+x)Al2O3 and free energies of solution of oxygen in liquid iron and nickel, available in the literature. Activities in the spinel solid solution were computed using a cation distribution model. The variation of the activity coefficient of oxygen with alloy composition in Fe-Ni-O system was calculated using both the quasichemical model of Jacob and Alcock and the Wagner's model, with the correlation of Chiang and Chang. The computed results for the oxygen potential and the composition of the spinel solid solution are in good agreement with the measurements. The measured oxygen concentration lies between the values computed using models of Wagner and Jacob and Alcock. The results of the study indicate that the deoxidation hyper-surface in multicomponent systems can be computed with useful accuracy using data for end member systems and thermodynamic models.

Stability of CU(2)Ln(2)O(5) compounds - Comparison, assessment and systematics

Phase diagram studies show that at ambient pressure only one ternary oxide, Cu(2)Ln(2)O(5), is stable in the ternary systems Cu-Ln-O (Ln = Tb, Dy, Ho, Er, Tm, Yb, Lu) at high temperatures. The crystal structure of Cu(2)Ln(2)O(5) can be described as a zig-zag arrangement of one-dimensional Cu2O5 chains parallel to-the a-axis with Ln atoms occupying distorted octahedral sites between these chains. Four sets of emf measurements on Gibbs energy of formation of Cu(2)Ln(2)O(5) (Ln = Tb, Dy, Ho, Er, Tm, Yb, Lu; Y) from component binary oxides and one set of high-temperature solution calorimetric data on enthalpy of formation have been reported in the literature. Except for Cu2Y2O5, the measured values for the Gibbs energies of formation of all other Cu(2)Ln(2)O(5) compounds fall in a narrow band (+/-1 kJ mol(-1)) and indicate a regular increase in stability with decreasing ionic radius of the lanthanide ion. The values for the second law enthalpy of formation, derived from the temperature dependence of emf obtained in different studies, show larger differences, as high as 25 kJ mol(-1) for Cu2Tm2O5. Though associated with an uncertainty of +/-4 kJ mol(-1), the calorimetric measurements help to identify the best set of emf data. The trends in thermodynamic data correlate well with the global instability index (GII) based on the overall deviation from the valence sum rule. Low values for the index calculated from crystallographic information indicate higher stability. Higher values are indicative of the larger stress in the structure.

Synergistic use of thermogravimetric and electrochemical techniques for thermodynamic study of TiOx (1.67 <= x <= 2.0) at 1573 K

A thermodynamic study of the Ti-O system at 1573 K has been conducted using a combination of thermogravimetric and emf techniques. The results indicate that the variation of oxygen potential with the nonstoichiometric parameter delta in stability domain of TiO2-delta with rutile structure can be represented by the relation, Delta mu o(2) = -6RT In delta - 711970(+/-1600) J/mol. The corresponding relation between non-stoichiometric parameter delta and partial pressure of oxygen across the whole stability range of TiO2-delta at 1573 K is delta proportional to P-O2(-1/6). It is therefore evident that the oxygen deficient behavior of nonstoichiometric TiO2-delta is dominated by the presence of doubly charged oxygen vacancies and free electrons. The high-precision measurements enabled the resolution of oxygen potential steps corresponding to the different Magneli phases (Ti-n O2n-1) up to n = 15. Beyond this value of n, the oxygen potential steps were too small to be resolved. Based on composition of the Magneli phase in equilibrium with TiO2-delta, the maximum value of n is estimated to be 28. The chemical potential of titanium was derived as a function of composition using the Gibbs-Duhem relation. Gibbs energies of formation of the Magneli phases were derived from the chemical potentials of oxygen and titanium. The values of -2441.8(+/-5.8) kJ/mol for Ti4O7 and -1775.4(+/-4.3) kJ/mol for Ti3O5 Obtained in this study refine values of -2436.2(+/-26.1) kJ/mol and-1771.3(+/-6.9) kJ/mol, respectively, given in the JANAF thermochemical tables.