Microstructure and Properties of the Spray-Formed and Extruded 7075 Al Alloy

In the present investigation, a very good combination of strength and ductility, 630MPa 0.2% proof stress and 14.8% elongation to fracture in tensile test, has been obtained for the 7075 Al alloy after optimizing the processing parameters for spray forming, hot extruding the spray deposit, and peak aging the samples taken from the extruded rod. The spray deposits contained some porosity but it was almost eliminated on hot extrusion. Electron probe microanalysis revealed that even though spray forming was carried out in an open atmosphere, it did not affect the oxygen content and its distribution in the material on spray forming, because the atomizing argon gas provided a protective cover to molten droplets and prevented their oxidation. The chemical composition of the spray-formed material was found to be almost the same as the raw material, and the major alloying elements were found to be uniformly distributed in the extruded rod.

Shell-model calculation of defect energies in alkali halides employing crystal-independent interionic potential parameters

Shell model calculation of defect energies in alkali halides have been carried out using the ion-dependent, crystal-independent potential parameters of Sangster and Atwood (1978). Results indicate that appreciable differences exist between barrier heights for migration of cations and anions. While barrier heights for cations are generally lower than for anions in alkali halides of NaCl structure, the opposite is true in alkali halides of CsCl structure.

Theoretical Treatment of Interaction Parameters in Multicomponent Metallic Solutions

A new theoretical equation for interaction parameter in multicomponent metallic solutions is developed using the pseudopotential formalism coupled with the free energy of the hard sphere system. The approximate expression for the pseudopotential term is given in terms of the heat of solution at infinite dilution, to allow easy evaluation of the interaction parameter in various multicomponent systems. This theory has been applied to 23 non-ferrous alloys based on Pb, Sn, Bi and indium. Comparison with the results of previous theoretical calculations using only the hard sphere model suggests that the inclusion of the pseudopotential term yields a quantitatively more correct prediction of interaction parameters in multicomponent metallic solutions. Numerical calculations were also made for 320 Fe-base solutions relevant to steelmaking and the agreement between calculation and experimental data appears reasonable, with 90% reliability in predicting the correct sign.

Regenerating Codes for Distributed Storage Networks

In a storage system where individual storage nodes are prone to failure, the redundant storage of data in a distributed manner across multiple nodes is a must to ensure reliability. Reed-Solomon codes possess the reconstruction property under which the stored data can be recovered by connecting to any k of the n nodes in the network across which data is dispersed. This property can be shown to lead to vastly improved network reliability over simple replication schemes. Also of interest in such storage systems is the minimization of the repair bandwidth, i.e., the amount of data needed to be downloaded from the network in order to repair a single failed node. Reed-Solomon codes perform poorly here as they require the entire data to be downloaded. Regenerating codes are a new class of codes which minimize the repair bandwidth while retaining the reconstruction property. This paper provides an overview of regenerating codes including a discussion on the explicit construction of optimum codes.

Equivalent circuit parameters of the film-covered magnesium/electrolyte interface in Mg/MnO2 dry cells from transient and ac impedance measurements

The electrochemical properties of the film-covered anode/solution interface in the magnesium/ manganese dioxide dry cell have been evaluated. The most plausible electrical equivalent circuit description of the Mg/solution interface with the passive film intact, has been identified. These results are based on the analysis of ac impedance and voltage transient measurements made on the dry cell under conditions which cause no damage to the protective passive film on the anode. The study demonstrates the complementary character of impedance and transient measurements when widely different frequency ranges are sampled in each type of investigation. The values and temperature dependence of the anode-film resistance, film capacitance, double-layer capacitance and charge-transfer resistance of the film-covered magnesium/solution interface have been determined. The magnitude of these values and its implications in understanding the important performance aspects of the magnesium/manganese dioxide dry cell are discussed. The study may be extended, in principle, to Li, Al and Ca batteries.

Equivalent circuit parameters of the film-covered magnesium/electrolyte interface in Mg/MnO2 dry cells from transient and ac impedance measurements

The electrochemical properties of the film-covered anode/solution interface in the magnesium/ manganese dioxide dry cell have been evaluated. The most plausible electrical equivalent circuit description of the Mg/solution interface with the passive film intact, has been identified. These results are based on the analysis of ac impedance and voltage transient measurements made on the dry cell under conditions which cause no damage to the protective passive film on the anode. The study demonstrates the complementary character of impedance and transient measurements when widely different frequency ranges are sampled in each type of investigation. The values and temperature dependence of the anode-film resistance, film capacitance, double-layer capacitance and charge-transfer resistance of the film-covered magnesium/solution interface have been determined. The magnitude of these values and its implications in understanding the important performance aspects of the magnesium/manganese dioxide dry cell are discussed. The study may be extended, in principle, to Li, Al and Ca batteries.

Ordered Ports – a Language Concept for High-level Distributed Programming

A new language concept for high-level distributed programming is proposed. Programs are organised as a collection of concurrently executing processes. Some of these processes, referred to as liaison processes, have a monitor-like structure and contain ports which may be invoked by other processes for the purposes of synchronisation and communication. Synchronisation is achieved by conditional activation of ports and also through port control constructs which may directly specify the execution ordering of ports. These constructs implement a path-expression-like mechanism for synchronisation and are also equipped with options to provide conditional, non-deterministic and priority ordering of ports. The usefulness and expressive power of the proposed concepts are illustrated through solutions of several representative programming problems. Some implementation issues are also considered.

Comparative measurements of HV impulses to evaluate different sets of response parameters

Results are reported of comparative measurements made in 14 HV (high-voltage) laboratories in ten different countries. The theory of the proposed methods of characterizing the dynamic behavior is given, and the parameters to be used are discussed. Comparative measurements made using 95 systems based on 53 dividers are analyzed. This analysis shows that many of the system now in use, even though they fulfil the basic response requirements of the standards, do not meet the accuracy requirements. Because no transfer measurements were made between laboratories, there is no way to detect similar errors in both the system under test and the reference system. Hence, the situation may be worse than reported. This has led to the recommendation that comparative measurements should be the main route for quantifying industrial impulse measuring systems

Impedance parameters and the state-of-charge. III. Zinc-manganese dioxide and magnesium-manganese dioxide dry batteries

The problem of non-destructive determination of the state-of-charge of zinc- and magnesium-manganese dioxide dry batteries is examined experimentally from the viewpoint of internal impedance and open-circuit voltage at equilibrium. It is shown that the impedance is mainly charge-transfer controlled at relatively high states-of-charge and progressively changes over to diffusion control as the state-of-charge decreases in the case of zinc-manganese dioxide dry batteries. On the other hand, the impedance is mainly diffusion controlled for undischarged batteries but becomes charge-transfer controlled as soon as there is some discharge in the case of magnesium-manganese dioxide batteries. It is concluded that the determination of state-of-charge is not possible for both types of batteries by the measurement of impedance parameters due to film-induced fluctuations of these parameters. The measurement of open-circuit voltage at equilibrium can be used as a state-of-charge indicator for Zn-MnO2 batteries but not for Mg-MnO2 batteries.

Impedance parameters and the state-of-charge. II. Lead-acid battery

The determination of the state-of-charge of the lead-acid battery has been examined from the viewpoint of internal impedance. It is shown that the impedance is controlled by charge transfer and to a smaller extent by diffusion processes in the frequency range 15–100 Hz. The equivalent series/parallel capacitance as well as the a.c. phase-shift show a parabolic dependence upon the state-of-charge, with a maximum or minimum at 50% charge. These results are explained on the basis of a uniform transmission-line analog equivalent circuit for the battery electrodes.

On the High Frequency Dielectric Behavior of Castor Oil

The low frequency dielectric behavior of castor oil (a vegetable oil) has been analyzed quite exhaustively in the context of its application as impregnant in capacitors. For the sake of completeness and in order to understand the relaxation phenomena in this liquid dielectric, this high frequency dielectric study was undertaken. In order to compare its properties with a liquid dielectric used in similar application and whose high frequency behavior has been quite well analyzed, Arochlor 1476 was studied. It is observed that both liquids have distributed relaxation times. The distribution parameters together with the two distinct relaxation times have been calculated by measuring the average relaxation time. It has been found that the distinct relaxation times thus calculated represent the dielectric behavior quite satisfactorily. The average dipole moments, dipole radii and thermal activation energies for dipole relaxation have also been evaluated.