Size and temperature dependent stability and phase transformation in single-crystal zirconium nanowire

A novel size dependent FCC (face-centered-cubic) -> HCP (hexagonally-closed-pack) phase transformation and stability of an initial FCC zirconium nanowire are studied. FCC zirconium nanowires with cross-sectional dimensions < 20 are found unstable in nature, and they undergo a FCC -> HCP phase transformation, which is driven by tensile surface stress induced high internal compressive stresses. FCC nanowire with cross-sectional dimensions > 20 , in which surface stresses are not enough to drive the phase transformation, show meta-stability. In such a case, an external kinetic energy in the form of thermal heating is required to overcome the energy barrier and achieve FCC -> HCP phase transformation. The FCC-HCP transition pathway is also studied using Nudged Elastic Band (NEB) method, to further confirm the size dependent stability/metastability of Zr nanowires. We also show size dependent critical temperature, which is required for complete phase transformation of a metastable-FCC nanowire.

Gibbs energy formation of lead titanate

The Gibbs energy of formation of titania-saturated lead titanate has been determined by e.m.f. measurements on the solid state cell;Pt,Ir,Pb + Pb1−xTiO3−x + TiO2(rutile)/CaO-ZrO2/Ni + NiO,Pt in the temperature range 1075–1350 K. The results obtained are significantly different from those reported in the literature based upon vapour pressure measurements, employing Knudsen effusion and transportation techniques, and assuming that the vapor phase consisted entirely of monomeric PbO molecules. A reanalysis of the data obtained in the earlier vapor pressure studies using mass spectrometric measurements on polymeric PbO species in the gas phase, gives Gibbs energies of formation of lead titanate which are in better agreement with those obtained in this study. Earlier electrochemical measurements by Mehrotra et al. and more recent electrochemical measurements by Schmahl et al. both employing CaO-ZrO2 solid electrolytes are in good agreement with the present study. The electro-chemical measurements by Schmahl et al. using PbF 2 solid electrolyte give a slightly more positive Gibbs energy of formation. There was no evidence supporting the formation of compounds other than Pb1−xTiO3−x from yellow PbO and rutile form of TiO2 in the temperature range covered in this study.Résumé L'enthalpie libre de formation du titanate de plomb saturé en oxyde de titane a été déterminée par des mesures de FEM de la pile: Pt,Ir,Pb + Pb1−xTiO3−x + TiO2(rutile)/CaO-ZrO2/Ni + NiO,Pt dans le domaine de températures 1075–1350 K. Les résultats obtenus, different appréciablement de ceux publiés, déterminés par mesures de tensions de vapeur (techniques de transport et d'effusion de Knudsen) en supposant que la phase gazeuse etait uniquement constituée de molécules monomériques de PbO. Une réanalyse des résultats de la littérature, à partir de mesures par spectrométrie de masse sur les polymères de PbO gazeux, donne des enthalpies libres de formation du titanate de plomb se rapprochant de celles obtenues dans cette étude. Les mesures de Mehrotra et al. et plus récemment de Schmahl et al. utilisant toutes deux l'électrolyte CaO-ZrO2 concordent bien avec celles de la présente étude. Les mesures de Schmahl et al., à l'aide de l' électrolyte solide PbF2, donnent une enthalpie de formation légèrement plus positive. Pour la gammede températures étudiée, rien ne permet de supposer que des composés autres que Pb1−x TiO3−x puissent se former à partir du PbO Gaune) et du rutile (TiO2).

Time delay to firing of a triggered vacuum gap with barium titanate in trigger gap

The time delay to the firing of a triggered vacuum gap (t.v.g.) containing barium titanate in the trigger gap is investigated as a function of the main gap voltage, main gap length, trigger pulse duration, trigger current and trigger voltage. The time delay decreases steadily with increasing trigger current and trigger voltage until it reaches saturation. The effect of varying the main gap length and voltage on the time delay is not strong. Before `conditioning�¿ the t.v.g. two groups of time delays, long (>100�¿s) and short (<10�¿s), are simultaneously observed when a large number of trials are conducted. After conditioning, only the group of short time delays are present. This is attributed to the marked reduction of the resistance of the trigger gap across the surface of the solid dielectric resulting directly from the conditioning effect.

Designing copper-zirconium based nanowires for improving yield strength and plasticity by configuring surface atoms

Epitaxial-Bain-Path and Uniaxial-Bain-Path studies reveal that a B2-CuZr nanowire with Zr atoms on the surface is energetically more stable compared to a B2-CuZr nanowire with Cu atoms on the surface. Nanowires of cross-sectional dimensions in the range of similar to 20-50 are considered. Such stability is also correlated with the initial state of stress in the nanowires. It is also demonstrated here that a more stable structure, i.e., B2-CuZr nanowire with Zr atoms at surface shows improved yield strength compared to B2-CuZr nanowire with Cu atoms at surface site, over range of temperature under both the tensile and the compressive loadings. Nearly 18% increase in the average yield strength under tensile loading and nearly 26% increase in the averaged yield strength under compressive loading are observed for nanowires with various cross-sectional dimensions and temperatures. It is also observed that the B2-CuZr nanowire with Cu atom at the surface site shows a decrease in failure/plastic strain with an increase in temperature. On the other hand, B2-CuZr nanowires with Zr at the surface site shows an improvement in failure/plastic strain, specially at higher temperature as compared to the B2-CuZr nanowires which are having Cu atoms at the surface site. Finally, a possible design methodology for an energetically stable nano-structure with improved thermo-mechanical properties via manipulating the surface atom configuration is proposed.

Evaluation of physico-mechanical properties and in vitro biocompatibility of compression molded HDPE based biocomposites with HA/Al2O3 ceramic fillers and titanate coupling agents

The present article demonstrates how the stiffness, hardness as well as the cellular response of bioinert high-density polyethylene (HDPE) can be significantly improved with combined addition of both bioinert and bioactive ceramic fillers. For this purpose, different amounts of hydroxyapatite and alumina, limited to a total of 40 wt %, have been incorporated in HDPE matrix. An important step in composite fabrication was to select appropriate solvent and optimal addition of coupling agent (CA). In case of chemically coupled composites, 2% Titanium IV, 2-propanolato, tris iso-octadecanoato-O was used as a CA. All the hybrid composites, except monolithic HDPE, were fabricated under optimized compression molding condition (140 degrees C, 0.75 h, 10 MPa pressure). The compression molded composites were characterized, using X-ray diffraction, Fourier transformed infrared spectroscopy, and scanning electron microscopy. Importantly, in vitro cell culture and cell viability study (MTT) using L929 fibroblast and SaOS2 osteoblast-like cells confirmed good cytocompatibility properties of the developed hybrid composites. (C) 2011 Wiley Periodicals, Inc. J Appl Polym Sci, 2012

Residual strength of hot pressed zirconium diboride (ZrB2) after exposure to high temperatures

ZrB2 with different amounts of B4C additive (0-5 wt.%) has been hot pressed at 2000 degrees C and 25 MPa for 1 h. By addition of B4C, density as well as micro-hardness increased. For lower B4C content (0.5 and 1 wt.%), hot pressed ZrB2 shows considerable improvement in flexural strength after exposure in air at 1000 C for 5 h, while higher B4C content (3 and 5 wt.%) leads to marginal or no improvement. For any content of B4C, flexural strength after exposure in air at 1500 degrees C for 5 h is lower than as-hot pressed ZrB2. (C) 2011 Elsevier B.V. All rights reserved.

Better early osteogenesis of electroconductive hydroxyapatite-calcium titanate composites in a rabbit animal model

In view of the fact that bone healing can be enhanced due to external electric field application, it is important to assess the influence of the implant conductivity on the bone regeneration in vivo. To address this issue, this study reports the in vivo biocompatibility property of multistage spark plasma sintered hydroxyapatite (HA)-80 wt % calcium titanate (CaTiO3) composites and monolithic HA, which have widely different conductivity property (14 orders of magnitude difference). The ability of bone regeneration was assessed by implantation in cylindrical femoral bone defects of rabbit animal model for varying time period of 1, 4, and 12 weeks. The overall assessment of the histology results suggests that the progressive healing of bone defects around HA-80 wt % CaTiO3 is associated with a better efficacy with respect to (w.r.t) early stage neobone formation, which is histomorphometrically around 140% higher than monolithic HA. Overall, this study demonstrates that the in vivo biocompatibility property of HA-80 wt % CaTiO3 with respect to local effects after 12 weeks of implantation is not compromised both qualitatively and quantitatively, and a comparison with control implant (HA) points toward the critical role of electrical conductivity on better early stage bone regeneration. (c) 2013 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 102A: 842-851, 2014.

Pulsed Electrical Stimulation and Surface Charge Induced Cell Growth on Multistage Spark Plasma Sintered Hydroxyapatite-Barium Titanate Piezobiocomposite

The primary purpose of the present work was to illustrate whether cell proliferation can be enhanced on electroactive bioceramic composite, when the cells are cultured in the presence of external electrical stimulation. The two different aspects of the influence of electric field (E-field) application toward stimulating the growth/proliferation of bone/connective tissue cells in vitro, (a) intermittent delivery of extremely low strength pulsed electrical stimulation (0.5-4V/cm, 400s DC pulse) and (b) surface charge generated by electrical poling (10kV/cm) of hydroxyapatite (HA)-BaTiO3 piezobiocomposite have been demonstrated. The experimental results establish that the cell growth can be enhanced using the new culture protocol of the intermittent delivery of electrical pulses within a narrow range of stimulation parameters. The optimal E-field strength for enhanced cellular response for mouse fibroblast L929 and osteogenic cells is in the range of 0.5-1V/cm. The MTT 3-(4, 5-dimethylthiazol-2-yl)-2, 5-diphenyl tetrazolium bromide] assay results suggested the increased viability of E-field treated cells over 7d in culture, implicating the positive impact of electrical pulses on proliferation behavior. The alizarin red assay results showed noticeable increase in Ca-deposition on the E-field treated samples in comparison to their untreated counterparts. The negatively charged surfaces of developed piezocomposite stimulated the cell growth in a statistically noticeable manner as compared with the uncharged or positively charged surfaces of similar composition.

Correlations between mechanical and photoluminescence properties in Eu doped sodium bismuth titanate

Nanoindentation technique is utilized to examine mechanical property variation in Eu doped Na0.5Bi0.5 TiO3 (NBT). Doping levels of Eu in NBT is systematically varied. Dilute doping results in a linear reduction in both modulus and hardness. At higher concentrations, a recovery of the mechanical properties (to undoped NBT values) is observed. These experimental trends mirror variations in the optical emission intensities with Eu concentration. Observed trends are rationalized on the basis of a model, which hypothesizes phase segregation beyond a critical Eu doping level. Such segregation leads to the formation of pure NBT, nano-Eu saturated NBT, and nano-mixed Eu oxides in the microstructure. Pure NBT is optically inactive, while saturated Eu:NBT is a much better emitter when compared to europium oxide. Hence beyond the critical concentration, luminescence signal comes primarily from the saturated Eu:NBT phase. The model presented is supported by nanoindentation, and spectroscopic results. (C) 2013 Elsevier Ltd. All rights reserved.

Growth of hafnium and zirconium suicides by reactive diffusion

Diffusion controlled growth of the phases in Hf-Si and Zr-Si systems are studied by bulk diffusion couple technique. Only two phases grow in the interdiffusion zone, although several phases are present in both the systems. The location of the Kirkendall marker plane, detected based on the grain morphology, indicates that disilicides grow by the diffusion of Si. Diffusion of the metal species in these phases is negligible. This indicates that vacancies are present mainly on the Si sublattice. The activation energies for integrated diffusion coefficients in the HfSi2 and ZrSi2 are estimated as 394 +/- 37 and 346 +/- 34 kJ mol(-1), respectively. The same is calculated for the HfSi phase as 485 +/- 42 kJ mol(-1). The activation energies for Si tracer diffusion in the HfSi2 and ZrSi2 phases are estimated as 430 +/- 36 and 348 +/- 34 kJ mol(-1), respectively. (C) 2013 Elsevier B.V. All rights reserved.

Growth of hafnium and zirconium suicides by reactive diffusion

Diffusion controlled growth of the phases in Hf-Si and Zr-Si systems are studied by bulk diffusion couple technique. Only two phases grow in the interdiffusion zone, although several phases are present in both the systems. The location of the Kirkendall marker plane, detected based on the grain morphology, indicates that disilicides grow by the diffusion of Si. Diffusion of the metal species in these phases is negligible. This indicates that vacancies are present mainly on the Si sublattice. The activation energies for integrated diffusion coefficients in the HfSi2 and ZrSi2 are estimated as 394 +/- 37 and 346 +/- 34 kJ mol(-1), respectively. The same is calculated for the HfSi phase as 485 +/- 42 kJ mol(-1). The activation energies for Si tracer diffusion in the HfSi2 and ZrSi2 phases are estimated as 430 +/- 36 and 348 +/- 34 kJ mol(-1), respectively. (C) 2013 Elsevier B.V. All rights reserved.

Effect of Zirconium on the Densification of Reactively Hot-Pressed Zirconium Carbide

Densification mechanisms involved during reactive hot pressing (RHP) of zirconium carbide (ZrC) have been studied. RHP has been carried out using zirconium (Zr) and graphite (C) powders in the molar ratios 1:0.5, 1:0.67, 1:0.8, and 1:1 at 40MPa, 800 degrees C-1200 degrees C for different durations. The volume fractions of phases formed, including porosity, are determined from the measured density and from Rietveld analysis. Increased densification with an increasing nonstoichiometry in carbon has been observed. Microstructural and X-ray diffraction observations coupled with the predictions of a model based on the constitutive laws governing plastic flow of zirconium suggest that the better densification of nonstoichiometric compositions arise from the higher amount of starting Zr and also the longer duration of its availability for plastic flow during RHP. Volume shrinkage due to reaction between Zr and C and the gradual elimination of the soft metal phase limit the final density achievable. Based on these observations, a two-step RHP carried out at 800 degrees C and 1200 degrees C leads to a better densification than a single RHP at 1200 degrees C.

Effect of electrical parameters on morphology and in-vitro corrosion resistance of plasma electrolytic oxidized films formed on zirconium

The objective of the present work is to study the effect of electrical process Parameters (duty cycle and frequency) on morphological, structural, and in-vitro corrosion characteristics of oxide films formed on zirconium by plasma electrolytic oxidation in an electrolyte system consisting of 5 g/L of trisodium orthophosphate. The oxide films fabricated on zirconium by systematically varying the duty cycle and frequency are characterized for its phase composition, surface morphology, chemical composition, roughness, wettability, surface energy, scratch resistance, corrosion resistance, apatite forming ability and osteoblast cell adhesion. X-ray diffraction pattern of all the oxide films showed the predominance of m-ZrO2 phase. Dense and uniform films with thickness varying from 9 to 15 mu m and roughness in the range of 0.62 to 1.03 mu m are formed. Porosity of oxide films is found to be increased with an increase infrequency. The water contact angle results demonstrated that the oxide films exhibited similar hydrophilicity to zirconium substrate. All oxide films showed improved corrosion resistance, as indicated by far lower corrosion current density and passive corrosion potential compared to the zirconium substrate in simulated body fluid environment, and among the four different combinations of duty cycle and frequency employed in the present study, the oxide film formed at 95% duty cycle and 50 Hz frequency (HDLF film) showed superior pitting corrosion resistance, which can be attributed to its pore free morpholOgy. Scratch test results showed that the HDLF oxide film adhered firmly to the substrate by developing a notable scratch resistance at 19.5 +/- 1.2.N. Besides the best corrosion resistance and scratch retistance, the HDLF film also showed good apatite forming ability and osteo sarcoma cell adhesion on its surface. The HDLF oxide film on zirconium with superior surface characteristics is believed to be useful for various types of implants in the dental and orthopedic fields. (C) 2015 Elsevier B.V. All rights reserved.

Computational modeling of reactive hot pressing of zirconium carbide

A model of reactive hot pressing of zirconium carbide (ZrCx, 0.5 < x < 1) has been constructed that incorporates four processes that occur in parallel: creep of zirconium (Zr), reaction of Zr and carbon (C), increase in volume fraction of hard phase with progressive reaction that reduces the creep of Zr and, finally, de-densification associated with volume reduction during reaction. The reasonable agreement of the model with experimental results verifies that plastic deformation of Zr is the main factor that is responsible for the low-temperature reactive densification of ZrC and that ZrC may be treated as a rigid inclusion that contributes little to densification. It predicts that densification is impaired by increasing carbon stoichiometry due to the increasing amount of starting hard phase and the greater contraction upon reaction. Additionally, the model predicts that mixtures of Zr and ZrC should show equal or better densification than Zr and C mixtures.