Intercalation of n-alkylamines in iron thiohypophosphate (FePS3)

The intercalation of linear alkylamines (C1-C4) in the two-dimensional (2D) Ising antiferromagnet, FePS3, has been investigated. Intercalation proceeds with a dilation of the interlayer distance. The expansion (approximately 3.8 angstrom) is the same for all four amine molecules, suggesting that they are oriented flat with respect to the layers. From an analysis of the products of deintercalation, it is concluded that the intercalated species are the alkylammonium cations and neutral amine molecules. The intercalated compounds are highly moisture sensitive, as reflected in the chemical nature of the intercalated species. Charge neutrality of the lattice after intercalation is preserved by the loss of Fe2+ ions from the lattice. These Fe2+ ions are further oxidized to form superparamagnetic Fe2O3 clusters, as confirmed by Mossbauer spectra and magnetic measurements. This was further corroborated by in situ EPR studies. The Fe-57 Mossbauer spectra of the intercalated compounds showed evidence for two species other than Fe2O3. On the basis of the observed isomer shifts and quadrupole splittings, they have been assigned to Fe2+ in an environment similar to that in FePS3 and in a distorted FePS3 environment. The temperature and field dependence of the magnetic susceptibility of single crystals of the amine-intercalated FePS3 have been measured. Their magnetic behavior shows many of the features expected of a 2D Ising antiferromagnet with random defects, Fe1-xPS3, in agreement with the mechanism of intercalation.

Interaction of Inorganic Nanoparticles with Graphene

The changes in the electronic and magnetic properties of graphene induced by interaction with semiconducting oxide nanoparticles such as ZnO and TiO2 and with magnetic nanoparticles such as Fe3O4, CoFe2O4, and Ni are investigated by using Raman spectroscopy, magnetic measurements, and first-principles calculations. Significant electronic and magnetic interactions between the nanoparticles and graphene are found. The findings suggest that changes in magnetization as well as the Raman shifts are directly linked to charge transfer between the deposited nanoparticles and graphene. The study thus demonstrates significant effects in tailoring the electronic structure of graphene for applications in futuristic electronic devices.

Insertion of nickel nanoparticles in the interlayers of alpha-zirconium phosphate by the decomposition of the intercalated nickel acetate

By employing EXAFS and magnetic measurements, it is shown that nanoparticles of nickel along with those of NiO are incorporated between the layers of a-zirconium phosphate (ZrP) by the thermal decomposition of nickel acetate intercalated in ZrP. The nickel nanoparticles are superparamagnetic. Hydrogen reduction produces small ferromagnetic nickel particles, most of which appear to be outside the interlayer space of ZrP.

Superconductivity of embedded lead nano particles in metallic and amorphous matrices

Nanodispersed lead in metallic and amorphous matrices was synthesized by rapid solidification processing. The optimum microstructure was tailored to avoid percolation of the particles. With these embedded particles it is possible to study quantitatively the effect of size on the superconducting transition temperature by carrying out quantitative microstructural characterization and magnetic measurements. Our results suggest the role of the matrices in enhancement or depression of superconducting transition temperature of lead. The origin of this difference in behavior with respect to different matrices and sizes is discussed.

Continuous phase transition in mixed-valent manganite Nd0.6Pb0.4MnO3

The critical behaviour has been investigated in single crystalline Nd0.6Pb0.4MnO3 near the paramagnetic to ferromagnetic transition temperature (TC) by static magnetic measurements. The values of TC and the critical exponents β, γ and δ are estimated by analysing the data in the critical region. The exponent values are very close to those expected for 3D Heisenberg ferromagnets with short-range interactions. Specific heat measurements show a broad cusp at TC (i.e., exponent α<0) being consistent with Heisenberg-like behaviour.

Evidence for low temperature glassy behavior in La0.5Sr0.5CoO3

We report the observed low temperature spin glass like feature in the optimally doped La0.5Sr0.5CoO3 ferromagnetic system. The characteristic of glassy behavior has been identified by noting (i) the frequency-dependent shift of the low temperature hump position in the out of phase ac susceptibility component; (ii) evolution of freezing temperature with dc biasing field that adheres to de Almeida-Thouless relation; (iii) memory effect; and (iv) sluggish magnetic relaxation. The results of magnetic measurements demonstrate that neither the inter-cluster interaction nor the spin disorder at the interface between ferromagnetic clusters is responsible for the manifestation of such collective glassy behavior. Rather, it is believed to arise from a distinct cluster glass like phase that possibly coexists with the dominant ferromagnetic phase. (C) 2012 American Institute of Physics. [doi:10.1063/1.3684610]

Glassy dielectric response in Tb2NiMnO6 double perovskite with similarities to a Griffiths phase

Results of frequency-dependent and temperature-dependent dielectric measurements performed on the double-perovskite Tb2NiMnO6 are presented. The real (epsilon(1)(f,T)) and imaginary (epsilon(2)(f,T)) parts of dielectric permittivity show three plateaus suggesting dielectric relaxation originating from the bulk, grain boundaries and the sample-electrode interfaces, respectively. The epsilon(1)(f,T) and epsilon(2)(f,T) are successfully simulated by a RC circuit model. The complex plane of impedance, Z'-Z `', is simulated using a series network with a resistor R and a constant phase element. Through the analysis of epsilon(f,T) using the modified Debye model, two different relaxation time regimes separated by a characteristic temperature, T*, are identified. The temperature variation of R and C corresponding to the bulk and the parameter alpha from modified Debye fit lend support to this hypothesis. Interestingly, the T* compares with the Griffiths temperature for this compound observed in magnetic measurements. Though these results cannot be interpreted as magnetoelectric coupling, the relationship between lattice and magnetism is markedly clear. We assume that the observed features have their origin in the polar nanoregions which originate from the inherent cationic defect structure of double perovskites. Copyright (C) EPLA, 2013

Synergetic effect of size and morphology of cobalt ferrite nanoparticles on proton relaxivity

Cobalt ferrite nanoparticles with average sizes of 14, 9 and 6 nm were synthesised by the chemical co-precipitation technique. Average particle sizes were varied by changing the chitosan surfactant to precursor molar ratio in the reaction mixture. Transmission electron microscopy images revealed a faceted and irregular morphology for the as-synthesised nanoparticles. Magnetic measurements revealed a ferromagnetic nature for the 14 and 9 nm particles and a superparamagnetic nature for the 6 nm particles. An increase in saturation magnetisation with increasing particle size was noted. Relaxivity measurements were carried out to determine T-2 value as a function of particle size using nuclear magnetic resonance measurements. The relaxivity coefficient increased with decrease in particle size and decrease in the saturation magnetisation value. The observed trend in the change of relaxivity value with particle size was attributed to the faceted nature of as-synthesised nanoparticles. Faceted morphology results in the creation of high gradient of magnetic field in the regions adjacent to the facet edges increasing the relaxivity value. The effect of edges in increasing the relaxivity value increases with decrease in the particle size because of an increase in the total number of edges per particle dispersion.

Oxygen-participated electrochemistry of new lithium-rich layered oxides Li3MRuO5 M = Mn, Fe)

We describe the synthesis, crystal structure and lithium deinsertion-insertion electrochemistry of two new lithium-rich layered oxides, Li3MRuO5 (M = Mn, Fe), related to rock salt based Li2MnO3 and LiCoO2. The Li3MnRuO5 oxide adopts a structure related to Li2MnO3 (C2/m) where Li and (Li0.2Mn0.4Ru0.4) layers alternate along the c-axis, while the Li3FeRuO5 oxide adopts a near-perfect LiCoO2 (R (3) over barm) structure where Li and (Li0.2Fe0.4Ru0.4) layers are stacked alternately. Magnetic measurements indicate for Li3MnRuO5 the presence of Mn3+ and low spin configuration for Ru4+ where the itinerant electrons occupy a pi*-band. The onset of a net maximum in the chi vs. T plot at 9.5 K and the negative value of the Weiss constant (theta) of -31.4 K indicate the presence of antiferromagnetic superexchange interactions according to different pathways. Lithium electrochemistry shows a similar behaviour for both oxides and related to the typical behaviour of Li-rich layered oxides where participation of oxide ions in the electrochemical processes is usually found. A long first charge process with capacities of 240 mA h g(-1) (2.3 Li per f.u.) and 144 mA h g(-1) (1.38 Li per f.u.) is observed for Li3MnRuO5 and Li3FeRuO5, respectively. An initial sloping region (OCV to ca. 4.1 V) is followed by a long plateau (ca. 4.3 V). Further discharge-charge cycling points to partial reversibility (ca. 160 mA h g(-1) and 45 mA h g(-1) for Mn and Fe, respectively). Nevertheless, just after a few cycles, cell failure is observed. X-ray photoelectron spectroscopy (XPS) characterisation of both pristine and electrochemically oxidized Li3MRuO5 reveals that in the Li3MnRuO5 oxide, Mn3+ and Ru4+ are partially oxidized to Mn4+ and Ru5+ in the sloping region at low voltage, while in the long plateau, O2- is also oxidized. Oxygen release likely occurs which may be the cause for failure of cells upon cycling. Interestingly, some other Li-rich layered oxides have been reported to cycle acceptably even with the participation of the O2- ligand in the reversible redox processes. In the Li3FeRuO5 oxide, the oxidation process appears to affect only Ru (4+ to 5+ in the sloping region) and O2- (plateau) while Fe seems to retain its 3+ state.

Origin of room temperature weak-ferromagnetism in antiferromagnetic Pb(Fe2/3W1/3)O-3 ceramic

We report the origin of room temperature weak ferromagnetic behavior of polycrystalline Pb(Fe2/3W1/3)O-3 (PFW) powder. The structure and magnetic properties of the ceramic powder prepared by a Columbite method were characterized by X-ray and neutron diffraction, Mossbauer spectroscopy and magnetization measurements. Rietveld analysis of diffraction data confirm the formation of single phase PFW, without traces of any parasitic pyrochlore phase. PFW was found to crystallize in the cubic structure at room temperature. The Rietveld refinement of neutron diffraction data measured at room temperature confirmed the G-type antiferromagnetic structure of PFW in our sample. However, along with the antiferromagnetic (AFM) ordering of the Fe spins, we have observed the existence of weak ferromagnetism at room temperature through: (i) a clear opening of hysteresis (M-H) loop, (ii) bifurcation of the field cooled and zero-field cooled susceptibility; supported by Mossbauer spectroscopy results. The P-E loop measurements showed a non-linear slim hysteresis loop at room temperature due to the electronic conduction through the local inhomogeneities in the PFW crystallites and the inter-particle regions. By corroborating all the magnetic measurements, especially the spin glass nature of the sample, with the conduction behavior of the sample, we report here that the observed ferromagnetism originates at these local inhomogeneous regions in the sample, where the Fe-spins are not perfectly aligned antiferromagnetically due to the compositional disordering. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Observation of the nuclear magnetic octupole moment of Yb-173 from precise measurements of the hyperfine structure in the P-3(2) state

We measure hyperfine structure in the metastable P-3(2) state of Yb-173 and extract the nuclear magnetic octupole moment. We populate the state using dipole-allowed transitions through the P-3(1) and S-3(1) states. We measure frequencies of hyperfine transitions of the P-3(2) -> S-3(1) line at 770 nm using a Rb-stabilized ring cavity resonator with a precision of 200 kHz. Second-order corrections due to perturbations from the nearby P-3(1) and P-1(1) states are below 30 kHz. We obtain the hyperfine coefficients as A = -742.11(2) MHz and B = 1339.2(2) MHz, which represent a two orders-of-magnitude improvement in precision, and C = 0.54(2) MHz. From atomic structure calculations, we obtain the nuclear moments quadrupole Q = 2.46(12) b and octupole Omega = -34.4(21) b x mu(N). DOI: 10.1103/PhysRevA.87.012512

Growth and electron effective mass measurements of strained Si and Si0.94Ge0.06 on relaxed Si0.62Ge0.38 buffers grown by rapid thermal chemical vapor deposition

Abstract: We report the growth and the electron cyclotron resonance measurements of n-type Si/Si0.62Ge0.38 and Si0.94Ge0.06/Si0.62Ge0.38 modulation-doped heterostructures grown by rapid thermal chemical vapor deposition. The strained Si and Si0.94Ge0.06 channels were grown on relaxed Si0.62Ge0.38 buffer layers, which consist of 0.6 mu m uniform Si0.62Ge0.38 layers and 0.5 mu m compositionally graded relaxed SiGe layers from 0 to 38% Ge. The buffer layers were annealed at 800 degrees C for 1 h to obtain complete relaxation. A 75 Angstrom Si(SiGe) channel with a 100 Angstrom spacer and a 300 Angstrom 2 X 10(19) cm(-3) n-type supply layer was grown on the top of the buffer layers. The cross-sectional transmission electron microscope reveals that the dense dislocation network is confined to the buffer layer, and relatively few dislocations terminate on the surface. The plan-view image indicates the threading dislocation density is about 4 X 10(6) cm(-2). The far-infrared measurements of electron cyclotron resonance were performed at 4 K with the magnetic field of 4-8 T. The effective masses determined from the slope of the center frequency of the absorption peak versus applied magnetic field plot are 0.203m(0) and 0.193m(0) for the two dimensional electron gases in the Si and Si0.94Ge0.06 channels, respectively. The Si effective mass is very close to that of a two dimensional electron gas in an Si MOSFET (0.198m(0)). The electron effective mass of Si0.94Ge0.06 is reported for the first time and is about 5% lower than that of pure Si.

High-Pressure Magnetic-Susceptibility Studies of Spin-State Transaction

High-pressure magnetic susceptibility measurements have been carried out on Fe(dipy)2(NCS)2 and Fe(phen)2(NCS)2 in the pressure range 1–10 kbar and tempeature range 80–300 K in order to investigate the factors responsible for the spin-state transitions. The transitions change from first order to second or higher order upon application of pressure. The temperature variation of the susceptibility at different pressures has been analysed quantitatively within the framework of available models. It is shown that the relative magnitudes of the ΔG0 of high-spin and low-spin conversion and the ferromagnetic interaction between high-spin complexes determines the nature of the transition.

Formative time lags in nitrogen, oxygen and dry air In crossed electric and magnetic fields

Formative time lags in nitrogen, oxygen, and dry air are measured with and without a magnetic field over a range of gas pressures (0.05 ' p ' 20.2 torr 5 kPa to 2 MPa, electric field strengths (1.8xO14 EEs 60xlO V m l) and magnetic field strengths (85xl0-4 < B ' 16x10-2 Tesla). For experiments below the Paschen minimum, the electrodes are designed to ensure that breakdown occurs over longer gaps and for experiments above the Paschen minimum, a coaxial cylindrical system is employed. The experimental technique consists of applying pulse voltages to the gap at various constant values of E/p and B/p and measuring the time lags from which the formative time lags are separated. In the gases studed, formative time lags decrease on application of a magnetic field at a given pressure for conditions below the Paschen minimum. The voltages at which the formative time lags remain the same without and with magnetic fields are determined, and electron molecule collision frequencies (v/p) are determined using the Effective Reduced Electric Field [EREF] concept. With increasing ratio of E/p in crossed fields, v/p decreases in all the three gases. Measurements above the Paschen minimum yield formative time lags which increase on application of a magnetic field. Formative time lags in nitrogen in ExB fields are calculated assuming an average collision frequency of 8.5x109 sec-1 torr 1. It is concluded that the EREF concept can be applied to explain formative time lags in ExB fields.

Molecular Dynamics in [(CH8)aN]z Cd14 A Proton Magnetic Relaxation Study

second moment measurements are carried out on [(CH,),N], CdI, in the temperature range 77 to 400 K. The results are interpreted based on a molecular dynamical model of randomly reorienting methyl groups and isotropically tumbling tetramethyl ammonium group. The relaxation data show contributions from spin-rotation interaction at high temperatures and presence of inequivalent methyl groups. The correlation times and associated activation energies, connected with this model, are calculated from the data. The structure in the absorption line and in the free-induction decay signal at 77 K indicates the possibility of tunnelling motion of the methyl groups. Im Temperaturbereich 77 bis 400 K werden an [(CH,),N],CdI, Protonen-Spin-Gitter-Relaxationsexperimente (bei Larmorfrequenzen von 10,20 und 30 MHz) und Messungen des zweiten Moments durchgefiihrt. Die Ergebnisse werden an Hand eines molekularen dynamischen Modells sich statistisch umorientierender Methylgruppen und isotrop taumelnder Tetramethyl-Ammoniumgruppen interpretiert. Die Relaxationswerte zeigen Beitriige von Spin-Rotations-Wechselwirkung bei hohen Temperaturen und die Anwesenheit von inaquivalenten Methylgruppen. Die Korrelationszeiten und verknupften Aktivierungsenergien, die mit diesem Model1 verbunden sind, werden am den Werten berechnet. Die Struktur in der Absorptionslinie und im Abklingsignal der freien Induktion bei 77 K zeigt die Moglichkeit einer Tunnelbewegung der Methylgruppen.