The proton magnetic resonance study of the structure of Na2Zn(SO4)2·4H2O

The proton magnetic resonance spectra of single crystals of Na2Zn(SO4)2·4H2O have been investigated and the orientations of the water molecules have been determined. Using the heavy atom structure determined by X-rays a system of hydrogen bonds between water and sulphate oxygens has been proposed.

Studies on the phase transitions in thiourea

Thiourea (CS(NH2)2) is one of the few examples of molecular crystals exhibiting ferroelectric properties. The dielectric constant along the ferroelectric axis [100] shows maxima at 169, 177 and 202 K. An inflection point occurs at 170.5 KZ Following Goldsmith and White the phases are named as I (F.E. below 169 K), II (A.F.E. 169 Kx-rays which is accounted for by defects like NH3+ and NH- formed by the breaking of hydrogen bonds.

Interaction of carbon monoxide with bimetallic overlayers

Interaction of carbon monoxide with a few chosen bimetallic overlayers has been investigated along with the core-level binding energies of the deposited metals by employing X-rays as well as UV photoelectron spectroscopies. Core-level binding energies of the deposited metals around monolayer coverages (0 similar to 1) are significantly different than those at high coverages or of the pure metals. Bimetallic overlayers such as Ni/Au and Cu/Pt showing large negative shifts in the surface core-level binding energy of the deposited metal interact strongly with carbon monoxide. In the case of Ni/Au (0(Ni) similar to 0.85), CO dissociates around 280 K. In contrast to this behavior, the interaction of CO with Pd/Mo or W, showing large positive shifts in the surface core-level binding energy, is very weak, and the CO desorption temperature is much lower than that from the clean Pd metal surface. The CO desorption temperature generally increases as the surface core-level shift of the deposited metal becomes more negative; the separation between the (5 sigma + 1 pi) and 4 sigma levels of CO also increases in this direction. These results suggest that the variation in the strength of interaction of CO with bimetallic overlayers is a chemical manifestation of the shift in the surface core-level binding energies of the deposited metals at monolayer coverages.

Phase-relations in the system CAO-SIO2-ZRO2 AT 1573-K

Zirconia-based solid electrolytes with zircon (ZrSiO4) as the auxiliary electrode have been suggested of sensing silicon concentrations in iron and steel melts. A knowledge of phase relations in the ternary system MO-SiO2-ZrO2 (M = Ca, Mg) is useful for selecting an appropriate auxiliary electrode. In this investigation, an isothermal section for the phase diagram of the system CaO-SiO2ZrO2 at 1573 K has been established by equilibrating mixtures of component oxides in air, followed by quenching and phase identification by optical miroscopy, energy disperse analysis of X-rays (EDAX) and X-ray diffraction analysis (XRD). The equilibrium phase relations have also been confirmed by computation using the available thermodynamic data on condensed phases in the system. The results indicate that zircon is not in thermodynamic equilibrium with calcia-stabilized zirconia or calcium zirconate. The silica containing phase in equilibrium with stabilized zirconia is Ca3ZrSi2O9. Calcium zirconate can coexist with Ca3ZrSi2O9 and Ca2SiO4.

Phase Relations in the System La-Rh-O and Thermodynamic Properties of LaRhO3

Phase relations in the system La-Rh-O at 1223 Ii have been determined by examination of equilibrated samples by optical and scanning electron microscopy, powder X-ray diffraction (XRD), and energy-dispersive analysis of X-rays (EDAX). Only one ternary oxide, LaRhO3, with distorted orthorhombic perovskite structure (Pbnm, a = 0.5525, b = 0.5680, and c = 0.7901 nm) was identified. The alloys and intermetallics along the La-Rh binary are in equilibrium with La2O3. The thermodynamic properties of LaRhO3 were determined in the temperature range 890 to 1310 K, using a solid-state cell incorporating yttria-stabilized zirconia as the electrolyte. A new four-compartment design of the emf cell was used to enhance the accuracy of measurement. For the reaction 1/2La(2)O(3) + 1/2Rh(2)O(3) --> LaRhO3, Delta G degrees = - 70 780 + 4.89T (+/- 90) J.mol(-1) The compound decomposes on heating to a mixture of La2O3, Ph and O-2. The calculated decomposition temperatures are 1843 (+/- 5) K in pure O-2 and 1728 (+/- 5) K in air at a pressure of 1.01 x 10(5) Pa. The phase diagrams for the system La-Rh-O at different partial pressures of oxygen are calculated from the thermodynamic information.

The CaO-SrO-CuO-O-2 system: Phase equilibria and thermodynamic properties at 1123 K

Phase relationships in the CaO-SrO-CuO system in pure oxygen at 1.01 x 10(5) Pa pressure were determined by equilibrating different compositions at 1123 K for similar to 120 h and analyzing the phases present in the quenched samples using X-ray diffraction (XRD), optical and scanning electron microscopy, and energy dispersive analysis of X-rays (EDAX). Four solid solution series were observed in the system, The CawSr1-wO monoxide solid solution with rock-salt structure was found to exhibit an asymmetric miscibility gap, The mixing properties of the monoxide system were deduced using a subregular solution model, For the (CaxSr1-x)(2)CuO3 series, a complete solid solution range with orthorhombic space group Immm was obtained. Calcium substituted for strontium up to 68 at. % in SrCuO2+delta and 51.5 at. % in Sr14Cu24O41-delta. The tie lines between the solid solutions were determined accurately, The activity-composition relations in (CaxSr1-x)(2)CuO3, CaySr1-yCuO2+delta, and (Ca2Sr1-z)(14)Cu24O41-delta solid solutions were determined from experimental tie lines. Activities in the (CaxSr1-x)(2)CuO3 and CaySr1-yCuO2+delta series were close to the predictions of the Temkin model, The behavior of the (CazSr1-(z))(14)Cu24O41-delta solid solution was more complex, with the activity of SrCu(24/14)O-(41-delta/14) exhibiting both positive and negative deviations from ideality. Gibbs energy of formation of the CaCuO2+delta metastable phase at 1123 K was deduced from an analysis of the phase diagram.

Preparation and dielectric properties of zinc and cadmium doped barium tantalates, Ba3Zn1?xCdxTa2O9

Members of the Ba2Zn1-xCdxTa2O9 (0 less than or equal to x less than or equal to 1) series have been synthesized by solid state reactions at 1473K. Powder x-ray diffraction studies show a cubic perovskite cell with a similar to 4.1 Angstrom which increases with increase in x. Electron diffraction studies show the presence of hexagonal ordered perovskite structure in addition to the cubic structure seen by x-rays, the x = 0.5 composition showing more ordered crystallites. These samples show high dielectric constants with a maximum (epsilon(r) = 30 at 1 kHz) for the x = 0.5 member. The dielectric loss increases with increase in x at all the frequencies under study.

Origin of carrier-type reversal in Pb-Ge-Se glasses: A detailed thermal, electrical, and structural study

A long-standing and important problem in glass science has been carrier-type reversal (CTR) in semiconducting glasses. This phenomenon is exhibited by Pb-Ge-Se glasses also. It has been addressed here by carrying out detailed electrical, thermal, and spectroscopic investigations. PbxGe42-xSe58 (x = 0-20) glasses were prepared by a two stage melt-quenching process and characterized using x-ray diffraction, high-resolution electron microscropy, and energy dispersive analysis of x-rays. Thermoelectric power and high-pressure electrical resistivity have been measured. IR, Raman, and X-ray adsorption near edge structure spectroscopies have been used for examining the glass structures as well as differential scanning calorimetry (DSC) for studying the thermal properties. A structural model based on the chemical nature of the constituents has been proposed to account for the observed properties of these glasses. Effect of Pb incorporation on local structures and qualitative consequences on the energy band structures of Ge-Se glasses has been considered. The p -->n transition has been attributed to the energetic disposition of the sp(3)d(2) band of Pb atoms, which is located closely above the lone pair band of selenium. This feature makes Pb unique in the context of p -->n transition of chalcogenide glasses. The model can be extended successfully to account for the CTR behavior observed in Bi containing chalcogenide glasses also.

Photoluminescence studies on gray tracked KTiOPO4 single crystals

The photochromic, electrochromic and x-ray irradiation damages (commonly called the gray tracks) produced in KTiOPO4 single crystals have been studied using photoluminescence (PL) spectroscopy. Gray tracks were produced in this material by exposure to high laser powers (similar to MW/cm(2)), application of electric fields (similar to kV), and exposure to x rays (30 kV). The PL spectra recorded for such gray tracked samples at 4.2 K, exhibited a luminescence band in the 1-1.8 eV range with a peak at 1.41 eV. Temperature and excitation intensity dependence of PL peaks were carried out to probe the exact nature of the broad emission band in the gray tracked samples. The observed photoluminescence is attributed to transitions in the Ti3+ levels, created on irradiation. The microscopic effects produced in the crystal by electric field, optical field, and x rays are similar, as can be concluded from the similarity of PL spectra as well as their intensity and temperature dependences. (C) 1999 American Institute of Physics. [S0021-8979(99)04512-0].

The effect of mischmetal addition on the structure and mechanical properties of a cast Al-7Si-0.3Mg alloy containing excess iron (up to 0.6 Pct)

The effect of Fe content (0.2 to 0.6 pct) on the microstructure and mechanical properties of a cast Al-7Si-0.3Mg (LM 25/356) alloy has been investigated. Further, 1 pct mischmetal (MM) additions (a mixture of rare-earth (RE) elements) were made to these alloys, and their mechanical properties at room and at elevated temperatures (up to 200 degreesC) were evaluated. A structure-property correlation on this alloy was attempted using optical microstructure analysis, fractographs, X-ray diffraction, energy-dispersive analysis of X-rays (EDX), and quantitative metallography by image analysis. An increase in Fe content increased the volume percentage of Fe-bearing intermetallic compounds (beta and pi phases), contributing to the lower yield strength (YS), ultimate tensile strength (UTS), percentage elongation, and higher hardness. An addition of 1 pct MM to the alloys containing 0.2 and 0.6 pct Fe was found to refine the microstructure; modify the eutectic silicon and La, Ce, and Nd present in the MM; form different intermetallic compounds with Al, Si, Fe, and Mg; and improve the mechanical properties of the alloys both at room and elevated temperatures.

Development and studies on microstrip detector

We report development of gas microstrip detectors using thin film and lithography techniques. The detectors were tested for their performance for X-rays (5.9 keV) and a maximum gas gain of similar to 13,000 and best resolution of similar to 12% was obtained. Factors affecting gain and resolution were investigated. The detectors were tested for their one-dimensional position sensitivity. Meandering resistive strips were used for charge division method. A position resolution of 0.48 mm was obtained.

Metal mould reactions during casting of titanium in zircon sand moulds

Metal-mold reaction during Ti casting in zircon sand molds has been studied using scanning electron microscope, energy and wave length dispersive analysis of X-rays, X-ray diffraction, microhardness measurements, and chemical analysis. Experimental results suggest that oxides from the mold are not fully leached out by liquid Ti, but oxygen is preferentially transferred to liquid Ti, leaving behind metallic constituents in the mold as lower oxides or intermetallics of Ti. The electron microprobe analysis has revealed the depth profile of contaminants from the mold into the cast Ti metal. The elements Si, Zr and O were found to have diffused to a considerable distance within the Ti metals. A possible mechanism has now been evolved in regard to the reactions that occur during casting of Ti in zircon sand molds.

Phase relations in the system SrO-Y2O3-CuO-O2 and CaO-Y2O3-CuO-O2 at 1173 K

Phase relations in the systems SrO-Y2O3-CuO-O2 and CaO-Y2O3-CuO-O2 at 1173 K were established by equilibrating different compositions in flowing oxygen gas at a pressure of 1.01 × 105 Pa. The quenched samples were examined by optical microscopy, X-ray diffraction (XRD), energy dispersive analysis of X-rays (EDAX), and electron spin resonance (ESR). In the system SrO-Y2O3-CuO-O2, except for the limited substitution of Y3+ for Sr2+ ions in the ternary oxide Sr14Cu24O41, no new quaternary phase was found to be stable. The compositions corresponding to the solid solution Sr14−xYxCu24O41 and the compound SrCuO2+δ lie above the plane containing SrO, Y2O3, and CuO,displaced towards the oxygen apex. However, in the system CaO-Y203-CuO-O2 at 1173 K, all the condensed phases lie on the plane containing CaO, Y203, and CuO, and a new quaternary oxide YCa2Cu306.s is present. The quaternary phase has a composition that lies at the center of the nonstoichiometric field of the analogous phase YBa2Cu307_~ in the BaO-Y203-CuO-O2 system. The compound YCa2Cu306.s has the tetragonal structure and does not become superconducting at low temperature. Surprisingly, phase relations in the three systems CaO-Y203-CuO-O2, SrO-Y203-CuO-O2, and BaO-Y203-CuO-O2 are found to be quite different.

System Nd-Pd-O: Phase diagram and thermodynamic properties of oxides using a solid-state cell with advanced features

An isothermal section of the phase diagram for the system Nd-Pd-O at 1350 K has been established by equilibration of samples representing 13 different compositions and phase identification after quenching by optical and scanning electron microscopy, x-ray diffraction, and energy dispersive analysis of x-rays. The binary oxides PdO and NdO were not stable at 1350 K. Two ternary oxides Nd4PdO7 and Nd2Pd2O5 were identified. Solid and liquid alloys, as well as the intermetallics NdPd3 and NdPd5, were found to be in equilibrium with Nd2O3. Based on the phase relations, three solidstate cells were designed to measure the Gibbs energies of formation of PdO and the two ternary oxides. An advanced version of the solid-state cell incorporating a buffer electrode was used for high-temperature thermodynamic measurements. The function of the buffer electrode, placed between reference and working electrodes, was to absorb the electrochemical flux of the mobile species through the solid electrolyte caused by trace electronic conductivity. The buffer electrode prevented polarization of the measuring electrode and ensured accurate data. Yttria-stabilized zirconia was used as the solid electrolyte and pure oxygen gas at a pressure of 0.1 MP a as the reference electrode. Electromotive force measurements, conducted from 950 to 1425 K, indicated the presence of a third ternary oxide Nd2PdO4, stable below 1135 (±10) K. Additional cells were designed to study this compound. The standard Gibbs energy of formation of PdO (†f G 0) was measured from 775 to 1125 Kusing two separate cell designs against the primary reference standard for oxygen chemical potential. Based on the thermodynamic information, chemical potential diagrams for the system Nd-Pd-O were also developed.

System Cu-Rh-O: Phase diagram and thermodynamic properties of ternary oxides CuRhO2 and CuRh204

An isothermal section of the phase diagram for the system Cu-Rh-O at 1273 K has been established by equilibration of samples representing eighteen different compositions, and phase identification after quenching by optical and scanning electron microscopy (SEM), X-ray diffraction (XRD), and energy dispersive analysis of X-rays (EDX). In addition to the binary oxides Cu2O, CuO, and Rh2O3, two ternary oxides CuRhO2 and CuRh2O4 were identified. Both the ternary oxides were in equilibrium with metallic Rh. There was no evidence of the oxide Cu2Rh2O5 reported in the literature. Solid alloys were found to be in equilibrium with Cu2O. Based on the phase relations, two solid-state cells were designed to measure the Gibbs energies of formation of the two ternary oxides. Yttria-stabilized zirconia was used as the solid electrolyte, and an equimolar mixture of Rh+Rh2O3 as the reference electrode. The reference electrode was selected to generate a small electromotive force (emf), and thus minimize polarization of the three-phase electrode. When the driving force for oxygen transport through the solid electrolyte is small, electrochemical flux of oxygen from the high oxygen potential electrode to the low potential electrode is negligible. The measurements were conducted in the temperature range from 900 to 1300 K. The thermodynamic data can be represented by the following equations: {fx741-1} where Δf(ox) G o is the standard Gibbs energy of formation of the interoxide compounds from their component binary oxides. Based on the thermodynamic information, chemical potential diagrams for the system Cu-Rh-O were developed.