Microstructure and mechanical properties of unidirectionally solidified Al-Si-Ni ternary eutectic

Al-10.98 pct Si-4.9 pct Ni ternary eutectic alloy was unidirectionally solidified at growth rates from 1.39μm/sec to 6.95μm/sec. Binary Al-Ni and Al-Si eutectics prepared from the same purity metals were also solidified under similar conditions to characterize the growth conditions under the conditions of present study. NiAl3 phase appeared as fibers in the binary Al-Ni eutectic and silicon appeared as irregular plates in the binary Al-Si eutectic. However, in the ternary Al-Si-Ni eutectic alloy both NiAl3 and silicon phases appeared as irregular plates dispersed in α-Al phase, without any regular repctitive arrangement. The size and spacing of NiAl3 and Si platelets in cone shaped colonies decreased with an increase in the growth rate of the ternary eutectic. Examination of specimen quenched during unidirectional solidification indicated that the ternary eutectic grows with a non-planar interface with both Si and NiAl3 phases protruding into the liquid. It is concluded that it will be difficult to grow regular ternary eutectic structures even if only one phase has a high entropy of melting. The tensile strength and modulus of unidirectionally solidified Al-Si-Ni eutectic was lower than the chill cast alloys of the same composition, and decreased with a decrease in growth rate. Tensile modulus and strength of ternary Al-Si-Ni eutectic alloys was greater than binary Al-Si eutectic alloy under similar growth conditions, both in the chill cast and in unidirectionally solidified conditions.

Modes of deformation in aluminium rings subjected to static axial compression

Aluminium rings of varying Image Image diameter ratios machined from extruded solid bars, were subjected to static axial compression. Etched diametral planes of deformed cylinders revealed the existence of shear bands, the configuration of which were found to change with initial specimen geometry and deformation.

An annotated checklist of amphibian of India with some insights into the patterns of species discoveries, distribution and endemism

An annotated checklist of 284 species of amphibians of India accommodated under 50 genera and 14 families is provided. Synonyms, English names, type localities, deposition of type specimens, type specimen availability and distributional records in India and outside India are provided for all the species. Among the 284 species of amphibians from India, 132 are endemic to Western Ghats; 29 to Northeastern India; and 5 to Andaman Nicobar islands. Species discovery patterns from the various biogeographic zones in India are discussed in detail. Cumulative discovery pattern with special reference to the genera Fejervarya (17 species), Nyctibatrachus (16 species), Indirana (10 species), Micrixalus (11 species), Philautus (46 species) and Gegeneophis (10 species) are also discussed.

Modelling heterogeneity of concrete using 2D lattice network for concrete fracture and comparison with AE study

In this paper, numerical modelling of fracture in concrete using two-dimensional lattice model is presented and also a few issues related to lattice modelling technique applicable to concrete fracture are reviewed. A comparison is made with acoustic emission (AE) events with the number of fractured elements. To implement the heterogeneity of the plain concrete, two methods namely, by generating grain structure of the concrete using Fuller's distribution and the concrete material properties are randomly distributed following Gaussian distribution are used. In the first method, the modelling of the concrete at meso level is carried out following the existing methods available in literature. The shape of the aggregates present in the concrete are assumed as perfect spheres and shape of the same in two-dimensional lattice network is circular. A three-point bend (TPB) specimen is tested in the experiment under crack mouth opening displacement (CMOD) control at a rate of 0.0004 mm/sec and the fracture process in the same TPB specimen is modelled using regular triangular 2D lattice network. Load versus crack mouth opening isplacement (CMOD) plots thus obtained by using both the methods are compared with experimental results. It was observed that the number of fractured elements increases near the peak load and beyond the peak load. That is once the crack starts to propagate. AE hits also increase rapidly beyond the peak load. It is compulsory here to mention that although the lattice modelling of concrete fracture used in this present study is very similar to those already available in literature, the present work brings out certain finer details which are not available explicitly in the earlier works.

Influence of tool rake angle on the quality of pure magnesium chip-consolidated product

Chips were produced by orthogonal Cutting of cast pure magnesium billet with three different tool rake angles viz., -15 degrees, -5 degrees and +15 degrees on a lathe. Chip consolidation by solid state recycling technique involved cold compaction followed by hot extrusion. The extruded products were characterized for microstructure and mechanical properties. Chip-consolidated products from -15 degrees rake angle tools showed 19% increase in tensile strength, 60% reduction ingrain size and 12% increase in hardness compared to +15 degrees rake chip-consolidated product indicating better chip bonding and grain refinement. Microstructure of the fracture specimen Supports the abovefinding. On the overall, the present work high lights the importance of tool take angle in determining the quality of the chip-consolidated products. (C) 2009 Elsevier B.V. All rights reserved.

Verification of the applicability of lattice model to concrete fracture by AE study

Notched three-point bend specimens (TPB) were tested under crack mouth opening displacement (CMOD) control at a rate of 0.0004 mm/s and the entire fracture process was simulated using a regular triangular two-dimensional lattice network only over the expected fracture proces zone width. The rest of the beam specimen was discretised by a coarse triangular finite element mesh. The discrete grain structure of the concrete was generated assuming the grains to be spherical. The load versus CMOD plots thus simulated agreed reasonably well with the experimental results. Moreover, acoustic emission (AE) hits were recorded during the test and compared with the number of fractured lattice elements. It was found that the cumulative AE hits correlated well with the cumulative fractured lattice elements at all load levels thus providing a useful means for predicting when the micro-cracks form during the fracturing process, both in the pre-peak and in the post-peak regimes.

Assessment of the residual fatigue strength in RC beams

In conventional analysis and design procedures of reinforced concrete structures, the ability of concrete to resist tension is neglected. Under cyclic loading, the tension-softening behavior of concrete influences its residual strength and subsequent crack propagation. The stability and the residual strength of a cracked reinforced concrete member under fatigue loading, depends on a number of factors such as, reinforcement ratio, specimen size, grade of concrete, and the fracture properties, and also on the tension-softening behavior of concrete. In the present work, a method is proposed to assess the residual strength of a reinforced concrete member subjected to cyclic loading. The crack extension resistance based approach is used for determining the condition for unstable crack propagation. Three different idealization of tension softening models are considered to study the effect of post-peak response of concrete. The effect of reinforcement is modeled as a closing force counteracting the effect of crack opening produced by the external moment. The effect of reinforcement percentage and specimen size on the failure of reinforced beams is studied. Finally, the residual strength of the beams are computed by including the softening behavior of concrete.

Induced swelling of kaolinitic soil in alkali solution

Unexpected swelling induced in foundation soils can cause distress to structures founded on them. In this paper, the swelling of kaolinitic soils due to interaction with alkali solution has been reported. The induced swelling is attributed to the formation of new minerals, which has been confirmed by X-ray diffraction patters and SEM studies. To understand the effect of alkali concentration and duration of interaction, two series of consolidation experiments have been carried out. In series 1, the specimen were remoulded with water and inundated with alkali solutions and in series 2, the specimen were remoulded and inundated with same alkali solutions. A steep compression during loading cycle and no abnormal swelling during unloading cycle has been noticed for the specimen remoulded with water and inundated with 1 N NaOH solutions. The steep compression is due to the segregation or break down of clay minerals due to alkali interactions. In case of specimen inundated with 4 N NaOH solutions, abnormal swelling has been observed during unloading cycle of the consolidation test. New minerals are formed on interaction of soil with 4 N solution as confirmed by X-ray diffraction patterns. These minerals are known to have very fine pores and possess high water holding capacity. The differences in the amount of swelling of samples remoulded with water and remoulded with alkali solution are due to variations in the concentration of alkali and duration of interaction.

Multiple excitation nano-spot generation and confocal detection for far-field microscopy

An imaging technique is developed for the controlled generation of multiple excitation nano-spots for far-field microscopy. The system point spread function (PSF) is obtained by interfering two counter-propagating extended depth-of-focus PSF (DoF-PSF), resulting in highly localized multiple excitation spots along the optical axis. The technique permits (1) simultaneous excitation of multiple planes in the specimen; (2) control of the number of spots by confocal detection; and (3) overcoming the point-by-point based excitation. Fluorescence detection from the excitation spots can be efficiently achieved by Z-scanning the detector/pinhole assembly. The technique complements most of the bioimaging techniques and may find potential application in high resolution fluorescence microscopy and nanoscale imaging.

In situ transmission electron microscope study of single asperity sliding contacts

Direct observation of events taking place at the contacting interfaces is important to understand many tribological phenomena. Transmission electron microscope (TEM) has the ability to look through materials at very high magnifications. Most of the TEM observations are done long after the deforming loads and stresses have been relaxed and the material state is further disturbed during the specimen preparation. We have developed a specimen holder in which two electron transparent surfaces can be brought in contact and moved relative to each other in JEOL 2000FX microscope. This holder enables visualization of not only the contacting surfaces at nanoscale but also the subsurface deformation resulting from the contact interaction. Sliding experimentS have been carried out mimicking a single asperity sliding contact. A sharp tungsten probe is moved laterally against a tip mounted on a cantilever. Magnitude of the contact instability, when the contact is broken is found to be dependent on the local geometry of the contact.(C) 2009 Elsevier Ltd. All rights reserved.

Parametric analysis of acoustic emission signals for evaluating damage in composites using a PVDF film sensor

With the increased utilization of advanced composites in strategic industries, the concept of Structural Health Monitoring (SHM) with its inherent advantages is gaining ground over the conventional methods of NDE and NDI. The most attractive feature of this concept is on-line evaluation using embedded sensors. Consequently, development of methodologies with identification of appropriate sensors such as PVDF films becomes the key for exploiting the new concept. And, of the methods used for on-line evaluation acoustic emission has been most effective. Thus, Acoustic Emission (AE) generated during static tensile loading of glass fiber reinforced plastic composites was monitored using a Polyvinylidene fluoride (PVDF) film sensor. The frequency response of the film sensor was obtained with pencil lead breakage tests to choose the appropriate band of operation. The specimen considered for the experiments were chosen to characterize the differences in the operation of the failure mechanisms through AE parametric analysis. The results of the investigations can be characterized using AE parameter indicating that a PVDF film sensor was effective as an AE sensor used in structural health monitoring on-line.

Syntheses of the trans,meso- and racemic C11 acids, degradation products of diterpene acids

Syntheses of the isomers of the C11 acid, 1(a),3(a)- dimethylcyclohexane-1 (e),2(e),3(e)-tricarboxylic acid (A) and 1(a),3(e)-dimethylcyclohexane-1(e),2(e),3(a)-tricarboxylic acid (B), the latter by two different routes, are reported. Two of the four possible isomers of the precursor triester, trimethyl 1-methylcyclohexane-1,2,3-tricarboxylate, on individual methylation followed by hydrolysis, gave the trans,meso-acid (A), identified by comparison with an authentic sample, and the cis,trans-form (B) whose structure and configuration were proved by comparison with a specimen obtained by the unambiguous and highly stereoselective second synthesis. This demonstrated that methylation of the triester isomers occurs stereospecifically and exclusively at C-3. In the second sequence, it has been possible to assign definite conformations to four key intermediates and the final product, directly from n.m.r. spectra, from changes in these spectra accompanying specific steps, and from chemical evidence. Comparison of the n.m.r. spectra of the isomeric triesters (A) and (B) has provided unequivocal proof of the accepted trans,meso configuration for the abietic acid degradation product (A).

The protein components of elastoidin

Not all elastoidin samples from different species of sharks show a high content of tryptophan in contrast to one specimen from an unidentified species examined in our earlier study. There may be considerable species-dependent variation in tryptophan content and analytical artefacts may have occurred. Available analyses for tyrosine in different specimens of fibres also suggest the possibility that the variation in tyrosine content is also species-dependent. Elastoidin, from Galeoscerdo cuveir (Tiger Shark) and another unidentified species, on treatment with formic acid yielded three fractions A,B and C. On the basis of analytical data it appears that specimens of elastoidin containing no (or little) tryptophan may yield fraction B through the solubilization of fraction A by formic acid. C fractions from two specimens of fibres were collagenous in nature. C fractions have been further purified in this study by charcoal treatment which removes a tyrosine-rich contaminant, to yield collagens with only approx. 2–4 residues of tyrosine per assumed mol. wt. of 360000. In the collagen from the unidentified species glucose and galactose were present in the ratio of 2:5; some glucosamine was also present.

Electron spin resonance in cupric acid fluoride

The electron spin resonance in undiluted single crystals of cupric acid fluoride has been investigated at room temperature with microwaves of frequency 9625 Mc/s. The anisotropy in the g value has been measured in three orthogonal planes. The principal g values gave gshort parallel = 2.410 ± 0.010, gperpendicular = 2.090 ± 0.010. The linewidth shows anisotropy with orientation. The exchange frequency has been estimated to be approximately 0.08 cm-1.The powdered specimen shows asymmetry in the line shape.

A low temperature Weissenberg camera

Details of the design and operation of a Weissenberg camera suitable for x-ray investigations between -180°c and 200°c are presented. The camera employs a novel arrangement of spur and bevel gears to couple the goniometer spindle to the worm rod which controls the range of oscillation. The entire drive system and the goniometer assembly are mounted on a support which permits the insertion or removal of a cylindrical cassette from the gear-box side without disturbing the cooling assembly and the layer-line screen. The cassette can also be inserted from the opposite side. The specimen can be cooled either directly by a stream of liquid air or by the cold gas from its evaporation. Condensation of moisture at low temperatures is prevented by heating the layer-line tubes internally.