Diffusion and Creep in Silica-Doped Tetragonal Zirconia

Silica segregation at two grain junctions or in amorphous triple junction pockets can influence creep by altering the grain-boundary diffusion coefficient. Although the addition of silica to superplastic yttria-stabilized tetragonal zirconia enhances ductility, differences in reported creep parameters have limited critical identification of rate controlling mechanisms. The present study on a pure 3 mol% yttria-stabilized tetragonal zirconia (3YTZ) and 3YTZ with 0.39 or 3.9 wt% silica involved a detailed characterization of creep over a wide range of experimental conditions and also tracer diffusion measurements. The data broadly show transitions in creep stress exponents from n∼1 to ∼2 to ∼3 with a decrease in the stress. The data at high stresses are consistent with Coble diffusion creep, and creep at lower stresses is attributed to interface-controlled diffusion creep. Measurements indicated that silica does not have any significant influence on grain boundary or lattice diffusion, and this is consistent with the observation that 3YTZ and 3YTZ with 0.39% or 3.9% silica exhibit essentially identical creep behavior in the Coble creep regime. Silica influences the interface control process so that the transitions in stress exponents are pushed to lower stresses with an increase in silica content.

Topological close packed mu phase formation and the determination of diffusion parameters in the Co-Mo system

The study on the formation and growth of topological close packed (TCP) compounds is important to understand the performance of turbine blades in jet engine applications. These deleterious phases grow mainly by diffusion process in the superalloy substrate. Significant volume change was found because of growth of the p phase in Co-Mo system. Growth kinetics of this phase and different diffusion parameters, like interdiffusion, intrinsic and tracer diffusion coefficients are calculated. Further the activation energy, which provides an idea about the mechanism, is determined. Moreover, the interdiffusion coefficient in Co(Mo) solid solution and impurity diffusion coefficient of Mo in Co are determined.

Precipitate growth with composition-dependent diffusivity: Comparison between theory and phase field simulations

We consider the growth of an isolated precipitate when the matrix diffusivity depends on the composition. We have simulated precipitate growth using the Cahn-Hilliard model, and find good agreement between our results and those from a sharp interface theory for systems with and without a dilatational misfit. With misfit, we report (and rationalize) an interesting difference between systems with a constant diffusivity and those with a variable diffusivity in the matrix.

High vacuum tribology of polycrystalline diamond coatings

Polycrystalline diamond coatings have been grown on unpolished side of Si(100) wafers by hot filament chemical vapour deposition process. The morphology of the grown coatings has been varied from cauliflower morphology to faceted morphology by manipulation of the growth temperature from 700 degrees C to 900 degrees C and methane gas concentration from 3% to 1.5%. It is found that the coefficient of friction of the coatings under high vacuum of 133.32 x 10(-7) Pa (10(-7) torr) with nanocrystalline grains can be manipulated to 0.35 to enhance tribological behaviour of bare Si substrates.

Tendency to promote ferroelectric distortion in Pr-modified PbTiO3

Structural, microstructural, and dielectric studies have been carried out on Pr-modified PbTiO3. A comparative analysis with La-modified PbTiO3 suggests that for chemical modification by same amount, the Pr-modified system has larger tetragonal strain and Curie point. No clear feature of relaxor ferroelectric state is observed for Pr concentration as high as x=0.35, suggesting that Pr modification is less effective, as compared to La-modification, in inducing a relaxor ferroelectric state. Results suggest that inspite of increased chemical disorder, Pr modification partly tends to restore the ferroelectric distortion of the lattice through partial occupancy of the Pr4+ ions on the Ti4+ sites.

Rainfall changes over tropical montane cloud forests of southern Western Ghats, India

The southern Western Ghats tropical montane cloud forest sites (Gavi, Periyar, High wavys and Venniyar), which are characterized by frequent or seasonal cloud cover at the vegetation level, are considered one of the most threatened ecosystems in India and the world. Three out of four montane cloud forest sites studied in the southern Western Ghats had experienced diminishing trends of seasonal average and total rainfall, especially during summer monsoon season. The highest level of reduction for summer monsoon season was observed at Gavi rainforest station (>20 mm/14 years) in Kerala followed by Venniyar (>20 mm/20 years) site in Tamil Nadu. Average annual and total precipitation increased during the study period irrespective of the seasons over Periyar area, and the greatest values were recorded for season 2 (>25 mm/28 years). Positive trends for winter monsoon rainfall has been observed for three stations (Periyar, High wavys and Venniyar) except Gavi, and the trend was positive and significant (90%) for Periyar and High wavys. Increase in summer monsoon rainfall was observed for Periyar site and the trend was found to be significant (95%).

Ab initio electronic structures of rhombohedral and cubic HgXO3 (X = Ti, Pb)

First-principles calculations were performed for orthorhombic HgO, rhombohedral and cubic phases of HgTiO3 (HTO) and HgPbO3 (HPO). The calculations show that in the rhombohedral phase HTO is a direct gap insulator with a gap of ~1.6 eV. The rhombohedral phase of HPO, on the other hand, shows a weak metallic character. The results provide an explanation for the electrical properties of these compounds. The cubic phases of HTO and HPO are invariably metallic in nature, thereby suggesting that for HTO the rhombohedral–cubic transition must also be accompanied by a change in the electrical state. Examination of the electronic density of states of these systems revealed no significant on-site mixing of Hg 5d and Hg 6s states in any of these materials.

Microbially induced flotation of galena and quartz from pyrite

Selective separation of pyrite from galena and quartz was achieved through microbiologically induced flotation in presence of Bacillus subtilis. B. subtilis functions as a depressant for pyrite while it promotes the flotation of galena and quartz. Bacterial extracellular protein (EP) was isolated and the protein profile of bacterial cells grown in presence and absence of minerals established.

Microbial aspects of acid generation and bioremediation with relevance to indian mining

The role of Acidithiobacillus group of bacteria in acid generation and heavy metal dissolution was studied with relevance to some Indian mines. Microorganisms implicated in acid generation such as Acidithiobacillus Acidithicibacillus thiooxidans and Leptospirillum ferrooxidans were isolated from abandoned mines, waste rocks and tailing dumps. Arsenite oxidizing Thiomonas and Bacillus group of bacteria were isolated and their ability to oxidize As (111) to As (V) established. Mine isolated Sulfate reducing bacteria were used to remove dissolved copper, zinc, iron and arsenic from solutions.

High-temperature heat capacity and heat content of CaCu3Ti4O12 (CCTO)

The isobaric heat capacity of CaCu3Ti4O12 (CCTO) was measured from 300 to 1100 K using differential scanning calorimetry (DSC). The results were verified using drop calorimetric measurement of enthalpy increment (H-T - H-298.15) at T= 973 and 1073 K. The samples were dropped from room temperature into a calorimeter maintained at high temperature. The results show small negative deviation from Neumann-Kopp rule. The enthalpy and entropy increments are computed as a function of temperature and compared with values available in the literature. The results obtained in this study are consistent with available information on enthalpy and Gibbs energy of formation of CCTO.

Phases in the (1-x)Na0.5Bi0.5TiO3-(x)CaTiO3 system

The structures of (1 - x) Na0.5Bi0.5TiO3-(x) CaTiO3 at room temperature have been investigated using neutron powder diffraction and dielectric studies. The system exhibits an orthorhombic (Pbnm) structure for x >= 0.15 and rhombohedral (R3c) for x <= 0.05. For x = 0.10, though the neutron diffraction pattern shows features of the orthorhombic (Pbnm) structure, Rietveld refinement using this structure shows a drastic reduction in the in-phase tilt angle (similar to 4 degrees) as compared to the corresponding value (similar to 8 degrees) for a neighbouring composition x = 0.15. The neutron diffraction pattern of x = 0.10 could be fitted equally well using a two-phase model (R3c + Pbnm) with orthorhombic as the minor phase (22%), without the need for a drastic decrease in the in-phase tilt angle. The dielectric studies of x = 0.10 revealed the presence of the polar R3c phase, thereby favouring the phase coexistence model, instead of a single-phase Pbnm structure, for this composition.

Influence of tool rake angle on the quality of pure magnesium chip-consolidated product

Chips were produced by orthogonal Cutting of cast pure magnesium billet with three different tool rake angles viz., -15 degrees, -5 degrees and +15 degrees on a lathe. Chip consolidation by solid state recycling technique involved cold compaction followed by hot extrusion. The extruded products were characterized for microstructure and mechanical properties. Chip-consolidated products from -15 degrees rake angle tools showed 19% increase in tensile strength, 60% reduction ingrain size and 12% increase in hardness compared to +15 degrees rake chip-consolidated product indicating better chip bonding and grain refinement. Microstructure of the fracture specimen Supports the abovefinding. On the overall, the present work high lights the importance of tool take angle in determining the quality of the chip-consolidated products. (C) 2009 Elsevier B.V. All rights reserved.

Mechanism of failure in a free-standing Pt-aluminide bond coat during tensile testing at room temperature

The room temperature (RT) tensile behaviour of a free-standing high activity Pt-aluminide bond coat has been evaluated by microtensile testing technique. The coating had a typical three-layer microstructure. The stress-strain plot for the free-standing coating was linear, indicating the coating to be brittle at RT. Different fracture features were observed across the coating layers, namely quasi-cleavage in the outer layer and inner interdiffusion zone, and cleavage in the intermediate layer. By employing interrupted tensile test and observing the cross-sectional microstructure of the tested specimens, it was determined that failure of the microtensile samples occurred by the initiation of a single crack in the intermediate layer of the coating and its subsequent inside-out propagation. Such a mechanism of failure has been explained in terms of the fracture features observed across the sample thickness. This mechanism of failure is consistent with fracture toughness values of the individual coating layers. (C) 2009 Elsevier B.V. All rights reserved.

Effect of recrystallization and grain growth on the mechanical properties of an extruded AZ21 Mg alloy

An experimental investigation into the effect of microstructural changes, which occur during post-extrusion annealing of a Mg based AZ21 alloy, on tensile and fatigue properties is conducted. Mechanical properties in the as-cast, as-extruded, and microstructural states that correspond to recovery, recrystallization and grain growth stages of annealing are compared. Results show that these microstructural changes do not alter the yield strength of the alloy markedly whereas significant differences were noted in the ultimate tensile strength as well as ductility. The initiation of abnormal grain growth (or secondary recrystallization) renders the tensile stress-strain response elastic perfectly plastic and results in a large drop in ductility, as high as similar to 60% during intermediate stages of abnormal grain growth, vis-A-vis the ductility of the as-extruded alloy. While the fatigue performance of all the wrought alloys is far superior to as expected, abnormal grain growth leads to a marked decrease in the endurance that of the as-cast alloy, limit. Possible microscopic origins of these are discussed. (C) 2009 Elsevier B.V. All rights reserved.

Effect of Bottom Bubbling Conditions on Surface Reaction Rate in Oxygen-Water System

In secondary steelmaking, the enhancement of the reaction rate in the low carbon period during the decarburization of steel is considered the most effective method to produce ultralow carbon steel. In a previous study, it was revealed that the surface reaction is dominant during the final stage of the actual refining process. In order to improve the surface reaction rate, it is necessary to enlarge the reaction region, which is usually achieved by increasing the plume eye area. In this study, water model experiments were carried out to estimate the influence of bottom stirring conditions on the gas-liquid reaction rate; for this purpose, the deoxidation rate during the bottom bubbling process was measured. Five types of nozzle configurations were used to study the effect of the plume eye area on the reaction rate at various gas flow rates. The results reveal that the surface reaction rate is influenced by the gas flow rate and the plume eye area. An empirical correlation was developed for the reaction rate and the plume eye area. This correlation was applied to estimate the gas-liquid reaction rate mat the bath surface.