Structure and properties of fibre reinforced zn-27% al alloy based cast MMCs

Metal matrix composites (MMCs) based on a zinc-27% aluminium alloy (ZA-27) were produced using a pressure infiltration technique. Preforms of alumina fibres and aluminosilicate fibres were used for reinforcement. Uniform distribution of fibres and satisfactory interfacial bonding were achieved. UTS, specific strength, hardness and wear resistance were improved significantly by the alumina fibre reinforcement, but UTS decreased when using aluminosilicate fibres for reinforcement mainly due to unavoidable clustering of particles in the fibre preforms. Structure-property relations have been analysed in all cases.

Transport properties, structure, and radiation induced defect studies in amorphous carbon films

Amorphous conducting carbon films are prepared by plasma assisted chemical vapour deposition and their d.c. conductivity (similar to 100 Scm(-1)) is studied from 300K down to 4.2K. The films were irradiated by high energy ion beam(I+13, 170 MeV) with a dose of 10(13) ions/cm(2). As a result a marked decrease in conductivity by two to three orders in magnitude was observed. The structural changes and the defects in the films caused by ion irradiation are studied using photoluminescence, persistent photoconductivity, and ESR spectroscopy.

X-ray-reflectivity study of Ge-Si-Ge films

Here we report on an x-ray specular reflectivity study of Ce-Si-Ge trilayers grown on Si(001) single-crystal substrate by ion beam sputtering deposition at various substrate temperatures. The electron-density profile of the trilayer as a function of depth, obtained from x-ray-reflectivity data, reveals an intermixing of Si and Ge. The x-ray-reflectivity data have been analyzed using a scheme based on the distorted-wave Born approximation, and the validity of the analysis scheme was checked using simulated data. Analyzed results provided information regarding interdiffusion in this system. We notice that although the Si-on-Ge interface is sharp, a Si0.4Ge0.6 alloy is formed at the Ge-on-Si interface.

Enhanced magnetoresistance in as?deposited oxygen?deficient La0.6Pb0.4MnO3-y thin films

The La0.6Pb0.4MnO3(LPMO) thin films were in situ deposited at different oxygen partial pressure and at a substrate temperature of 630 degrees C by pulsed laser deposition. The films grown at lower oxygen partial pressures showed an increase in lattice parameter and resistivity and a decrease in the insulator-metal transition temperature as compared to the stoichiometric LPMO thin film grown at 400 mTorr. Further, these oxygen-deficient thin films showed over 70% giant magnetoresistance (GMR) near the insulator-metal transition temperature against the 40% GMR in the case of stoichiometric thin films. (C) 1995 American Institute of Physics.

Ferroelectric properties of Bi2VO5.5 thin films on LaAlO3 and SiO2/Si substrates with LaNiO3 base electrode

Ferroelectric bismuth vanadate Bi2VO5.5 (BVO) thin films have been grown on LaAlO3 (LAO) and SiO2/Si substrates with LaNiO3 (LNO) base electrodes by the pulsed laser deposition technique. The effect of substrate temperature on the ferroelectric properties of BVO thin films, has been studied by depositing the thin films at different temperatures. The BVO thin films grown on LNO/LAO were textured whereas the thin films grown on LNO/SiO2/Si were polycrystalline. The BVO thin films grown at 450?°C exhibited good ferroelectric properties indicating that LNO acts as a good electrode material. The remanent polarization Pr and coercive field Ec obtained for the BVO thin films grown at 450?°C on LNO/LAO and LNO/SiO2/Si were 2.5 ?C/cm2, 37 kV/cm and 4.6?C/cm2, 93 kV/cm, respectively. © 1995 American Institute of Physics.

Orientational disorder and other aspects of C70 and C60-C70 films deposited on single-crystal substrates

C-70 films deposited on highly oriented pyrolytic graphite (HOPG), Ag(110), Ag(111) and Pt(110) substrates have been investigated by scanning tunnelling microscopy. Interesting observations on novel molecular arrangements, as well as orientational disorder, are presented. Solid solutions of C-60 and C-70 show interesting packing of these molecules when deposited on HOPG.

Oriented ferroelectric thin films of PbTiO3, (Pb,La)TiO3, and Pb(Zr,Ti)O3 by nebulized spray pyrolysis

Nebulized spray pyrolysis provides a good low?temperature chemical route for preparing thin films of PbTiO3, (Pb0.9,La0.1)TiO3 and Pb(Zr0.52,Ti0.48)O3. The films are a? or c? axis oriented, with spherical grains of ?30 nm and give satisfactory P?E hysteresis loops. © 1995 American Institute of Physics.

Oriented films of LaNiO3 and other members of the Lan+1NinO3n+1 series, LaCuO3−δ and Pb(Zr0.52Ti0.48)O3, obtained by nebulized spray pyrolysis

The technique of nebulized spray pyrolysis has been explored to find out whether oriented films of certain important oxides can be produced on single-crystal substrates by this relatively gentle method. Starting with acetylacetonate precursors, oriented films of metallic LaNiO3 containing nearly spherical grains (30 nm) have been obtained. Films of near-stoichiometric La4Ni3O10 and La3Ni2O7 showing metallic conductivity have been obtained by this method. This is indeed gratifying since it is difficult to prepare monophasic and stoichiometric bulk samples of these materials. Films of La2NiO4 show the expected semiconducting behavior. In the La-Cu-O system, starting with acetylacetonates, we have obtained films mainly comprising semiconducting La2Cu2O5, which is generally difficult to prepare in bulk form. More interestingly, nebulized spray pyrolysis gives excellent stoichiometric films of Pb(Zr0.52Ti0.48)O-3 consisting of nearly spherical grains (30 nm) which show ferroelectric behavior. The present investigation demonstrates that nebulized spray pyrolysis provides a useful and desirable route to deposite oriented films of complex oxide materials on single-crystal substrates.

Rapid thermal processed thin films of niobium pentoxide (Nb2 O5) deposited by reactive magnetron sputtering

Niobium pentoxide thin films have been deposited on silicon and platinum-coated silicon substrates by reactive magnetron sputtering. The as-deposited films were amorphous and showed good electrical properties in terms of a dielectric permittivity of about 30, and leakage current density of 10(-6) A cm(-2) al a field of 120 kV cm(-1). A rapid thermal annealing process at 800 degrees C further increased the dielectric constant to 90 and increased the leakage current density to 5 x 10(-6) A cm(-2). The current-voltage characteristics observed at low and high fields suggested a combination of phenomena at different regimes of applied electric field. The capacitance-voltage characteristics performed in the metal-insulator-semiconductor configuration indicated good electronic interfaces with a nominal trap density of 4.5 x 10(12) cm(-2) eV(-1), which is consistent with the behavior observed with conventional dielectrics such as SiO2 on silicon surfaces.

Rapid thermal processed thin films of reactively sputtered Ta2O5

Rapid thermal processed thin films of reactively sputtered tantalum pentoxide Ta2O5 thin films have been deposited on silicon and platinum coated silicon substrates by reactive magnetron sputtering. The as-deposited films were amorphous and showed good electrical properties in terms of a dielectric permittivity of about 24 and leakage current density of 9 x 10(-8) A cm(-2). A rapid thermal annealing process at temperatures above 700 degrees C crystallized the films, increased the dielectric relative permittivity, and decreased the leakage current. The dielectric constant for a film rapidly annealed at 850 degrees C increased to 45 and its leakage current density lowered to 2 x 10(-8) A cm(-2). The dielectric measurements in the MIS configuration showed that Ta2O5 might be used as a dielectric material instead of SiO2 or Si3N4 for integrated devices. The current voltage characteristics observed at low and high fields suggested different conduction mechanisms.

Reactive magnetron co?sputtered antiferroelectric lead zirconate thin films

Antiferroelectric lead zirconate thin films were formed on platinum coated silicon substrates by a reactive magnetron co-sputtering method. The films showed (240) preferred orientation. The crystallization temperatures and the preferred orientation were affected by the lead content in the films. The electric field forced transformation from the antiferroelectric phase to the ferroelectric phase was observed at room temperature with a maximum polarization value of 36 mu C/cm(2). The average field to excite the ferroelectric state and that for the reversion to the antiferroelectric state were 267 and 104 kV/cm respectively. (C) 1995 American Institute of Physics.

Structural ordering of diamond like carbon films by applied electric field

Diamond like carbon films deposited by RF magnetron sputter deposition technique contain both SP2 and SP3 hybridized carbons. These films are structurally disordered and inhomogeneous. By the application of electric field across the film, these films are transformed to a more orderly structured diamond like carbon, bringing homogenity in the film. This transformation has resulted in the increase of the reflectivity of the metal(Aluminum), which is used as one of the electrodes for applying the electric field, by 5 times.

Structure and composition related properties of titania thin films

The dependence of optical constants, structure and composition of titania thin films on the process parameters has been investigated. Films were deposited using both reactive electron beam evaporation and ion Assisted Deposition(IAD). If has been observed that the refractive index of IAD films is higher than that for the reactively deposited films, without much difference in the extinction coefficient. Electron paramagnetic resonance has been used to estimate qualitatively the presence of non-stoichiometry in the films. It has been found that these spectra correlate very well the optical behaviour of the films. X-ray diffraction studies revealed that the neutral oxygen deposited films were stress free, while the IAD films showed tensile stress. The lattice parameters showed anisotropic change with ion beam parameters.

Surface resistance and residual losses of Ag?doped YBa2Cu3O7?? thin films on sapphire

High?quality Ag?doped YBa2Cu3O7?? thin films have been grown by laser ablation on R?plane ?1102? sapphire without any buffer layer. Thin films have been found to be highly c?axis oriented with Tc=90 K, transition width ?T?1 K, and transport Jc=1.2×106 A?cm?2 at 77 K in self?field conditions. The microwave surface resistance of these films measured on patterned microstrip resonators has been found to be 530 ?? at 10 GHz at 77 K which is the lowest reported on unbuffered sapphire. Improved in?plane epitaxy and reduced reaction rate between the substrate and the film caused due to Ag in the film are believed to be responsible for this greatly improved microwave surface resistance. © 1995 American Institute of Physics.