Copper Diffusion Barrier Deposition on Integrated Circuit Devices by Atomic Layer Deposition Technique

Transfer from aluminum to copper metallization and decreasing feature size of integrated circuit devices generated a need for new diffusion barrier process. Copper metallization comprised entirely new process flow with new materials such as low-k insulators and etch stoppers, which made the diffusion barrier integration demanding. Atomic Layer Deposition technique was seen as one of the most promising techniques to deposit copper diffusion barrier for future devices. Atomic Layer Deposition technique was utilized to deposit titanium nitride, tungsten nitride, and tungsten nitride carbide diffusion barriers. Titanium nitride was deposited with a conventional process, and also with new in situ reduction process where titanium metal was used as a reducing agent. Tungsten nitride was deposited with a well-known process from tungsten hexafluoride and ammonia, but tungsten nitride carbide as a new material required a new process chemistry. In addition to material properties, the process integration for the copper metallization was studied making compatibility experiments on different surface materials. Based on these studies, titanium nitride and tungsten nitride processes were found to be incompatible with copper metal. However, tungsten nitride carbide film was compatible with copper and exhibited the most promising properties to be integrated for the copper metallization scheme. The process scale-up on 300 mm wafer comprised extensive film uniformity studies, which improved understanding of non-uniformity sources of the ALD growth and the process-specific requirements for the ALD reactor design. Based on these studies, it was discovered that the TiN process from titanium tetrachloride and ammonia required the reactor design of perpendicular flow for successful scale-up. The copper metallization scheme also includes process steps of the copper oxide reduction prior to the barrier deposition and the copper seed deposition prior to the copper metal deposition. Easy and simple copper oxide reduction process was developed, where the substrate was exposed gaseous reducing agent under vacuum and at elevated temperature. Because the reduction was observed efficient enough to reduce thick copper oxide film, the process was considered also as an alternative method to make the copper seed film via copper oxide reduction.

Radical Enhanced Atomic Layer Deposition of Metals and Oxides

Atomic Layer Deposition (ALD) is a chemical, gas-phase thin film deposition method. It is known for its ability for accurate and precise thickness control, and uniform and conformal film growth. One area where ALD has not yet excelled is film deposition at low temperatures. Also deposition of metals, besides the noble metals, has proven to be quite challenging. To alleviate these limitations, more aggressive reactants are required. One such group of reactants are radicals, which may be formed by dissociating gases. Dissociation is most conveniently done with a plasma source. For example, dissociating molecular oxygen or hydrogen, oxygen or hydrogen radicals are generated. The use of radicals in ALD may surmount some of the above limitations: oxide film deposition at low temperatures may become feasible if oxygen radicals are used as they are highly reactive. Also, as hydrogen radicals are very effective reducing agents, they may be used to deposit metals. In this work, a plasma source was incorporated in an existing ALD reactor for radical generation, and the reactor was used to study five different Radical Enhanced ALD processes. The modifications to the existing reactor and the different possibilities during the modification process are discussed. The studied materials include two metals, copper and silver, and three oxides, aluminium oxide, titanium dioxide and tantalum oxide. The materials were characterized and their properties were compared to other variations of the same process, utilizing the same metal precursor, to understand what kind of effect the non-metal precursor has on the film properties and growth characteristics. Both metals were deposited successfully, and silver for the first time by ALD. The films had low resistivity and grew conformally in the ALD mode, demonstrating that the REALD of metals is true ALD. The oxide films had exceptionally high growth rates, and aluminium oxide grew at room temperature with low cycle times and resulted in good quality films. Both aluminium oxide and titanium dioxide were deposited on natural fibres without damaging the fibre. Tantalum oxide was also deposited successfully, with good electrical properties, but at slightly higher temperature than the other two oxides, due to the evaporation temperature required by the metal precursor. Overall, the ability of REALD to deposit metallic and oxide films with high quality at low temperatures was demonstrated.

Atomic Layer Deposition of Multicomponent Oxide Materials

Atomic layer deposition (ALD) is a method for thin film deposition which has been extensively studied for binary oxide thin film growth. Studies on multicomponent oxide growth by ALD remain relatively few owing to the increased number of factors that come into play when more than one metal is employed. More metal precursors are required, and the surface may change significantly during successive stages of the growth. Multicomponent oxide thin films can be prepared in a well-controlled way as long as the same principle that makes binary oxide ALD work so well is followed for each constituent element: in short, the film growth has to be self-limiting. ALD of various multicomponent oxides was studied. SrTiO3, BaTiO3, Ba(1-x)SrxTiO3 (BST), SrTa2O6, Bi4Ti3O12, BiTaO4 and SrBi2Ta2O9 (SBT) thin films were prepared, many of them for the first time by ALD. Chemistries of the binary oxides are shown to influence the processing of their multicomponent counterparts. The compatibility of precursor volatilities, thermal stabilities and reactivities is essential for multicomponent oxide ALD, but it should be noted that the main reactive species, the growing film itself, must also be compatible with self-limiting growth chemistry. In the cases of BaO and Bi2O3 the growth of the binary oxide was very difficult, but the presence of Ti or Ta in the growing film made self-limiting growth possible. The application of the deposited films as dielectric and ferroelectric materials was studied. Post-deposition annealing treatments in different atmospheres were used to achieve the desired crystalline phase or, more generally, to improve electrical properties. Electrode materials strongly influenced the leakage current densities in the prepared metal insulator metal (MIM) capacitors. Film permittivities above 100 and leakage current densities below 110-7 A/cm2 were achieved with several of the materials.