Using the finite-difference-time-domain method, the near-field optical distribution and properties of Sb thin film thermal lens are calculated and simulated. The results show as follows. Within the near-field distance to the output plane of thermal lens, the spot size is approximately 100 nm, and its intensity is greatly enhanced, which is higher than that of incident light. The spot shape gradually changes from ellipse to round at the distance of more than 12 nm to the output plane. The above-simulated results are further demonstrated by the static optical recording experiment. (C) 2005 American Institute of Physics.

应用离子后处理技术提高薄膜激光损伤阈值

利用电子束热蒸发方法在K9玻璃基底上沉积氧化锆薄膜,并对其中一些样品用低能O2^+进行了后处理.采用表面热透镜技术测量薄膜样品表面弱吸收,采用显微镜观察样品离子后处理前后的显微缺陷密度.测试结果表明:经离子后处理样品表面的缺陷密度从18.6/mm^2降低到6.2/mm^2,且其激光损伤阈值从15.9 J/cm^2提高到23.1 J/cm^2,样品的平均吸收率从处理前的1.147×10^-4降低到处理后的9.56×10^-5.通过对处理前后样品的表面微缺陷密度、吸收率及损伤形貌等的分析发现:离子后处理可以降

表面热透镜薄膜吸收测量灵敏度提高方法

为提高表面热透镜薄膜吸收测量仪的灵敏度，在表面热透镜衍射理论基础上，通过数值模拟给出了探测激光腰斑半径、探测激光腰斑到样品表面距离、样品到探测光纤端面距离等仪器参数的优化方法．经优化调整后该仪器能达到优于0．1ppm量级的薄膜吸收率测量灵敏度．

表面热透镜技术应用于薄膜微弱吸收测量的理论和实验

由薄膜表面光热形变简化理论和表面热透镜衍射理论导出表面热透镜信号表达式,从理论上证明了表面热透镜信号和薄膜吸收率的线性关系.应用表面热透镜技术研制了薄膜吸收测量仪,测量结果表明其吸收率测量灵敏度和精度均达10-6量级.

The intensity distribution and thermal stability of InnoSlab laser

Partially end-pumped slab laser is an innovative solid state laser, namely InnoSlab. Combining the hybrid resonator with partially end-pumping, the output power can be scaled with high beam quality. In this paper, the output intensity distributions are simulated by coordinate transformation fast Fourier transform (FFT) algorithm, comparing the thermal lens influence. As the simulated curves showed, the output mode is still good when the thermal lens effect is strong, indicating the good thermal stability of InnoSlab laser. Such a new kind of laser can be designed and optimized on the base of this simulation.

Thermal lensing effect in ridge structure InGaN multiple quantum well laser diodes

Time-resolved light-current curves, spectra, and far-field distributions of ridge structure InGaN multiple quantum well laser diodes grown on sapphire substrate are measured with a temporal resolution of 0.1 ns under a pulsed current condition. Results show that the thermal lensing effect clearly improves the confinement of the higher order modes. The thermal lens leads to a lower threshold current for the higher order modes, a higher slope efficiency, and a change in the lasing mode of the device. The threshold current for the higher modes decreases by about 5 mA in every 10 ns in a pulse, and the slope efficiency increases by 7.5 times on the average when higher modes lase. (c) 2006 American Institute of Physics.

Influence of processing medium on frictional wear properties of ball bearing steel prepared by laser surface melting coupled with bionic principles

Coupling with bionic principles, an attempt to improve the wear resistance of ball bearing steel (GCr15) with biomimetic units on the surface was made using a pulsed Nd: YAG laser. Air and water film was employed as processing medium, respectively. The microstructures of biomimeitc units were examined by scanning electron microscope and X-ray diffraction was used to describe the microstructure and identify the phases as functions of different mediums as well as water film with different thicknesses. The results indicated that the microstructure zones in the biomimetic specimens processed with water film were more refined and had better wear resistance increased by 55.8% in comparison with that processed in air; a significant improvement in microhardness was achieved by laser surface melting. The application of water film provided considerable microstructural changes and much more regular grain shape in biomimetic units, which played a key role in improving the wear resistance of ball bearing steel. (c) 2010 Elsevier B.V. All rights reserved.

梯度补偿法控温晶体的高功率绿光激光器

研究了平均功率超过30 W的稳定高效全固态绿光激光器,分析得出影响全固态腔内倍频激光器倍频效率和输出稳定性的主要因素是倍频晶体局部温升造成的相位失配和热透镜效应,采用温度梯度补偿控温法对大尺寸倍频晶体进行温度控制,降低激光器工作中倍频晶体内外温度梯度从而有效地克服因晶体局部温升造成的倍频相位匹配角失配和热透镜效应。采用三条60 W的半导体激光二极管阵列板条侧面抽运Nd:YAG激光增益介质棒,采用声光调Q,平凹直腔和腔内倍频结构配合温度梯度补偿控温法对大尺寸倍频晶体进行温度控制,得到了稳定高效的532 nm

激光二极管端面抽运Nd∶YVO4固体激光器热致光束畸变非对称的平衡

由于a轴切割Nd∶YVO4晶体的非对称性,使得激光二极管(LD)端面抽运Nd∶YVO4固体激光器不同于Nd∶YAG激光器,输出的激光经常产生非对称结果。用有限元法分析激光二极管端面抽运a轴切割Nd∶YVO4固体激光器的晶体热效应,包括温度分布、内部应力和产生的形变。分析结果表明端面抽运a轴切割Nd∶YVO4晶体产生了椭球热透镜效应。从结构方面和抽运方面提出了热透镜非对称性的平衡方法,实验验证了方法的可行性。

机载测深激光雷达千赫兹全固态激光器设计及特性研究

将千赫兹高功率全固态Nd：YAG激光器的增益介质当作厚透镜处理，使用矩阵的方法对等效热透镜腔进行分析。采用多条半导体激光列阵侧向紧凑抽运结构设计，提高了增益介质光抽运的均匀性。根据实际抽运功率，通过模拟计算，设计了平凸非稳腔。选择的凸面全反镜的最佳曲率半径有效地补偿了增益介质热透镜效应，激光器实现了动态稳腔运转，激光脉冲能量输出斜度效率大于13％，光束发散角优于1.3mrad。

高功率高重复频率全固态激光器热透镜效应补偿与分析

将kHz高功率固体激光器增益介质当作厚透镜处理，建立了热透镜效应分析的理论模型，使用矩阵的方法对等效热透镜腔进行分析。对增益介质抽运均匀性进行了改善，通过分析模拟计算结果。设计了混合非稳腔结构，选择了最佳凸面镜曲率半径对热透镜效应进行补偿。试验结果表明，补偿效果明显，kHz高功率全固态激光器的光束发散角优于1．3mrad。

热畸变对单板条热容激光器输出的影响

开展了激光二极管(LD)抽运的全固态热容激光器的理论与实验研究, 数值模拟了在热容工作条件下侧面抽运的Nd:YAG板条激光器的热透镜效应, 分析了热透镜效应对激光输出的影响, 并进行了相应的实验论证。实验中采用的晶体尺寸为57 mm×40 mm×4 mm, 激光二极管阵列的抽运峰值功率为12 kW, 重复频率为1 kHz, 占空比为20%, 为了获得较高的增益, 将抽运光通过光学系统进行聚焦, 抽运光在晶体侧面的光斑大小为15 mm×57 mm。实验中观察了1 s内的脉冲能量输出的波动情况, 在开始工作的

热退偏损耗完全补偿的千赫兹电光调QNd:YAG激光器

为了同时补偿固体增益介质的热致双折射及热透镜效应,进一步提高重复频率1 kHz激光二极管(LD)侧向抽运高平均功率电光调Q Nd:YAG激光器的输出功率,设计了一种完全消除热退偏损耗的双调Q开关谐振腔结构,此结构在传统调Q谐振腔的基础上沿着偏振片的退偏方向增加了一个调Q谐振支路,并使得激光从增益介质方向输出。实验结果表明,此激光器的单脉冲能量比单Q开关结构的非补偿腔输出能量高出74.7%。当侧面抽运的激光二极管输出脉冲能量达到307 mJ时,激光输出能量达到26.2 mJ,光-光转换效率为8.5%,光束发