The influence of hard-segments on two-phase structure and shape memory properties of PCL-based segmented polyurethanes

Poly(epsilon-caprolactone)-based segmented polyurethanes (PCLUs) were prepared from poly(epsilon-caprolactone) diol, diisocyanates (DI), and 1,4-butanediol. The DIs used were 4,4'-diphenylmethane diisocyanate (MDI), 2,4-toluenediisocyanate (TDI), iso-phorone diisocyanate (IPDI), and hexamethylene diisocyanate (HDI). Differential scanning calorimetry, small-angle X-ray scattering, and dynamic mechanical analysis were employed to characterize the two-phase structures of all PCLUs. It was found that HDI- and MDI-based PCLUs had higher degree of microphase separation than did IPDI- and TDI-based PCLUs, which was primarily due to the crystallization of HDI- and MDI-based hard-segments. As a result, the HDI-based PCLU exhibited the highest recovery force up to 6 MPa and slowest stress relaxation with increasing temperature. Besides, it was found that the partial damage in hard-segment domains during the sample deformation was responsible for the incomplete shape-recovery of PCLUs after the first deformation, but the damage did not develop during the subsequent deformation.

A Smart Frequency Presetting Technique for Fast Lock-in LC-PLL Frequency Synthesizer

This paper proposes a smart frequency presetting technique for fast lock-in LC-PLL frequency synthesizer. The technique accurately presets the frequency of VCO with small initial frequency error and greatly reduces the lock-in time. It can automatically compensate preset frequency variation with process and temperature. A 2.4GHz synthesizer with 1MHz reference input was implemented in 0.35 mu m CMOS process. The chip core area is 0.4mm(2). Output frequency of VCO ranges from 2390 to 2600MHz. The measured results show that the typical lock-in time is 3 mu s. The phase noise is -112dBc/Hz at 600KHz offset from center frequency. The test chip consumes current of 22mA that includes the consumption of the I/O buffers.

SYNTHESIS AND CHARACTERIZATION OF A CROSSLINKING POLYETHYLENIMINE AS SMART GENE CARRIER AND EFFECTS OF PEGYLATION DEGREE

A smart biodegradable cationic polymer (CBA-PEI) based on the disulfide bond-containing cross-linker cystamine bisacrylamide (CBA) and low molecular weight branched polyethylenimine (1800-Da, PEI1800) was successfully synthesized by Michael addition reaction in our recent study. Furthermore, a series of copolymers (CBA-PEI-PEG) with different PEGylation degree were obtained by the mPEG-SPA (5000-Da) reacting with CBA-PEI at various weight ratios directly. The molecular structures of the resulting polymers CBA-PEI and CBA-PEI-PEG were evaluated by nuclear magnetic resonance spectroscopy (H-1-NMR) and capillary viscosity measurements, all of which had successfully verified formation of the copolymers. The polymer/DNA complexes based on CBA-PEI and CBA-PEI-PEG were measured by dynamic light scattering and gel retardation assay. The results showed that the particle size and zeta potential of complexes were reduced with increasing amount of PEG grafting, even no particle formation. The particle size of CBA-PEI/DNA complexes was in range of 103.1 to 129.1 nm, and the zeta potential was in range of 14.2 to 24.3 mV above the 2:1 weight ratio. In the same measure condition, the particle size of CBA-PEI-PEG complexes was reduced to a range of 32.2 to 55 nm, and the zeta potential was in range of 9.3 to 13.8 mV at the 2:1 weight ratio.