Role of amorphous silicon domains on Er3+ emission in the Er-doped hydrogenated amorphous silicon suboxide film

An investigation on the correlation between amorphous Si (a-Si) domains and Er3+ emission in the Er-doped hydrogenated amorphous silicon suboxide (a-Si:O:H) film is presented. On one hand, a-Si domains provide sufficient carriers for Er3+ carrier-mediated excitation which has been proved to be the highest excitation path for Er3+ ion; on the other hand, hydrogen diffusion from a-Si domains to amorphous silicon oxide (a-SiOx) matrix during annealing has been found and this possibly decreases the number of nonradiative centres around Er3+ ions. This study provides a better understanding of the role of a-Si domains on Er3+ emission in a-Si:O:H films.

Microstructure of GaN films grown on Si(111) substrates by metalorganic chemical vapor deposition

We report the transmission electron microscopy (TEM) study of the microstructure of wurtzitic GaN films grown on Si(I I I) substrates with AlN buffer layers by metalorganic chemical vapor deposition (MOCVD) method. An amorphous layer was formed at the interface between Si and AlN when thick GaN film was grown. We propose the amorphous layer was induced by the large stress at the interface when thick GaN was grown. The In0.1Ga0.9N/GaN multiple quantum well (MQW) reduced the dislocation density by obstructing the mixed and screw dislocations from passing through the MQW. But no evident reduction of the edge dislocations by the MQW was observed. It was found that dislocations located at the boundaries of grains slightly in-plane misoriented have screw component. Inversion domain is also observed. (C) 2003 Elsevier B.V. All rights reserved.

The growth of SiC on Si substrates with C2H4 and Si2H6

SiC was grown on Si (100) substrates oriented and off-oriented by 2-5 degrees towards [011] with simultaneous supply of C2H4 and S2H6 at 1050 degrees C. SiC formed during removal of oxide could be removed at 1150 degrees C. Twinned growth occurred on both oriented and off-oriented substrates during carbonization, but fewer twins formed on the off-oriented substrate than that on the oriented substrate. In SiC growth process, twinned growth continued on the off-oriented substrate whereas twinned growth stopped and single crystal SiC with double-domain (2 x 1) superstructure formed on the oriented substrate. SiC single crystal could grow on a carbonized twinned buffer layer. Obvious SiC LO and TO phonon modes were observed with Raman spectroscopy in the epilayer grown on the oriented substrate. The surface of the epilayer grown on the oriented substrate was smooth, while there was a high density of islands on the epilayer grown on the off-oriented substrate. The film grown on the oriented substrate is superior than that grown on the off-oriented substrate. (C) 1999 Elsevier Science B.V. All rights reserved.