Fabrication of Nano-structured VOx Film by Low Temperature Ion Beam Sputtering and Reductive Annealing

VOx thin films have been fabricated by low temperature ion beam sputtering and post reductive annealing process. Semiconductor-metal phase transition is observed for the film annealed at 400 degrees C for 2 hours. The film also shows a polycrystal structure with grain size from 50nm to 150nm. The VOx thin films fabricated by this process have a TCR up to -2.7% at room temperature. Our results indicate a promising fabrication method of the nano-structured VOx film with relatively high TCR and semiconductor-metal phase transition.

Study of thin-film SO2 gas sensors by photometric and ellipsometric methods

Pt-, Pd-, and Zr-doped SnO2 thin films and dopant-free VOx films were fabricated by planar magnetron sputtering. Tests for sensitivity to SO2 for all samples were conducted at 180 degreesC, and the sensitivities were investigated ex situ with photometric and ellipsometric methods at room temperature. It was found that the optical sensitivities as well as the sensitive wavelength region for SnO2 films could be tuned by doping. The Pd-doped SnO2 films had good sensitivity in the visible range, and the Zr-doped in the near IR. The dominant sensitive wavelength region for VOx films fell into the visible range, and the ratio of the sensitivity in the visible to that in the near IR increased with O-2/Ar in the depositing atmosphere. (C) 2001 society of Photo-Optical instrumentation Engineers .

Fabrication and Infrared Optical Properties of Nano Vanadium Dioxide Thin Films

Vanadium dioxide thin films were fabricated by ion beam sputtering on Si3N4/SiO2/Si after a post reductive annealing process in a nitrogen atmosphere. X-ray Diffraction (XRD), scanning electron microscope (SEM), and X-ray photoelectron spectroscopy (XPS) were employed to analyze the effects of post annealing temperature on crystallinity, morphology, and composition of the vanadium oxide thin films. Transmission properties of vanadium dioxide thin films were measured by Fourier transform-infrared (FT-IR) spectroscopy. The results showed that the as-deposited vanadium oxide thin films were composed of non-crystalline V2O5 and a tetragonal rutile VO2. After annealing at 400 degrees C for 2 h, the mixed phase vanadium oxide (VOx) thin film changed its composition and structure to VO2 and had a (011) oriented monoclinic rutile structure. When increasing the temperature to 450 degrees C, nano VO2 thin films with smaller grains were obtained. FT-IR results showed that the transmission contrast factor of the nano VO2 thin film was more than 0.99 and the transmission of smaller grain nano VO2 thin film was near zero at its switched state. Nano VO2 thin film with smaller grains is an ideal material for application in optical switching devices.

Low Temperature Deposited Nano-structured Vanadium Oxide Thin Films for Uncooled Infrared Detectors

A novel process of room temperature ion beam sputtering deposition of vanadium oxide films and low temperature post annealing for uncooled infrared detectors was proposed in this work. VOx thin films with relatively low square resistance (70 K Omega / square) and large temperature coefficient of resistance (more than 3%/K) at room temperature were fabricated using this low temperature process which was very compatible with the process of uncooled infrared detectors based on micromachined technology. Furthermore, chemical composition and film surface have been characterized using X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) respectively. The results showed that the main composition of the processed thin films was V2O5 and the thin films were in the process of crystallization.