The Surface Modification of Hydroxyapatite Nanoparticles by the Ring Opening Polymerization of gamma-Benzyl-L-glutamate N-carboxyanhydride

The surface modification of hydroxyapatite (HA) nanoparticles by the ring opening polymerization (ROP) of gamma-benzyl-L-glutamate N-carboxyanhydride (BLG-NCA) was proposed to prepare the poly(gamma-benzyl-L-glutamate) (PBLG)-grafted HA nanoparticles (PBLG-g-HA) for the first time. HA nanoparticles were firstly treated by 3-aminopropylthriethoxysilane (APS) and then the terminal amino groups of the modified HA particles initiated the ROP of BLG-NCA to obtain PBLG-g-HA. The process was monitored by XPS and FT-IR. The surface grafting amounts of PBLG on HA ranging from 12.1 to 43.1% were characterized by thermal gravimetric analysis (TGA). The powder X-ray diffraction (XRD) analysis confirmed that the ROP only underwent on the surface of HA nanoparticles without changing its bulk properties. The SEM measurement showed that the PBLG-g-HA hybrid could form an interpenetrating net structure in the self-assembly process.

Surface-grafted silica linked with L-lactic acid oligomer: A novel nanofiller to improve the performance of biodegradable poly(L-lactide)

A new surface modification method by grafting L-lactic acid oligomer onto the surface silanol groups of silica nanoparticles has been developed. The surface-grafting reaction is confirmed by IR and Si-29 MAS NMR analyses. TEM and SEM results show that grafted SiO2 (g-SiO2) nanoparticles can be comparatively uniformly dispersed in chloroform or PLLA matrix, while the unmodified SiO2 nanoparticles tend to aggregate. The loading of g-SiO2 nanoparticles in poly(L-lactide) (PLLA) matrix greatly improves the toughness and tensile strength of this material. In contrast, the incorporation of un-grafted SiO2 nanoparticles into PLLA leads to the deterioration of its mechanical properties. DSC analysis shows that g-SiO2 nanoparticles can serve as a nucleating agent for the crystallization of PLLA in the composites. SEM characterization shows the tough characteristics and great interfacial combination strength for g-SiO2 (5wt%)/PLLA nanocomposites.

Grafting polymerization of L-lactide on the surface of hydroxyapatite nano-crystals

A novel method of grafting ring-opening polymerization of L-lactide (LLA) onto the surface of hydroxyapatite nano-particles (n-HAP) was developed. PLLA was directly connected onto the HAP surface through a chemical linkage. The PLLA-g-HAP particles could be stably dispersed in organic solvent such as chloroform for several weeks. The n-HAP particles still retained the original dimension and shape after the grafting of PLLA. Compared with the P-31 MAS-NMR spectrum of pure HAP powders, there appeared a downfield displacement of 1.2 ppm in the spectrum of PLLA-g-HAP. Fourier transformation infrared (FT-IR) spectra further confirmed the existence of PLLA on the surface of PLLA-g-HAP. The amount of grafted polymer determined by thermal gravimetric analysis (TGA) was about 6% in weight. The tensile strength and elongation at break of the PLLA/PLLA-g-HAP composite containing 8 wt% of PLLA-g-HAP were 55 MPa and about 10-13%, respectively, while those of the PLLA/n-HAP composites were 40 MPa and 3-5%, respectively.

Grafting of diaminoalkane on glassy carbon surface and its functionalization

Diaminoalkanes (NH2(CH2)(n)NH2, n = 7,10,12) were grafted onto a glassy carbon electrode (GCE) surface by amino cation radical formed during electrooxidation of amino group. The presence of diamine grafted layer at the GCE is demonstrated by X-ray photoelectron spectroscopy. The effect of the grafted layer at the GCE surface on the redox responses of Ru(NH3)(6)(3+) and Fe(CN)(6)(3-) redox probes has been investigated. Electrochemical impedance experiments indicate that the kinetics of electron transfer are slowed down when the scan rate taken to modify the GCE is low, and that diaminoalkane with longer alkyl-chain used has higher blocking characteristics. The amine-functionalized GCE is versatile not only to further covalently immobilize ferrocene acetic acid via carbodiimide coupling, but also as a charge-rich substrate to successfully adsorb heteropolyanion P2W18 in acidic solution by electrostatic interaction. (C) 2000 Elsevier Science S.A. All rights reserved.

Surface modification of bioactive glass nanoparticles and the mechanical and biological properties of poly(L-lactide) composites

Novel bioactive glass (13G) nanoparticles/poly(L-lactide) (PLLA) composites were prepared as promising bone-repairing materials. The BG nanoparticles (Si:P:Ca = 29:13:58 weight ratio) of about 40 run diameter were prepared via the sol-gel method. In order to improve the phase compatibility between the polymer and the inorganic phase, PLLA (M-n = 9700 Da) was linked to the surface of the BG particles by diisocyanate. The grafting ratio of PLLA was in the vicinity of 20 wt.%. The grafting modification could improve the tensile strength, tensile modulus and impact energy of the composites by increasing the phase compatibility.

Grafting BSA onto poly[(L-lactide)-co-carbonate] microspheres by click chemistry

Model protein bovine serum albumin (BSA) was covalently grafted onto poly[(L-lactide)co-carbonate] microsphere surfaces by "click chemistry." The grafting was confirmed by confocal laser scanning microscopy and X-ray photoelectron spectroscopy. The maximum amount of surface-grafted BSA was 45 mg.g(-1). The secondary structure of the grafted BSA was analyzed by FTIR and the results demonstrated that the grafting did not affect protein structure. This strategy can also be used on microspheres prepared from poly(L-lactide)/poly[(L-lactide)-co-carbonate] blend materials.

Microphase Separation of Mixed Polymer Brushes: Dependence of the Morphology on Grafting Density, Composition, Chain-Length Asymmetry, Solvent Quality, and Selectivity

Microphase separation of binary mixed A/B polymer brushes exposed to different solvents is studied using Single-Chain-in-Mean-Field simulations. Effects of solvent quality and selectivity, grafting density, composition, and chain-length asymmetry are systematically investigated, and diagrams of morphologies in various solvents are constructed as a function of grafting density and composition or chain-length asymmetry. The structure of the microphase segregated morphologies lacks long-range periodic order, and it is analyzed quantitatively Using Minkowski measures.

Preparation and Characterization of Melt Grafting 2-acrylamido-2-methyl-1-propanesulfonic Acid onto Pre-Irradiated Linear Low Density Polyethylene

Linear low density polyethylene (LLDPE) was functionalized with 2-acrylamido-2-methyl-1-propanesulfonic acid (AMPS) by using -ray pre-irradiation in air in a twin-screw extruder. Fourier-transformed infrared spectroscopy (FT-IR) and electron spectroscopy for chemical analysis (ESCA) were used to characterize the formation of LLDPE-g-AMPS copolymers. The content of AMPS in LLDPE-g-AMPS was determined by using element analysis instrument. The effects of concentrations of monomer, reaction temperature and pre-irradiation dose on degree of grafting were investigated. The critical surface tension of LLDPE-g-AMPS was measured by using contact angle method. The influences of the degree of grafting on crystallization properties were studied by using DSC. Compared with neat LLDPE, the crystallization temperature increased about 4C, and crystallinity decreased with increasing degree of grafting. Crystallization rates of grafted LLDPE were faster than that of plain LLDPE at the same crystallization temperature.

Preparation and Bioactivity of the Composite of PLGA and Hydroxyapatite Nanocrystals Surface-grafted with L-lactic Acid Oligomer

The hydroxyapatite (HA) nanocrystals of 100-200 nm in length and 20-30 nm in width were hydrothermally synthesized by the reaction of phosphoric acid and calcium hydroxide. Lactic acid oligomer surface grafted HA(op-HA) nanoparticles were obtained by oligomeric lactic acid with a certain molecular weight grafting onto the HA surface to form a Ca carboxylate bond in the absence of any catalyst. The op-HA was further blended with poly(lactide-co-glycolide) (PLGA) to prepare the nanocomposite of op-HA/PLGA. FTIR, TGA, ESEM and EDX were used to analyze grafting reaction, the graft ratio of op-HA, surface topography and calcium deposition of the composites, respectively. The rabbit osteoblasts were seeded and cultured on the surface of composites in vitro. The cell morphology, adhesion, proliferation and gene expression were evaluated with FITC staining, NIH image J software and the analysis of real-time PCR, respectively. The results show that the graft ratio of op-HA is 8.3% (mass fraction). The op-HA/PLGA nanocomposite possessed more suitable surface properties, including roughness and plenty of calcium and phosphor. It exhibited better cell adhesion, spreading and proliferation of rabbit osteoblasts, compared to pure PLGA.

Bifunctional magnetic-optical nanocomposites: Grafting lanthanide complex onto core-shell magnetic silica nanoarchitecture

Anew class of bifunctional architecture combining the useful functions of superparamagnetism and terbium complex luminescence into one material has been prepared via two main steps by a modified Stober method and the layer-by-layer (LbL) assembly technique. The obtained bifunctional nanocomposites exhibit superparamagnetic behavior, high fluorescence intensity, and color purity. The architecture has been characterized by field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), UV-vis absorption and emission spectroscopy, X-ray diffraction, and superconducting quantum interference device (SQUID) magnetometry.

Patterned self-adaptive polymer brushes by "grafting to" approach and microcontact printing

Patterned self-adaptive PS/P2VP mixed polymer brushes were prepared by "grafting to" approach combining with microcontact printing (muCP). The properties of the patterned surface were investigated by lateral force microscopy (LFM), XPS and water condensation figures. In the domains with grafted P2VP, the PS/P2VP mixed brushes demonstrated reversible switching behavior upon exposure to selective solvents for different components. The chemical composition of the top layer as well as the surface wettability can be well tuned due to the perpendicular phase segregation in the mixed brushes. While in the domains without grafted P2VP, the grafted PS did not have the capability of switching. The development and erasing of the pattern is reversible under different solvent treatment.

Acid-stable amperometric soybean peroxidase biosensor based on a self-gelatinizable grafting copolymer of polyvinyl alcohol and 4-vinylpyridine

A peroxidase was extracted from Chinese soybean seed coat, and its thermostability and acid-stability were characterized. This peroxidase was immobilized into a self-gelatinizable grafting copolymer of polyvinyl alcohol with 4-vinylpyridine(PVA-g-PVP) to construct an acid-stable hydrogen peroxide biosensor. The effect of pH was studied for optimum analytical performances by amperometric and spectro-photometric methods, also the K-m(app) and the stability of the soybean peroxidase-based biosensor are discussed. At pH 3.0, the soybean peroxidase maintained its bioactivity and the enzyme electrode had a linear range from 0.01 to 6.2 mM with a detection limit of 1.0 x 10(-7) M. In addition, the main characteristics of different hydrogen peroxide sensors were compared.

PLASMA-INDUCED GRAFTING OF STYRENE ONTO NASCENT POLYETHYLENE POWDER

In this paper, the graft copolymers of styrene to nascent linear polyethylene reactor powders were prepared through plasma graft polymerization. The grafting reaction was initiated by the alkyl radicals formed on the surface of nascent polyethylene with plasma treatment as indicated by electron spin resonance spectra. In graft copolymerization by alkyl radicals, the grafting yield increased with either the plasma power or the plasma treatment lime. Compared with ordinary polyethylene powders, nascent polyethylene reactor powders were found to be more easily plasma-grafted. This has been attributed to the greater sensitivity to irradiation in producing reactive centres under the same conditions. High density polyethylene showed almost the same grafting yield as linear low density polyethylene at 50 degrees C. The surface morphology of nascent polyethylene observed by scanning electron microscope before and after the grafting showed that the silk-like fibrils were not destroyed by plasma treatment.