Porous ZnAl2O4 spinel nanorods doped with Eu3+: synthesis and photoluminescence

Eu3+-doped zinc aluminate (ZnAl2O4) nanorods with a spinel structure were successfully synthesized via an annealing transformation of layered precursors obtained by a homogeneous coprecipitation method combined with surfactant assembly. These spinel nanorods, which consist of much finer nanofibres together with large quantities of irregular mesopores and which possess a large surface area of 93.2 m(2) g(-1) and a relatively narrow pore size distribution in the range of 6 - 20 nm, are an ideal optical host for Eu3+ luminescent centres. In this nanostructure, rather disordered surroundings induce the typical electric-dipole emission (D-5(0) --> F-7(2)) of Eu3+ to predominate and broaden.

Magnetism and photoluminescence in manganese-gallium oxide nanowires with monoclinic and spinel structures

Manganese-gallium oxide nanowires were synthesized via in situ Mn doping during nanowire growth using a vapor phase evaporation method. The microstructure and composition of the products were characterized via transmission electron microscopy (TEM), field emission scanning electron microscopy (SEM), X-ray diffraction (XRD) and Raman spectroscopy. The field and temperature dependence of the magnetization reveal the obvious hysteresis loop and large magnitude of Curie-Weiss temperature. The photoluminescence of the manganese-gallium oxide nanowires were studied in a temperature range between 10 and 300 K. A broad green emission band was observed which is attributed to the T-4(1)-(6)A(1) transition in Mn2+ (3d(5)) ions. (c) 2005 Elsevier B.V. All rights reserved.

The influence of the microstructure evolution on the surface morphology in the annealing process of helium-implanted spinel

Single-crystalline spinel (MgAl2O4) specimens were implanted with helium ions of 100 keV at three successively increasing fluences of (0.5, 2.0 and 8.0) x 10(16) ions/cm(2) at room temperature. The specimens were subsequently annealed in vacuum at different temperatures ranging from 500 to 1100 degrees C. Different techniques, including Fourier transformed infrared spectroscopy (FTIR), thermal desorption spectrometry (TDS), atomic force microscopy (AFM) and scanning electron microscopy (SEM) were used to investigate the specimens, It was found that the absorbance peak in the FTIR due to the stretching vibration of the Al-O bond shifts to smaller wave numbers with increasing fluence, shifting back to larger wave numbers with an increase of annealing temperature. The absorbance peak shift has a linear relationship with the fluence increase in the as-implanted state, while it does not have a linear relationship with the fluence increase after the annealing process. Surface deformation occurred in the specimens implanted with fluences of 2.0 and 8.0 x 10(16) ions/cm(2) in the annealing process. The phenomena described above can be attributed to differences in defect formation in the specimens. (C) 2008 Elsevier B.V. All rights reserved.

The annealing behavior of Cu nanoparticles in Ar-ion implanted spinel

Magnesium aluminate spinel crystals (MgAl2O4 (1 1 0)) deposited with 30 nm Cu film on surface were implanted with 110 key Ar-ions to a fluence of 1.0 x 10(17) ions/cm(2) at 350 degrees C, and then annealed in vacuum condition at the temperature of 500, 600, 700, 800 and 900 degrees C for 1 h, respectively. Ultraviolet-visible spectrometry (UV-VIS), scanning electron microscopy (SEM), Rutherford backscattering (RBS) and transmission electron microscopy (TEM) were adopted to analyze the specimens. After implantation, the appearance of surface plasmon resonance (SPR) absorbance peak in the UV-VIS spectrum indicated the formation of Cu nanoparticles, and the TEM results for 500 degrees C also confirmed the formation of Cu nanoparticles at near-surface region. In annealing process, The SPR absorbance intensity increased at 500 and 700 degrees C, decreased with a blue shift of the peak position at 600 and 800 degrees C, and the peak disappeared at 900 degrees C. The SPR absorbance intensity evolution with temperature was discussed combined with other measurement results (RBS, SEM and TEM). (C) 2010 Elsevier B.V. All rights reserved.

Enhanced nucleation of Ag nanoparticles by vacancy-type defects in Ar-ions implanted spinel

Vacancy-type defects are introduced into magnesium aluminate spine] (MgAl2O4 (1 1 0)) by Ar-ions implantation, and then Ag-ions are implanted into the depth rich in vacancy-type defects. The ultraviolet-visible spectrometry (UV-VIS) and positron annihilation spectroscopy (PAS) are used to study the influence of vacancy-type defects on nucleation of Ag nanoparticles. After introduction of vacancy-type defects the pronounced increase of surface plasmon resonance (SPR) absorbance intensity indicates that defects enhance the nucleation of Ag nanoparticles. The PAS results reveal that vacancy-type defects provide pre-nucleating centers for Ag nanoparticles nucleation and growth. (C) 2010 Elsevier B.V. All rights reserved.

Electrochemical behaviour of spinel LiMn2O4 as positive electrode in rechargeable lithium cells

The spinel, lithium intercalation compound LiMn2O4 is prepared and studied using the techniques of a.c. impedance and cyclic voltammetry. The impedance behaviour of the LiMn2O4 electrode varies as lithium ions are intercalated or de-intercalated. The reversible behaviour of lithium ions in the LiMn2O4 electrode is confirmed by the results of cyclic voltammetry.

STUDIES OF SPINEL LICRXMN2-XO4 FOR SECONDARY LITHIUM BATTERY

X-ray and electrochemical studies of spinel-related manganese chromium oxides, LiCrxMn2-xO4 (0 less-than-or-equal-to x less-than-or-equal-to 1) were carried out in a lithium nonaqueous cell. X-ray diffraction spectra indicated that the substitution of manganese in LiMn2O4 by trivalent transition metals (Cr3+) cause the linear decrease of lattice parameter with the x in the LiCrMn2-xO4. Some discharge-capacity loss was obtained due to the lattice contraction of LiCrMn2-xO4, but it has a better rechargeability than LiMn2O4. Cyclic voltammetry and electrochemical impedance experiments have shown that the excellent rechargeability of LiCrxMn2-xO4 may be attributed to the good reversibility of the change in its crystal structure for the insertion and extraction of lithium ions.

Mesoporous spinel MgAl2O4 prepared by in situ modification of boehmite sol particle surface: I Synthesis and characterization of the unsupported membranes

Mesoporous spinel membranes as ultrafiltration membranes were prepared through a novel sol-gel technique. By in situ modification of the sol particle surface during the sol-gel process, control of the material structure on a nanometer scale from the earliest stages of processing was realized. Nano-particles with a chocolate-nut-like morphology, i.e. spinel MgAl2O4 as a shell and gamma -Al2O3 as a core, were first revealed by HRTEM results. The formation of the spinel phase was confirmed by X-ray diffraction (XRD). N-2 adsorption-desorption results showed that the mesoporous membranes had a narrow pore size distribution. (C) 2001 Elsevier Science B.V. All rights reserved.

Enhanced luminescence from transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics by Ga2O3 addition

Transparent Ni2+-doped MgO-Al2O3-SiO2 glass ceramics without and with Ga2O3 were synthetized. The precipitation of spinel nanocrystals, which was identified as solid solutions in the glass ceramics, could be favored by Ga2O3 addition and their sizes were about 7.6 nm in diameter. The luminescent intensity of the Ni2+-doped glass ceramics was largely enhanced by Ga2O3 addition which could mainly be caused by increasing of Ni2+ in the octahedral sites and the reduction of the mean frequency of phonon density of states in the spinel nanocrystals of solid solutions. The full width at half maximum (FWHM) of emissions for the glass ceramics with different Ga2O3 content was all more than 200 nm. The emission lifetime increased with the Ga2O3 content and the longest lifetime is about 250 mu s. The Ni2+-doped transparent glass ceramics with Ga2O3 addition have potential application as broadband optical amplifier and laser materials. (C) 2007 Elsevier Ltd. All rights reserved.

Magnetic properties of ZnO-doped cobalt ferrite

The cobalt ferrites with chemical composition Co1+xZnxFe2-2xO4 (r=0.0, 0.1, 0.2, 0.4) were obtained with conventional solid reaction. The ZnO-doped samples have lower lattice constant than CoFe2O4 by adjusting Co ions to the octahedral sites. The results show that doping ZnO could extremely improve the magnetic properties. In comparison with pure CoFe2O4, the little ZnO-doped sample has higher permeability and much lower coercivity at the condition of a little decrease of magnetization saturation. Sample with x=0.1 shows evident magnetostrictive effect at the magnetic field of 30-60 mT while pure cobalt ferrite sample does not, though the saturation magnetostriction decreases. These indicate that ZnO-doping improves the magnetostrictive sensitivity of the cobalt ferrites and have potential applications in magnetoelectric devices and magnetic detector.

Magnetic properties of ZnO-doped cobalt ferrite

The cobalt ferrites with chemical composition Co1+xZnxFe2-2xO4 (r=0.0, 0.1, 0.2, 0.4) were obtained with conventional solid reaction. The ZnO-doped samples have lower lattice constant than CoFe2O4 by adjusting Co ions to the octahedral sites. The results show that doping ZnO could extremely improve the magnetic properties. In comparison with pure CoFe2O4, the little ZnO-doped sample has higher permeability and much lower coercivity at the condition of a little decrease of magnetization saturation. Sample with x=0.1 shows evident magnetostrictive effect at the magnetic field of 30-60 mT while pure cobalt ferrite sample does not, though the saturation magnetostriction decreases. These indicate that ZnO-doping improves the magnetostrictive sensitivity of the cobalt ferrites and have potential applications in magnetoelectric devices and magnetic detector.

MoNi/gamma-Al2O3 Catalyst: Preparation and Catalytic Activity for Acetic Acid Hydrotreating

MoNi/gamma-Al2O3 catalysts were prepared by the impregnation method. The catalyst samples were characterized by XRD and TPR. The effects of Mo promoter content and the catalyst reducing temperature Oil hydrotreatment activity of the catalyst were studied under 200 degrees C and 3 MPa hydrogen pressure using acetic acid as the model compound. The XRD results indicate that the addition of Mo promoter is beneficial to the uniformity of nickel species on the catalyst and decreases the Interaction between nickel species and the support Which results in the decrease the of NiAl2O4 spinel formation. The addition of Mo promoter also decreases the reducing temperature of the catalyst. After the catalyst of 0.06 MoNi/gamma-Al2O3 being reduced Under the atmosphere of H-2/N-2(5/95, V/V), nickel oxide was reduced to Ni-0. The reaction was promoted obviously upon the addition of the MoNi/gamma-Al2O3 catalyst reduced at 600 degrees C. The Mo-modified Ni/gamma-Al2O3 catalyst reduced at 600 degrees C displayed the highest activity during the reaction, the conversion of acetic acid reached the highest point of 33.2%. The products included ethyl acetate and water.