Effects of process on microstructure and properties of translucent Dy-alpha-SiAlON sintered at lower temperatures

Hot pressing (HP) at higher sintering temperature has been a traditional and prevalent technique for the fabrication of alpha-SiAlON. In order to prepare translucent SiAlON more easily, LiF was used as a non-oxide sintering additive to lower the sintering temperature to <= 1650 degrees C. As a result, all of the samples possessed a good hardness and fracture toughness. At the same time, the lower temperature sintered samples showed a higher optical transmittance in the range of 2.5-5.5 mu m wavelength (0.5 mm in thickness). The maximum infrared transmission reached 68% at a wavelength of 3.3 mu m. The present work shows that the sintering process has a strong effect on microstructure and property of alpha-SiAlON. To be exact, a lower sintering temperature and longer holding time can produce some fully-developed microstrcture, which is beneficial for the optical transmittance. (C) 2008 The Ceramic Society of Japan. All rights reserved.

凝胶-燃烧法合成YAG：Eu^3＋纳米荧光材料的结构和发光性能

Y3Al5O12:Eu nanophosphors were synthesized by a gel combustion method. The structure of phosphors was characterized by XRD and FTIR. YAG phase came to occur when YAG:Eu precursors were sintered at 800 ℃, although the phase was mainly amorphous. The organ

Influence of Fe3+ on perovskite oxides: La2/3Ca1/3Mn1-xFexO3

The structure and magnetoresistance properties in sintered samples of La-2/3 Ca-1/3 Mn1-x FexO3 (0 less than or equal to x less than or equal to 0.84) are studied by using Mossbauer spectroscopy, XRD and magnetic measurement. There are antiferromagnetic interactions between Fe and its nearest neighbors (Fe, Mn) when 0 less than or equal to x less than or equal to 0.67, which are important factors influencing the double-exchange between Mn3+ and Mn4+, Curie temperature, magnetic moment and GMR. It is suggested that the Mn3+(Fe3+)/Mn4+ system also consists of magnetic clusters with different sizes.

Structure and impedance of ZrO2 doped with SC2O3 and CeO2

Scandia and ceria doped zirconia samples, with 10 mol% SC2O3 and different content of CeO2, were synthesized and characterized. The XRD results depict that the sintered samples have a cubic phase structure. However, Raman spectra show that besides the main cubic phase, a secondary phase is also present in the sintered samples. The addition of CeO2 can raise the content of the cubic phase, but the minor metastable tetragonal phase (t'-phase) exists even at the CeO2 content as high as 10 mol%. The near-UV Raman spectra indicate that the deformed tetragonal structure predominates at the grain boundary. The addition of CeO2 can reduce the impurity at grain boundary, and no impurity can be found by near-UV Raman spectroscopy at the grain boundary of the samples with high CeO2 content. The impedance measurements show that with the increase of CeO2 content, the impedance of grain boundary decreases and the bulk impedance increases. The low impedance of grain boundary can be attributed to the formation of a clean grain boundary upon CeO2 doping, and the increase of the bulk impedance is due to the blocking effect of the large Ce(IV) ions. (c) 2005 Elsevier B.V All rights reserved.

High-pressure sintered yttria stabilized zirconia ceramics

Fast densification of 8YSZ ceramics under a high pressure of 4.5 GPa was carried out at different temperatures (800, 1000, 1450 degrees C), by which a high relative density above 92% could be obtained. FT-Raman spectra indicate that the 8YSZ underwent a phase transition from partially tetragonal to partially cubic phase as temperatures increase from 1000 to 1450 degrees C when sintering under high pressure. The electrical properties of the samples under different high-pressure sintering conditions were measured by complex impedance method. The total conductivity of 0.92 x 10(-2) S cm(-1) at 800 degrees C has been obtained for 8YSZ under high pressure at 1450 degrees C, which is about 200 degrees C lower than that of the samples prepared by conventional pressureless sintering.

Real-Time Measurement on Deformation Fields of Hole-Excavated Samples under Impact Tension

In this paper, the real-time deformation fields are observed in two different kinds of hole-excavated dog-bone samples loaded by an SHTB, including single hole sample and dual holes sample with the aperture size of 0.8mm. The testing system consists of a high-speed camera, a He-Ne laser, a frame grabber and a synchronization device with the controlling accuracy of I microsecond. Both the single hole expanding process and the interaction of the two holes are recorded with the time interval of 10 mu s. The observed images on the sample surface are analyzed by newly developed software based on digital correlation theory and a modified image processing method. The 2-D displacement fields in plane are obtained with a resolution of 50 mu m and an accuracy of 0.5 mu m. Experimental results obtained in this paper are proofed, by compared with FEM numerical simulations.

Real-Time Measurement on Deformation Fields of Notched Samples Under Impact Tension

In this paper, a real-time and in situ optical measuring system is reported to observe high-velocity deformations of samples subjected to impact loading. The system consists of a high-speed camera, a He-Ne laser, a frame grabber, a synchronization device and analysis software based on digital correlation theory. The optical system has been adapted to investigate the dynamic deformation field and its evolution in notched samples loaded by an split Hopkinson tension bar, with a resolution of 50 pin and an accuracy of 0.5 mum. Results obtained in experiments are discussed and compared with numerical simulations. It is shown that the measuring system is effective and valid.

Magnetic properties of sintered sm2fe17ny magnets

Sintered magnets of Sm2Fe17Ny nitrides, with a density of 6.0-7.4 g/cm3, have been prepared by using an explosion technique. Both crystalline structure and the magnetic properties of Sm2Fe17Ny nitrides were retained in the process. The sintered magnet had a remanence B(r)=0.83 T, an intrinsic coercivity mu(0i)H(c)=0.57 T and an energy product (BH)max=88 kJ/m3. The temperature dependence of coercivity and remanence were also measured. The temperature coefficients alpha of remanence and beta of coercivity are -0.076%/degrees-C and -0.51%/degrees-C, respectively.

Real-Time Measurement on Deformation Fields of Hole-Excavated Samples under Impact Tension

In this paper, the real-time deformation fields are observed in two different kinds of hole-excavated dog-bone samples loaded by an SHTB, including single hole sample and dual holes sample with the aperture size of 0.8mm. The testing system consists of a high-speed camera, a He-Ne laser, a frame grabber and a synchronization device with the controlling accuracy of I microsecond. Both the single hole expanding process and the interaction of the two holes are recorded with the time interval of 10 mu s. The observed images on the sample surface are analyzed by newly developed software based on digital correlation theory and a modified image processing method. The 2-D displacement fields in plane are obtained with a resolution of 50 mu m and an accuracy of 0.5 mu m. Experimental results obtained in this paper are proofed, by compared with FEM numerical simulations.

Effect of La2O3 on microstructure and transmittance of transparent alumina ceramics

Optically transparent alumina ceramics were fabricated by conventional process and sintered without pressure in H-2 atmosphere. The results indicate that relative densities of alumina specimens increase to theoretical densities (T. D.) with increasing content of La2O3. With increasing holding time during sintering, much less pores and larger grains were found in the sintered alumina samples. Higher transmittance was achieved in alumina codoped with MgO and La2O3 as compared with that doped with MgO only. The total-transmittance of alumina sample is up to 86% at a wavelength range of 300 - 800 nm.

Diode-pumped passively q-switched Nd : YAG ceramic laser with a Cr4+: YAG crystal-satiable absorber

Transparent polycrystalline Nd:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3,Y2O3, and Nd2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1750 degrees C in vacuum. Transparent fully dense samples with average grain sizes of 10 mu m were obtained. The 1 at.% Nd:YAG ceramic was used to research passively Q-switched laser output with a Cr4+:YAG crystal as a saturable absorber. An average output power of 94 mW with a pulse width of 50 ns was obtained when the incident pump power was 750 mW. The slope efficiency was 13%. The pulse energy is 5 mu J, and the peak power is about 100 W.

Diode-pumped Yb : YAG ceramic laser

Transparent polycrystalline Yb:YAG ceramics were fabricated by solid-state reactive sintering a mixture of commercial Al2O3, Y2O3, and Yb2O3 powders. The powders were mixed in ethanol and doped with 0.5 wt% tetraethoxysilane, dried, and pressed. Pressed samples were sintered at 1730 degrees C in vacuum. Transparent fully dense samples with grain sizes of several micrometers were obtained. The phase from 1500 degrees to 1700 degrees C was important for the grain growth, in which the grains grew quickly and a mass of pores were eliminated from the body of the sample. Annealing was an important step to remove the vacancies of oxygen and transform Yb2+ to Yb3+. The 1 at.% Yb:YAG ceramic sample was pumped by a diode laser to study the laser properties. The maximum output power of 1.02 W was obtained with a slope efficiency of 25% at 1030 nm. The size of the lasering sample was 4 mm x 4 mm x 3 mm.

Phylogenetic study of complete cytochrome b genes in musk deer (genus Moschus) using museum samples

As an endangered animal group, musk deer (genus Moschus) are not only a great concern of wildlife conservation, but also of special interest to evolutionary studies due to long-standing arguments on the taxonomic and phylogenetic associations in this group. Using museum samples, we sequenced complete mitochondrial cytochrome b genes (1140 bp) of all suggested species of musk deer in order to reconstruct their phylogenetic history through molecular information. Our results showed that the cytochrome b gene tree is rather robust and concurred for all the algorithms employed (parsimony, maximum likelihood, and distance methods). Further, the relative rate test indicated a constant sequence substitution rate among all the species, permitting the dating of divergence events by molecular clock. According to the molecular topology, M. moschiferus branched off the earliest from a common ancestor of musk deer (about 700,000 years ago); then followed the bifurcation forming the M. berezouskii lineage and the lineage clustering M. fuscus, M. chrysogaster, and M. leucogaster (around 370,000 years before present), interestingly the most recent speciation event in musk deer happened rather recently (140,000 years ago), which might have resulted from the diversified habitats and geographic barriers in southwest China caused by gigantic movements of the Qinghai-Tibetan Plateau in history. Combining the data of current distributions, fossil records, and molecular data of this study, we suggest that the historical dispersion of musk deer might be from north to south in China. Additionally, in our further analyses involving other pecora species, musk deer was strongly supported as a monophyletic group and a valid family in Artiodactyla, closely related to Cervidae. (C) 1999 Academic Press.