67 resultados para Scanning Electronic Mirror
em Chinese Academy of Sciences Institutional Repositories Grid Portal
Resumo:
研究了温度梯度法生长的γ-LiAlO2晶体在1100℃不同气氛处理的热稳定性。借助扫描电子显微镜和X射线衍射分析发现:1100℃/10h真空和空气处理后的样品表面分别形成了均匀微孔状和岛状LiAl5O8多晶;而富Li气氛处理后样品表面仍然光滑且仍为LiAlO2。用Leitz大视场显微镜观察重新抛光后样品内部宏观缺陷,发现空气和真空处理后样品缺陷增多,分别为岛状和条纹状缺陷;而富Li气氛处理后样品中缺陷明显减少。对比不同气氛处理的4块样品吸收光谱,确认了真空和空气处理产生的196nm吸收峰可能是Li空位吸收
Resumo:
Glass transition and crystallization process of bulk Nd60Al10Fe20Co10 metallic glass were investigated by means of dynamic mechanical thermal analysis (DMTA), differential scanning calorimetry (DSC), X-ray diffraction (XRD) and scanning electronic microscopy (SEM). It is shown that the glass transition and onset crystallization temperature determined by DMTA at a heating rate of 0.167 K/s are 480 and 588 K respectively. The crystallization process of the metallic glass is concluded as follows: amorphous alpha-->alpha' + metastable FeNdAl novel phase -->alpha' + primary delta phase-->primary delta phase + eutectic delta phase Nd3Al phase + Nd3Co phase. The appearance of hard magnetism in this alloy is ascribed to the presence of amorphous phase with highly relaxed structure. The hard magnetism disappeared after the eutectic crystallization of amorphous phase.
Resumo:
Ultrasonic fractography and scanning electronic microscopy (SEM) are used to determine the direct relationship between the fracture surface morphology and the main crack velocity during the rapid rupture of polymethylmethacrylate (PMMA). Two critical crack velocities are found for the fracture. Quasi-parabolic markings will appear when the crack speed exceeds the first critical speed. Crack propagating at speed above the second critical speed leaves a thicket of small branches penetrating the surface behind them. Both critical speeds are functions of the thickness of the specimens.
Resumo:
Glass transition and thermal stability of bulk Nd60Al10Fe20Co10 metallic glass were investigated by means of dynamic mechanical thermal analysis (DMTA), differential scanning calorimetry (DSC), X-ray diffraction (XRD) and scanning electronic microscopy (SEM). The glass transition temperature, not revealed by DSC, is alternatively determined by DMTA via storage modulus E' and loss modulus E" measurement to be 498 K at a heating rate of 0.167 K s (-1). The calculated reduced glass transition temperature (T-g/T-m) is 0.63. The large value of T-g/T-m of this alloy is consistent with its good glass-forming ability. The crystallization process of the metallic glass is concluded as follows: amorphous --> amorphous + metastable FeNdAl phase --> amorphous + primary delta-FeNdAl phase --> primary delta-phase + eutectic delta-phase + Nd3Al + Nd3Co. The appearance of hard magnetism in this alloy is ascribed to the presence of amorphous phase with highly relaxed structure. The hard magnetism disappeared after the eutectic crystallization of the amorphous phase. (C) 2002 Elsevier Science B.V. All rights reserved.
Resumo:
Two-dimensional ZnO nanowall networks were grown on ZnO-coated silicon by thermal evaporation at low temperature without catalysts or additives. All of the results from scanning electronic spectroscope, X-ray diffraction and Raman scattering confirmed that the ZnO nanowalls were vertically aligned and c-axis oriented. The room-temperature photoluminescence spectra showed a dominated UV peak at 378 nm, and a much suppressed orange emission centered at similar to 590 nm. This demonstrates fairly good crystal quality and optical properties of the product. A possible three-step, zinc vapor-controlled process was proposed to explain the growth of well-aligned ZnO nanowall networks. The pre-coated ZnO template layer plays a key role during the synthesis process, which guides the growth direction of the synthesized products. (C) 2007 Elsevier B.V. All rights reserved.
Resumo:
The ablation in zinc selenide (ZnSe) crystal is studied by using 150-fs, 800-nm laser system. The images of the ablation pit measured by scanning electronic microscope (SEM) show no thermal stress and melting dynamics. The threshold fluence is measured to be 0.7 J/cm2. The ultrafast ablation dynamics is studied by using pump and probe method. The result suggests that optical breakdown and ultrafast melting take place in ZnSe irradiated under femtosecond laser pulses.
Resumo:
利用具有纳焦能量、高重复频率的偏振光飞秒双脉冲对金属铬膜样品进行微加工,样品表面都会产生微突起状结构,它们的宽度在0~400 ps的双脉冲时延范围内没有明显的变化,但高度却都在1~10 ps的双脉冲时延范围内呈现明显的下降,在此时延范围之外并没有明显的变化。通过加工样品的扫描电子显微镜(SEM)图片发现,对于偏振光,利用双脉冲方法,可以获得更好的加工质量。并且线偏振光得到的微突起状结构比较细长,在入射光束的偏振方向上有所伸长;圆偏振光得到的微突起状结构比较接近圆形。即在低脉冲能量、高重复频率情况下,具体的微加工特征形貌与入射光束的偏振状态有关。
Resumo:
使用倾斜角沉积(GLAD)的电子束蒸发技术,制备了倾斜角度在60°~85°之间的ZnS双折射雕塑薄膜(STF)。使用X射线衍射(XRD)和扫描电镜(SEM)检测了ZnS薄膜的结晶状态和断面形貌,使用Lamda-900分光光度计测量了薄膜在不同的偏振光入射时的透过率。研究发现,室温下倾斜沉积ZnS薄膜断面为倾斜柱状结构,且薄膜的结晶程度不高。在相同的监控厚度时,随倾斜角度增大,沉积到基片上的薄膜厚度逐渐变小,但仍然大于余弦曲线显示的理论厚度。根据偏振光垂直入射时薄膜的透过光谱计算了不同角度沉积的薄膜的折射率
Resumo:
Redescription of Balantidium polyvacuolum Li 1963, collected from the hindgut of Xenocypris davidi and Xenocypris argentea, from Niushan Lake Fishery (30A degrees 19' N, 114A degrees 31' E) in Wuhan City, Hubei Province, China in April and June 2007 is presented in this paper to complete Li's description at both light and scanning electronic microscopic levels. The unique body shape of B. polyvacuolum-highly arched dorsal side and flattened ventral surface-as well as its remarkable concave platelet present in the centroventral were well described and compared with other close Balantidium species. Besides, two types of vestibulum shape are observed in our present work, which may suggest the existence of two subspecies or genotype species of these balantidia.
Resumo:
Two types of microfabrics relating to pollutant adsorption were studied in the scanning electronic microscope (SEM) in a polluted, eutrophic lake, the Yangtze delta region. Agglutinational texture or the aggregates of small particles are composed of clay minerals and fine organic fragments among the silty grains and the coatings with a thickness about 1 mu m were on the surfaces of the silty grains in the sediments. The chemical constituents of the aggregates and the coatings are K, Na, Ca, Mg, Si, Al, O, Fe, Ti, C, N and P determined in X-ray energy spectrometry connected with the SEM. In some cases, Pb was detected in the aggregates in the top sediment. It is suggested that nutrients and metals are adsorbed to the aggregates, which were formed by electrostatic attraction of physicochemical floes. The coatings on the surface of quartz grains were formed by the interaction of dissociated Al, Si, Fe, etc from silicates with dissolved N, P and C nutrients in interstitial water, which was aroused by human pollution to the lake in recent two decades.
Resumo:
Thick GaN films of high quality are directly grown on wet-etching patterned sapphire in a vertical hydride vapour phase epitaxy reactor. The optical and structural properties of GaN films are studied using scanning electronic microscopy and cathodoluminescence. Test results show that initial growth of hydride vapour phase epitaxy GaN occurs not only on the mesas but also on the two asymmetric sidewalls of the V-shaped grooves without selectivity. After the two-step coalescence near the interface, the GaN films near the surface keep on growing along the direction perpendicular to the long sidewall. Based on Raman results, GaN of the coalescence region in the grooves has the maximum residual stress and poor crystalline quality over the whole GaN film, and the coalescence process can release the stress. Therefore, stress-free thick GaN films are prepared with smooth and crack-free surfaces by this particular growth mode on wet-etching patterned sapphire substrates.
Resumo:
Two-dimensional ZnO nanowall networks were grown on ZnO-coated silicon by thermal evaporation at low temperature without catalysts or additives. All of the results from scanning electronic spectroscope, X-ray diffraction and Raman scattering confirmed that the ZnO nanowalls were vertically aligned and c-axis oriented. The room-temperature photoluminescence spectra showed a dominated UV peak at 378 nm, and a much suppressed orange emission centered at similar to 590 nm. This demonstrates fairly good crystal quality and optical properties of the product. A possible three-step, zinc vapor-controlled process was proposed to explain the growth of well-aligned ZnO nanowall networks. The pre-coated ZnO template layer plays a key role during the synthesis process, which guides the growth direction of the synthesized products. (C) 2007 Elsevier B.V. All rights reserved.
Resumo:
Surface micro-roughness, surface chemical properties, and surface wettability are three important aspects of wafer surfaces during a wafer cleaning process, which determine the bonding quality of ordinary direct wafer bonding. In this study, InP wafers are divided into four groups and treated by different chemical processes. Subsequently, the characteristics of the treated InP surfaces are carefully studied by X-ray photoelectron spectroscopy (XPS), atomic force microscopy (AFM), and contact angle measurements. The optimal wafer treatment method for wafer bonding is determined by comparing the results of the processes as a whole. This optimization is later evaluated by a scanning electronic microscope (SEM), and the ridge waveguide 1.55 mu m Si-based InP/InGaAsP multi-quantum-well laser chips are also fabricated. (c) 2005 Elsevier B.V. All rights reserved.
Resumo:
The microstructure and mechanical properties of beta-nucleated iPP before and after being annealed at different temperatures (90-160 degrees C) have been analyzed, Annealing induced different degrees of variation in fracture toughness of beta-nucleated iPP samples. namely, slight enhancement at relatively low annealing temperatures (< 110 degrees C) and great improvement at moderate temperatures (120-130 degrees C), whereas dramatic deterioration at relatively high temperatures ( > 140 degrees C) has been observed. The variation of fracture toughness of beta-nucleated iPP is observed to be dependent on the content of beta-NA. Experiments, including scanning electronic microscope (SEM), wide-angle X-ray diffraction (WAXD), differential scanning calorimetry (DSC), small-angle X-ray scattering (SAXS), and dynamic mechanical analysis (DMA), are performed to study the variations of microstructures as well as the toughening mechanism of the beta-nucleated iPP after being annealed.
Resumo:
Preparation of poly(vinylidene fluoride-co-hexafluoro propylene) (F2.6) flat-sheet asymmetric porous membrane has been studied for the first time. Factors affecting F2.6 membrane pore structure and permeate performance, such as macromolecule pore formers (polyethylene glycol-400, 1000, 1540, 2000 and 6000), the small molecule former (glycerol), swelling agent (trimethyl phosphate) in casting solution, precipitating bath component and temperature, exposure time and ambient humidity, were investigated in detail. Average pore radius and porosity were used to characterize F2.6 membrane structure, and respectively, determined by ultrafiltration and gravimetric method for the wet membrane. Morphology of the resultant membranes was observed by scanning electronic microscopy (SEM). Final test on permeate performance of F2.6 porous membrane was carried out by a direct contact membrane distillation (DCMD) setup. The experimental F2.6 membrane exhibits a higher distilled flux than PVDF membrane under the same operational situations. The determination of contact angle to distilled water also reveals higher hydrophobic nature than that of PVDF membrane.